Abstract
A 2 mm thick Mg-2Nd-0.3Zn-0.4Zr (NZ20K) and AZ31 plates were friction stir welded. The microstructures of joint were compared and the tensile properties at room temperature and 200 °C were measured. The fracture features and the microhardness of joints were investigated. The effect of the strengthening phases in NZ20K joint was discussed compared with AZ31 joint. The results indicate that NZ20K shows better property especially at high-temperature environment. The grain of NZ20K in the nugget zone (NZ) is refined obviously with uniform distribution of strengthening phase particles and it shows clear boundary between NZ and thermo-mechanically affected zone (TMAZ). The grains of TMAZ are elongated because of the stir action of tool pin. The heat-affected zone is narrow with coarse grains. Mg12Nd is the main strengthening phase in NZ20K joint through XRD analysis. The ultimate tensile strength of NZ20K joint decreases a little from room temperature to 200 °C for its main strengthening phase particle-Mg12Nd being stable when the temperature goes up. On the contrast, the ultimate tensile strength of AZ31 joint decreases a lot at 200 °C for its strengthening phase soften or dissolve at high temperature. The hardness of NZ20K joint is higher than AZ31 joint and the lowest hardness of both joints is achieved on the advancing side where the fracture occurred.
Similar content being viewed by others
References
L. Zhou, K. Nakata, J. Liao, and T. Tsumura, Microstructural Characteristics and Mechanical Properties of Non-combustive Mg-9Al-Zn-Ca Magnesium Alloy Friction Stir Welded Joints, Mater. Des., 2012, 42, p 505–512
L.Z. Wang, J. Shen, and N. Xu, Effects of TiO2 Coating on the Microstructures and Mechanical Properties of Tungsten Inert Gas Welded AZ31 Magnesium Alloy Joints, Mater. Sci. Eng. A, 2011, 528, p 7276–7284
G. Padmanaban, V. Balasubramanian, and J.K. Sarin, Sundar, Influences of Welding Processes on Microstructure, Hardness, and Tensile Properties of AZ31B Magnesium Alloy, J. Mater. Eng. Perform., 2010, 19, p 155–165
Y.X. Wang, J.W. Fu, and Y.S. Yang, Effect of Nd Addition on Microstructures and Mechanical Properties of AZ80 Magnesium Alloys, Trans. Nonferrous Met. Soc. China, 2012, 22, p 1322–1328
M.E. Mohammadi, B. Nami, and S.M. Miresmaeili, Investigation on the Impression Creep Properties of a Cast Mg-6Al-1Zn Magnesium Alloy, Mater. Des., 2013, 51, p 427–431
J. Wang, J.W. Fu, X.G. Dong, and Y.S. Yang, Microstructure and Mechanical Properties of As-Cast Mg-Al-Sn-Y-Nd Alloy, Mater. Des., 2012, 36, p 432–437
J. Wang, L.M. Wang, J. An, and Y.B. Liu, Microstructure and Elevated Temperature Properties of Die-Cast AZ91-xNd Magnesium Alloys, J. Mater. Eng. Perform., 2008, 17, p 725–729
M.A. Easton, M.A. Gibson, D. Qiu, S.M. Zhu, and J. Gröbner, The Role of Crystallography and Thermodynamics on Phase Selection in Binary Magnesium-Rare Earth (Ce or Nd) Alloys, Acta Mater., 2012, 60, p 4420–4430
A.R. Wu and C.Q. Xia, Study of the Microstructure and Mechanical Properties of Mg-Rare Earth Alloys, Mater. Des., 2007, 28, p 1963–1967
V.K. Patel, S.D. Bhole, and D.L. Chen, Ultrasonic Spot Welded AZ31 Magnesium Alloy: Microstructure, Texture, and Lap Shear Strength, Mater. Sci. Eng. A, 2013, 569, p 78–85
K. Mroczka, A. Wójcicka, and A. Pietras, Characteristics of Dissimilar FSW Welds of Aluminum Alloys 2017A and 7075 on the Basis of Multiple Layer Research, J. Mater. Eng. Perform., 2013, 22, p 2698–2705
N. Afrin, D.L. Chen, X. Cao, and M. Jahazi, Microstructure and Tensile Properties of Friction Stir Welded AZ31B Magnesium Alloy, Mater. Sci. Eng. A, 2008, 472, p 179–186
S. Rajakumar, V. Balasubramanian, and A. Razalrose, Friction Stir and Pulsed Current Gas Metal Arc Welding of AZ61A Magnesium Alloy: A Comparative Study, Mater. Des., 2013, 49, p 267–278
R.P. Dobriyal, B.K. Dhindaw, S. Muthukumaran, and S.K. Mukherjee, Microstructure and Properties of Friction Stir Butt-Welded AE42 Magnesium Alloy, Mater. Sci. Eng. A, 2008, 477, p 243–249
J.F. Nie, Effects of Precipitate Shape and Orientation on Dispersion Strengthening in Magnesium Alloys, Scripta Mater., 2003, 48, p 1009–1015
J. Dai, J. Huang, M. Li, Z.G. Li, J. Dong, and Y.X. Wu, Effects of Heat Treatments on Laser Welded Mg-Rare Earth Alloy NZ30K, Mater. Sci. Eng. A, 2011, 529, p 401–405
GB/T 228.1-2010, Metallic Materials Tensile Testing—Part 1: Method of Test at Room Temperature, CN-GB.2010
GB/T 4338-2006, Metallic Materials-Tensile Testing at Elevated Temperature, CN-GB.2006
L. Wu, C. Cui, R. Wu, J. Li, H. Zhan, and M. Zhang, Effects of Ce-Rich RE Additions and Heat Treatment on the Microstructure and Tensile Properties of Mg-Li-Al-Zn-Based Alloy, Mater. Sci. Eng. A, 2011, 528, p 2174–2179
F.Y. Zheng, Y.J. Wu, L.M. Peng, X.W. Li, P.H. Fu, and W.J. Ding, Microstructures and Mechanical Properties of Friction Stir Processed Mg-2.0Nd-0.3Zn-1.0Zr Magnesium Alloy, J. Magn. Alloys, 2013, 1, p 122–127
Z.L. Ning, H. Wang, H.H. Liu, F.Y. Cao, S.T. Wang, and J.F. Sun, Effects of Nd on Microstructures and Properties at the Elevated Temperature of a Mg-0.3Zn-0.32Zr Alloy, Mater. Des., 2010, 31, p 4438–4444
J. Dai, J. Huang, and Y.X. Wu, Research on Laser Welding of Mg-Rare Earth Alloy Mg-3Nd-0.2Zn-0.4Zr, J. Mater. Eng. Perform., 2012, 21, p 208–212
W. Wang, K.S. Wang, Q. Guo, and N. Wu, Effect of Friction Stir Processing on Microstructure and Mechanical Properties of Cast AZ31 Magnesium Alloy, Rare Met. Mater. Eng., 2012, 41, p 1522–1526
S.M. Zhu, M.A. Gibson, J.F. Nie, M.A. Easton, and T.B. Abbott, Microstructural Analysis of the Creep Resistance of die-cast Mg-4Al-2RE alloy, Scripta Mater., 2008, 58, p 477–480
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhao, Y., Wang, Q., He, X. et al. Microstructure and Mechanical Properties of Friction Stir-Welded Mg-2Nd-0.3Zn-0.4Zr Magnesium Alloy. J. of Materi Eng and Perform 23, 4136–4142 (2014). https://doi.org/10.1007/s11665-014-1173-7
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-014-1173-7