Abstract
The effects of ambient directional rolling and heat treatments on ultimate tensile strength (UTS), hardness (HD), percent elongation (PE), and impact energy (IE) on Al-Si-Mg-Cu alloy casting with reference to inclination to rolling direction are discussed in this article. The results show that rolled and quenched (CQ) sample possess superior UTS and HD to as-cast and those of rolled and aged samples (CA). Improved IE resistance with ductility is shown by both CQ and CA samples. However, these mechanical properties are enhanced as changes in the test sample direction moved away from rolling direction for all heat-treated samples. The CQ samples displayed highest tensile strength (108 MPa) and PE (19.8%) in the 90° direction.
Similar content being viewed by others
References
P.K. Rohatgi, D. Nath, S.S. Singh, and B.N. Keshavaram, J. Mater. Sci. 29, 5975 (1994).
C. Jeong, Mater. Trans. 54, 588 (2013).
L.A. Dobrzanski, W. Borek, and R. Maniara, J. Achiev. Mater. Manuf. Eng. 18, 211 (2006).
Z. Li, A.M. Samuel, F.H. Samuel, C. Ravindran, H.W. Doty, and S. Valtierra, Mater. Sci. Eng. A 367, 111 (2004).
Z. Li, A.M. Samuel, C. Rayindran, S. Valtierra, and H.W. Doty, Mater. Sci. Eng. 367, 111 (2004).
G. Mrówka-Nowotnik and J. Sieniawski, Arch. Mater. Sci. Eng. 47, 85 (2011).
M.A. Mohamed and F.H. Samuel, Heat Treatment—Conventional and Novel Applications, ed. F. Czerwinski (Rijeka, Croatia: Intech, 2012), pp. 55–72.
S.D. Dumolt, D.E. Laughlin, and J.C. Williams, Scripta Metall. 18, 1347 (1984).
D.J. Chakrabarti, B.K. Cheong, and D.E. Laughlin, Automotive Alloys, ed. S.K. Das (Warrendale, PA: TMS, 1998), p. 27.
W.F. Miao and D.E. Laughlin, Scripta Mater. 40, 873 (1999).
W.F. Miao and D.E. Laughlin, Metall. Mater. Trans. A 31A, 361 (2000).
W.F. Miao and D.E. Laughlin, J. Mater. Sci. Lett. 19, 201 (2000).
D.J. Chakrabarti, Y. Peng, and D.E. Laughlin (Paper presented at the 8th International Conference of Al Alloys, Cambridge, U.K., 2–5 July 2002).
S.K. Chaudhury and D. Apelian, Metall. Mater. Trans. A 37A, 2295 (2006).
J. Gauthier, P. Louchez, and F.H. Samuel, Cast Metals 8, 91 (1995).
J.H. Sokolowski, M.B. Djurdjevic, C.A. Kierkus, and D.O. Northwood, J. Mater. Process. Technol. 109, 174 (2001).
P. Ouellet and F.H. Samuel, J. Mater. Sci. 34, 4671 (1999).
P.S. Wang, S.L. Lee, and J.C. Lin, J. Mater. Res. 15, 2027 (2000).
N. Unlu, B.M. Gable, G.J. Shiflet, and E.A. Starke, Metall. Mater. Trans. 34, 2757 (2003).
V. Raghavan, J. Phase Equilib. Diffus. 28, 213 (2007).
M. Syahid, B.T. Sofyan, S.G. Basuki, and B. Adam, Adv. Mater. Res. 789, 324 (2013)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Adeosun, S.O., Akpan, E.I., Balogun, S.A. et al. Anisotropic Responses of Mechanical and Thermal Processed Cast Al-Si-Mg-Cu Alloy. JOM 67, 916–921 (2015). https://doi.org/10.1007/s11837-015-1302-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11837-015-1302-2