Abstract
The deformation behavior of the Zr3Al-Nb alloys was studied by measuring hardness at different temperatures, by hot rolling, and by hot pressing. Using the hardness data, elasticity and plasticity parameters were estimated and were used to determine the suitable temperature range of deformation for these alloys. Hot rolling and hot pressing were applied to determine the optimum temperatures and annealing time for carrying out deformation successfully in these alloys. Microstrural investigation of the hotdeformed samples revealed that the matrix β phase has undergone substantial deformation and the second intermetallic phase, Zr2(Al,Nb), underwent dissolution and re-precipitation. The hardness of the fully annealed Zr3Al-Nb alloys showed two types of temperature dependence. Transition temperatures for the change in behavior, intrinsic hardness, and softening coefficient were determined. The hardness of the fully annealed alloys rolled to different extent at various temperatures and subsequently heat treated was used to study the recovery process. The microstructural study of room-temperature deformed binary Zr3Al alloy showed the splitting of the superlattice dislocations into partials containing superlattice intrinsic stacking faults.
Similar content being viewed by others
References
E.M. Schulson: J. Nucl. Mater., 1979, vol. 83, p. 239.
E.M. Schulson: in Intermetallic Compounds, J.H. Westbrook and R.L. Fleischer, eds., John Wiley & Sons Ltd., New York, NY, 1994, vol. 2, p. 133.
E.M. Schulson and J.A. Roy: J. Nucl. Mater., 1977, vol. 71, p. 124.
H.E. Rosinger and B.J.S. Wilkins: J. Nucl. Mater., 1980, vol. 89, pp. 347–53.
K. Aoki and O. Izumi: J. Mater. Sci., 1979, vol. 14, p. 1800.
C.G. Mckamey, J.A. Horton, and C.T. Liu: J. Mater. Res., 1989, vol. 4, p. 1156.
D. Banerjee, A.K. Gogia, T.K. Nandy, and V.A. Joshi: Acta Metall., 1988, vol. 36, p. 871; D.A. Koss, D. Banerjee, D.A. Lukasak, and A.K. Gogia: in High Temperature Aluminides and Intermetallics, S.H. Whang, C.T. Liu, D.P. Pope, and J.O. Stiegler, eds., TMS, Warrendale, PA, 1990, p. 175.
L.M. Hsiung and H.N.G. Wadley: Scripta Metall. Mater., 1992, vol. 26, pp. 35–40.
L.M. Hsiung and H.N.G. Wadley: Scripta Metall. Mater., 1992, vol. 26, pp. 1071–76.
H.D. Merchant, G.S. Murthy, S.N. Bhadur, L.T. Dwivedi, and Y. Mehrotra: J. Mater. Sci., 1973, vol. 8, p. 437.
J.H. Westbrook: Trans. ASM, 1953, vol. 45, p. 221.
E.R. Petty: Metallurgica, 1957, vol. 56, p. 231.
Binary Alloy Phase Diagrams, T.B. Massalski, J.C. Murry, L.H. Bernett, and H. Baker, eds., ASM, Metals Park, OH, 1986, vol. 1, p. 187.
T.R.G. Kutty: Ph.D. Thesis, Indian Institute of Sciences, Bangalore, 1996.
R. Tewari, N. Prabhu, G.K. Dey, P. Mukhopadhyay, and S. Banerjee: Mater. Trans., 2002, vol. 33A, p. 1919.
R. Tewari: Ph.D. Thesis, IIT, Mumbai, 2000.
S. Banerjee and R.W. Cahn: Acta Metall., 1983, vol. 31, p. 721.
A. Howie and M.J. Whelan: Proc. R. Soc. A, 1962, vol. 267, p. 206.
G.E. Dieter: Mechanical Metallurgy, McGraw-Hill Book Company, New York, NY, 1986.
Y.V. Milman, B.A. Galanov, and S.I. Chugnova: Acta Metall. Mater., 1993, vol. 41, p. 2523.
P. Holdway and A.E. Staton-Bevan: J. Mater. Sci., 1986, vol. 21, pp. 2843–49.
Hand Book of Ternary Alloy Phase Diagrams, P. Villars, A. Prince, and H. Okamoto, eds., ASM INTERNATIONAL., Materials Park, OH, 1995, vol. 4, p. 4148.
R. Tewari, G.K. Dey, R.K. Fotedar, and N. Prabhu: Proc. Adv. Mater. Processing, Nov. 9–10, 2001, Roorkee, S. Ray, S. Singh, and S.K. Nath, eds., R.K. Printers and Publishers, Roorkee, 2001, p. 210.
A. Peruzzi and J. Bolcich: J. Nucl. Mater., 1990, vol. 174, p. 1.
R. Tewari, G.K. Dey, T.R.G. Kutty, A.K. Sengupta, N. Prabhu, and S. Banerjee: Metall. Mater. Trans. A, 2004, vol. 35A, pp. 205–16.
T.R.G. Kutty, K. Ravi, and C. Ganguly: J. Nucl. Mater., 1999, vol. 265, p. 91.
T.R.G. Kutty, T. Jarvis, and C. Ganguly: J. Nucl. Mater., 1997, vol. 246, p. 189.
A. Salnas-Rodriguez, M.G. Akben, J.J. Jonas, and E.F. Ibrahim: Can. Met. Q., 1985, vol. 24, p. 259.
S.G. Song and G.T. Gray III: Metall. Trans. A, 1995, vol. 26A, pp. 2665–76.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Tewari, R., Dey, G.K., Fotedar, R.K. et al. Deformation behavior of Zr3Al-Nb alloys I: Room-temperature and high-temperature deformation study. Metall Mater Trans A 35, 189–203 (2004). https://doi.org/10.1007/s11661-004-0120-x
Received:
Issue Date:
DOI: https://doi.org/10.1007/s11661-004-0120-x