A solution blending route to ethylene propylene diene terpolymer/layered double hydroxide nanocomposites

Open Access
Nano Express

DOI: 10.1007/s11671-006-9020-x

Cite this article as:
Acharya, H., Srivastava, S.K. & Bhowmick, A.K. Nanoscale Res Lett (2007) 2: 1. doi:10.1007/s11671-006-9020-x


Ethylene propylene diene terpolymer (EPDM)/MgAl layered double hydroxide (LDH) nanocomposites have been synthesized by solution intercalation using organically modified LDH (DS-LDH). The molecular level dispersion of LDH nanolayers has been verified by the disappearance of basal XRD peak of DS-LDH in the composites. The internal structures, of the nanocomposite with the dispersion nature of LDH particles in EPDM matrix have been studied by TEM and AFM. Thermogravimetric analysis (TGA) shows thermal stability of nanocomposites improved by ≈40 °C when 10% weight loss was selected as point of comparison. The degradation for pure EPDM is faster above 380 °C while in case of its nanocomposites, it is much slower.


Layered double hydroxide Nanocomposites Solution blending 

[1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19]


The authors are grateful to Ministry of Human Research and Development (MHRD), India for the financial support.

Copyright information

© to the authors 2006

Authors and Affiliations

  • H. Acharya
    • 1
  • S. K. Srivastava
    • 1
  • Anil K. Bhowmick
    • 2
  1. 1.Department of ChemistryIndian Institute of TechnologyKharagpurIndia
  2. 2.Rubber Technology CentreIndian Institute of TechnologyKharagpurIndia

Personalised recommendations