Abstract
We prepared the nano-inorganic phase-change “alloy” materials through the modification of Na2SO4•10H2O using Na2HPO4•12H2O and GO nano-nucleating agent, and further investigated their thermophysical properties such as melting/solidification temperatures and enthalpies via differential scanning calorimetry. When the weight ratio of Na2SO4•10H2O and Na2HPO4•12H2O was 8:2 and the weight ratio of graphene oxide was 0.5% of phase change material, the phase change “alloy” material showed excellent performances, specifically, the melting temperature and latent heat were found to be 22 °C and 190 J/g with a degree of subcooling decreased from 8.6°C to 2.1°C. In order to extend the application of the phase change “alloy” material to building energy saving field, it was adsorbed on expanded glass beads under vacuum and further covered with diatomite. When the adsorption rate of EGB (volume) and PCAM (weight) was 2.5:1, the particle size of diatomaceous earth was found to be 3.6μm, while the best packaging result was obtained with the melting temperature and latent heat being 21°C and 135J/g, and no leakage was observed.
Similar content being viewed by others
References
Xiao LG, Ding R, Sun H. A New Kind of Shape-stabilized Phase Change Materials[J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2011, 26(3): 491–494
K Pielichowska, K Pielichowski. Phase Change Materials for Thermal Energy Storage[J]. Progress in Materials Science, 2014, 65(10): 67–123
Ling TC, Poon CS. Use of Phase Change Materials for Thermal Energy Storage in Concrete: An Overview[J]. Construction & Building Materials, 2013,46(8): 55–62
Zhou D, ZHAO CY, Tian Y, et al. Review on Thermal Energy Storage with Phase Change Materials (PCMs) in Building Applications[J]. Applied Energy, 2012, 92 (4): 593–605
Shin HK, Park M, Kim HY, et al. Thermal Property and Latent Heat Energy Storage Behavior of Sodium Acetate Trihydrate Composites Containing Expanded Graphite and Carboxymethyl Cellulose for Phase Change Materials[J]. Applied Thermal Engineering, 2015, 75(1):978–983
Sanusi O, Warzoha R, Fleischer AS. Energy Storage and Solidification of Paraffin Phase Change Material Embedded with Graphite Nanofibers[J]. International Journal of Heat & Mass Transfer, 2011, 54: 4429–4436
Geim AK. Graphene: Status and Prospects[J]. Science, 2009, 324 (5934): 1530–1534
Fan LW, Fang X, Wang X, et al. Effects of Various Carbon Nanofillers on The Thermal Conductivity and Energy Storage Properties of Paraffin-based Nano-composite Phase Change Materials[J]. Applied Energy, 2013, 110: 163–172
Yuan K, Wang H, Liu J, et al. Novel Slurry Containing Graphene Oxide-grafted Microencapsulated Phase Change Material with Enhanced Thermo-physical Properties and Photo-thermal Performance[J]. Solar Energy Materials & Solar Cells, 2015, 143: 29–37
Qi GQ, Yang J, Bao RY, et al. Enhanced Comprehensive Performance of Polyethylene Glycol Based Phase Change Material with Hybrid Graphene Nanomaterials for Thermal Energy Storage[J]. Carbon, 2015,88: 196–205
Author information
Authors and Affiliations
Corresponding author
Additional information
Fund by the National Key Technologies Research and Development Program of China (No. 2016YFC0701002)
Rights and permissions
About this article
Cite this article
Xiao, L., Zhao, M. & Hu, H. Study on Graphene Oxide Modified Inorganic Phase Change Materials and Their Packaging Behavior. J. Wuhan Univ. Technol.-Mat. Sci. Edit. 33, 788–792 (2018). https://doi.org/10.1007/s11595-018-1894-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11595-018-1894-9