Abstract
The effects of nitrogen incorporation by high-dose ion implantation in epitaxial gadolinium oxide (Gd2O3) films on Si (111) followed by annealing have been investigated. The nitrogen content in the oxide layer was changed by altering the implantation dose. The presence of nitrogen incorporation on the Gd2O3 layer was studied using Auger electron spectroscopy. Nitrogen incorporation is believed to occur by filling the oxygen vacancies or by removing hydroxyl group ions in Gd2O3. A maximum concentration of 11% was obtained for nitrogen in the interface between the silicon dioxide and Gd2O3 layer and the implanted areas of the Gd2O3 oxide layer after sputter depth profiling. The nitrogen distribution in the layer was found to be non-uniform. Nitrogen incorporation sharply reduced the leakage current and effectively suppressed the hysteresis. Leakage current was two orders lower compared with the pure Gd2O3.
Article PDF
Similar content being viewed by others
References
H.S. Momose, S. Nakamura, T. Ohguro, T. Yoshitomi, E. Morifuji, T. Morimoto, Y. Katsumata, and H. Iwai, IEEE Trans. Electron Devices 45, 691 (1998).
J.L. Zhang, J.S. Yuan, Y. Ma, and S. Oates, Solid State Electron. 45, 373 (2001).
H.H. Ko, L.B. Chang, M.J. Jeng, P.Y. Kuei, and K.Y. Horng, Jpn. J. Appl. Phys. 44, 3205 (2005).
A.K. Jonsson, G.A. Niklasson, and M. Veszelei, Thin Solid Films 402, 242 (2002).
D.O. Lee, P. Roman, C.T. Wu, P. Mumbauer, M. Brubaker, R. Grant, and J. Ruzyllo, Solid State Electron. 46, 1671 (2002).
Y.C. Quan, J.E. Lee, H. Kang, Y. Roh, D. Jung, and C.W. Yang, Jpn. J. Appl. Phys. 41, 6904 (2002).
Y. Zhang, A. Navrotsky, H. Li, L. Li, L.L. Davis, and D.M. Strachan, J. Non-Cryst. Solids 296, 93 (2001).
L. Kang, B.H. Lee, W.J. Qi, Y. Jeon, R. Nich, S. Gopalan, K. Onishi, and J.C. Lee, IEEE Electron. Device Lett. 21, 181 (2000).
A. Chin, Y.H. Wu, S.B. Chen, C.C. Liao, and W.J. Chen, in Symposium on VLSI Technology (2000), p. 16.
J.K. Yang, M.G. Kang, and H.H. Park, Thin Solid Films 420–421, 571 (2002).
H.J. Osten, A. Laha, M. Czernohorsky, E. Bugiel, R. Dargis, and A. Fissel, Phys. Status Solidi (a) 205, 695 (2008).
M. Badylevich, S. Shamuilia, V.V. Afanas’ev, A. Stesmans, A. Laha, H.J. Osten, and A. Fissel, Appl. Phys. Lett. 90, 252101 (2007).
M.C. Lemme, H.D.B. Gottlob, T.J. Echtermeyer, M. Schmidt, H. Kurz, R. Endres, U. Schwalke, M. Czernohorsky, D. Tetzlaff, and H.J. Osten, J. Vac. Sci. Technol. B27, 258 (2009).
F. Natali, B.J. Ruck, N.O.V. Plank, H.J. Trodahl, S. Granville, C. Meyer, and W.R.L. Lambrecht, Prog. Mater Sci. 58, 1316 (2013).
J.C. Wang, Y.R. Ye, Y.H. Wu, C.F. Ai, and W.F. Tsai, Int. J. Nanotechnol. 11, 135 (2014).
K. Xiong, J. Robertson, and S.J. Clark, J. Appl. Phys. 99, 044105 (2006).
K. Tse, D. Liu, K. Xiong, and J. Robertson, Microelectron. Eng. 84, 2028 (2007).
C.H. Choi, S.J. Rhee, T.S. Jeon, N. Lu, J.H. Sim, R. Clark, M. Niwa, and D.L. Kwong, in Technical Digest—International Electron Devices Meeting (2003), p. 857.
X.B. Lu, Z.G. Liu, Y.P. Wang, Y. Yang, X.P. Wang, H.W. Zhou, and B.Y. Nguyen, J. Appl. Phys. 94, 1229 (2003).
C.S. Kang, H.J. Cho, K. Onishi, R. Nieh, R. Choi, S. Gopalan, S. Krishnan, J.H. Han, and J.C. Lee, Appl. Phys. Lett. 81, 2593 (2002).
A.R. Chaudhuri, A. Fissel, and H.J. Osten, J. Appl. Phys. 113, 184108 (2013).
A. Joseph, D. Tetzlaff, J. Schmidt, R. Böttger, T.F. Wietler, and H.J. Osten, J. Appl. Phys. 120, 144103 (2016).
M. Czernohorsky, A. Fissel, E. Bugiel, O. Kirfel, and H.J. Osten, Appl. Phys. Lett. 88, 152905 (2006).
W.R. McKenzie, P.R. Munroe, F. Budde, B.J. Ruck, S. Granville, and H.J. Trodhal, Curr. Appl. Phys. 6, 407 (2006).
M. Czernohorsky, D. Tetzlaff, E. Bugiel, R. Dargis, H.J. Osten, H.D.B. Gottlob, M. Schmidt, M.C. Lemme, and H. Kurz, Semicond. Sci. Technol. 23, 035010 (2008).
L.C. Feldman and J.W. Mayer, Fundamentals of Surface and Thin Film Analysis (Upper Saddle River: Prentice Hall, 1986).
T. Mizutani, Jpn. J. Appl. Phys. 30, L628 (1991).
J. Robertson, K. Xiong, S.J. Clark, and S.J. Clark, Defects in High-k Gate Dielectric Stacks NATO Science Series, Vol. 220, ed. E. Gusev (Dordrecht: Springer, 2006), p. 175.
S. Guha and V. Narayanan, Phys. Rev. Lett. 98, 196101 (2007).
R.M. Fleming, D.V. Lang, C.D.W. Jones, M.L. Steigerwald, D.W. Murphy, G.B. Alers, Y.-H. Wong, R.B. van Dover, J.R. Kwo, and A.M. Sergent, J. Appl. Phys. 88, 850 (2000).
P. Broqvist and A. Pasquarello, Appl. Phys. Lett. 89, 262904 (2006).
K. Xiong and J. Robertson, Appl. Phys. Lett. 95, 022903 (2009).
D. Liu, S.J. Clark, and J. Robertson, Appl. Phys. Lett. 96, 032905 (2010).
R. Meyer, R. Liedtke, and R. Waser, Appl. Phys. Lett. 86, 112904 (2005).
J. Wang and S. Trolier-Mckinstry, Appl. Phys. Lett. 89, 172906 (2006).
N. Umezawa, K. Shiraishi, T. Ohno, H. Watanabe, T. Chikyow, K. Torii, K. Yamabe, K. Yamada, H. Kitajima, and T. Arikado, Appl. Phys. Lett. 86, 143507 (2005).
A.R. Chaudhuri, A. Fissel, V.R. Archakam, and H.J. Osten, Appl. Phys. Lett. 102, 022904 (2013).
Acknowledgments
A.J. would like to thank the Hannover School for Nanotechnology (HSN) for a fellowship. Thanks to TU Clausthal for Auger electron spectroscopy characterization and Helmholtz-Zentrum Dresden-Rossendorf e.V., a member of the Helmholtz Association for ion implantation. We also thank the Laboratory of Nano and Quantum Engineering (LNQE) of the Leibniz Universitat Hannover.
Funding
Open Access funding provided by Projekt DEAL.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Joseph, A., Lilienkamp, G., Wietler, T.F. et al. Ion-Implanted Epitaxially Grown Gd2O3 on Silicon with Improved Electrical Properties. J. Electron. Mater. 49, 6270–6275 (2020). https://doi.org/10.1007/s11664-020-08392-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-020-08392-4