Abstract
Three amphiphilic peroxophosphomolybdates [C4mim]3PMo4O24, [C8mim]3PMo4O24 and [C16mim]3PMo4O24 were synthesized and characterized. These catalysts were used for extraction and catalytic oxidative desulfurization of fuel with H2O2 as an oxidant and ionic liquid [C4mim]BF4 as an extractant. It was found that [C16mim]3PMo4O24 showed the highest catalytic activity and the sulfur content could decrease to 7.5 ppm. In contrast, the desulfurization system shows very low performance without H2O2 or ionic liquid. The detailed reaction conditions were optimized including reaction time, temperature, the dosage of H2O2 and catalyst, and different sulfur compounds. After the reaction, the catalysts and the ionic liquid can be cycled 8 times with a little decrease in desulfurization efficiency.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Avoid common mistakes on your manuscript.
1 Introduction
The combustion of sulfur-containing compounds in fuel oils produces a large amount of sulfur oxides, which are major air pollutants (Zhang et al. 2018; Hou et al. 2018). In the recent years, deep desulfurization of fuel oils has attracted worldwide interests due to the growing environmental concerns. Although the traditional hydrodesulfurization (HDS) can remove aliphatic sulfur compounds, it is less effective in removing alkyl-substituted aromatic sulfur compounds such as dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) (Jiang et al. 2017a, b; Li et al. 2018). At present, the possible tactics to improve desulfurization efficiency include adsorptive desulfurization (Yang et al. 2018; Nejad and Beigi 2015), extractive desulfurization (Raj et al. 2018; Jiang et al. 2015) and oxidative desulfurization (Jiang et al. 2014a, b; Yang et al. 2017).
Among these strategies, oxidative desulfurization combined with extraction shows a promising prospect owing to its high desulfurization efficiency (He et al. 2017; Lu et al. 2017; Hao et al. 2017; Xun et al. 2016; Zhang et al. 2014). In this approach, the sulfur compounds are firstly oxidized to the corresponding sulfones or sulfoxides, which can be removed by extraction with polar solvents. In the early stage, Li and his group reported emulsion systems with amphiphilic catalysts, showing high catalytic activity for oxidative desulfurization (Li et al. 2004; Zhang et al. 2012). However, the use of organic solvents after oxidation may do harm to the environment. Ionic liquids (ILs) are being explored as “green” substitutes for volatile organic solvents because of their low volatility (Dai et al. 2017; Sun and Zhao 2011). Recently, a one-step desulfurization system, ionic liquid extraction combined with oxidative desulfurization (EODS), has been widely studied (Zhang et al. 2017; Xu et al. 2017; Moghadam et al. 2017; Rafiee et al. 2016). In this process, the sulfur compounds are firstly extracted by ILs and oxidized by aqueous hydrogen peroxide in the IL phase. Compared with extractive desulfurization only by ILs, the system consisted of imidazolium-based ILs and H2O2–acetic acid and showed a great increase in desulfurization efficiency (Lo et al. 2003). However, a large amount of ILs and H2O2 are required, which increases the cost to the refinery.
In order to solve this problem, an efficient extraction and catalytic oxidative desulfurization (ECODS) system has been raised by our group (Jiang et al. 2014a, b, 2017a, b; Zhu et al. 2015; Wang et al. 2017). The aim of this system is to explore efficient catalysts and select suitable ILs as solvents. To date, several kinds of catalyst have been reported, e.g., polyoxometalates (Hao et al. 2015), tetrachloroferrates (Jiang et al. 2014a, b), iron porphyrins (Zhao et al. 2017) and metal oxide (Chen et al. 2017). However, there are few reports that focus on exploring peroxo-polyoxometalates as catalysts for oxidative desulfurization. In this work, three amphiphilic peroxophosphomolybdates were synthesized and characterized by elemental analysis, Fourier transformer infrared (FTIR), and thermogravimetric and differential scanning calorimetry (TG-DSC). It was found that [C16mim]3[PMo4O24] showed the best sulfur removal probably because of its long carbon chain. After optimizing the reaction conditions, the removal of DBT could get to 98.8% at 60 °C with [C4mim]BF4 IL as the extractant. In addition, the reaction system could be cycled at least for 8 times without a significant loss of desulfurization efficiency.
2 Experimental
2.1 Materials
All chemicals used were from commercial sources. Phosphomolybdic acid hydrate (H3PMo12O40·13H2O), 30 wt% H2O2, ether, ethanol, tetradecane and n-octane were supplied by Sinopharm Chemical Reagent. Dibenzothiophene (DBT), benzothiophene (BT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) were bought from Sigma-Aldrich. 1-butyl-3-methylimidazolium chloride ([C4mim]Cl), 1-octyl-3-methylimidazolium chloride ([C8mim]Cl), 1-hexadecyl-3-methylimidazolium chloride ([C16mim]Cl) and 1-butyl-3-methylimidazolium tetrafluoroborate ([C4mim]PF4) were obtained from Shanghai Chenjie Chemical Co. Ltd., China.
2.2 Characterization
Fourier transformer infrared (FTIR) spectrum was performed on a Nicolet 7100 spectrophotometer at room temperature. Determination of element content was recorded on an elemental analyzer (CHN-O-Rapid, Germany Heraeus Co. Ltd.). Thermogravimetric analysis was undertaken on a simultaneous thermal analyzer (STA-449C Jupiter, Germany NETZSCH Co. Ltd.)
2.3 Synthesis of [Cnmim]3PMo4O24 (n = 4, 8, 16)
Typically, 1 mmol H3PMo12O40·13H2O was dissolved in 10 mL H2O2 under continuous stirring. Then, a mixture of 40 mL H2O2 and 3.1 mmol [Cnmim]Cl (n = 4, 8, 16) was dropped into the above mixture solution, which was kept at 100 °C for 4 h. Subsequently, the sample was centrifuged and washed. The final products, [Cnmim]3[PMo4O24], were kept in a vacuum.
2.4 Desulfurization tests
The DBT, BT and 4,6-DMDBT were dissolved in n-octane and tetradecane was used as the internal standard. The content of DBT, BT and 4,6-DMDBT was 500 ppm, 250 ppm and 250 ppm, respectively.
The extractive desulfurization experiments were conducted in a double-neck flask with 1 mL ionic liquid IL and 5 mL model oil for 5 min under continuous stirring. With the addition of a certain amount of H2O2, 5 mL model oil and catalyst, the oxidative desulfurization process was performed. After the reaction, 1 μL of the oil phase (upper layer) was collected and analyzed by gas chromatography until the two phases were separated. The sulfur removal was used to indicate the desulfurization rate of the model oil. A gas chromatograph with a flame ionization detector (GC-FID) (Agilent 7890A; HP-5, 30 m × 0.32 mm × 0.25 μm) was used to investigate the content of sulfur-containing compounds in the model oil.
3 Results and discussion
3.1 Characterization
The results of the elemental analysis and the determination of the active oxygen content of the three catalysts are given in Table 1. The active oxygen content of the catalyst was determined by the following method: A certain amount of catalyst was added to 10 mL of DMF. Then, 5 mL of 0.5 mol L−1 H2SO4 was used to adjust the pH to 2.5. After that, 0.5 g KI and 3 drops of 3% ammonium molybdate solution were added to the above solution, which was kept in the shade for 5 min. Finally, the well-calibrated Na2S2O3 solution was used to titrate the above solution until the color was light yellow, and then 3 mL of 0.5% starch indicator was added to the solution, continuing dropping to the blue exactly disappeared. The mass percentage of active oxygen can be calculated by Eq. (1):
where c(Na2S2O3) is the concentration of Na2S2O3 solution, V(Na2S2O3) is the volume of consumed Na2S2O3 solution, and M(O22−) is the molecular weight of O22−. As given in Table 1, the experimental data of samples were similar to the theoretical calculation data.
The FTIR spectra of catalysts are given in Table 2. For [C4mim]3PMo4O24, the peaks at 956, 877, 589, 532, 1078 and 1062 cm−1 were assigned to Mo=O vibration, O–O vibration, Mo(O)2 asymmetrical stretching vibration, Mo(O)2 symmetrical stretching vibration and PO4 vibration, respectively. For [C8mim]3PMo4O24, the peaks at 957, 875, 592, 545 and 1062 cm−1 were assigned to Mo=O vibration, O–O vibration, Mo(O)2 asymmetrical stretching vibration, Mo(O)2 symmetrical stretching vibration and PO4 vibration, respectively. For [C16mim]3[PMo4O24], the peaks at 965, 873, 588, 543, 1071 and 1040 cm−1 were assigned to Mo=O vibration, O–O vibration, Mo(O)2 asymmetrical stretching vibration, Mo(O)2 symmetrical stretching vibration and PO4 vibration, respectively. The characteristic peaks of the catalysts were similar to the literature values (He et al. 2008).
The differential thermal analysis and thermogravimetric results of [C4mim]3[PMo4O24] are shown in Fig. 1. There was no mass loss of the catalyst below 100 °C, indicating that the catalyst did not contain crystal water. The sample exhibited weight loss between 158.0 and 202.4 °C, corresponding to the decomposition of peroxides groups. Above 305.8 °C, the main weight loss of catalyst was attributed to the decomposition of the cation [C4mim]+ and anion without peroxides groups. The final product may be molybdenum oxides. For [C8mim]3[PMo4O24] and [C16mim]3[PMo4O24] in Figs. 2 and 3, the stability of these catalysts showed a similar trend with increasing temperature in air.
3.2 The performance comparison among different desulfurization systems
As given in Table 3, the extractive efficiency was 13.6% with [C4mim]BF4 as an extractant. With the addition of H2O2 as the oxidant, the oxidative desulfurization efficiency was increased to 27.0%. When [C4mim]3PMo4O24, [C8mim]3PMo4O24 and [C16mim]3PMo4O24 were used as catalysts, the sulfur removal reached 87.5%, 44.3% and 29.1%, respectively, in the absence of extractant. The result indicated that the long carbon chain could improve the desulfurization efficiency probably due to the formation of an emulsion system (Zhang et al. 2010). When [C4mim]BF4 was used, a bi-phase system was produced in the ECODS process due to the incompatibility between the IL and model oil, and the catalysts and oxidant were dissolved into the IL phase. The sulfur removal achieved 98.3% for [C16mim]3PMo4O24, 88.9% for [C8mim]3PMo4O24 and 41.6% for [C4mim]3PMo4O24, respectively. It could be concluded that the IL played a vital role in the desulfurization system not just as an extractant but also improving the usage of oxidant. The DBT dissolved in model oil could be removed quickly through the ECODS process, which showed much better performance than just single extraction or catalytic oxidation without IL.
3.3 The effects of reaction time and temperature for desulfurization performance
The experiment was performed at 40, 50 and 60 °C, respectively, to study the effect of reaction temperature on sulfur removal. The results in Fig. 4 showed that the sulfur removal increased when reaction time increased. When the temperature rose from 40 to 60 °C, the catalytic performance on desulfurization was 34.1%, 41.0% and 56.2% after 10 min and increased to 82.7%, 93.3% and 98.3% after 60 min, respectively. It could be concluded that reaction time and temperature are important for desulfurization.
3.4 The effect of oxidant usage on desulfurization performance of catalysts
The effect of oxidant usage on desulfurization performance was investigated, and the result is shown in Fig. 5. Using [C16mim]3[PMo4O24] as the catalyst, the sulfur removal increased when the molar ratio of H2O2 to sulfur (O/S) increased from 2:1 to 4:1. Despite the O/S molar ratio being 2:1, the sulfur removal of DBT model oil could achieve 55.8% in 10 min and 95.9% in 60 min. However, when the O/S molar ratio was increased to 4:1, the sulfur removal of DBT model oil only improved to 58.4% in 10 min and 98.8% in 60 min. This feature indicated the high utilization of oxidant in the ECODS system due to the high sulfur removal at a low O/S molar ratio.
3.5 Investigation of the different sulfur-containing compounds
As shown in Fig. 6, another two sulfur-containing compounds benzothiophene (BT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT) were evaluated with [C16mim]3[PMo4O24] as the catalyst. The removals of BT and 4,6-DMDBT are 41.7% and 88.6%, respectively, after 1 h under optimized conditions. The removal rates are lower than the removal of DBT. According to the previous study (Li et al. 2016), it is found that the catalytic activity of desulfurization was affected commonly by two factors, which are the electron density and the steric hindrance around the sulfur atoms. For one thing, it is the low electron density around the sulfur atoms of BT that leads to the lowest catalytic activity. For DBT and 4,6-DMDBT, the difference of the electron density is very small. The steric hindrance of the methyl groups around the sulfur atoms will be the main role affecting the reactivity. Thus, the desulfurization activity of different substrates decreased in the following order of DBT > 4,6-DMDBT > BT.
3.6 Influence of the usage of the catalyst
Table 4 reveals effects of the usage of the catalyst on sulfur removals. It is seen that the removal of DBT increased from 38.7% to 98.3%, when the molar ratios of catalyst/sulfur increased from 1:100 to 1:10. However, the sulfur removal rose by only 1.3% when the molar ratio of catalyst/sulfur was 1:5. Hence, it was proved that the amount of catalyst had an important influence on the removal of DBT and the appropriate catalyst/sulfur molar ratio might be 1:10.
3.7 Recycling of the IL and catalyst
The recycling performance of the IL and catalyst plays a key role in the practical application. The recycling experiment was carried out as follows. After the first reaction, the IL phase containing the catalyst was separated and heated at 110 °C for 3 h to remove the remaining hydrogen peroxide. Then, the regenerated IL and catalyst, fresh hydrogen peroxide and model oil were added to the flask for the next reuse. The sulfur removal only decreased from 98.3% to 95.9% after the 8th cycle (Fig. 7), which indicated that the IL and catalyst had good recycling performance. Along with the recycling, more and more reaction products could be deposited in the IL phase including [C16mim]3[PMo4O24] with more recycling, causing IL curing and the accompanying decrease in sulfur removal.
3.8 The possible reaction process
DBT, a typical representative of an aromatic sulfur compound, can be removed completely by the desulfurization system containing [C16mim]3[PMo4O24], H2O2 and [C4mim]BF4. The [C4mim]BF4 acts as both extractant and reaction medium to create a favorable environment in the reaction. The catalyst is easily dissolved in the IL. First, DBT is extracted into the IL phase and then oxidized to a more polar sulfone (Scheme 1) (Zhu et al. 2015; Lu et al. 2013). The sulfone is in the lower ionic liquidIL phase, which will promote the desulfurization reaction process. When the ionic liquidIL extraction is saturated, the sulfone is precipitated as a white solid from the ionic liquidIL and the sulfone can be removed from the desulfurization system by centrifugation.
4 Conclusion
Three peroxophosphomolybdates were successfully synthesized and characterized. Compared with the short carbon chains in cations of catalysts, a long carbon chain showed a positive effect on catalytic oxidation of DBT. The sulfur removal could reach 98.3% with [C16mim]3[PMo4O24] as catalyst at 60 °C with n(DBT)/n(Catalyst)/n(H2O2) = 10:1:30. The desulfurization activity of different substrates decreased in the following order DBT > 4,6-DMDBT > BT. Apart from its high catalytic efficiency, the catalyst also showed outstanding recycling properties and it could be cycled 8 times with very little loss of activity.
References
Chen K, Liu N, Zhang M, Wang D. Oxidative desulfurization of dibenzothiophene over monoclinic VO2 phase-transition catalysts. Appl Catal B. 2017;212:32–40. https://doi.org/10.1016/j.apcatb.2017.04.046.
Dai C, Zhang J, Huang C, Lei Z. Ionic liquids in selective oxidation: catalysts and solvents. Chem Rev. 2017;117(10):6929–83. https://doi.org/10.1021/acs.chemrev.7b00030.
Hao L, Wang M, Shan W, Deng C, Ren W, Shi Z, et al. l-Proline-based deep eutectic solvents (DESs) for deep catalytic oxidative desulfurization (ODS) of diesel. J Hazard Mater. 2017;339:216–22. https://doi.org/10.1016/j.jhazmat.2017.06.050.
Hao XL, Ma YY, Zang HY, Wang YH, Li YG, Wang EB. A polyoxometalate-encapsulating cationic metal-organic framework as a heterogeneous catalyst for desulfurization. Chem Eur J. 2015;21(9):3778–84. https://doi.org/10.1002/chem.201405825.
He J, Wu P, Wu Y, Li H, Jiang W, Xun S, et al. Taming interfacial oxygen vacancies of amphiphilic tungsten oxide for enhanced catalysis in oxidative desulfurization. ACS Sustain Chem Eng. 2017;5(10):8930–8. https://doi.org/10.1021/acssuschemeng.7b01741.
He LN, Li HM, Zhu WS, Guo JX, Jiang X, Lu JD, et al. Deep oxidative desulfurization of fuels using peroxophosphomolybdate catalysts in ionic liquids. Ind Eng Chem Res. 2008;47(18):6890–5. https://doi.org/10.1021/ie800857a.
Hou Y, Li H, Xu Y, Niu Q, Wu W. Influence of polyethylene glycol on the deep desulfurization of catalytic cracking gasoline by polyurethane membranes via pervaporation. Energy Fuels. 2018;32(2):2089–94. https://doi.org/10.1021/acs.energyfuels.7b03654.
Jiang W, Dong L, Liu W, Guo T, Li H, Zhang M, et al. Designing multifunctional SO3H-based polyoxometalate catalysts for oxidative desulfurization in acid deep eutectic solvents. RSC Adv. 2017a;7(87):55318–25. https://doi.org/10.1039/c7ra10125b.
Jiang W, Zheng D, Xun S, Qin Y, Lu Q, Zhu W, et al. Polyoxometalate-based ionic liquid supported on graphite carbon induced solvent-free ultra-deep oxidative desulfurization of model fuels. Fuel. 2017b;190:1–9. https://doi.org/10.1016/j.fuel.2016.11.024.
Jiang W, Zhu W, Chang Yh, Li HM, Chao Yh, Xiong J, et al. Oxidation of aromatic sulfur compounds catalyzed by organic hexacyanoferrates in ionic liquids with a low concentration of H2O2 as an oxidant. Energy Fuels. 2014a;28(4):2754–60. https://doi.org/10.1021/ef500082y.
Jiang W, Zhu WS, Chang YH, Chao YH, Yin S, Liu H, et al. Ionic liquid extraction and catalytic oxidative desulfurization of fuels using dialkylpiperidinium tetrachloroferrates catalysts. Chem Eng J. 2014b;250:48–54. https://doi.org/10.1016/j.cej.2014.03.074.
Jiang W, Zhu WS, Li HP, Wang X, Yin S, Chang YH, et al. Temperature-responsive ionic liquid extraction and separation of the aromatic sulfur compounds. Fuel. 2015;140:590–6. https://doi.org/10.1016/j.fuel.2014.09.083.
Li C, Jiang ZX, Gao JB, Yang YX, Wang SJ, Tian FP, et al. Ultra-deep desulfurization of diesel: oxidation with a recoverable catalyst assembled in emulsion. Chem Eur J. 2004;10(9):2277–80. https://doi.org/10.1002/chem.200305679.
Li HP, Zhu WS, Zhu SW, Xia JX, Chang YH, Jiang W, et al. The selectivity for sulfur removal from oils: an insight from conceptual density functional theory. AIChE J. 2016;62(6):2087–100. https://doi.org/10.1002/aic.15161.
Li S-W, Yang Z, Gao R-M, Zhang G, J Zhao. Direct synthesis of mesoporous SRL-POM@MOF-199@MCM-41 and its highly catalytic performance for the oxidesulfurization of DBT. Appl Catal B. 2018;221:574–83. https://doi.org/10.1016/j.apcatb.2017.09.044.
Lo WH, Yang HY, Wei GT. One-pot desulfurization of light oils by chemical oxidation and solvent extraction with room temperature ionic liquids. Green Chem. 2003;5(5):639–42. https://doi.org/10.1039/b305993f.
Lu H, Li P, Liu Y, Hao L, Ren W, Zhu W, et al. Synthesis of a hybrid Anderson-type polyoxometalate in deep eutectic solvents (DESs) for deep desulphurization of model diesel in ionic liquids (ILs). Chem Eng J. 2017;313:1004–9. https://doi.org/10.1016/j.cej.2016.10.140.
Lu H, Ren W, Liao W, Chen W, Li Y, Suo Z. Aerobic oxidative desulfurization of model diesel using a B-type Anderson catalyst [(C18H37)2N(CH3)2]3Co(OH)6Mo6O18·3H2O. Appl Catal B. 2013;138:79–83. https://doi.org/10.1016/j.apcatb.2013.02.034.
Moghadam FR, Azizian S, Bayat M, Yarie M, Kianpour E, Zolfigol MA. Extractive desulfurization of liquid fuel by using a green, neutral and task specific phosphonium ionic liquid with glyceryl moiety: a joint experimental and computational study. Fuel. 2017;208:214–22. https://doi.org/10.1016/j.fuel.2017.07.025.
Nejad NF, Beigi AAM. Efficient desulfurization of gasoline fuel using ionic liquid extraction as a complementary process to adsorptive desulfurization. Pet Sci. 2015;12(2):330–9. https://doi.org/10.1007/s12182-015-0020-2.
Rafiee E, Sahraei S, Moradi GR. Extractive oxidative desulfurization of model oil/crude oil using KSF montmorillonite-supported 12-tungstophosphoric acid. Pet Sci. 2016;13(4):760–9. https://doi.org/10.1007/s12182-016-0127-0.
Raj JJ, Magaret S, Pranesh M, Lethesh KC, Devi WC, Mutalib MIA. Extractive desulfurization of model fuel oil using ester functionalized imidazolium ionic liquids. Sep Purif Technol. 2018;196:115–23. https://doi.org/10.1016/j.seppur.2017.08.050.
Sun X, Zhao S. Revealing the catalytic mechanism of an ionic liquid with an isotope exchange method. Pet Sci. 2011;8(4):495–501. https://doi.org/10.1007/s12182-011-0167-4.
Wang C, Chen Z, Zhu W, Wu P, Jiang W, Zhang M, et al. One-pot extraction and oxidative desulfurization of fuels with molecular oxygen in low-cost metal-based ionic liquids. Energy Fuels. 2017;31(2):1376–82. https://doi.org/10.1021/acs.energyfuels.6b02624.
Xu H, Zhang D, Wu F, Cao R. Deep oxidative desulfurization of fuels based on C4mimCl/CoCl2 ionic liquid oxone solutions at room temperature. Fuel. 2017;208:508–13. https://doi.org/10.1016/j.fuel.2017.07.060.
Xun SH, Zhu WS, Chang YH, Li HP, Zhang M, Jiang W, et al. Synthesis of supported SiW12O40-based ionic liquid catalyst induced solvent-free oxidative deep-desulfurization of fuels. Chem Eng J. 2016;288:608–17. https://doi.org/10.1016/j.cej.2015.12.005.
Yang E, Yao C, Liu Y, Zhang C, Jia L, Li D, et al. Bamboo-derived porous biochar for efficient adsorption removal of dibenzothiophene from model fuel. Fuel. 2018;211:121–9. https://doi.org/10.1016/j.fuel.2017.07.099.
Yang H, Jiang B, Sun Y, Zhang L, Sun Z, Wang J, et al. Polymeric cation and isopolyanion ionic self-assembly: novel thin-layer mesoporous catalyst for oxidative desulfurization. Chem Eng J. 2017;317:32–41. https://doi.org/10.1016/j.cej.2017.01.135.
Zhang BY, Jiang ZX, Li J, Zhang YN, Lin F, Liu Y, et al. Catalytic oxidation of thiophene and its derivatives via dual activation for ultra-deep desulfurization of fuels. J Catal. 2012;287:5–12. https://doi.org/10.1016/j.jcat.2011.11.003.
Zhang H, Zhang Q, Zhang L, Pei T, Dong L, Zhou P, et al. Acidic polymeric ionic liquids based reduced graphene oxide: an efficient and rewriteable catalyst for oxidative desulfurization. Chem Eng J. 2018;334:285–95. https://doi.org/10.1016/j.cej.2017.10.042.
Zhang L, Wang J, Sun Y, Jiang B, Yang H. Deep oxidative desulfurization of fuels by superbase-derived Lewis acidic ionic liquids. Chem Eng J. 2017;328:445–53. https://doi.org/10.1016/j.cej.2017.07.060.
Zhang M, Zhu W, Li H, Xun S, Ding W, Liu J, et al. One-pot synthesis, characterization and desulfurization of functional mesoporous W-MCM-41 from POM-based ionic liquids. Chem Eng J. 2014;243:386–93. https://doi.org/10.1016/j.cej.2013.12.093.
Zhang Y, Lue H, Wang L, Zhang Y, Liu P, Han H, et al. The oxidation of benzothiophene using the Keggin-type lacunary polytungstophosphate as catalysts in emulsion. J Mol Catal A Chem. 2010;332(1–2):59–64. https://doi.org/10.1016/j.molcata.2010.08.021.
Zhao R, Wang J, Zhang D, Sun Y, Han B, Tang N, et al. Deep catalytic oxidative desulfurization of model fuel based on modified iron porphyrins in ionic liquids: anionic ligand effect. ACS Sustain Chem Eng. 2017;5(3):2050–5. https://doi.org/10.1021/acssuschemeng.6b02916.
Zhu W, Wang C, Li H, Wu P, Xun S, Jiang W, et al. One-pot extraction combined with metal-free photochemical aerobic oxidative desulfurization in deep eutectic solvent. Green Chem. 2015;17(4):2464–72. https://doi.org/10.1039/c4gc02425g.
Acknowledgements
All authors appreciate the financial support from National Science and Technology Program (2017YFB0306*04-1*), the National Natural Science Foundation of China (Nos. 21506080, 21722604, 21776116), Natural Science Foundation of Jiangsu Province (No. BK20150485) and the Priority Academic Program Development of Jiangsu Higher Education Institutions.
Author information
Authors and Affiliations
Corresponding authors
Additional information
Handling editor: Wenshuai Zhu
Edited by Xiu-Qin Zhu
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Zhang, B., Jiang, W., Fan, X. et al. Synthesis of amphiphilic peroxophosphomolybdates for oxidative desulfurization of fuels in ionic liquids. Pet. Sci. 15, 890–897 (2018). https://doi.org/10.1007/s12182-018-0272-8
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s12182-018-0272-8