Abstract
In this article, fracture toughness behavior of tool steel was investigated using Acoustic Emission (AE) monitoring. Fracture toughness (K IC) values of a specific tool steel was determined by applying various approaches based on conventional AE parameters, such as Acoustic Emission Cumulative Count (AECC), Acoustic Emission Energy Rate (AEER), and the combination of mechanical characteristics and AE information called sentry function. The critical fracture toughness values during crack propagation were achieved by means of relationship between the integral of the sentry function and cumulative fracture toughness (KICUM). Specimens were selected from AISI D2 cold-work tool steel and were heat treated at four different tempering conditions (300, 450, 525, and 575 °C). The results achieved through AE approaches were then compared with a methodology proposed by compact specimen testing according to ASTM standard E399. It was concluded that AE information was an efficient method to investigate fracture characteristics.
Similar content being viewed by others
References
L. Bourithis, G.D. Papadimitriou, and J. Sideris, Comparison of Wear Properties of Tool Steels AISI, D2 and O1 with the Same Hardness, J. Tribol. Int., 2006, 39, p 479–489
D. Dasa, A.K. Duttab, and K.K. Rayc, Influence of Varied Cryotreatment on the Wear Behavior of AISI, D2 Steel, J. Wear, 2009, 266, p 297–309
X. Ma, R. Liu, and D.Y. Li, Abrasive Wear Behaviour of D2 Tool Steel with Respect to Load and Sliding Speed Under Dry Sand/Rubber Wheel Abrasion Condition, J. Wear, 2000, 241, p 79–85
H. Chang, E. Han, J.Q. Wang, and W. Ke, Acoustic Emission Study of Corrosion Fatigue Crack Propagation Mechanism for LY12CZ and 7075-T6 Aluminum Alloys, J. Mater. Sci., 2005, 40, p 5669–5674
C.K. Mukhopadhyay, K.V. Kasiviswanathan, T. Jayakumar, and B. Raj, Acoustic Emission During Tensile Deformation of Annealed and Cold-Worked AISI Type 304 Austenitic Stainless Steel, J. Mater. Sci., 1993, 28, p 145–154
Y. Blanchettea, J.I. Dicksona, and M.N. Bassim, Detection of General Yielding in a516 Steel by Acoustic Emission, J. Eng. Fract. Mech., 1983, 17, p 227–234
M.N. Bassim, Detection of Fatigue Crack Propagation with Acoustic Emission, J. NDT & E Int., 1992, 25, p 287–289
M.N. Bassima, S.S. Lawrence, and C.D. Liu, Detection of the Onset of Fatigue Crack Growth in Rail Steels Using Acoustic Emission, J. Eng. Fract. Mech., 1994, 47, p 207–214
V.V. Korchevskii, Measurement of the Parameters of the Acoustic Emission When Metals are Stretched Acoustic Measurements, J. Meas. Tech., 2006, 49, p 517–523
C.T. Sindi, M.A. Najafabadi, and S.A. Ebrahimian, Fracture Toughness Determination of Heat Treated AISI, D2 Tool Steel Using AE Technique, J. ISIJ Int, 2011, 51, p 305–312
A. Refahi Oskouei, A. Zucchelli, M. Ahmadi, and G. Minak, An Integrated Approach Based on Acoustic Emission and Mechanical Information to Evaluate the Delamination Fracture Toughness at Mode I in Composite Laminate, J. Mater. Des., 2010. doi:10.1016/j.matdes.2010.08.048.
G. Minak and A. Zucchelli, Damage Evaluation and Residual Strength Prediction of CFRP Laminates by Means of Acoustic Emission Technique, Composite Materials Research Progress, L.P. Durand, Ed., Nova Science Publishers, New York, 2008, p 165–207
G. Minak, P. Morelli, and A. Zucchelli, Fatigue Residual Strength of Circular Laminate Graphite-Epoxy Composite Plates Damaged by Transverse Load, Compos. Sci. Technol., 2009, 69(9), p 1358–1363
G. Minak, S. Abrate, D. Ghelli, R. Panciroli, and A. Zucchelli, Residual Torsional Strength after Impact of CFRP Tubes, ICCE-17, World J. Eng., Honolulu (HI), 26 Luglio-1 August.
Y. Blanchettea, J.I. Dicksona, and M.N. Bassim, The Use of Acoustic Emission to Evaluate Critical Values of K and J in 7075-T651 Aluminum Alloy, J. Eng. Fract. Mech., 1984, 20, p 359–371
C.S. Camerini, J.M.A. Rebello, and S.D. Soares, Relationship Between Acoustic Emission and CTOD Testing for a Structural Steel, J. NDT & E Int., 1992, 25, p 127–133
T. Ohira, and Y.-H. Pao, Microcrack Initiation and Acoustic Emission During Fracture Toughness Tests of A533B Steel, J. Metall. Mater. Trans. A, 1986, 17, p 843–852
X. Long, G. Cai, and L.-E. Svensson, Investigation of Fracture and Determination of Fracture Toughness of Modified 9Cr-1Mo Steel Weld Metals Using AE Technique, J. Mater. Sci. Eng. A, 1999, 270, p 260–266
ASTM E399, Annual Book of ASTM Standards, Vol 03.01, American Society for Testing and Materials, New York, 2001
ASTM E8-01, Annual Book of ASTM Standards, Vol 03.01, American Society for Testing and Materials, New York, 2001
D. Dilipkumar, V.S.R. Gudimetla, and W.E. Wood, Amplitude-Distribution Analysis of Acoustic Emission, a Simplified Method of Amplitude-Distribution Analysis Based on Cumulative Counts and Events is Presented and a New Model for Amplitude Distribution is Proposed, J. Exp. Mech., 1979, 19, p 438–443
M. Arii, H. Kashiwaya, and T. Yanuki, Slow Crack Growth and Acoustic Emission Characteristics in COD Test, J. Eng. Fract. Mech., 1975, 7, p 551–552
H. Roy, N. Parida, S. Sivaprasad, S. Tarafder, and K.K. Ray, Acoustic Emissions During Fracture Toughness Tests of Steels Exhibiting Varying Ductility, J. Mater. Sci. Eng. A, 2008, 486, p 562–571
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Mostafavi, S., Fotouhi, M., Motasemi, A. et al. Acoustic Emission Methodology to Evaluate the Fracture Toughness in Heat Treated AISI D2 Tool Steel. J. of Materi Eng and Perform 21, 2106–2116 (2012). https://doi.org/10.1007/s11665-011-0119-6
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11665-011-0119-6