Biosynthesis of metal and semiconductor nanoparticles using microorganisms has emerged as a more eco-friendly, simpler and reproducible alternative to the chemical synthesis, allowing the generation of rare forms such as nanotriangles and prisms. Here, we report the endophytic fungus Aspergillus clavatus, isolated from surface sterilized stem tissues of Azadirachta indica A. Juss., when incubated with an aqueous solution of chloroaurate ions produces a diverse mixture of intracellular gold nanoparticles (AuNPs), especially nanotriangles (GNT) in the size range from 20 to 35 nm. These structures (GNT) are of special interest since they possess distinct plasmonic features in the visible and IR regions, which equipped them with unique physical and optical properties exploitable in vital applications such as optics, electronics, catalysis and biomedicine. The reaction process was simple and convenient to handle and was monitored using ultraviolet–visible spectroscopy (UV–vis). The morphology and crystalline nature of the GNTs were determined from transmission electron microscopy (TEM), atomic force spectroscopy (AFM) and X-ray diffraction (XRD) spectroscopy. This proposed mechanistic principal might serve as a set of design rule for the synthesis of anisotropic nanostructures with desired architecture and can be amenable for the large scale commercial production and technical applications.
At present, there is a greater need to develop safe, reliable, clean and eco-friendly methods for the preparation of nanoparticles and other high structured nanomaterials. With the rapid development of new chemical/physical methods, concern for environmental contaminations is regularly heightened as the chemical procedures involved in the synthesis of nanomaterials generates a large amount of hazardous by-products. Thus, there is an urgent need for 'green chemistry' that includes clean, nontoxic and environment-friendly methods of nanoparticle synthesis with precise control over the shape and size. In the recent years, 'green synthesis' of the nanoparticles has paid much more attention in the rapidly growing area of nanoscience and nanotechnology [1–5]. Utilization of cheap nontoxic chemicals, eco-friendly solvents and renewable materials are some of the pivotal issues that merit important concern in a green synthesis strategy for nanomaterials. In this context, biological synthesis of nanoparticles as an emerging highlight of the intersection of nanotechnology and biotechnology has received increasing attention to come up the need of environmentally benign technologies in nanomaterial synthesis, not only because it reduce the use and generation of hazardous substances to human health and environment but also in providing the facile and convenient entry to produce multiple inorganic nanoparticles . Thus, synthesis of nanomaterials using microorganisms is compatible with the green chemistry principles, resulted in a surge of interest in scientists towards biological systems for inspiration [7–9]. Many microbes are known to produce highly structured metallic nanoparticles with very similar properties to that of chemically synthesized materials, while having precise control over size, shape and monodispersity. The magnetosome or the magnetotactic bacteria synthesize the magnetic nanoparticles in nature since long back, which is a very good biosystem to learn the basic principles of biofabrication . Many prokaryotes like Pseudomonas stutzeri  and Schizosacchromyces pombe  are reported to produce silver and cadmium nanocrystals within their periplasmic spaces. Besides these, there are several other eukaryotic microbes such as fungi Verticillium and Fusarium that synthesize the gold nanoparticles with variable shape and size [13, 14]. These all examples rectify the importance of bio-systems to get inspiration in fabricating nanomaterials.
In this report, we present the single step 'green synthesis' protocol for biofabricating highly anisotropic, monocrystalline gold nanotriangles utilizing extracts of endophytic (endophytes are microbe that resides within the internal living tissues of higher plants as endosymbionts) fungi Aspergillus clavatus, which was isolated from the surface-sterilized stem tissues of Azadirachta indica A. Juss. Earlier, there are many other species of Aspergillus have been reported of their potential to synthesize silver and gold nanoparticles such as Aspergillus niger , A. flavus , A. Fumigatus , A. oryzae var. Viridis . Although this endophytic microbe was earlier investigated by our group for the biofabrication of silver nanoparticles , but no reports are available about their potential in biofabrication of gold nanoaparticles. This strain is largest among the Aspergillus spp. and conidiophores can be seen from unaided eye. This is first ever report of an endophytic A. Clavatus, in bio-fabricating gold nanoparticles, although some other endophytic fungi like Colletotrichum sp. from Pelargonium graveolens leaves are reported for gold bio-fabrication . Most of the earlier works are emphasizing with the size of nanoparticles in contrast to this report which shows a precise control not only over size but also its shape specially nanotriangle.
Isolation of Endophytic Aspergillus clavatus
The host plant Azadirachta indica A. Juss. was surveyed, and samples were randomly collected from within the campus premises of Banaras Hindu University, Varanasi, India. The stem tissues were collected with cut ends sealed with parafilms™ and collected in paper bags. The samples were than washed properly in running tap water for 5–8 min followed by rinse in sterile distilled water to remove the adhered debris and spores. After successive surface sterilization in 75% ethanol (5 min), the stem tissues were rinsed three times in sterilized distilled water and aseptically cut into small pads (0.5 × 0.5 cm2). The small pads were carefully placed onto PDA plates and incubated at 25°C for 20 days until the mycelia of endophytic fungi appeared. Each isolate was then grown and examined to ascertain that it originated from a single spore. Based on literature and other morphotaxonomic features under microscope (Nikon Eclipse E-600), one of the strains is identified as Aspergillus clavatus.
Biological Synthesis of Gold Nanotriangles
The endophytic Aspergillus clavatus strain was grown in 500-ml Erlenmeyer flasks containing 200 ml MGYP medium which is composed of malt extract (0.3%), glucose (1%), yeast extract (0.3%) and peptone (0.5%), and after adjusting the pH of the medium to 7.0, the culture was grown with continuous shaking on a rotary shaker (200 rpm) at 27°C for 8 days. After the fermentation of the culture, biomass was harvested by centrifugation (5,000 rpm) at 20°C for 20 min, and then the mycelia were washed thrice with sterile distilled water under aseptic conditions. In the present study, we have used both the biomass (wet mycelia) and the culture-free spent medium (culture extract) as reducing agent. The thoroughly washed and harvested mycelial biomass (10 g wet weight) was suspended in 100 ml of aqueous 1 mM HAuCl4 in 500-ml Erlenmeyer's flasks. This reaction mixture was then put onto a shaker at room temperature and 200 rpm. The reaction mixture was routinely monitored by visual colour change as well as periodic sampling of aliquots (2 ml) of the reaction mixture and measuring the UV–vis spectra on a Hitachi dual-beam spectrophotometer (Hitachi, UV-2910) operated at a resolution of 1 nm. Similarly, the broth extract of the endophytic strain is also utilized for bioreduction of aqueous gold ion solution. In a flask, 90 ml of aqueous 1 mM HAuCl4 solution was taken and 10 ml of fungal extract solution is added, thereafter the reaction mixture is placed on rotary shaker as in conditions similar to the biomass-based reduction.
Characterization of Gold Nanotriangles
Once the reactions in the flasks have been completed, the nanoparticles formed were accordingly characterized with TEM, XRD and AFM. For XRD studies, the biomass of fungal mycelia after the reaction has been taken and dried in sterile condition in hot air oven and ground into fine powder. The characterization of gold nanoparticles was carried out by XRD (Cu-Kα radiation source) using a 12-kW rotoflux rotating Cu anode (Rigaku Tokyo, Japan) powder diffractometer (RINT 2000/PC series) operating in Bragg–Brentano geometry and fitted with a curved crystal graphite monochromator in the diffraction beam and a high temperature attachment. For TEM analysis, the samples were prepared by placing 5 μl of gold nanoparticle suspension on a 300-mesh carbon-coated copper grid, and the solution was allowed to stand for 5 min, then excess solution was removed carefully, and the grid was allowed to dry for an additional 5 min; the average size and size distributions of gold nanoparticles were determined by processing the TEM images with image processing software on a Tecnai G-20 transmission electron microscope, a 200-kV TEM with a W-source and an ultra high-resolution pole piece with a point–point resolution of 1.9 A° (TEM, Tecnai [FEI]-12v.G-20). Surface topology was measured by atomic force microscopy (AFM) in the contact mode on a VEECO Digital Instruments multimode scanning probe microscope equipped with a Nanoscope IV controller.
Results and Discussion
The endophytic Aspergillus clavatus strain was isolated from sterilized stem tissues of Azadirachta indica. This strain is identified using modern taxonomic keys with microscopic observations (Figure 1). One can observe the conidiophore with the naked eye, since this species of Aspergillus possesses largest conidiophores among the Aspergillus spp. (Figure 1a), the club-shaped conidiophores are 2–4 mm in length, stipes smooth-walled hyaline (inset Figure 1c). Conidial heads radiate, later splitting into several columns. Vesicles are clavate, 40–60 mm diameter conidiogenous cells are uniseriate, conidia smooth walled, pale green, ellipsoidal, 7–8 × 2–3 micrometre (Figure 1b, c). The morphotaxonomic keys of this fungus was so strong that one does not require any molecular identification. When the biomass of fungus was challenged with 1 mM HAuCl4 aqueous solution, a rapid change in the colour of the biomass was observed from fresh white to the dark purple (Figure 2), similarly the reaction mixture for fungal extract was also observed (inset, Figure 2). This change in colour was due to the collective coherent oscillation of conduction electrons at the surface of the gold nanoparticles when these particles interact with the oscillating electric field of the incident light, a phenomenon called surface plasmon resonance (SPR). This change in colour indicates that reduction in AuCl4- ions takes place. When this reaction was traced with UV–vis spectroscopy, gold SPR bands were observed at ca. 540 nm, which steadily increases in intensity as a function of time of reaction. A 72-h reaction mixture has greater absorption intensity at ca. 540 than 48 h reaction mixture (Figure 3). The surface plasmon bands for the gold nanoparticles usually ranges between 510 and 560 nm in aqueous solution depending upon the function of their morphology, since plasmon bands are very sensitive to the length and sharpness of the tips of nanomaterials. The spherical nanoparticles, however, have strong absorption at about 520 nm with almost no absorption after 600 nm; however, the triangular shape has absorption at 540 which extends well in near infra red region (NIR). At maturation of reaction, the wavelength of surface plasmon bands stabilizes at 555 nm (Figure 3). Thus, the wavelength of peak absorption depends upon several factors such as particle size, dielectric constant of surrounding media and the inter-particle distance . The representative bright field TEM images (Figure 4a, b) shows a relatively large population of flat gold nanotriangles along with some spherical and hexagonal gold nanoparticles formed by the spontaneous reduction in aqueous chloroaurate ions (AuCl-4) by fermentation extract of A. clavatus. The images also confirm that the gold nanotriangles are single crystalline in nature and could be indexed based on the face-centred cubic (fcc) structure of gold. The purified gold nanotriangles showed a particle size distribution ranging from 20–35 nm with an average particle size of 30 ± 2 nm (inset Figure 4b), this indicates that distribution is monodispersed. Consequently, we obtained a much higher population of nanotriangles in comparison with other morphologies, this encourage us to go deep into the optimization of parameters to get a control over the shape. All the nanotriangles observed under low-resolution TEM were ostensibly flat (Figure 4c–h), and showing tip truncation and rounding from sharp angle (Figure 4c, f, h) to sniped angle (Figure 4d, g) nanotriangles. When significant rounding (snipping) occurs, these nanostructures remains no longer as triangular nanoprisms and generally transformed into nanodisks or in cases of truncation without rounding, hexagonal nanoprisms. Synthesis of gold nanotriangles are kinetically driven process and is a result of aggregation and rearrangement of smaller size particles, which act as a nuclei for further growth into anisotropic triangular structures. It is also observed that the low rate of reduction in metal ions at normal room temperature possibly facilitate the growth of anisotropic nanoparticles, and with slight modifications in the temperature and the reaction medium one can be enabled in fabricating the well-defined triangular gold nanoparticles . We have made efforts for the measurements of comparatively large, single gold nanotriangles (inset Figure 5), the height of the nanotriangles was about 140 nm, however, the facets length varies from 130 to 350 nm (Figure 5). But this may not be the case for all the nanotriangles, some has heights as low as 25–30 nm (Figure 7b, d). The AFM studies showed a maximum height of smallest nanotriangle was within 30 nm and the thickness ranges in between 2–8 nm (Figure 7b, d), and that all the triangles observed are equilateral with flat surfaces. In order to confirm the monocrystalline nature of the gold nanoparticles, XRD analysis was performed. Figure 6 shows the X-ray diffraction pattern obtained from the gold nanotriangles. The Bragg reflections obtained from the gold nanotriangle clearly correspond to the fcc crystalline structure of gold. The XRD pattern exhibits four identical diffraction peaks corresponding to the , ,  and  appearing at 2θ = 38. 2°, 44. 5°, 65. 6° and 78. 6° of metal gold, respectively, (International Centre for Diffraction Data, ICDD No. 4–0783), indicating that the precipitate is composed of pure crystalline gold (Figure 6). As per the XRD pattern, a very intense Bragg reflection for the  lattice is observed, suggesting that the  oriented gold nanotriangles are lying flat  on the planar surface, while the reflections correspond to  and  with lattice spacing of 1.44 and 1.23 A° is specific for the triangular morphology, respectively. It is also notable that the ratio of intensity between the  and  diffraction peaks for the prepared sample is much lower than the standard (0.042 vs. 0.33), and this rationally decreases as the particles size increases. These observations confirm that as-formed gold nanoparticles are primarily dominated by  facets , which are quite consistent with the above electron diffraction observation. AFM has been performed on the glass substrate in contact mode, for the two reaction mixture one of 48 h and another was 72 h incubation periods. The Figure 7b, d shows heterogeneous vertical and lateral dimensions since stacking defaults of gold nanotriangles takes place due to longer incubation of the reaction mixture. The three-dimensional images of these nanostructures show surface roughness of about 30 nm (Figure 7b) and 25 nm (Figure 7d), interestingly stacking faults of nanotriangles was observed as they grow in size, which results in an overall increase in the surface roughness. The Figure 7a, c also tested and verified the results already obtained in short incubated samples. The gold nanoparticles are not resolved into single crystals due to the vertical stacking of nanotriangles, and thus the measurement and estimation of size for single nanoparticle with AFM remains intricating. Although the exact mechanism of the synthesis of nanomaterials are not known, but it was observed that when fungal biomass was treated with 1 mM aqueous solution of HAuCl4, there are negligible amount of nanoparticles present in the solution (Figure 2), the biomass instead changed into purple colour, this clearly indicates that the reduction in gold ions takes place intracellular (surface reduction). For getting some more insight into the exact mechanism of bioreduction, a TEM analysis of fungal cells had been performed that are challenged with aqueous gold ions for 72 h. The thin sections of fungal cells shows the presence of plenty of triangular, hexagonal and spherical gold nanoparticles bound to the surface of the cells (Figure 8a–c); however, the triangular nanoparticles are relatively smaller in size than the spherical and other shapes. The presence of these shapes indicates that many particles are not transformed into triangle (Figure 8b) due to lack of nucleation or undergone surface reorganization in such a way that they no longer exhibit the ideal triangular nanostructures. A lot of research in green synthesis of nanomaterials are currently focused on the mechanistic approach to define the mechanism involved in this process [22–24]. A huge number of microbial strains are screened for their potential of producing metal nanoparticles; however, the mechanism of biosynthesis has not been established yet. The metabolic convolutions of viable microorganisms are even more complicating the process of analysis and identification of active species in the nucleation and growth of metal nanoparticles. Many researchers, however, speculated about the role of secretary enzymes such as NADH-dependent reductase of microbial origin, which may be responsible for the reduction in metal ions for growth and nucleation of nanoparticles [25, 26]. However, the biochemical mechanism of metal ion reduction and the subsequent NP formation remain unexplored and need further research. Thus, thorough and in-depth understanding of the biochemical mechanisms associated with nanomaterials biosynthesis is needed. The analysis and identification of active constituents with HPLC and other analytical tools are required to solve the mystery of nucleation and growth of metal nanoparticles in the microbial system.
In summary, we have demonstrated the shape controlled biosynthesis of gold nanotriangles using endophytic fungi Aspergillus clavatus, isolated from surface sterilized stem tissues of Azadirachta indica A. Juss. Results showed that triangular gold nanoparticles are formed along with some spherical as well as hexagonal morphology. It was also observed that the synthesis of gold nanotriangles are extracellular and showing a high aspect ratio. The study reported herein serve as a unique single-step green protocol for the generation and stabilization of nontoxic gold nanotriangles (GNT), exploitable in a myriad of diagnostic and therapeutic applications. A. clavatus induced synthesis of GNT will provide unprecedented opportunities towards the design and development of engineered 'green' gold nanotriangles that can be widely utilized in biomedical applications.
Korbekandi H, Iravani S, Abbasi S: Crit Rev Biotech. 2009, 29: 279. 10.3109/07388550903062462
Basu N, Bhattacharya R, Mukherjee P: Nanotechnology. 2008, 3: 034105.
Kim J, Rheem Y, Yoo B, Chong Y, Bozhilov KN, Kim D, Sadowsky MJ, Hur HG, Myung NV: Acta Biomater. 2010, 7: 2681. 10.1016/j.actbio.2010.01.019
Verma VC, Kharwar RN, Gange AC: Nanomedicine. 2010, 5: 33. 10.2217/nnm.09.77
Huang P, Kong Y, Li Z, Gao F, Cui D: Nanoscale Res Lett. 2010, 5: 949. 10.1007/s11671-010-9587-0
Huang P, Lin J, Li Z, Hu H, Wang K, Gao G, He R, Cui D: Chem Comm. 2010, 46: 4800. 10.1039/c0cc00307g
Nangia Y, Wangoo N, Sharma S, Wu JS, Dravid V, Shekhawat G, Suri CR: Appl Phys Lett. 2009, 94: 233901. 10.1063/1.3141519
Das SK, Das AR, Guha AK: Langmuir. 2009, 25: 8192. 10.1021/la900585p
Binupriya AR, Sathishkumar M, Vijayaraghavan K, Yun SI: J Hazard Mat. 2010, 177: 539. 10.1016/j.jhazmat.2009.12.066
Sarikaya M: PNAS-USA. 1999, 96: 14183. 10.1073/pnas.96.25.14183
Klaus T, Joerger R, Olsson E, Granqvist CG: PNAS USA. 1999, 96: 13611. 10.1073/pnas.96.24.13611
Gericke M, Pinches A: Gold Bull. 2006, 39: 22.
Mukherjee P, Ahmad A, Mandal D, Senapati S, Sainkar SR, Khan MI, Ramani R, Parischa R, Kumar PAV, Alam M, Sastry M, Kumar R: Angew Chem Int Ed. 2001, 40: 3585. 10.1002/1521-3773(20011001)40:19<3585::AID-ANIE3585>3.0.CO;2-K
Ahmad A, Senapati S, Khan MI, Kumar R, Ramani R, Srinivas V, Sastry M: Nanotechnology. 2003, 14: 824. 10.1088/0957-4484/14/7/323
Gade AK, Bonde PP, Ingle AP, Marcato P, Duran N, Rai MK: J Biobased Mat Bioener. 2008, 2: 1. 10.1166/jbmb.2008.204
Vigneshwaran N, Ashtaputre NM, Varadarajan PV, Nachane RP, Paralikar KM, Balasubramanya RH: Mat Lett. 2007, 61: 1413. 10.1016/j.matlet.2006.07.042
Bhainsa KC, D'Souza SF: Coll Surf B Biointer. 2006, 47: 160. 10.1016/j.colsurfb.2005.11.026
Shankar SS, Ahmad A, Pasricha R, Sastry M: J Mat Chem. 2003, 13: 1822. 10.1039/b303808b
Link S, El-Sayed MA: Ann Rev Phys Chem. 2003, 54: 331. 10.1146/annurev.physchem.54.011002.103759
Shankar SS, Rai A, Ahmad A, Sastry M: Chem Mat. 2005, 17: 566. 10.1021/cm048292g
Jin R, Cao YC, Hao E, Metraux GS, Schatz GC, Mirkin CA: Nature. 2003, 425: 487. 10.1038/nature02020
Sun X, Dong S, Wang E: Ange Chemie Intl Ed. 2004, 46: 6360. 10.1002/anie.200461013
Sajanlal PR, Pradeep T: Advan Mat. 2008, 20: 980. 10.1002/adma.200701790
Das SK, Marsili E: Rev Environ Sci Biotechnol. 2010. 10.1007/s11157-010-9188-5
Ahmed A, Mukherjee P, Senapati S, Mandal D, Khan MI, Kumar R, Sastry M: Colloids Surf B Biointerfaces. 2003, 28: 313. 10.1016/S0927-7765(02)00174-1
He S, Guo Z, Zhang Y, Zhang S, Wang J, Gu N: Mater Lett. 2007, 61: 3984. 10.1016/j.matlet.2007.01.018
This work is a part of the PhD thesis of VCV, and was financially supported from Council of Scientific and Industrial Research (CSIR-09/013(205)/2008/EMR-I, dt.28-09-2008), New Delhi India. Authors are thankful to the Professor-in-charge, Centre of Experimental Medicine and Surgery (CEMS). Authors also extend their thanks to Dr. R. N. Kharwar, Mycopathology and Microbial Technology Laboratory, CAS in Botany, Banaras Hindu University India for his support and help to conduct some part of this work in his laboratory. Authors also extend their thanks to Prof. Dhananjai Pandey, School of Material Science and Technology, Institute of Technology, Banaras Hindu University for assistance with the XRD and AFM studies and to Dr. Madhu Yashpal scientist-in-charge, Electron Microscopy Facility, Department of Anatomy, Institute of Medical Sciences, Banaras Hindu University, India for the TEM analysis of the gold nanoparticles.
An erratum to this article is available at http://dx.doi.org/10.1186/1556-276X-6-261.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Verma, V.C., Singh, S.K., Solanki, R. et al. Biofabrication of Anisotropic Gold Nanotriangles Using Extract of Endophytic Aspergillus clavatus as a Dual Functional Reductant and Stabilizer. Nanoscale Res Lett 6, 16 (2011). https://doi.org/10.1007/s11671-010-9743-6
- Azadirachta indica
- Gold nanotriangles
- Endophytic fungi
- Aspergillus clavatus