High-temperature strength and thermal shock resistance of austempered ductile iron (ADI) in high temperatures because of instability of ausferrite phase has been less interest. The aim of this study is to investigate the tensile properties of ADI and pearlitic ductile cast iron by using the short-time tensile test in high temperatures. Tensile test was conducted in temperatures of 298 K, 673 K, 873 K, and 1073 K (25 °C, 400 °C, 600 °C, and 800 °C). Thermal shock test also was conducted by using the molten lead bath at 1273 K (1000 °C). In this experiment, samples of pearlitic ductile cast iron and ADI were divided in two groups; that after immersing in the molten lead bath for 25 seconds, one group was cooled in the air and other one was quenched in the water. Results showed that strength and thermal shock resistance of ADI samples are higher than those of the pearlitic ductile cast iron.
Similar content being viewed by others
References
S. Seshan, S.Y. Buni, and N. Raman: Proc. Indian Academy of Sciences. (Sadhana), vol. 29, Part I, 2004, pp. 117–27.
K. Roehrig: AFS Trans., 1978, vol. 86. pp.75-88.
K.G. Davis, D.A. Brown, J.G. Magny, and D. Hui: AFS Trans., 1989, vol. 97, pp. 85-104.
C.P. Cheng, T.S. Lui, and L.H. Chen: Mater. Sci. Technol., 2004, vol. 20, pp. 243-50.
S. Kogoh, H. Ogino, T. Nakagawa, M. Kobayashi, and K. Asami: Int. J. Fatigue, 1990, vol. 12, pp. 199-205.
J. Pelleg and M. Engr: AFS Trans., 1963, vol. 71, pp. 315-20.
Y.J. Park and R.B. Gundlach: AFS Trans., 1987, vol. 95, pp.267-72.
C.P. Cheng, T.S. Lui, L.H. Chen, and S.M. Chen: Metall. Mater. Trans. A, 1997, vol. 28A, pp. 325-33.
C.P. Cheng, T.S. Lui, and L.H. Chen: Metall. Mater. Trans. A, 1999, vol. 30A, pp. 1549-58.
J.M. Massone, R.E. Boeri, and J.A. Sikora: Int. J. Cast Met. Res., 1996, vol. 9, pp. 79-85.
R.B. Gundlach: AFS Trans., 1983, vol. 91, pp. 389-421.
J.M. Gallardo, F.G. Cuevas, J. Cintas, J.M. Montes, and E.J. Herrera: Eng. Fail. Anal., 2006, vol. 13. pp. 292-300.
I.S. Kamenichnyĭ: A short handbook of heat treatment, Mir Publishers, Moscow, 1969, 275 p.
G. Krauss: Steels: Heat Treatment and Processing Principles, ASM, Materials Park, OH, 1990.
O. Celik, H. Ahlatci, E.S. Kayali, and H. Cimenoglu: Wear, 2005, vol. 258, pp.189-93.
C.S. Shieh, T.S. Lui, L.H. Chen: Mater. Trans., 1995, vol. 36, pp. 620-25.
S. Nadkarni, S. Gokhale, J.D. Boyd: AFS Trans., 1996, vol. 104, pp. 985-94.
D. Sosa, M.D. Echeverria, and O.J. Moncada: ISIJ. Int., 2004, vol. 44, pp. 195-1200.
M.D. Echeverria, O.J. Moncada, and J.A. Sikora: ISIJ Int., 2001, vol. 41. pp 25-30.
S. Korichi, R. Priestner: Mater. Sci. Technol., 1995, vol. 11, pp. 901-07.
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted October 28, 2007.
Rights and permissions
About this article
Cite this article
Ajabshiri, M., Sharafi, S. & Moeini, A. Comparison of High-Temperature Properties and Thermal Shock Resistance of Austempered Ductile Irons (ADI) with Those of Pearlitic Ductile Cast Irons. Metall Mater Trans A 43, 56–60 (2012). https://doi.org/10.1007/s11661-011-0855-0
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-011-0855-0