A newly synthesized, single-step silicone acrylate formulation cured by conventional radiation produced a reflection spectrum that showed an unusual interference pattern for a single-step coating. The acrylate was prepared by transesterification of silicate oligomer with ω-functionalized acrylic alcohol. The reflectance spectrum was analyzed by means of the Fourier transformation, followed by a separation of variables and constrained conditions. The separation of variables was based on the refractive index as a function of the layer depth, which revealed the coating was non-uniform in refractive index. An interface within the coating was independently observed by microscopy, showing that the coating separated into two layers, supporting the numerical analysis. Although the coating was manufactured by a single-step coating process, the two-layer structure that was formed is normally constructed with multiple coating processes, such as applications of a primer and a top coat. Experiments varying the formulation components show that the new silicone acrylate and an aliphatic di-functional acrylic ester were essential components for the formation of the two-layer structure. Outdoor weathering results are presented after 1 year of testing in Florida and Arizona, which showed better performance than conventional coating systems.
Similar content being viewed by others
References
Whitesides, GM, Grzybowski, B, “Self-Assembly at All Scales.” Science, 295 (5564) 2418–2421 (2002)
Lu, Y, Fan, H, Doke, N, Loy, DA, Assink, RA, LaVan, DA, Brinker, CJ, “Evaporation-Induced Self-Assembly of Hybrid Bridged Silsesquioxane Film and Particulate Mesophases with Integral Organic Functionality.” J. Am. Chem. Soc., 122 (22) 5258–5261 (2000)
Zhou, H, Ye, Q, Xu, J, “Polyhedral Oligomeric Silsesquioxane-Based Hybrid Materials and Their Applications.” Mater. Chem. Front., 1 212–230 (2017)
Zhang, W, Fang, B, Walther, A, Muller, AHE, “Synthesis Via RAFT Polymerization of Tadpole-Shaped Organic/Inorganic Hybrid Poly(Acrylic Acid) Containing Polyhedral Oligomeric Silsesquioxane (POSS) and Their Self-Assembly in Water.” Macromolecules, 42 (7) 2563–2569 (2009)
Zheng, L, Hong, S, Cardoen, G, Burgaz, E, Gido, SP, Coughlin, EB, “Polymer Nanocomposites Through Controlled Self-Assembly of Cubic Silsesquioxane Scaffolds.” Macromolecules, 37 (23) 8606–8611 (2004)
Brinker, CJ, Lu, Y, Sellinger, A, Fan, H, “Evaporation-Induced Self-Assembly: Nanostructures Made Easy.” Adv. Mater., 11 (7) 579–585 (1999)
Ferriera, M, Cheung, JH, Rubner, MF, “Molecular Self-Assembly of Conjugated Polyions: A New Process for Fabricating Multilayer Thin Film Heterostructures.” Thin Solid Films, 244 (1–2) 806–809 (1994)
IHS Markit, News Releases, “Vehicles Getting Older: Average Age of Light Cars and Trucks in U.S. Rises Again in 2016 to 11.6 Years, IHS Markit Says.” 2016
“Performance of Headlamp Lens System Durability.” SAE J3086 Improved Headlamp Lens Durability Task Force, Society of Automotive Engineers
Kawai, K, Shuhei, K, “Composition for Coating Plastic Substrate, Coating Film Formed Therefrom, and Formed Body.” US Patent 8,426,027, 2013
Haubrich, JE, Slocum, SS, “Radiation Curable Hardcoat with Improved Weatherability.” US Patent 8,754,145, 2014
Weber, EM, “UV Curable Coating Compositions Containing Aliphatic Urethane Acrylate Resins.” US Patent 9,109,139, 2015
Weber, EM, “UV Curable Coating Compositions Containing Aliphatic Urethane Acrylate Resins.” US Patent 9,988,556, 2018
Kim, JW, Park, KY, Kim, KS, Ryu, SH, “Radiation Curable Paint Composition and Molded Product Comprising Cured Coating Layer Formed Therefrom.” US Patent 9,938,427, 2018
Odaka, K, Furukawa, K, Satou, H, “Active Energy Ray-Curable Coating Composition and Molded Article Having Cured Coating Film of the Composition.” US Patent 7,785,713, 2010
Higuchi, K, Aoki, Y, “Reactive UV Absorber, Making Method, Coating Composition, and Coated Article.” US Patent 9,873,675, 2018
Noda, T, Nakaya, F, Okutsu, H, “Curable Composition and Polymer.” US Patent 9,663,603, 2017
Eduok, U, Faye, O, Szpunar, J, “Recent Developments and Applications of Protective Silicone Coatings: A Review of PDMS Functional Materials.” Prog. Org. Coat., 111 124–163 (2017)
Schwalm, R, UV Coatings: Basics, Recent Developments, and New Applications. Elsevier Science, Amsterdam (2006)
Hutchins, M, McClung, J, “Energy Curable Coatings for Automotive Interior.” SAE Technical Paper (2018)
Higuchi, K, Gilliam, M, Yamaya, M, “Organic Resin Laminate.” US Patent 8,361,607 B2, 2013
Ichisono, S, Noda, T, “The Film Thickness Measuring Apparatus and Thickness Measuring Method.” JP Patent JP5782353B2, 2015
Maniscalco, B, Kaminski, PM, Walls, JM, “Thin Film Thickness Measurements Using Scanning White Light Interferometry.” Thin Solid Films, 550 (1) 10–16 (2014)
Biegen, JF, “Interferometric Surface Profiler.” US Patent 4,869,593, 1989
“Plastic Material or Materials for Use in Optical Parts Such as Lenses and Reflex Reflectors of Motor Vehicle Lighting Devices,” SAE J576-2017, SAE International, 2017
Masuda, K, Higuchi, K, Furudate, M, Inoue, T, “Organic Solvent Dispersion of Titanium Oxide Solid-Solution Particles, Making Method and Coating Composition.” European Patent EP29332301B1, 2018
“Color Specification,” SAE J578, SAE International, 2016
“Standard Practice for Computing the Colors of Objects by Using the CIE System,” ASTM E308, ASTM International, 2017
“Standard Test Method for Haze and Luminous Transmittance of Transparent Plastics,” ASTM D1003, ASTM International, 2013
Masuda, K, Tsuchida, K, Inoue, T, Gilliam, M, “Self-orientation of Radiation Curable Coating Films.” In: Proceedings of the 12th International Conference on Coatings on Glass and Plastics, Wurzburg, Germany (2018)
United States National Weather Service, https://www.weather.gov/mfl/climate. Accessed 19 June 2018
United States National Weather Service Forecast Office, “Monthly Climate Normals (1981–2010)—Phoenix, AZ,” NOWData—NOAA Online Weather Data https://w2.weather.gov/climate/xmacis.php?wfo=psr. Accessed 19 June 2018
Arizona State Climate Office, Table: “Average Temperature and Relative Humidity by Five-Year Periods 1896–1995,” https://azclimate.asu.edu/climate/climate-of-phoenix-summary/. Accessed 19 June 2018
National Solar Radiation Data Base, 1961–1990: Typical Meteorological Year 2. https://rredc.nrel.gov/solar/old_data/nsrdb/1961-1990/tmy2/
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Masuda, K., Tsuchida, K., Inoue, T. et al. A self-assembled, silicone acrylate coating formulation and detection of the optically non-uniform structure with reflectance spectroscopy. J Coat Technol Res 16, 923–931 (2019). https://doi.org/10.1007/s11998-018-00171-5
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11998-018-00171-5