Abstract
The article reports on low-temperature high-rate sputtering of hydrophilic transparent TiO2thin films using dc dual magnetron (DM) sputtering in Ar + O2mixture on unheated glass substrates. The DM was operated in a bipolar asymmetric mode and was equipped with Ti(99.5) targets of 50 mm in diameter. The substrate surface temperature Tsurfmeasured by a thermostrip was less than 180 °C for all experiments. The effect of the repetition frequency frwas investigated in detail. It was found that the increase of frfrom 100 to 350 kHz leads to (a) an improvement of the efficiency of the deposition process that results in a significant increase of the deposition rate aDof sputtered TiO2films and (b) a decrease of peak pulse voltage and sustaining of the magnetron discharge at higher target power densities. It was demonstrated that several hundreds nm thick hydrophilic TiO2films can be sputtered on unheated glass substrates at aD = 80 nm/min, Tsurf < 180 °C when high value of fr = 350 kHz was used. Properties of a thin hydrophilic TiO2film deposited on a polycarbonate substrate are given.
References
Fujishima A, Honda K: Nature. 1972, 238: 37. COI number [1:CAS:528:DyaE38XltVykurw%3D] 10.1038/238037a0
Sakai N, Fujishima A, Watanable T, Hashimoto K: J. Phys. Chem. B. 2003, 107: 1028. COI number [1:CAS:528:DC%2BD3sXhtFI%3D] 10.1021/jp022105p
A. Fujishima, X. Zhang, C.R. Chimie 9, 750 (2006)
L. Miao, S. Tanemura, Y. Kondo, M. Iwata, S. Toh et al., Appl. Surf. Sci. 238, 125 (2004)
O.H. Fenner, in Handbook of Plastics and Elastomers, ed. By C. A. Harper (McGraw-Hill, New York USA 1975)
Musil J, Herman D, Sicha J: J. Vac. Sci. Technol. A. 2006,24(3):521. COI number [1:CAS:528:DC%2BD28XksFCgtr0%3D] 10.1116/1.2187993
Zeman P, Takabayashi S: J. Vac. Sci. Technol. A. 2001,20(2):1.
Zhao G, Tian Q, Liu Q, Han G: Surf. Coat. Technol.. 2005, 198: 55. COI number [1:CAS:528:DC%2BD2MXltlWqt7k%3D] 10.1016/j.surfcoat.2004.10.064
Modes. T, Scheffel B, Meetzner Chr, Zywitzki O, Reinhold E: Surf. Coat. Technol.. 2005, 200: 306. COI number [1:CAS:528:DC%2BD2MXpvFahtbc%3D] 10.1016/j.surfcoat.2005.02.080
W. Ho, J.C. Yu, S. Lee, Appl. Catal. B: Environ. DOI:10.1016/j.apcatb.2006.06.019 (2006)
Mathur S, Kuhn P: Surf. Coat. Technol.. 2006, 201: 807. COI number [1:CAS:528:DC%2BD28XptlOhs70%3D] 10.1016/j.surfcoat.2005.12.039
Frach P, Gloss D, Metzner Chr, Modes T, Scheffel B, Zywitzki O: Vacuum. 2006, 80: 679. COI number [1:CAS:528:DC%2BD28XltVersr8%3D] 10.1016/j.vacuum.2005.11.001
Amor SB, Guedri L, Baud G, Jacquet M, Ghedira M: Mater. Chem. Phys.. 2002, 77: 903. 10.1016/S0254-0584(02)00189-X
Hou Y-Q, Zhuang D-M, Zhang G, Zhao M, Wu M-S: App. Surf. Sci.. 2003, 218: 97. COI number [1:CAS:528:DC%2BD3sXntVKjsbY%3D] 10.1016/S0169-4332(03)00569-5
Frach P, Gloss D, Goedicke K, Fahland M, Gnehr W-M: Thin Solid Films. 2003, 445: 251. COI number [1:CAS:528:DC%2BD3sXps1Citrw%3D] 10.1016/S0040-6090(03)01153-2
Zywitzki O, Modes T, Sahm H, Frach P, Goedicke K, Gloss D: Surf. Coat. Technol.. 2004, 180–181: 538. 10.1016/j.surfcoat.2003.10.115
Barnes C, Kumar S, Green L, Hwang N-M, Gerson AR: Surf. Coat. Technol.. 2005, 190: 321. COI number [1:CAS:528:DC%2BD2cXhtVakurjN] 10.1016/j.surfcoat.2004.04.003
Ohno S, Takasawa T, Sato Y, Yoshikawa M, Suzuki K, Frach P, Shigesato Y: Thin Solid Films. 2006, 496: 126. COI number [1:CAS:528:DC%2BD2MXht1Gls77P] 10.1016/j.tsf.2005.08.252
Lapostolle F, Perry F, Billard A: Surf. Coat. Technol.. 2006, 201: 2633. COI number [1:CAS:528:DC%2BD28Xht1agsrbO] 10.1016/j.surfcoat.2006.05.015
Baroch P, Musil J, Vlcek J, Nam KH, Han JG: Surf. Coat. Technol.. 2005, 193: 107. COI number [1:CAS:528:DC%2BD2MXhtleks7o%3D] 10.1016/j.surfcoat.2004.07.060
D. Herman, J. Musil, J. Sicha, Photoactivated properties of TiO2 films prepared by magnetron sputtering, Proceedings of the PSE 2006 in Plasma Processes & Polymers, accepted for publication, November 2006
Welzel Th, Dunger Th, Richter F: Surf. Coat. Technol.. 2006, 201: 3959. COI number [1:CAS:528:DC%2BD28Xht1Cisb%2FL] 10.1016/j.surfcoat.2006.08.003
Musil J, Baroch P, Vlček J, Nam KH, Han JG: Thin Solid Films. 2005, 475: 208. COI number [1:CAS:528:DC%2BD2MXhtVKgtbg%3D] 10.1016/j.tsf.2004.07.041
Bradley JW, Bäcker H, Kelly PJ, Arnell RD: Surf. Coat. Technol.. 2001, 142: 337. 10.1016/S0257-8972(01)01084-2
Zheng SK, Wang TM, Xiang G, Wang C: Vacuum. 2001, 62: 361. COI number [1:CAS:528:DC%2BD3MXkvFSiu7c%3D] 10.1016/S0042-207X(01)00353-0
Safi I: Surf. Coat. Technol.. 2000, 127: 203. COI number [1:CAS:528:DC%2BD3cXktVSju7Y%3D] 10.1016/S0257-8972(00)00566-1
Berg S, Nyberg T: Thin Solid Films. 2005, 476: 215. COI number [1:CAS:528:DC%2BD2MXhvF2itr8%3D] 10.1016/j.tsf.2004.10.051
J. Sicha, J. Musil, D. Herman, Z. Stryhal, J. Pavlik, Surface morphology of magnetron sputtered TiO2 films, Proceedings of the PSE 2006 in Plasma Processes & Polymers, accepted for publication, November 2006
Acknowledgments
This work was supported in part by the Ministry of Education of the Czech Republic under Project No. MSM 4977751302 and in part by the Grant Agency of the Czech Republic under Project No. 106/06/0327.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Šícha, J., Heřman, D., Musil, J. et al. High-rate low-temperature dc pulsed magnetron sputtering of photocatalytic TiO2films: the effect of repetition frequency. Nanoscale Res Lett 2, 123 (2007). https://doi.org/10.1007/s11671-007-9042-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11671-007-9042-z
Keywords
- TiO2film
- Hydrophilicity
- Deposition rate
- Unheated substrate
- Dual magnetron sputtering
- Polycarbonate