Failure Investigations on Low Velocity Ballistic Impact Deformation of Closed-Cell Aluminum Metal Foam Targets

  • Technical Article
  • Published:
Journal of Materials Engineering and Performance Aims and scope Submit manuscript

Abstract

Low velocity ballistic deformation behavior of closed-cell aluminum metal foam targets fabricated by powder metallurgy technique has been investigated. The metal matrix of aluminum (60 micron) was mixed with carbamide (CH4N2O) particles of size one mm. Green samples were obtained by compacting the mixture followed by sintering process using a muffle furnace and the metallic foam thus obtained had an average pore size of 1.5 mm. Compared to metallic material, significant reduction in hardness and density was observed when the porosity was increased from 5 to 30%. Using a gas gun setup, low velocity (100 m/s and conical projectile) ballistic experiments were conducted on metal foam targets to understand the deformation behavior. Not any penetration of the projectile was observed when the percentage of porosity was less than 5%. When the percentage of porosity was increased, the projectile was able to perforate the target as the fracture toughness decreases. The size of fragmented areas of the perforated targets and depth of penetration (DoP) of the projectile were measured. Decrease in DoP (improved ballistic resistance) was observed with the increase in relative density of the closed foam target. Even though the projectile could perforate the foam target, no cracks were observed which enhances the suitability of the metal foams to be used as structural applications of defense vehicles.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13

Similar content being viewed by others

References

  1. J. Banhart, Metal foams-from fundamental research to applications. Frontiers in the Design of Materials, 2007, pp 279–289.

  2. J.C. Marx, S.J. Robbins, Z.A. Grady, F.L. Palmieri, C.J. Wohl, and A. Rabiei, Polymer Infused Composite Metal Foam as a Potential Aircraft Leading Edge Material, Appl. Surf. Sci., 2020, 505, p 144114.

    Article  CAS  Google Scholar 

  3. M.F. Ashby, T. Evans, N.A. Fleck, J.W. Hutchinson, H.N.G. Wadley, and L.J. Gibson, Metal Foams: A Design Guide, Elsevier, 2000.

    Google Scholar 

  4. S. Xu, M. Bourham, and A. Rabiei, A Novel Ultra-Light Structure for Radiation Shielding, Mater. Des., 2010, 31(4), p 2140–2146.

    Article  CAS  Google Scholar 

  5. S. Chen, M. Bourham, and A. Rabiei, Novel Light-Weight Materials for Shielding Gamma Ray, Radiat. Phys. Chem., 2014, 96, p 27–37.

    Article  CAS  ADS  Google Scholar 

  6. J. Marx, M. Portanova, and A. Rabiei, A Study on Blast and Fragment Resistance of Composite Metal Foams Through Experimental and Modeling Approaches, Compos. Struct., 2018, 194, p 652–661.

    Article  Google Scholar 

  7. S.S. Sharma and Y.S. Rajpoot, Development of Aluminum Metal Foam Using Blowing Agent, in IOP Conference Series: Materials Science and Engineering, 2018, Vol.377, No. 1, p 012150). IOP Publishing.

  8. I. Paulin, B. Sustarsic, V. Kevorkijan, S.D. Skapin, and M. Jenko, Synthesis of Aluminium Foams by the Powder-Metallurgy Process: Compacting of Precursors, Mater. Tehnol, 2011, 45(1), p 13–19.

    CAS  Google Scholar 

  9. M. Garcia-Avila, M. Portanova, and A. Rabiei, Ballistic Performance of Composite Metal Foams, Compos. Struct., 2015, 125, p 202–211.

    Article  Google Scholar 

  10. M. Peroni, G. Solomos, and V. Pizzinato, Impact Behaviour Testing of Aluminium Foam, Int. J. Impact Eng, 2013, 53, p 74–83.

    Article  Google Scholar 

  11. Y. Sun, R. Burgueño, W. Wang, and I. Lee, Modeling and Simulation of the Quasi-Static Compressive Behavior of Al/Cu Hybrid Open-Cell Foams, Int. J. Solids Struct., 2015, 54, p 135–146.

    Article  CAS  Google Scholar 

  12. G. Srinath, A. Vadiraj, G. Balachandran, S.N. Sahu, and A.A. Gokhale, Characteristics of Aluminium Metal Foam for Automotive Applications, Trans. Indian Inst. Met., 2010, 63(5), p 765–772.

    Article  CAS  Google Scholar 

  13. B. Su, Z. Zhou, J. Zhang, Z. Wang, X. Shu, and Z. Li, A Numerical Study on the Impact Behavior of Foam-Cored Cylindrical Sandwich Shells Subjected to Normal/Oblique Impact, Latin American Journal of Solids, and Structures, 2015, 12(11), p 2045–2060.

    Article  Google Scholar 

  14. J.U. Cho, S.J. Hong, S.K. Lee, and C. Cho, Impact Fracture Behavior at the Material of Aluminum Foam, Mater. Sci. Eng., A, 2012, 539, p 250–258.

    Article  CAS  Google Scholar 

  15. Y. Hangai, H. Kamada, T. Utsunomiya, S. Kitahara, O. Kuwazuru, and N. Yoshikawa, Tensile Properties and Fracture Behavior of Aluminum Alloy foam Fabricated from die Castings Without Using Blowing Agent by Friction stir Processing Route, Materials, 2014, 7(3), p 2382–2394.

    Article  PubMed  PubMed Central  ADS  Google Scholar 

  16. X.P. Yan, N.M. Zhang, W.M. Liang, Y.G. Zhao, and G.T. Yang, Mechanical Behaviours of Open-Cell and Closed-Cell Aluminium Foams against Spherical-Nosed Projectile Penetration, Appl. Mech. Mater., 2010, 29, p 321–325.

    Article  ADS  Google Scholar 

  17. M. Damghani and M. Gonabadi, Investigation of Energy Absorption in Aluminum Foam Sandwich Panels by Drop Hammer Test: Experimental Results, Mech. Mater. Sci. Eng. J. Magnolithe, 2017, 2017, p 7.

    Google Scholar 

  18. N. Movahedi, T. Fiedler, A. Taşdemirci, G.E. Murch, I.V. Belova, and M. Güden, Impact Loading of Functionally Graded Metal Syntactic Foams, Mater. Sci. Eng., A, 2022, 839, p 142831.

    Article  CAS  Google Scholar 

  19. M. Alteneiji, K. Krishnan, Z.W. Guan, W.J. Cantwell, Y. Zhao, and G. Langdon, Dynamic Response of Aluminium Matrix Syntactic Foams Subjected to High Strain-Rate Loadings, Compos. Struct., 2023, 303, p 116289.

    Article  CAS  Google Scholar 

  20. N. Movahedi, M. Vesenjak, L. Krstulović-Opara, I.V. Belova, G.E. Murch, and T. Fiedler, Dynamic Compression of Functionally-Graded Metal Syntactic Foams, Compos. Struct., 2021, 261, p 113308.

    Article  CAS  Google Scholar 

  21. N. Novak, M. Borovinšek, O. Al-Ketan, Z. Ren, and M. Vesenjak, Impact and Blast Resistance of Uniform and Graded Sandwich Panels with TPMS Cellular Structures, Compos. Struct., 2022, 300, p 116174.

    Article  CAS  Google Scholar 

  22. G. Epasto, F. Distefano, L. Gu, H. Mozafari, and E. Linul, Design and Optimization of Metallic Foam Shell Protective Device Against Flying Ballast Impact Damage in Railway Axles, Mater. Des., 2020, 196, p 109120.

    Article  Google Scholar 

  23. B.A. Gama, T.A. Bogetti, B.K. Fink, C.J. Yu, T.D. Claar, H.H. Eifert and J.W. Gillespie Jr., Aluminum Foam Integral Armor: A New Dimension in Armor Design, Compos. Struct., 2001, 52(3–4), p 381–395.

    Article  Google Scholar 

  24. J. Jerz, F. Simancik, M. Bortel, S. Kubo, J. Kovacik, J. Banhart,, and N.A. Fleck, The Design of Lightweight Armour Sheets, in J. Banhart, N.A. Fleck, A. Mortensen, (eds.) Cellulare Metals: Manufacture, Properties, Applications, MIT-Verlag, 2003, pp 43–46.

  25. S.F. Aida, H. Zuhailawati, and A.S. Anasyida, The Effect of Space Holder content and Sintering Temperature of Magnesium foam on Microstructural and Properties Prepared by Sintering Dissolution Process (SDP) Using Carbamide Space Holder, Procedia Eng., 2017, 184, p 290–297.

    Article  CAS  Google Scholar 

  26. M. Shiomi and Y. Tanino, Molding of Aluminum Foams by using hot Powder Extrusion, Metals, 2012, 2(2), p 136–142.

    Article  CAS  Google Scholar 

  27. H. Qingxian, Q. Sawei, and H. Yuebo, Development on Preparation Technology of Aluminum Foam Sandwich Panels, Rare Metal Mater. Eng., 2015, 44(3), p 548–552.

    Article  Google Scholar 

  28. B.U. Vinay and K.S. Rao, Development of Aluminum Foams by Different Methods and Evaluation of its Density by Archimedes Principle, Bonfring Int. J. Indust. Eng. Manag. Sci., 2012, 2(4), p 148–152.

    Google Scholar 

  29. A. Klavzara, M. Chirolia, A. Jungb, and B. Recka, Protective Performance of Hybrid Metal Foams as MMOD Shields, Procedia Eng., 2015, 103, p 294–301.

    Article  Google Scholar 

Download references

Acknowledgments

The authors would like to acknowledge the financial support received from the management of Sri Sivasubramaniya Nadar College of Engineering to develop the gas gun setup.

Author information

Authors and Affiliations

  1. Department of Mechanical Engineering, Sri Sivasubramaniya Nadar College of Engineering, Kalavakkam, Chennai, 603 110, India

    S. Suresh Kumar, R. Sabareeswar, S. Siddharth Krishna, R. Suraj & B. Vishal

Authors
  1. S. Suresh Kumar
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. R. Sabareeswar
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. S. Siddharth Krishna
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. R. Suraj
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. B. Vishal
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to S. Suresh Kumar.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Suresh Kumar, S., Sabareeswar, R., Siddharth Krishna, S. et al. Failure Investigations on Low Velocity Ballistic Impact Deformation of Closed-Cell Aluminum Metal Foam Targets. J. of Materi Eng and Perform 33, 1842–1851 (2024). https://doi.org/10.1007/s11665-023-08079-x

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11665-023-08079-x

Keywords

Search

Navigation