Abstract
The hot tearing susceptibility of Mg-1Ca-xSr (x=0, 0.2, 0.4, 0.6, wt.%) alloys was investigated by CRC mold with a contraction force measurement system with a load cell and a temperature monitor. The results showed that the hot tearing susceptibility of Mg-1Ca-xSr alloys significantly improved with increasing of Sr content. Especially in Mg-1Ca-0.6Sr alloy, no visible tear was found on the casting sample. The force dropped and the final force value from the time-force-temperature curve derived from the hot tearing instruments could reflect the hot tearing susceptibility of different alloys. The mechanism of improved hot tearing resistance of Mg-1Ca-xSr alloys was clarified. In addition to susceptible temperature range and eutectic liquid fraction, it is found that the formation tendency of divorced eutectic also plays an important role on the hot tearing behavior of Mg-1Ca-xSr alloys.
Similar content being viewed by others
References
A.A. Luo, Magnesium Casting Technology for Structural Applications, J. Magnesium Alloys, 2013, 1(1), p 2-22.
J. Song, F. Pan, B. Jiang, A. Atrens, M.-X. Zhang and Y. Lu, A Review on Hot Tearing of Magnesium Alloys, J. Magnesium Alloys, 2016, 4(3), p 151-172.
G. Cao, C. Zhang, H. Cao, Y.A. Chang and S. Kou, Hot-Tearing Susceptibility of Ternary Mg-Al-Sr Alloy Castings, Metall. Mater. Trans. A, 2010, 41(3), p 706-716.
J.F. Song, Z. Wang, Y.D. Huang, A. Srinivasan, F. Beckmann, K.U. Kainer and N. Hort, Effect of Zn Addition on Hot Tearing Behaviour of Mg-0.5Ca-xZn Alloys, Mater. Des., 2015, 87, p 157-170.
Z. Wang, Y.Z. Li, F. Wang, J.F. Song, Z. Liu and P.L. Mao, Effect of Cu Additions on Microstructure, Mechanical Properties and Hot-Tearing Susceptibility of Mg-6Zn-0.6Zr Alloys, J. Mater. Eng. Perform., 2016, 25(12), p 5530-5539.
S.F. Luo, G.Y. Yang, Z. Zou, S.X. Ouyang, L. Xiao and W.Q. Jie, Hot Tearing Susceptibility of Binary Mg-Gd Alloy Castings and Influence of Grain Refinement, Adv. Eng. Mater., 2018, 20(8), p 1800139.
Y. Zhou, P.L. Mao, Z. Wang, Z. Liu and F. Wang, Investigations on Hot Tearing Behavior of Mg-7Zn-xCu-0.6Zr Alloys, Acta Metall. Sin., 2017, 53(7), p 851-860.
H.K. Dong, F. Wang, Z. Wang, J.K. Liu, Z. Liu and P.L. Mao, Effect of Sn Addition on Hot Tearing Susceptibility of AXJ530 Alloy, Mater. Res. Express, 2018, 5(3), p 036513.
Z. Yang, K. Wang, P. Fu, L. Peng, B. Hu, M. Liu and A.K. Sachdev, Influence of Alloying Elements on Hot Tearing Susceptibility of Mg-Zn Alloys Based on Thermodynamic Calculation and Experimental, J. Magnesium Alloys, 2018, 6(1), p 44-51.
G. Zhang, Y. Wang, Z. Liu and S. Liu, Influence of Al Addition on Solidification Path and Hot Tearing Susceptibility of Mg-2Zn-(3 + 0.5x)Y-xAl Alloys, J. Magnesium Alloys, 2019, 7(2), p 272-282.
H. Pan, C. Yang, Y. Yang, Y. Dai, D. Zhou, L. Chai, Q. Huang, Q. Yang, S. Liu, Y. Ren and G. Qin, Ultra-Fine Grain Size and exceptionally high strength in dilute Mg-Ca alloys achieved by conventional one-step extrusion, Mater. Lett., 2019, 237, p 65-68.
H. Pan, G. Qin, M. Xu, H. Fu, Y. Ren, F. Pan, Z. Gao, C. Zhao, Q. Yang, J. She and B. Song, Enhancing Mechanical Properties of Mg-Sn Alloys By Combining Addition of Ca and Zn, Mater. Des., 2015, 83, p 736-744.
E.L. Zhang and L. Yang, Microstructure, Mechanical Properties And Bio-Corrosion Properties of Mg-Zn-Mn-Ca Alloy for Biomedical Application, Mater. Sci. Eng. A-Struct. Mater. Prop. Microstruct. Process., 2008, 497(1-2), p 111-118.
C.J. Bettles, M.A. Gibson and K. Venkatesan, Enhanced Age-Hardening Behaviour in Mg-4 wt% Zn Micro-Alloyed with Ca, Scr. Mater., 2004, 51(3), p 193-197.
G.H. Wu, Y. Fan, H.T. Gao, C.Q. Zhai and Y.P. Zhu, The Effect of Ca and Rare Earth Elements on the Microstructure, Mechanical Properties and Corrosion Behavior of AZ91D, Mater. Sci. Eng. A-Struct. Mater. Prop. Microstruct. Process., 2005, 408(1-2), p 255-263.
W.-C. Kim, J.-G. Kim, J.-Y. Lee and H.-K. Seok, Influence of Ca on the Corrosion Properties of Magnesium for Biomaterials, Mater. Lett., 2008, 62(25), p 4146-4148.
A.A. Luo, M.P. Balogh and B.R. Powell, Creep and Microstructure of Magnesium-Aluminum-Calcium Based Alloys, Metall. Mater. Trans. A-Phys. Metall. Mater. Sci., 2002, 33(3), p 567-574.
Q.D. Wang, W.D. Chen, X.Q. Zeng, Y.Z. Lu, W.J. Ding, Y.P. Zhu, X.P. Xu and M. Mabuchi, Effects of Ca Addition on the Microstructure and Mechanical Properties of AZ91 Magnesium Alloy, J. Mater. Sci., 2001, 36(12), p 3035-3040.
A. Krause, N. von der Hoeh, D. Bormann, C. Krause, F.-W. Bach, H. Windhagen and A. Meyer-Lindenberg, Degradation Behaviour and Mechanical Properties of Magnesium Implants in Rabbit Tibiae, J. Mater. Sci., 2010, 45(3), p 624-632.
J.F. Song, Z. Wang, Y.D. Huang, A. Srinivasan, F. Beckmann, K.U. Kainer and N. Hort, Hot Tearing Susceptibility of Mg-Ca Binary Alloys, Metall. Mater. Trans. A-Phys. Metall. Mater. Sci., 2015, 46A(12), p 6003-6017.
S.S. Li, B. Tang, X.Y. Jin and D.B. Zeng, An Investigation on Hot-Cracking Mechanism of Sr Addition into Mg-6Al-05Mn Alloy, J. Mater. Sci., 2012, 47(4), p 2000-2004.
M. Pekguleryuz, P. Labelle and D. Argo, Magnesium Die Casting Alloy AJ62x with Superior Creep Resistance, Ductility and Die Castability, SAE Trans., 2003, 112, p 24-29.
H. Pan, K. Pang, F.Z. Cui, F. Ge, C. Man, X. Wang and Z.Y. Cui, Effect of Alloyed Sr on the Microstructure and Corrosion Behavior of Biodegradable Mg-Zn-Mn Alloy in Hanks’ Solution, Corrosion Sci., 2019, 157, p 420-437.
H.F. Li, S.J. Pang, Y. Liu, L.L. Sun, P.K. Liaw and T. Zhang, Biodegradable Mg-Zn-Ca-Sr Bulk Metallic Glasses with Enhanced Corrosion Performance for Biomedical Applications, Mater. Des., 2015, 67, p 9-19.
Z. Wang, Y.D. Huang, A. Srinivasan, Z. Liu, F. Beckmann, K.U. Kainer and N. Hort, Hot Tearing Susceptibility of Binary Mg-Y Alloy Castings, Mater. Des., 2013, 47, p 90-100.
S. Yao, Z. Wang, F. Wang, Z. Liu, P.L. Mao and X.P. Jiang, An Investigation on Hot Tearing of AZ91 Alloys with Yttrium Additions, Mater. Res. Express, 2019, 6(1), p 016554.
W.J. Liu, B. Jiang, Q.S. Yang, J.Q. Tao, B. Liu and F.S. Pan, Effect of Ce Addition on Hot Tearing Behavior of AZ91 Alloy, Prog. Nat. Sci., 2019, 29(4), p 453-456.
Y.H. Liu, Z.H. Wang, K. Liu, S.B. Li and W.B. Du, Effects of Er on Hot Cracking Susceptibility of Mg-5Zn-xEr Magnesium Alloys, Acta Metall. Sin., 2019, 55(3), p 389-398.
Z. Liu, S.B. Zhang, P.L. Mao and F. Wang, Effects of Y on hot tearing formation mechanism of Mg-Zn-Y-Zr alloys, Mater. Sci. Technol., 2014, 30(10), p 1214-1222.
S. Lun Sin and C. Ravindran, Effect of Silicon on the Hot Tearing Susceptibility of AZ91E Magnesium Alloy (11-080), Trans. Am. Foundry Soc., 2011, 119, p 461.
G. Vinodh, H.R.J. Nodooshan, D.J. Li, X.Q. Zeng, B. Hu, J.T. Carter and A.K. Sachdev, Effect of Al Content on Hot-Tearing Susceptibility of Mg-10Zn-xAl Alloys, Metall. Mater. Trans. A-Phys. Metall. Mater. Sci., 2020, 51(4), p 1897-1910.
Z.Q. Wei, S.M. Liu, Z. Liu, F. Wang, P.L. Mao, X.X. Wang and X.X. Li, Effects of Zn Content on Hot Tearing Susceptibility of Mg-7Gd-5Y-0.5Zr Alloy, Metals, 2020, 10(3), p 414.
B. Tang, S.-S. Li, X.-S. Wang, D.-B. Zeng and R. Wu, Effect of Ca/Sr composite addition into AZ91D alloy on hot-crack mechanism, Scr. Mater., 2005, 53(9), p 1077-1082.
Acknowledgment
The present work was supported by the National Natural Science Foundation of China (No. U2037601, 52071036) and the Fundamental Research Funds for the Central Universities Project (No. 2020CDJQY-A002).
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Zhao, H., Song, J., Jiang, B. et al. The Effect of Sr Addition on Hot Tearing Susceptibility of Mg-1Ca-xSr Alloys. J. of Materi Eng and Perform 30, 7645–7654 (2021). https://doi.org/10.1007/s11665-021-05925-8
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-021-05925-8