Abstract
It is generally challenging to predict the post-abandonment behaviour and integrity of wellbores. Leakage is, moreover, difficult to mitigate, particularly between the steel casing and outer cement sheath. Radially expanding the casing with some form of internal plug, thereby closing annular voids and fractures around it, offers a possible solution to both issues. However, such expansion requires development of substantial internal stresses. Chemical reactions that involve a solid volume increase and produce a force of crystallisation (FoC), such as CaO hydration, offer obvious potential. However, while thermodynamically capable of producing stresses in the GPa range, the maximum stress obtainable by CaO hydration has not been validated or determined experimentally. Here, we report uniaxial compaction/expansion experiments performed in an oedometer-type apparatus on precompacted CaO powder, at 65 °C and at atmospheric pore fluid pressure. Using this set-up, the FoC generated during CaO hydration could be measured directly. Our results show FoC-induced stresses reaching up to 153 MPa, with reaction stopping or slowing down before completion. Failure to achieve the GPa stresses predicted by theory is attributed to competition between FoC development and its inhibiting effect on reaction progress. Microstructural observations indicate that reaction-induced stresses shut down pathways for water into the sample, hampering ongoing reaction and limiting the magnitude of stress build-up to the values observed. The results nonetheless point the way to understanding the behaviour of such systems and to finding engineering solutions that may allow large controlled stresses and strains to be achieved in wellbore sealing operations in future.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Avoid common mistakes on your manuscript.
1 Introduction
As ageing hydrocarbon fields approach the end of their productive and economic life [63, 81, 125], and as various options for their potential reuse, such as geological storage of CO2 [3, 50, 127] or of energy [8, 52, 99] emerge, wellbore sealing issues are becoming ever more important [5, 19]. In particular, effective plug and wellbore sealing procedures, ensuring long-term zonal isolation, are essential (a) for complying with increasingly stringent environmental regulations applying to well and reservoir abandonment [109] and (b) for enabling reuse of reservoirs in future applications [51].
In most existing wells, the borehole is lined with a string of concentric steel tubes (called casings and liners). The tubes are fixed in place and sealed against the wall rock using Portland-based cement [91]. These cement seals are susceptible to various forms of failure [42, 90]. For example, during emplacement, poor removal of drilling mud or filter cake may impair bonding between the cement, the casing and the surrounding rock [1, 76]. Moreover, cement shrinkage upon hardening, inherent to some of the processes involved in hydration [117], produces radial contraction that may result in tensile fracturing of the cement or debonding at the casing-cement and cement-formation interfaces [26, 33]. In addition, fluctuations in temperature and stress state, endured by the wellbore during field operations, may further contribute to the accumulation of structural damage [77, 80, 83, 93, 102].
Regardless of their origin, such defects offer pathways for fluid flow that may compromise well integrity [132]. Indeed, considerable numbers of wells are known to have zonal isolation issues. Analysis of 315,000 oil, gas and injection wells in Alberta showed that ~4.6% of these wells displayed surface casing vent flow or gas migration [4]. For energy wells completed since 1971, this percentage is higher, with ~14% exhibiting surface casing vent flow of >300 m3 day−1 [58]. Of 41,381 wells drilled in Pennsylvania between 2000 and 2012, ~1.9% showed some form of structural integrity failure [55]. Moreover, sustained casing pressure (unintended development of pressure at the surface, at the well, which rebuilds after bleeding off) is reported in ~43% of the producing and abandoned wells located on the outer continental shelf of the Gulf of Mexico [15]. If unwanted fluid migration phenomena such as these progressively impair the well or already exceed the maximum rate allowed by regulations, remedial measures are required.
Squeeze cementing operations are common practice in mitigating leakage occurring behind the casing, i.e. outside of the steel pipe (annular leakage). Squeeze cementing involves perforation of the casing over the defective wellbore interval, followed by injection of cement to seal annular voids and fractures [91]. However, this conventional approach is often ineffective. A performance study of squeeze cementing operations performed on wells in west Texas found that first-attempt remediation was successful in only 47 of 137 cases (34%), and that the success rate for multiple attempts (up to five per well) was <60% [25]. There is therefore substantial interest in alternative approaches to leakage mitigation, such as the casing expansion procedure recently proposed by Kupresan et al. [74, 75]. This involves permanent radial expansion of the casing pipe, thereby closing annuli, fractures and other voids outside the casing, while placing the cement there under compression. Kupresan et al. [74, 75] tested this method in three laboratory experiments on composite samples consisting of two concentric steel cylinders (length 60 cm, diameter inner pipe ~6 cm, diameter outer pipe ~10.2 cm), where cement was injected in the annular region between these two pipes. After curing, sealing was poor due to the induction/presence of debonding defects at the inner pipe wall, producing apparent sample permeabilities of 1.4 × 10−13–7.1 × 10−12 m2. Subsequent expansion of the inner pipe, by 2–8% via internal pressurisation or swaging, caused significant reduction in permeability, reducing this to ~3 × 10−19 m2 in the initially most permeable sample and to values below detection in the other two samples [74, 75]. These findings are promising, especially since increased confinement may help maintain the mechanical stability of the cement, i.e. by promoting permanent cohesive compaction as opposed to fracture [129].
A potential limitation to the method proposed by Kupresan et al. [74, 75], is that the casing diameter must be plastically expanded. In their experiments, this was achieved using (ductile) expandable casing tube technology [18, 88], swaged open with a pull-through mandrel and internal expansion cones. While expandable steel casings can be used in both new and existing wells, and have been applied effectively in remedial operations targeting punctured casings [6], it remains a relatively new technology [32]. This means that both legacy and presently operating wells, i.e. wells requiring abandonment in the coming decades, are generally furnished with conventional casing strings. This raises the question of whether or not the casing expansion concept can be applied, perhaps in modified form, to traditional casings. In such cases, the maximum attainable expansion ratios would necessarily be low (<2%), since generally less ductile types of steel have been employed to date [56] than now appearing. However, even this limited expansion could still be effective, particularly in remedying leakage of CO2-bearing fluids. For CO2-rich fluids, it may be sufficient to reduce the aperture of fractures and debonding defects only to the point where reactive transport leads to self-sealing behaviour [17, 20, 53, 130], rather than completely closing interfacial flaws by purely mechanical means. Yet, it would not be trivial to expand conventional casing strings by even 1–2% using the pull-through mandrel methods that are now being applied to expandable wellbore casing tubes. These approaches require the pipe wall to be smooth and of uniform thickness [18], while the wall thickness of conventional casing is rather poorly controlled, with specifications allowing for 12.5% variability [56]. Alongside mineral scaling, present in many existing wellbores [34, 62], significant lubrication issues are therefore expected [30], which in turn could cause swaging to induce considerable damage to the casing tube [18]. Given these difficulties, alternative approaches are needed for expanding conventional wellbore casings to seal leakage pathways outside of the casing in existing wellbores, e.g. during wellbore abandonment procedures.
Chemical reactions that involve a solid volume increase and produce a force of crystallisation (FoC) [38, 110, 126], such as the hydration of CaO [21], offer obvious potential as agents causing expansion, and already find use in controlled, non-explosive demolition of building infrastructure [48]. These reactions are thermodynamically capable of producing very large mechanical stresses [67, 94, 119]. For the case of CaO hydration, thermodynamic models [67, 68], taking Gibbs energy of reaction and solid volume change data representative for downhole temperatures [82], predict FoC-induced stresses of up to ~3.4 GPa. By comparison, preliminary calculations using Barlow’s formula for the expansion of a cylindrical metal tube [7, 124], plus typical casing tube dimensions and plastic yield data for conventional casing steels [56], suggest that expanding conventional wellbore casing via internal pressurisation would require effective internal stresses in the range of 100–300 MPa. Constraints from casing burst studies provide similar values [39, 64]. As such, the stresses that could potentially be induced, if a wellbore would be plugged with low-porosity CaO aggregate, are more than sufficient to bring about casing expansion leading to mechanical closure of annuli and fractures similar to that seen in the experiments of Kupresan et al. [74, 75]. However, whether these theoretical FoC stresses can be attained in practice depends on whether reaction can go to completion, and hence on the reaction kinetics, the supply of reactants, the reaction mechanism, and the effect of stress on reaction. Moreover, at least some degree of control on the strains that develop upon CaO hydration would be required, to avoid excessive expansions that otherwise may lead to casing rupture.
Successful application of CaO hydration-induced FoC development in the expansion of wellbore casing would require a thorough, quantitative understanding of (a) the reaction mechanism controlling CaO hydration, (b) the deformation and fluid transport processes controlling stress and strain evolution and (c) whether the hydration process can be sufficiently regulated. In this study, we take a first step in this regard, by directly measuring the force of crystallisation generated during CaO hydration. Our results show FoC-induced stresses of up to 153 MPa. We discuss the reasons for the shortfall compared with thermodynamic theory and provide some suggestions for finding engineering solutions that may allow larger hydration-induced stresses and strains to be achieved in wellbore sealing operations in future.
2 Background information
Before presenting and analysing our experiments, we first introduce the basic concept of force of crystallisation, and briefly summarise previous experimental measurements and thermodynamic models addressing the phenomenon. We go on to derive our own thermodynamic model, establishing a framework in which to consider CaO hydration in our experiments.
2.1 Force of crystallisation: examples and previous measurements
Consider a fluid-mediated chemical reaction that involves dissolution of the reacting solid phases and precipitation of solid products from a supersaturated solution. When such a reaction involves an increase in solid volume and proceeds in a confined space, this can lead to development of a so-called force of crystallisation (FoC) [9, 22, 38, 105, 114, 126]. In other words, reaction can result in stress being exerted on the confining boundaries of the system. In principle, any thermodynamic driving force that can produce a supersaturation with respect to the solid product phase can generate a FoC, as long as precipitation can occur under confined conditions, e.g. within load-bearing grain contacts [10, 103]. Well-known examples of such reactions include salt damage [24, 106], where supersaturation is achieved via evaporation and surface curvature effects [108, 110, 111], and a wide range of mineral reactions where the solid products comprise a larger volume than the solid reactants. Frost heave [24, 49, 115], where crystallisation is driven by a temperature-related phase change (cf. [114]), is a similar process. Examples of mineral reactions that have been shown or are believed to produce a FoC include (a) uptake of crystallisation water by thenardite to produce mirabilite [35, 118], (b) delayed ettringite formation in concrete [37, 54, 116], (c) serpentinisation and possibly carbonation of peridotite [60, 67, 68, 97, 104], (d) replacement of leucite by analcime in low-silica rocks [61], (e) conversion of anhydrite into gypsum [70] and (f) the hydration of metal oxides such as quicklime (CaO) and periclase (MgO) [43, 94]. In a geological context, development of a force of crystallisation is widely considered to play an important role in pseudomorphic replacement [40, 89], as well as vein formation [40, 47, 87, 114] and reaction-driven fracturing [61, 97, 100, 104].
Despite this previous work on FoC-related processes, relatively few studies have been conducted where the magnitude of the FoC is determined directly. Becker and Day [9] attempted FoC measurement via the placement of dead weights on crystals growing from supersaturated solutions, created by gradual evaporation or cooling. They found that centimetre-sized crystals of alum, growing between glass plates, continued to grow and could raise a weight of 1 kg through distances of several hundreds of micrometres, and reported similar findings for copper sulphate, lead nitrate and potassium ferrocyanide. On the lower surface of the crystals, precipitation of new material was restricted to the periphery, producing a hopper-like morphology (see also [103]), preventing accurate determination of load-supporting area and hence stress corresponding to the FoC. The presence of unloaded crystals in the same solution was found to inhibit growth of the loaded crystal surfaces [10, 16, 114]. Performing similar experiments with improved resolution in displacement, Correns and Steinborn [23] and Correns [22] collected extensive data and demonstrated that the ability of alum crystals to lift a dead weight depended not only on the supersaturation, but also on which crystallographic plane was the loaded surface (see [38] for a recent commentary on these experiments). Khaimov-Mal’kov [71] repeated many of the earlier experiments on alum and reported crystal growth against a stress of 20 kg cm−2 (~1.96 MPa) at 20% supersaturation. Also using a dead weight approach, Keulen et al. [70] reported hydration of anhydrite to form gypsum, causing expansion against stresses of up to ~11 MPa. However, by far the largest stresses measured to date, at least to our knowledge, have been observed during CaO and MgO hydration. In experiments reported by Ostapenko [94], MgO samples were tightly confined in steel cylinders and subsequently hydrated, causing the sample to expand. This resulted in bulging or rupturing of the cylinders. The FoC that developed was estimated on the basis of the strength of the steel, by performing tests using cylinders of different wall thickness. The FoC-related stress estimates obtained ranged from 20 to 200 MPa. Similarly, using high-pressure expansion cells, Ghofrani and Plack [43] found that swelling cements based on CaO and MgO additives expand effectively against hydrostatic pressures up to 120 MPa.
2.2 Thermodynamic models
2.2.1 Previous work
The first steps towards a thermodynamic treatment of the force of crystallisation were made by Correns and Steinborn [23]. Based on chemical potential and energy balance arguments, they derived an expression for maximum stress generated as a function of supersaturation of the solution phase (S), represented by S = c/c s, with c and c s solute concentrations in the supersaturated and a saturated solution, respectively. The result obtained was:
where σ eff = σ n – P is the maximum effective stress generated due to crystallisation, P is the fluid pressure, σ n is the normal stress on the loaded surface of the growing crystal, R is the gas constant, T is the absolute temperature, and V m is the molar volume of the precipitating solid phase. Correns and Steinborn [23] further stated that, for a stressed crystal to continue to grow, there must exist a solution phase that separates the loaded crystal face from its constraint, as otherwise deposition of matter and growth in the load-bearing interface would be impossible (cf. [22, 105].
Several thermodynamic treatments and models have subsequently been published [36, 72, 105, 106, 126]. The models differ mainly in how the supersaturation (S) is defined, e.g. in terms of solute activities, ion activity products, or in terms of the surface curvature of neighbouring crystals. Steiger [110, 111] reviewed these thermodynamic models and provided a comprehensive analysis, deriving an equation for the FoC based on chemical potentials of stressed and unstressed crystal faces, demonstrating the equivalence of the previous expressions, and considering effects of non-ideal behaviour of the solution phase.
The thermodynamic models discussed above consider direct precipitation from a (typically stoichiometrically) supersaturated solution, as investigated in the bulk of quantitative experimental studies to date (Sect. 2.1). Though without explicitly stating the steps involved, a number of studies [67, 68, 94] have generalised these models to include more complex chemical reactions, obtaining the result
where ΔG r is the Gibbs energy change of reaction and ΔV s denotes the solid volume change associated with the reaction per mole (cf. Eqn. E5 of Kelemen and Hirth [67]). To our knowledge, these models have not been experimentally verified.
2.2.2 Model for FoC development and application to CaO hydration
We will now explicitly derive a similar expression to Eq. 2 and subsequently apply the result to CaO hydration, which is the target of our experiments. Throughout, we adopt the convention that compressive stresses and volume expansions are represented positive. In deriving the model, it is assumed that reaction will not be inhibited by clogging of transport pathways, by sealing of grain boundaries, or by stress-driven expulsion of the solution phase from grain boundaries. In other words, it is assumed that a solution phase remains present in the loaded interfaces (cf. [22, 105]). This may, for instance, be in the form of thin films or microscale channels, observed to occur during stress-driven dissolution or pressure solution [28, 29, 120, 121]. The initial solid (CaO powder in our experiments) will be considered to consist of a single, pure phase. Reaction will be treated as a replacement process, i.e. with solid products and reactants in contact across fluid-filled grain boundaries and therefore experiencing the same stress. The aqueous solution phase present in the open pores is assumed to be well mixed and to exist at a reference pressure (P) and temperature (T). Prior to any reaction, the initial solid phase is assumed to be in mechanical and thermal equilibrium with this solution phase, i.e. also characterised by a hydrostatic stress state of magnitude P and temperature T. In addition, we assume that reaction occurs under isothermal conditions and that no other dissipative processes operate in the system.
Under hydrostatic reference conditions (P, T), the Gibbs free energy change of reaction (i.e. the thermodynamic driving force) for any given reaction involving I solid phases and J components in the solution phase can be written as
Here, ν are stoichiometric coefficients for the I solid phases and J components in the solution phase participating in reaction, while μ PT are the chemical potentials of these components in the hydrostatic reference state (P, T). Of course, ν is positive for reaction products and negative for reactants.
If the growth of the solid products is restricted by a zero or limited displacement boundary condition, then reaction will lead to the build-up of a normal stress (σ) at the interfaces of the product and reactant grains. Assuming drained conditions, i.e. that the fluid phase remains at the initial pressure P, ongoing reaction in the stressed state will be associated with the free energy change (cf. Eq. 3)
Here, μ σT i are chemical potentials of the solid phases at stress σ and temperature T, while μ (σ)PT j are the chemical potentials of the components present in the solution phase, which in general will be different compared with the initial (P, T) conditions, due to changes in their concentration in the stressed state.
As constricted reaction proceeds, the stress experienced by the solid phases will continue to increase, until the stressed solids are in equilibrium with the components present in the solution phase, i.e. until Δr G σT = 0. Putting this into Eq. 4 and making use of Eq. 3, the change in total free energy of the solid phases in the stressed state (σ, T) compared with the reference state (P, T) can be written as
For solid phases, the chemical potential is a surface property [44], which from thermodynamic treatments of stressed solids [27, 44, 65, 66, 78, 79, 86, 95] can be related to the normal stress (σ) acting on the crystal surface via:
Here, f σT i and V σTm,i denote the molar Helmholtz free energy and molar volume of solid i in the stressed state (e.g. [78]). For the hydrostatic reference conditions (P, T), we have μ PT i = f PT i + PV PTm,i . Considering elastic strain of the solids and assuming the normal stress on the solids (σ) to be isotropic, the molar volume of the solid in the stressed state (σ, T) can be written in terms of the molar volume of the solid under hydrostatic conditions (P, T), yielding
where ΔV m,i is the difference in molar volume between the stressed and unstressed solid, and B i is the bulk modulus of the solid. The energy associated with elastic strain of the stressed solid contributes to its molar Helmholtz free energy, for which we may correspondingly write
where Δf i is the difference in molar Helmholtz free energy between the stressed and unstressed solid, and e V is the volumetric strain associated with application of isotropic stress σ. Equations 5, 6, 7 and 8 can be combined to obtain
For FoC-induced stresses of up to a few GPa, the terms σ/(2B i ) will be small (given typical bulk moduli in the range of 10–100s of GPa). As such, it is easily shown that small differences in elastic strain between the stressed and unstressed solids may be neglected. Taking f σT i ≈ f PT i and V σTm,i ≈ V PTm,i , Eq. 9 simplifies to
This gives the maximum effective normal stress that can develop due to precipitation of a confined solid product phase, i.e. the stress attained at equilibrium or the stress required to remove the driving force for further reaction. Note that Eq. 10 corresponds to Eq. 2 only if reaction-induced changes in the chemical potentials of the components present in the solution phase can be neglected, which in general is by no means clear, for example, when considering complex chemical reactions.
Let us now apply Eq. 10 to the specific case of CaO hydration. When CaO is exposed to water, this will lead to the formation of Ca(OH)2 (portlandite). Two different reaction mechanisms have been reported for this hydration, namely (a) “vapour phase hydration”, which occurs via a pseudomorphic, topotactic, solid-state transformation involving an intermediate, disordered Ca(OH)2 phase [11, 45, 73], and (b) so-called “through-solution” or “wet hydration”. For this second mechanism, it is at present unclear whether (a) the CaO first dissolves in the solution phase (water) and subsequently precipitates as Ca(OH)2 [12, 84, 101, 128], or (b) direct conversion of CaO into Ca(OH)2 occurs, as in vapour phase hydration, followed by (partial) dissolution (and re-precipitation) of the Ca(OH)2 formed [12, 113].
In the confined experiments reported here, “wet hydration” is considered the most likely mechanism, at least initially, as reaction was initiated by vacuum-flushing liquid water into the sample chamber. Assuming a stoichiometrically balanced chemical reaction (as expressed in Eqs. 3 and 10), we now have to consider the two possible reaction pathways for the wet hydration process discussed above. If this process involves a true dissolution–precipitation mechanism (e.g. [101]), and we allow for complete reaction being prevented by stress build-up, then we must have
where per mole of CaO that dissolves α moles of Ca(OH)2 precipitate, with α ≤ 1. Alternatively, if wet hydration would involve direct transformation of CaO into Ca(OH)2 (e.g. [113]), then we must have
where per mole of CaO that converts (1 − α) moles of the Ca(OH)2 formed subsequently dissolves again with α ≤ 1. Note that Eqs. 11a and 11b yield the same net reaction, regardless of the specific pathway. The value of α will depend on various system properties, such as the fluid composition and the effective fluid-to-solid ratio. Considering the overall transfer of mass that is involved in attaining equilibrium, i.e. in going from the initial, hydrostatic reference state (P, T) to the stressed equilibrium state (σ, T), the final equilibrium state must be such that the Ca2+ and OH− concentrations in the fluid (or, rather, their chemical activities) are in equilibrium with the solids, so that at least some dissolved material remains in solution, with α < 1. However, given the low solubility of Ca(OH)2 [31], combined with low fluid-to-rock ratios characterising the experiments reported here, we expect that taking α ≈ 1 will not introduce significant error. In other words, the mass of calcium hydroxide stored in the solution phase will be negligible compared with that precipitated. Making the assumption α ≈ 1, Eq. 11 simplifies to
and, in turn, means that Eq. 10 can be simplified and rewritten as
where Δr G PT is now expressed in terms of the Gibbs energies of formation (Δf G PT) of the subscripted chemical species at the reference P, T conditions. This result is essentially equivalent to Eq. 2 (cf. Eqn. E5 of Kelemen and Hirth [67]). However, note that it rests on the assumption that α = 1, i.e. it neglects compositional change in the solution phase, as well as neglecting stress-induced changes in f i and V m,i .
The standard molar thermodynamic properties of the chemical species involved (i.e. in Eq. 12) can be found for P = 0.1 MPa (1 bar) and T = 298.15 K (25 °C) in the papers by Matschei et al. [85] and Lothenbach et al. [82], and are listed in Table 1. Following Lothenbach et al. [82], the corresponding values at 65 °C were calculated using [2]
where T 0 is the reference (standard) temperature (298.15 K) and β x (x = 0, 1, 2, 3) are the empirical coefficients of a heat capacity equation of the form C P (T) = β 0 + β 1 T + β 2 T −2 + β 3 T −0.5.
Using Eq. 13 with the thermodynamic data in Table 1, it is straightforward to calculate the maximum stress that can develop at the surface of a confined crystal of portlandite [Ca(OH)2] growing as a result of CaO hydration under initial conditions (P, T). Doing so for reaction at 65 °C and atmospheric fluid pressure yields a value of ~3.4 GPa.
3 Experimental methods
To measure the force of crystallisation that is generated during CaO hydration, we performed compaction/expansion experiments on CaO powder at a temperature of 65 °C, representative for shallow crustal reservoirs, using a uniaxial deformation (oedometer-type) set-up located in an Instron loading frame. After dry precompaction, the sample assembly containing the CaO aggregate was flooded with water, initiating the hydration reaction. Three types of experiments were performed, namely (a) position-control experiments, in which the Instron position was fixed so as to restrict sample expansion as much as possible, thus allowing a force of crystallisation to develop, (b) load-limit experiments, in which the Instron was programmed to initially maintain a fixed position, but switch to load-control mode once the FoC-induced axial stress attained a preset threshold value and (c) constant-load experiments, where the Instron load was fixed, allowing measurement of CaO hydration-induced expansion against a constant axial force (and hence stress). A complete list of the experiments performed, together with key experimental data, is given in Table 2.
3.1 Sample material and assembly
The CaO powder used in this study was prepared from Carrara marble (high-purity CaCO3), which for this purpose was crushed and sieved to a grain size of 90–150 μm. Prior to each experiment, a batch of marble powder was calcined at 1100 °C for ~16 h. The calcined powder was retrieved after allowing the furnace to cool to ~350 °C. After thorough mixing and disaggregation of the CaO powder obtained, some 120–360 mg was located in the sample assembly, depending on desired sample thickness. This assembly consisted of a small compaction die furnished with upper and lower loading pistons (outer diameter 19.8 mm, bore diameter 9.8 mm—Fig. 1a), all constructed from Monel K-500, a corrosion resistant nickel-copper alloy. The top piston of the assembly contained a central bore and was tipped with a stainless steel porous plate (Fig. 1a) to provide pore fluid access to the sample during the experiments. The bottom piston was solid. Note that before loading the sample into the sample assembly, the assembly was oven-dried overnight at 50 °C.
3.2 Experimental set-up
The CaO hydration experiments were performed by placing the sample assembly/die into an externally heated, uniaxial compaction apparatus (Fig. 1b), applying load by means of an Instron 8862 servo-controlled testing machine (Fig. 1c)—see Schutjens [107] and Pluymakers et al. [98]. The compaction apparatus consists of a pressure vessel with a fixed bottom piston and movable top piston, constructed from Monel K-500. The diameter of the vessel bore and loading pistons are nominally 20 mm, with the sample assembly described above fitting closely inside (Fig. 1a). Sealing of the loading piston in the main compaction vessel was achieved using Viton O-rings. Pore fluid was supplied to the sample assembly via a central bore in the top piston. The force applied to the sample assembly via the top piston was measured externally, using the Instron load cell (100 kN range, resolution ±0.05 kN), while that supported by the bottom piston was measured using an internal load cell located in the bottom piston of the main compaction vessel (100 kN range, resolution ±0.05 kN). Displacement of the main vessel piston relative to the main vessel was measured externally using a linear variable differential transformer (LVDT; range ±1 mm, resolution, ±1 μm), mounted between the top piston and the top of the pressure vessel (Fig. 1b). Experiment temperature was regulated to within ±0.5 °C using a K-type chromel–alumel thermocouple, located between the furnace windings, connected to a proportional-integral-derivative controller. Sample temperature was measured using a second K-type thermocouple, embedded in the vessel wall close to the sample position.
3.3 Testing procedure
In each experiment, the CaO-loaded sample assembly (Fig. 1a) was first precompacted outside the main compaction vessel for 1 h at 250 MPa axial stress, under laboratory dry conditions. This was done by directly loading the sample assembly/die using only the Instron loading frame and produced disc-shaped CaO aggregates. The top piston of the sample assembly was then extracted to remove powder adhering to the piston and sample vessel bore. After returning the top piston, the sample assembly was weighed to determine the mass of CaO powder (m 0—Table 2) present in the sample assembly. The assembly was then carefully lowered into the main deformation apparatus, and the corresponding top piston was inserted until close to touch (Fig. 1b). This was done on the bench. Note this main top piston was dried overnight (at 50 °C) prior to each experiment. The main vessel was then installed in the Instron loading frame (Fig. 1c), and the Instron loading ram advanced to apply and maintain a small, constant load of 0.1 kN, corresponding to ~1.3 MPa axial stress. The apparatus was then heated to 65 °C over the course of ~3 h, in load-control mode. After reaching a stable target temperature, the Instron ram was retracted in position-control mode, creating a ~1-mm gap between the loading frame and the top piston, to establish the zero-value of the external force signal. The original small load was then reapplied in load-control mode. The dry samples were then subjected to a second precompaction stage. This involved (a) loading the sample to an effective axial stress of 250 MPa, by increasing the applied force linearly over 5 min, (b) maintaining this stress for ~5 min, and then (c) unloading to the initial load (~1.3 MPa), again over 5 min.
Following this second precompaction stage, the samples were placed under the desired initial effective stress (σ a,0), using a 5-min duration, linear load ramp, in experiments where σ a,0 > 1.3 MPa, establishing a corresponding initial, zero-displacement piston position at the chosen stress (note that in experiments A02PC, A03PC, A04PC and A09TH, this reference position was established without first performing the second precompaction stage). The thicknesses (L 0) and porosities (ϕ 0) of the samples at this point are listed in Table 2.
From this point in the experiments, the testing procedure employed differed slightly between the three types of test. For the position-control (A01PC–A08PC) and load-limit experiments (A09TH, A10TH), operation of the Instron loading frame was transferred to position-control mode prior to the start of the experiment. However, the Instron loading frame was programmed such that the operation mode would switch from position-control back to load-control once a specified load was attained. While merely a safety measure in the position-control experiments, this transfer in operation mode was actively employed in the load-limit experiments, by applying lower load limits, corresponding to an axial stress σ TH (Table 2). In the case of the load-control experiments (A11CL–A14CL), the Instron was operated in load-control mode from the start, maintaining the initial effective stress (σ a,0) throughout the hydration experiment.
In all three types of experiments, measurement was initiated by vacuum-flushing water into the upper piston plus sample assembly at t = 0. To ensure the sample was saturated with water, the pore fluid system was briefly pressurised to ~10 MPa, using a hand pump. This pressurised state lasted for a few tens of seconds before the pressure was released, maintaining an open connection to atmospheric (laboratory air) pressure throughout the remainder of the experiment. Upon experiment termination, the sample was unloaded fully. This was done by retracting the Instron loading ram to create a ~1-mm gap between it and the top piston of the deformation apparatus. Subsequently, the furnace was switched off and the deformation apparatus was allowed to cool for 1–2 h before retrieving the sample assembly.
3.4 Data acquisition and processing
During each experiment, the external and internal load, Instron position, local position (displacement between the upper piston and main vessel) and temperature were logged every second, using a 16-bit National Instruments data acquisition system and VI Logger software. Data processing yielded effective axial stress (σ a) and axial strain (e a). The effective axial stress was measured directly using the external load cell signal, as the fluid pressure was atmospheric. The displacement and strain data were corrected for distortion of the deformation apparatus and Instron loading frame using predetermined stiffness calibrations, obtained at experimental temperature. Note that the axial strain was defined in terms of the engineering strain e a = ΔL/L 0, where L 0 denotes the reference (initial) thickness of the sample (Table 2), and ΔL represents the finite axial displacement associated with the expansion or compaction of the sample at a given moment, i.e. the thickness change of the sample, corrected for machine effects. The initial sample porosity (ϕ 0), i.e. that of the dry CaO aggregate, was estimated using \( \phi_{0} = 1 - m_{0} /(\rho_{\text{CaO}} L_{0} A) \), where m 0 denotes sample mass,\( \rho_{\text{CaO}} \) is the density of pure CaO (3340 kg m−3), and A is the cross-sectional area of the sample assembly bore (7.543 × 10−5 m2—Fig. 1a). Sample porosity evolution after the addition of water (ϕ) could not be determined, as the experimental design did not allow for pore volume changes to be distinguished from hydration-induced changes in solid volume.
3.5 Microstructural analysis
After retrieving the sample assembly from the deformation apparatus, the top piston of the assembly was removed and the sample plus bottom piston were carefully pushed out to minimise sample disturbance. The samples were then dried in a furnace at 50 °C for ~12 h, and subsequently stored in individual containers. Selected samples were studied optically and using scanning electron microscopy (SEM). To obtain cross sections through the disc-shaped samples, these were broken axially using a razor blade and subsequently mounted on a SEM stub using carbon paint. In addition, samples of our CaO starting material (i.e. the calcination product of Carrara marble) were characterised by means of SEM, thermogravimetric analysis (TGA) and laser diffraction particle size distribution analysis.
4 Results and analysis
4.1 Mechanical data
In the following, compressive axial stresses and dilatant axial strains (e a), i.e. sample expansion, are taken as positive. The maximum force of crystallisation was defined as the maximum axial stress (σ max) measured while the sample showed a positive axial displacement (ΔL), i.e. net expansion, with ΔL max denoting the greatest axial expansion observed. In addition, the displacement and effective axial stress supported by the hydrating CaO samples at t = 5 h were also employed as measures for the force of crystallisation. The key mechanical data obtained in the experiments are summarised in Table 2.
4.1.1 Constant-position experiments
Figure 2a, and 2b shows effective axial stress and axial strain versus time data obtained from hydration experiments A01PC, A02PC, A03PC, A04PC and A05PC (Table 2). These tests were performed with the Instron loading frame in position-control mode, imposing an initial (effective) axial stress (σ a,0) of ~1.3 MPa and using an axial stress limit (σ TH ) of 250 MPa. Note that A01PC, A02PC, A03PC and A04PC were characterised by initial porosities ranging from 35.4 to 36.8%, whereas A05PC was precompacted slightly further, with ϕ 0 = 29.0%. However, the main variable in this subset of experiments was initial sample thickness (L 0), which varied from 2.18 mm in A01PC and A02PC, to 1.11 mm in A03PC and A04PC, and 0.7 mm in A05PC (Table 2). In all five experiments, vacuum-flushing of water into the CaO sample resulted in the rapid development of an axial stress, attaining values >75 MPa within 30 min (Fig. 2a). At 5 h of reaction, axial stresses ranged from ~95 MPa for samples of L 0 < 1.2 mm (A03PC, A04PC and A05PC) to 135 MPa in experiments with L 0 = 2.18 mm (A01PC and A02PC). The σ max values also increased with increasing L 0 (Fig. 2a; Table 2). Conversely, the swelling strains (e a) decreased with increasing initial sample thickness (Fig. 2b). Figure 2c shows axial stress versus axial expansion (ΔL) of the samples generated by hydration. Note that the data obtained in experiments A01PC, A02PC, A03PC, A04PC and A05PC all plot on the same trend, regardless of initial sample thickness or porosity. This is because, rather than sample behaviour, the stress–strain relationship reflects the finite stiffness of the deformation apparatus and Instron loading frame. Due to elastic distortion with increasing axial stress, it was impossible to confine the samples perfectly (i.e. impose fixed-position boundary conditions on the sample directly). This implies that the stiffness of the machine determined how much the sample had to expand before the axial stress could increase further, resulting in the stress-displacement shown in Fig. 2c. Figure 2d shows axial swelling strain measured after 5 h of hydration versus the reciprocal of the initial sample thickness. The data produced a linear trend, described by ΔL 5h = 0.174 + 0.031L 0.
Since machine distortion was a factor in our measurements (Fig. 2c), we performed a number of position-control experiments at higher initial axial stress (A06PC, A07PC and A08PC, with σ a,0 of 60, 120 and 90 MPa, respectively—Table 2). This was done in order to increase the (load-dependent) stiffness of the deformation apparatus, allowing us to assess the effect of improved confinement of the hydrating CaO samples. The results are shown in Fig. 3, which depicts effective axial stress and axial strain versus time data for these three experiments, together with the data from A01PC and A05PC for reference purposes. Note that the initial sample thickness and porosity were ~0.7 mm and ~30% in A05PC, A06PC and A07PC, whereas L 0 and ϕ 0 measured 2.1–2.3 mm and 35–40% in A01PC and A08PC. In general, the axial stresses generated were larger with increasing σ a,0, reaching 146 MPa after 5 h of hydration in A07PC (Fig. 3a). However, note that the initial response of the samples reacted at σ a,0 values of 60–120 MPa was to compact, as evidenced by small decreases in axial stress at t < 1 min (Fig. 3b). Figure 3c shows σ a versus ΔL data (cf. Fig. 2c), illustrating the machine behaviour. Note that machine stiffness (i.e. the slope of the curves) is constant for a given axial stress. Further note that samples A01PC and A08PC, with comparable L 0 and ϕ 0, produced comparable axial stresses, while higher σ a,0 resulted in larger stresses to build up in tests A06PC and A07PC. In both sets of experiments, however, axial strain decreased with increasing initial axial stress (Fig. 3d).
4.1.2 Load-limit experiments
At the start of measurement, load-limit experiments A09TH and A10TH showed comparable behaviour to position-control experiments A01PC and A02PC. In A09TH and A10TH, however, Instron operation was transferred to load-control mode once axial stresses of 30 and 60 MPa were attained. From that point onward, the axial load was maintained constant at these values, allowing the samples to expand further at constant stress. Runs A01PC, A02PC, A09TH and A010TH all employed an initial axial load of ~1.3 MPa as well as samples with comparable L 0 and ϕ 0, ranging 2.09–2.18 mm and 33–36% (Table 2). Figure 4 shows axial stress and strain versus time data for these experiments, where Fig. 4a, b shows the complete measurements, and Fig. 4c, d shows axial stress and strain evolution during the first hour of hydration. In both experiments A09TH and A10TH, transfer to load-control occurred early on in the measurements (t < 10 min). Maintaining the axial stress at 30 MPa in A09TH resulted in rapid expansion, with a sample strain of nearly 27.5% developing within 1 h and reaching a maximum value of 28.5% after 173 min. Note that the sample subsequently compacted, with axial strain slowly decreasing to 28.3% at test termination after ~17 h of measurement. Compared to A09TH, maintaining the axial stress at 60 MPa in A10TH resulted in reduced axial strain, attaining ~11% after 1 h. However, slow expansion of the sample against the constant stress limit continued for the duration of the test, reaching 20.9% upon termination at t ≈ 65 h.
4.1.3 Constant-load experiments
Figure 5a shows the axial strain versus time data obtained for experiments A11CL, A12CL, A13CL and A14CL, in which the CaO samples were exposed to water with the Instron in load-control mode from the onset (Table 2). Experiments A11CL, A12CL and A13CL were performed on CaO samples with L 0 of about 0.7 mm, and employed operating loads corresponding to axial stresses of 60, 120 and 225 MPa, respectively. Conversely, sample A14CL had an initial thickness of ~2.1 mm and was tested under an axial stress of 225 MPa. The samples exposed to water under a constant axial stress of 60 or 120 MPa (A11CL and A12CL), i.e. stresses lower than the force of crystallisation that was generated in the constant-position experiments (Sect. 4.1.1), showed sample expansion with time (Fig. 5a). Conversely, the CaO samples hydrated under 225 MPa axial stress (A13CL and A14CL) showed compaction, whereby compactive displacement appeared to be independent of L 0, showing the same amount of displacement for the 0.7 and 2.1 mm-thick samples (Fig. 5b).
4.2 Microstructural and chemical data
4.2.1 Characterisation of the starting CaO material
Representative samples of the calcined powder used in the FoC experiments were analysed using a laser diffraction particle sizer technique, SEM and TGA, to characterise the CaO starting material. The apparent grain size was determined using a Malvern Instruments Mastersizer S long bed instrument, using hexane as the dispersing fluid to minimise hydration during analysis. In four consecutive measurements on the same powder sample, the mean grain size decreased from 144 to 93 μm while the grain size distribution narrowed (Fig. 6). The third and fourth Malvern measurements gave comparable results, with a grain size distribution of roughly 95 ± 60 μm. SEM observations showed that these “grains” consisted of sintered clusters of about 1–5 μm large particles (Fig. 7a, b). Accordingly, the grain size evolution as seen in the Malvern particle sizer data (Fig. 6) likely reflected disintegration of these agglomerates of sintered particles, falling apart as the dispersing fluid was agitated. As such, the character of the CaO samples is better defined by the 1–5 μm large particles (Fig. 7c), than by the clusters these particles comprise.
Possible hydration and carbonation of the CaO powder samples during experiment preparation and initial precompaction, i.e. before water injection and starting the force of crystallisation measurement, were investigated using TGA. Contamination by hydration or carbonation prior to testing was minor, with the analysis of a powder that experienced the same preparation procedure as the samples that were hydrated in the deformation apparatus yielding Ca(OH)2 and CaCO3 contents of <1 wt%, calculated in terms of CaO equivalents [117].
4.2.2 Post-experiment observations on the hydrated samples
Upon removal from the sample assembly, the top side of all samples appeared white or light greyish, glassy and translucent. In some samples, the bottom side was dull and opaque by comparison. However, this zonation was generally not stable, with the white-greyish colouration sometimes visibly migrating downwards through the samples after their retrieval. This presumably reflected ongoing hydration, making it difficult to assess confidently which characteristics of the samples were representative of their condition during the FoC measurements, i.e. under load, and which features were post-experimental artefacts, produced (a) via subsequent hydration during the unloading and cooling of the deformation apparatus, or (b) during sample retrieval and preparation for microstructural analysis.
Samples A03PC, A04PC, A05PC and A09TH formed cohesive pellets (e.g. Fig. 8a), which could easily be retrieved intact. When broken using a razor blade, these samples often displayed a sub-optical, crystalline texture (Fig. 8b), in some cases featuring (remnants of) axially oriented, reaction front-like structures (Fig. 8c). Note that all four these samples experienced axial stresses of <100 MPa (cf. σ max in Table 2). Samples A01PC, A02PC, A06PC, A07PC, A011CL, A012CL, A013CL and A014CL were more friable. While some of these samples could be obtained relatively intact, most disintegrated into disc-fractured fragments and powder, either upon sample retrieval or (more often) sometime after (Fig. 8d). It is notable that the white, opaque material at the bottom side of the samples was generally less consolidated and disintegrated into a powder, whereas the white-greyish, translucent material on the top side formed thin (typically 100–500 μm thick) discs that were more cohesive and remained largely intact (Fig. 8e). Sample A10TH was lost and could not be studied microstructurally.
Samples A01PC and A09TH were studied using SEM. Focussing on sample A01PC, the most prominent feature was a 150–200-µm-wide zone of dense material, present along the top side of the sample, which was most directly exposed to water during testing. This low-porosity zone was broken up into regular segments (Fig. 9a) and consisted of a fine grained, fibrous material (Fig. 9b). The remainder of A01PC was heavily fractured/jointed (Fig. 9c). Considering that the sample spalled apart, after it was cut, mounted on a stub and Pt-coated, and before it was studied using SEM (Fig. 8d), these joints may have represented post-experimental hydration, which could also have caused the regular breakup of the top part. Alternatively, the joints in the bottom part and breakup of the top part could be unloading features. Besides being heavily fractured, the bulk of A01PC broadly resembled the low-porosity zone at the top side, consisting of a similar, fibrous material (Fig. 9c). Turning to sample A09TH, the reaction front-like structure present, clearly visible by visual inspection, and detectable under the optical microscope (Fig. 8c), could not be distinguished using SEM. The microstructure consisted mostly of fibrous material, not unlike that seen in sample A01PC (Fig. 9d). In addition to the fibrous material (Fig. 9e), rare, submicron-sized, hexagonal platelets could locally be distinguished (Fig. 9f), which, on the basis of their euhedral crystal-shape, most likely were portlandite [117]. In A09TH, microstructure remained more or less constant in the axial direction.
5 Discussion
The present experiments have successfully recorded the development of axial stress driven by a force of crystallisation during confined hydration of porous CaO powder samples, at 65 °C and at atmospheric fluid pressure. Confinement was achieved using an Instron testing machine to limit axial expansion of the sample within the rigid cylindrical die containing the sample. With the Instron ram held in fixed position (position control), sample expansion was accordingly limited to concomitant elastic machine distortion, thus allowing the observed force of crystallisation to develop. We measured hydration-induced axial stresses of up to nearly 153 MPa (Figs. 2, 3, 4, 5; Table 2), which is well in excess of the tensile strength of most rock materials [59] and of in situ lithostatic stress at depths up to 6 km. However, the measured stresses constitute only ~5% of the maximum value predicted by the thermodynamic theory for FoC (Sect. 2.2.2). Alongside this, the position-controlled experiments showed a decrease in swelling strain with increasing sample thickness (Fig. 2b). Increased initial confining stress, accomplished by increasing the initial axial stress, increased the FoC stresses that developed, but decreased the swelling strains attained (Fig. 3). In experiments where samples were hydrated under constant axial stress, samples subjected to 60 or 120 MPa showed expansion, while those subjected to 225 MPa compacted (Fig. 5). Microstructural observations showed that the samples that supported axial stresses >100 MPa often contained a dense, cohesive layer, consisting of white or greyish, slightly translucent material and about 100–500 μm thick, at the top of the samples, i.e. adjacent to the fluid inlet (Figs. 8e, 9a). By contrast, the remainder of these samples was generally friable and disintegrated over time (Figs. 8d, e, 9a, c).
In the following, we will analyse our experimental data and attempt to explain the observed behaviour and why the GPa stresses predicted by thermodynamic theory were not achieved in the experiments. We go on to discuss the implications with respect to the applicability of FoC processes in achieving wellbore casing expansion and sealing, and consider ways in which the FoC achievable by CaO hydration can be increased.
5.1 Factors affecting FoC development: sample expansion versus machine stiffness
So far, we have considered the effective stress pertaining at thermodynamic equilibrium (Eqs. 10, 13) to be the maximum FoC-induced stress that can develop due to precipitation of a confined solid product phase. However, strictly speaking, this equilibrium was calculated as the force that the surroundings must exert on a growing crystal to prevent precipitation from occurring. Whether a growing crystal can actually exert this maximum stress on its environment will depend on the degree of confinement and attainable expansion. In our experiments, confinement is imposed by the Instron loading frame and the stress generated by a given sample expansion is controlled by the apparatus stiffness. This is clearly demonstrated in Fig. 2c, where the data plotted show an identical axial stress-axial displacement behaviour to that obtained in independent machine stiffness calibrations. Accordingly, in the present constant-position experiments, the hydration-induced stresses that develop cannot exceed the stress generated by machine distortion equal to the maximum swelling strain of the sample. This means that the FoC we measured is determined by the combined effects of sample swelling plus apparatus stiffness, with finite sample swelling being essential for producing a FoC. Measured sample swelling (ΔV m, ΔL m) is in turn determined by the increase in solid volume (ΔV s) caused by converting CaO to Ca(OH)2, i.e. by the extent of reaction (ξ), plus the change in pore volume of the sample (ΔV p), plus elastic changes in solid grain density (and hence sample volume, ΔV el) due to increasing mean stress in the sample during FoC development. Changes in pore volume in such a reacting system will in general include a component of pore volume increase ΔV +p (>0), due to entrapment and expansion of pores as a direct consequence of reaction, plus a component of pore volume decrease ΔV −p (<0) related to stress-driven mechanical compaction involving grain rearrangement/deformation and hence solid redistribution.
On this basis, we can accordingly write \( \Delta V_{\text{m}} =\Delta V_{\text{s}} (\xi ) +\Delta V_{\text{p}} (\xi ,\sigma ) +\Delta V_{\text{el}} (\xi ,\sigma ,V_{\text{p}} ) \, \) where ΔV p = ΔV +p + ΔV −p , which on dividing by the initial sample volume (and assuming no radial strain) gives measured sample strain at any instant as
where each term can be viewed as volumetric strain contributions due to solid conversion (e s), permanent pore volume change (e p), and elastic deformation of the sample (e el). However, as reasoned above, in fixed-position experiments, sample swelling strain and associated axial displacement (ΔL m) are accommodated by apparatus distortion, so that ΔL m = σ/C where C is the apparatus stiffness (itself a function of stress in our set-up) measured in Pa m−1. Equivalently, e m = σ/(CL 0). Now, at a given value of reaction extent (ξ) and sample porosity (ϕ), e el = σ/E C where E C is the instantaneous constrained elastic stiffness of the sample. This means we can rewrite Eq. 15 as
In general, however, E C ≫ CL 0 (elastic stiffness of the sample is much greater than of the much larger machine), so that e el ≪ e m and e el can be neglected, yielding e m ≈ e s(ξ) + e p(ξ, σ) or ΔV m ≈ ΔV s(ξ) + ΔV p(ξ, σ). In addition, the FoC-driven stress that develops during reaction of a given sample tested in fixed-position mode can be written as σ ≈ CL 0(e s(ξ) + e p(ξ, σ)). This is important to analysing and interpreting our experimental results.
5.2 Analysis of sample volume changes and implications for mechanism controlling FoC
Having established that the build-up of a FoC requires sample volume expansion, let us now consider in detail the different volumetric strain contributions that have occurred in our experiments. Given the molar volumes of CaO, Ca(OH)2 and water (Table 1), complete reaction of CaO, with a given (excess) volume of water, to form Ca(OH)2, involves an increase in the solid volume of ~1.6 × 10−5 m3 mol−1, i.e. almost a doubling if reaction proceeds as given in Eq. 12. By contrast, the total solid-plus-fluid volume decreases by ~2 × 10−6 m3 mol−1. In our experiments, the hydration reaction contributes to the strain e s (solid volume change ΔV s) according to the extent of reaction (ξ).
5.2.1 Endmember strain development scenarios
To progress further, it is useful to analyse the sample volume changes (ΔV m, e m) that can occur in a set of endmember scenarios that are relevant for our experiments. Figure 10 shows that maximum attainable volumetric strain as a function of initial porosity for four such scenarios. The first two scenarios (Fig. 10, dashed curves denoted S1a and S1b) represent closed-system endmember behaviour. Here, the initial sample porosity is water-filled (e.g. established by vacuum-flushing at the start of experiment), but no further water can enter the samples, i.e. the system is closed with respect to pore fluid transport. For realistic initial porosities of ϕ 0 < 52%, the maximum extent of reaction is then determined by the availability of water, and conversion of quicklime to portlandite will be incomplete. Scenarios S1a and S1b differ in how sample porosity evolves. In S1a (Fig. 10), the initial pore volume is maintained, i.e. solid product phases do not occupy the initial pore space. This should be considered an upper limit for expansion, unlikely to be attained in practice. Scenario S1b represents the cases where porosity goes to zero during hydration, thus representing the minimum swelling associated with complete initial pore water consumption. The other two scenarios addressed in Fig. 10 (dotted curves denoted S2a and S2b) consider open systems, where water can freely enter or leave the samples (e.g. through the bore of the top piston in our experiments), thus allowing CaO hydration to go to completion regardless of initial porosity. Scenarios S2a and S2b again differ in how the sample porosity evolves with reaction, with S2a being characterised by a constant pore volume, similar to S1a. In scenario S2b, similar to S1b, sample porosity is assumed to go to zero, so that the plotted strains represent minimum values for complete (open system) CaO hydration. While the evolution of porosity (ϕ) is undetermined in our experiments, assuming that the porosity of highly hydrated material approaches zero is likely reasonable, given the dense, translucent nature of the hydrated portions of our hydrated samples (Figs. 8b, c, 9b, d). Initial sample porosity (ϕ 0) is known from \( \phi_{0} = 1 - m_{0} /(\rho_{\text{CaO}} L_{0} A) \).
Also plotted in Fig. 10 are our experimental data, specifically the final axial strains attained in our experiments versus the initial sample porosity. Error bars represent uncertainty in our data related to initial sample length and sample porosity determinations.
5.2.2 Role of reaction extent in determining stress development
The first thing to note in Fig. 10 is that all samples but A03PC, A04CP and A09TH plot below the dark grey, dotted curve corresponding to the scenario S2b of complete hydration (open-system reaction) plus complete porosity reduction. This implies that, within uncertainty of the strain measurements, stress development in position-controlled experiments A03PC and A04PC could possibly have been limited by hydration going to completion, i.e. the system reaching chemical equilibrium by eliminating all CaO, before higher axial stresses developed. Experiment A09TH was conducted in load-limit mode, with σ TH = 30 MPa, allowing reaction to proceed without the build-up of stress beyond this value, potentially attaining complete hydration. However, in all other samples tested (A01PC, A02PC, A05PC, A06PC, A07PC, A08PC, A10TH, A11CL, A12CL, A13CL and A14CL), the measured sample strains are less than the minimum value expected for complete hydration (S2b). In general, it is likely that sample porosity did not go to zero, but instead attained some small residual value, which would have contributed to the final volumetric expansion. These measured strains must therefore imply that CaO hydration was incomplete at the time of experiment termination in the majority of the samples. Accordingly, the limited stresses in most experiments, particularly in position-controlled experiments A01PC, A02PC, A05PC, A06PC, A07PC and A08PC, cannot be explained by the system running out of CaO to hydrate. This further implies that larger swelling strains should have been possible in experiments A01PC, A02PC, A05PC, A06PC, A07PC and A08PC, were reaction to proceed. It follows that the axial stresses developed here were not limited by insufficient machine stiffness but by incomplete reaction progress and net expansion.
5.2.3 The role of transport processes and water access
Given the zoned nature (Figs. 8c, 9a) and brittle/friable post-experiment character of our samples, with many of them spalling (Fig. 8d) or partially crumbling into a powder (Fig. 8e), our microstructural data strongly support the notion that the hydration reaction was incomplete in many of the experiments. Indeed, with CaO remaining in the samples after completion of the experiments (i.e. following unloading), any ongoing hydration via the air could subsequently have caused internal expansions, explaining the observed disintegration of the samples (cf. [113]). On the other hand, some of the samples, which either were very thin (A03PC, A04PC, A05PC), or experienced low load (A09TH), did form dense cohesive pellets (Sect. 4.2.2), suggesting that a larger extent of reaction occurred in these experiments. Indeed, spalling may be a consequence of differential expansion during unloading. We therefore need to consider what processes and effects may have contributed to this variability in extent of reaction occurring during our experiments. A clear candidate is the question of water access into the reacting sample from the external fluid system, i.e. the issue of the evolving permeability of the (reacted part of the) sample during the reaction progress.
Lacking post-experiment sample mass measurements, there is no direct means of determining the extent of reaction in our experiments, as the volume of water consumed and hence total system volume with time, are unknown. However, as discussed above, some constraints can be obtained by comparing measured sample strain, which represents the combined effect of hydration-induced changes in solid volume (i.e. extent of reaction) and porosity change, with the endmember scenarios represented in Fig. 10. Returning to Fig. 10, all samples except A13CL and A14CL plot well above the line corresponding to scenario S1b, representing complete porosity reduction plus closed-system reaction. This means that the measured strain is more than can be explained by closed-system behaviour, assuming strong porosity reduction, suggesting that at least some water entered our samples during the hydration process in addition to that initially injected. Transport of water into the sample porosity certainly occurred in samples A05PC and A11CL, as the data for these experiments plot above the constraint corresponding to closed-system reaction at constant pore volume (scenario S1a). Further, we note that experiments A13CL and A14CL, which plot below the scenario S1b line, were conducted in load-control mode, at a constant and high axial stress of 225 MPa. These samples showed compaction rather than expansion (Fig. 5). For A13CL and A14CL, we therefore infer that hydration (i.e. solid volume increase), combined with compaction of the reacting sample material under the large applied axial stress, rapidly reduced porosity and permeability when water was first introduced, thus quickly limiting the potential for inflow of additional water and strongly limiting reaction. Based on volumetric strain considerations, the extent of hydration (with respect to open-system conditions) was <60% in A13CL and A14CL.
Evidence for complete hydration was encountered only in A09TH (Fig. 10). The sample retrieved from this experiment formed a dense pellet, and its strain/initial porosity data plot slightly above the scenario S2b line in Fig. 10, i.e. the constraint that corresponds to open-system reaction plus complete porosity reduction. It is important to note that A09TH was a load-limit experiment, in which we used a low axial stress limit of 30 MPa. As such, hydration occurred under much lower axial stresses than was the case in any of the other samples (Table 2). We infer that water remained able to enter the sample under these conditions, allowing ongoing expansion in the approach to complete hydration (Figs. 2a, b, 4a, b). The observed subsequent compaction of A09TH (Fig. 4b) further suggests that grain boundaries were still wetted at this point (allowing compaction mechanisms such as pressure solution to operate), and that at least some porosity remained (to compact into). Load-limit experiment A10TH, employing an axial stress limit of 60 MPa, also shows continued sample expansion during nearly 70 h of testing, though at a slower rate (Fig. 4). Similar behaviour is seen in load-controlled experiments A11CL and A12CL, employing constant axial stresses of 60 and 120 MPa, respectively (Fig. 5). Indeed, by comparing the data for samples A09TH, A10TH, A11CL and A12CL, we observe that in all cases expansion and/or stress development continues throughout the experiments, but the rate slows down markedly with increasing axial stress, indicating that the apparent rate of CaO hydration slows down with increasing axial stress.
On basis of the above, and since hydration was found to be incomplete in most of our samples at the time of experiment termination, we infer that the development of a FoC, and hence the stresses we measured, depends on the availability and inward transport of water from outside the original pore volume. In turn, we have clear indications, as discussed above, that access of water to the samples strongly depended on axial stress (Figs. 4, 5). Combined, the above observations bring us back to the key assumptions in the thermodynamic theory for FoC development, namely that an aqueous phase must be present to allow reaction and must remain present in stressed contacts [22, 23, 105], for instance in the form of a thin film or occupying a microchannel network. Alternatively stated, the presence of a fluid phase is imperative for continued reaction and precipitation of the solid product phase, while grain boundary wetting and pore connectivity are essential for the development of a force of crystallisation. Based on our data and limited microstructural observations, the implication is that the combined effects of reaction progress, Ca(OH)2 precipitation and build-up of axial stress led to the shutdown of the pore network and hence transport pathways for water into samples, and/or to the disconnection of, or expulsion of water films from, grain interfaces.
To facilitate comparison between position-controlled and load-controlled experiments, we plotted sample displacement after 5 h versus initial axial stress, as shown in Fig. 11. In this graph, sample displacement can be regarded as a measure of a sample’s capacity to generate a force of crystallisation. Note that sample displacement also is directly related to swelling strain, hence the extent of reaction in our samples. The initial axial stress can be considered a measure for the resistance against expansion. We observe a monotonic decrease in sample displacement with increasing initial axial stress, transgressing from net expansion to net compaction. Since expansion is a requirement for a FoC-driven axial stress to develop, this implies that the stress required to cut off water access to the samples in our experiments was of the order of 150–175 MPa. It should be noted, however, that these values represent the overall stress on the sample, and the stresses at grain contacts may be higher, e.g. if force chains occur.
5.2.4 Transport path shutdown mechanisms
Several different processes could play a role in the shutdown of transport pathways and grain contact fluid films (Fig. 12). As the already fine (~5 μm) CaO particles hydrate, an even finer Ca(OH)2 nanocrystalline mush will be produced (cf. [73]). This presumably is weak and deforms by frictional granular flow or even diffusion or pressure solution accommodated granular flow [96, 131]. Accordingly, the Ca(OH)2 phase could easily become extruded from hydrating CaO grain contacts into the intervening pores, leading to mechanical compaction of the CaO framework and to a reduction in sample porosity and permeability. The pore-sizes in the Ca(OH)2 mush will presumably be very small (less than the grain size), so that the permeability of regions filled with this reaction product will be low, even if the porosity remains connected. More likely, though, the material will cement up by reaction-driven precipitation or by grain growth and sintering processes, promoting permeability reduction. Moreover, at free, unloaded surfaces such as larger pore walls between hydrating CaO grains or Ca(OH)2 grain clusters, the solution phase will be supersaturated with respect to Ca(OH)2, leading to precipitation in pore throats, rapidly reducing permeability and restricting water access, preventing further reaction.
As load generated by expansion is progressively transferred to the product mush, due to elimination of the initially load-supporting CaO framework, the nanocrystalline Ca(OH)2 product phase may further compact via pressure solution plus intergranular sliding. This will further reduce the porosity and permeability of the Ca(OH)2 produce and whole sample until healing of the grain contacts occurs by internal or contact margin precipitation, i.e. via contact asperity or neck growth phenomena [122, 123]. As indicated above, grain growth involving grain boundary migration, driven by surface energy reduction in the fine product phase, could also disconnect pores and reduce permeability simply by overgrowing and isolating pores [69]. This grain growth could potentially occur during filling of larger pores with fine Ca(OH)2 reaction product, blocking the pores very quickly and trapping fluid. Another explanation would be that fluid infiltration and hence reaction progress is facilitated by reaction-induced fracturing [92], with build-up of higher normal stresses hampering the opening of such microfractures.
Alternatively to the above clogging mechanisms limiting reaction progress and hence FoC development, the stresses measured in our experiments may correspond to attaining or exceeding the effective normal stress required to displace a fluid film from a flat grain-to-grain contact, i.e. the so-called disjoining pressure [57, 105, 106]. Exceeding this pressure could lead to “drying-out” of the stressed grain contacts, impeding further reaction/hydration and dissolution/precipitation at these locations. When precipitation takes place on pore walls, this will lead to porosity reduction, which may cut off permeability. However, this will also result in more grain–grain contacts, i.e. a larger load-bearing surface area, thus bringing the maximum possible stress on a sample scale closer to the maximum possible stress from thermodynamic calculations. Unfortunately, to our knowledge, there have been no studies published in which the disjoining pressure between calcium hydroxide and calcium oxide surfaces, and various combinations thereof, was measured or calculated. We therefore have no basis upon which to evaluate this hypothesis further. Moreover, the exact surface area of the loaded contacts within our CaO samples is unknown, precluding direct comparison even if such data would be available. Nevertheless, it is interesting to note that our experimental data show a transition from net expansion to net compaction at an axial stress of 150–175 MPa (Fig. 11). This transition could perhaps represent complete cessation of FoC development, e.g. due to healing of grain boundaries, but could also reflect a regime shift in the (relative) kinetics of compaction and expansion, e.g. due to water transport limitations or local depletion of CaO. Such a competition between hydration-induced expansion and stress-induced compaction may explain the late-stage compaction observed in A09TH (Fig. 4b).
Last, it should be noted that, given the relatively short duration of our laboratory experiments, we cannot rule out the possibility that CaO hydration did not stop in our experiments but merely slowed down, due to increasingly constricted inflow of water, to the point where the build-up of further stress became negligible on the timescale of our experiments (up to ~65 h). In Portland-based cement, residual (i.e. unhydrated) clinker phases can remain present for years [117], demonstrating that restricted water availability can slow down reaction, even in the absence of high stress.
5.3 Applicability to casing expansion and suggestions for future work
In Introduction, we raised the question of whether the force of crystallisation generated during confined hydration of CaO [43] can be used to expand the casing of leaking wellbores, thus achieving sealing, e.g. via the construction of some form of internal plug using a CaO-based material. We argued that if sufficiently high internal stresses can be attained, then hydration of the plug may bring about a permanent radial expansion of the casing pipe, thereby closing the annular voids and fractures that constitute leakage pathways outside of the casing [74, 75]. However, any such application of CaO hydration-induced stresses would require the stresses and strains that develop during CaO hydration to be predictable and controllable.
Our experiments on precompacted CaO powder samples have shown the development of CaO hydration-induced stresses of up to 153 MPa (Fig. 11). Preliminary calculations, made using Barlow’s formula for plastic yielding of a cylindrical metal pipe [7, 124], show that stresses in the range of 100–300 MPa are required to initiate expansion of a typical wellbore casing constructed from conventional steel [56]. Therefore, while noting that the true stress requirements will be wellbore specific and require analysis of the geomechanical state of the wellbore, our preliminary laboratory results are quite encouraging. On the other hand, the hydration-induced stresses measured in our experiments constitute only a small fraction of the GPa stresses predicted by thermodynamic theory, so there remains scope for further study and attempts to increase achievable reaction-driven stress. The main goal of such work should be to elucidate the mechanism underlying the shutdown of water transport, which seems to have arrested FoC development in our experiments. A possible first step in this direction would be to conduct CaO hydration experiments similar to ours, but using a controlled fluid pressure, and a deformation apparatus with flow-through capability, to monitor sample permeability. This type of set-up would further allow for the investigation of certain additives, such as mineral phases with grossly different surface energies, porous ceramics particles, or glass fibre, which could potentially help maintain the transport pathways for water open for longer.
In addition, the following two aspects of FoC development by CaO hydration require further study, from both a scientific and an application perspective. First, our experiments involved CaO powder samples that were precompacted at 250 MPa to reduce initial porosity. Conducting a similar procedure on an industrial scale would be costly. It would therefore be interesting to study in more detail the effect of initial porosity on the development and maximum magnitude of the force of crystallisation, e.g. to determine allowable porosity ranges for the method to be workable. Second, in the present study we prepared our CaO by calcining Carrara marble at 1100 °C for 16 h. There exists a substantial body of literature dealing with the effects of calcination temperature, starting carbonate material and grain size, and various other processes (e.g. sintering) on the nature of the final CaO product [13, 14, 41, 46, 112]. For example, the rate of hydration is slower for dead-burnt lime (calcined at >1600 °C) than for “normal” CaO, prepared at <1200 °C [43]. Larger FoC-induced stresses could potentially be generated by optimising properties of the CaO material used.
6 Conclusions
This study was motivated by noting that leakage of CO2 or other fluids occurring behind the steel casing in a wellbore could potentially be mitigated by producing a small radial expansion of the casing by means of hydration of CaO, thus mechanically closing annular voids, debonding defects and/or fractures outside the casing. For the hydration of CaO, thermodynamic models predict reaction are capable of producing very large stresses, or forces of crystallisation (FoC), in the range of 3.4 GPa. However, the stresses produced by CaO hydration have never been directly measured in the laboratory. To assess what FoC-induced stresses can be attained in practice, we studied their development in uniaxial expansion experiments on precompacted (at 250 MPa axial stress) powder aggregates of CaO (precompacted discs with initial porosities of 24.9–40% and initial thicknesses of 0.68–2.34 mm), which were one-sidedly exposed to water a temperature of 65 °C. Our main findings can be summarised as follows:
-
1.
In experiments where CaO powder aggregates were hydrated under confined conditions, i.e. where axial (volumetric) expansion of the samples was limited to that allowed due to the finite stiffness of the deformation apparatus, we observed that samples continued to expand until effective axial stresses of up to 153 MPa were generated. While these stresses are substantial, they constitute only about 5% of the thermodynamically predicted maximum. Volumetric considerations, accounting for both reaction-induced changes in solid volume and the possible range of porosity reduction, suggest that in at least some of these experiments hydration cannot have been complete. Note that hydration was also incomplete in the test where 153 MPa axial stress was achieved.
-
2.
In experiments where the hydration of CaO powder aggregates proceeded under a constant axial stress, we observed a decrease in the swelling strain with increasing axial stress, from 60 to 120 MPa, while samples that were hydrated under 225 MPa showed compaction rather than expansion. Volumetric considerations show that the extent of reaction was <60% in the experiments performed at 225 MPa. In terms of the observed axial displacement, about 50 μm of compaction occurred, regardless of sample thickness, suggesting the responsible process occurred in a limited region. Plotting the measured sample expansion versus initial axial stress showed a transition from net expansion to net compaction around 150–175 MPa.
-
3.
The samples that experienced axial stresses of <100 MPa formed dense, cohesive pellets, displaying a cryptocrystalline texture. Conversely, in samples subjected to >100 MPa, microstructural analysis revealed very dense, about 100–300 μm thick rims, present at the top of the samples (which was directly exposed to water). The remainder of these samples was comparatively porous, and rather friable, with these parts of the samples often disintegrating into a powder. We infer this represents ongoing, post-experiment hydration of these parts of the samples.
-
4.
Given our stress measurements, there must be a process that stops or significantly slows down the rate of hydration, well before the thermodynamic maximum stress is attained. In only a few of the experiments could this be attributed to hydration reaching completion. This notion of partial hydration is substantiated by our microstructural observations, with samples for which volumetric considerations suggest incomplete hydration showing thin, dense zones developed at the top side, where water entered the samples. We infer that the development of such dense zones by the combined effects of sample cementation and stress-driven compaction led to shutdown of transport pathways for water into the sample pore structure and into grain contacts. Moreover, a key assumption in the thermodynamic model, namely that a solution phase, for instance in the form of thin films or microchannels, remains present may not hold at high grain boundary contact stresses, corresponding to our measured sample-scale stresses of about 150–175 MPa, e.g. due to a disjoining pressure effect.
-
5.
With regard to possible application to leakage remediation in wellbores, the present laboratory experiments documented hydration-induced stresses of a magnitude equivalent to that of the internal pressures required for casing expansion. However, the development of these stresses is strongly dependent on the influx of water, which may yield practical limitations. Nevertheless, the present results point the way to finding engineering solutions that may in future allow controllable, reaction-induced stresses and strains to be achieved and applied in wellbore sealing operations. For example, usage of certain additives may help maintain transport pathways for water open longer, which could potentially allow larger stresses to develop.
References
Agbasimalo N, Radonjic M (2014) Experimental study of the impact of drilling fluid contamination on the integrity of cement–formation interface. J Energy Resour Technol 136:42908
Anderson GM, Crerar DA (1993) Thermodynamics in geochemistry: the equilibrium model. Oxford University Press, Oxford
Bachu S (2003) Screening and ranking of sedimentary basins for sequestration of CO2 in geological media in response to climate change. Environ Geol 44:277–289. doi:10.1007/s00254-003-0762-9
Bachu S, Watson T (2006) Possible indicators for CO2 leakage along wells. In: 8th International conference on greenhouse gas control technologies, pp 19–22
Barclay I, Pellenbarg J, Tettero F, Pfeiffer J (2001) The beginning of the end: a review of abandonment and decommissioning practices. Oilf Rev 13(4):28–41
Bargawi RA, Zhou S, Al-Umran MI, Aghnim WA (2005) Expandable tubular successfully scab off severe casing leaks. In: SPE/IADC middle east drilling technology conference and exhibition, 12–14 September, Dubai, United Arab Emirates. Society of Petroleum Engineers. doi:10.2118/97357-MS
Barlow P (1836) On the force excited by hydraulic pressure in a Bramah press; the resisting power of the cylinder, and rules for computing the thickness of metal for presses of various powers and dimensions. Trans Inst Civ Eng 1:133–139. doi:10.1680/itrcs.1836.24488
Bauer S, Beyer C, Dethlefsen F, Dietrich P, Duttmann R, Ebert M, Feeser V, Görke U, Köber R, Kolditz O, Rabbel W, Schanz T, Schäfer D, Würdemann H, Dahmke A (2013) Impacts of the use of the geological subsurface for energy storage: an investigation concept. Environ Earth Sci 70:3935–3943. doi:10.1007/s12665-013-2883-0
Becker GF, Day AL (1905) The linear force of growing crystals. Proc Wash Acad Sci 8:238–288
Becker GF, Day AL (1916) Note on the linear force of growing crystals. J Geol 24:313–333
Beruto D, Barco L, Belleri G, Searcy AW (1981) Vapor phase hydration of submicrometer CaO particles. J Am Ceram Soc 64:74–80
Birss FW, Thorvaldson T (1955) The mechanism of the hydration of calcium oxide. Can J Chem 33:881–886
Borgwardt RH (1989) Sintering of nascent calcium oxide. Chem Eng Sci 44:53–60
Bruce KR, Gullett BK, Beach LO (1989) Comparative SO2 reactivity of CaO derived from CaCO3 and Ca(OH)2. AIChE J 35:37–41
Brufatto C, Cochran J, Conn L, Power D, El-Zeghaty SZAA, Fraboulet B, Griffin T, James S, Munk T, Justus F (2003) From mud to cement—building gas wells. Oilfield Rev. 15:62–76
Bruhns W, Mecklenburg W (1913) Über die sogennante Kristallisationskraft. Jahresbericht des Niedersächsischen Geol. Vereins zu Hann. VI
Brunet J-PL, Li L, Karpyn ZT, Huerta NJ (2016) Fracture opening or self-sealing: critical residence time as a unifying parameter for cement–CO2–brine interactions. Int J Greenh Gas Control 47:25–37
Byrom TG (2014) Casing and liners for drilling and completion: design and application. Elsevier, Amsterdam
Campbell K, Smith R (2013) Permanent Well Abandonment. Way Ahead 9:25–27
Cao P, Karpyn ZT, Li L (2015) Self-healing of cement fractures under dynamic flow of CO2-rich brine. Water Resour Res. doi:10.1002/2014WR016162
Chatterji S (1995) Mechanism of expansion of concrete due to the presence of dead-burnt CaO and MgO. Cem Concr Res 25:51–56
Correns CW (1949) Growth and dissolution of crystals under linear pressure. Discuss Faraday Soc 5:267–271
Correns CW, Steinborn W (1939) Experimente zur Messung und Erklärung der sogenannten Kristallisationskraft. Z Krist Mater 101:117–133
Coussy O (2005) Poromechanics of freezing materials. J Mech Phys Solids 53:1689–1718. doi:10.1016/j.jmps.2005.04.001
Cowan M (2007) Field study results improve squeeze cementing success. In: Production and operations symposium, 31 March–3 April, Oklahoma City, Oklahoma, USA. Society of Petroleum Engineers. doi:10.2118/106765-MS
Daccord G, Craster B, Ladva H, Jones T, Manescu G (2006) Cement–formation interactions. In: Nelson EB, Guillot D (eds) Well cementing. Schlumberger, Sugar Land, p 773
de Boer RB (1977) On the thermodynamics of pressure solution—interaction between chemical and mechanical forces. Geochim Cosmochim Acta 41:249–256
de Meer S, Spiers CJ, Nakashima S (2005) Structure and diffusive properties of fluid-filled grain boundaries: an in situ study using infrared (micro) spectroscopy. Earth Planet Sci Lett 232:403–414
de Meer S, Spiers CJ, Peach CJ, Watanabe T (2002) Diffusive properties of fluid-filled grain boundaries measured electrically during active pressure solution. Earth Planet Sci Lett 200:147–157
Di Crescenzo D, Shuster M, Petlyuk A, Ernens D, Zijsling D, Pasaribu H (2015) Lubricants and accelerated test methods for expandable tubular application. In: SPE/IADC drilling conference and exhibition, 17–19 March, London, England, UK. Society of Petroleum Engineers. doi:10.2118/173111-MS
Duchesne J, Reardon EJ (1995) Measurement and prediction of portlandite solubility in alkali solutions. Cem Concr Res 25:1043–1053
Dupal KK, Campo DB, Lofton JE, Weisinger D, Cook RL, Bullock MD, Grant TP, York PL (2001) Solid expandable tubular technology—a year of case histories in the drilling environment. In: SPE/IADC drilling conference, 27 February–1 March, Amsterdam, Netherlands. Society of Petroleum Engineers. doi:10.2118/67770-MS
Dusseault MB, Gray MN, Nawrocki PA (2000) Why oilwells leak: cement behavior and long-term consequences. In: SPE international oil and gas conference and exhibition, SPE 64733. p 8. doi:10.2118/64733-MS
Dyer S, Graham G (2002) The effect of temperature and pressure on oilfield scale formation. J Pet Sci Eng 35:95–107. doi:10.1016/S0920-4105(02)00217-6
Espinosa Marzal RM, Scherer GW (2008) Crystallization of sodium sulfate salts in limestone. Environ Geol 56:605–621. doi:10.1007/s00254-008-1441-7
Everett DH (1961) The thermodynamics of frost damage to porous solids. Trans Faraday Soc 57:1541–1551
Flatt RJ, Scherer GW (2008) Thermodynamics of crystallization stresses in DEF. Cem Concr Res 38:325–336. doi:10.1016/j.cemconres.2007.10.002
Flatt RJ, Steiger M, Scherer GW (2006) A commented translation of the paper by C.W. Correns and W. Steinborn on crystallization pressure. Environ Geol 52:187–203. doi:10.1007/s00254-006-0509-5
Fleckenstein WW, Eustes AW, Miller MG (2000) Burst induced stresses in cemented wellbores. In: SPE/AAPG western regional meeting. Society of Petroleum Engineers
Fletcher RC, Merino E (2001) Mineral growth in rocks: kinetic-rheological models of replacement, vein formation, and syntectonic crystallization. Geochim Cosmochim Acta 65:3733–3748. doi:10.1016/S0016-7037(01)00726-8
Fuertes AB, Alvarez D, Rubiera F, Pis JJ, Marban G, Palacos JM (1991) Surface area and pore size changes during sintering of calcium oxide particles. Chem Eng Commun 109:73–88
Gasda SE, Bachu S, Celia MA (2004) Spatial characterization of the location of potentially leaky wells penetrating a deep saline aquifer in a mature sedimentary basin. Environ Geol 46:707–720. doi:10.1007/s00254-004-1073-5
Ghofrani R, Plack H (1993) CaO- and/or MgO-swelling cements: a key for providing a better annular sealing? In: SPE/IADC drilling conference. Society of Petroleum Engineers. doi:10.2118/25697-MS
Gibbs JW (1928) The collected works of J. Willard Gibbs, volume I: thermodynamics. Yale University Press, New Haven
Glasson DR (1958) Reactivity of lime and related oxides. II. Sorption of water vapour on calcium oxide. J Appl Chem 8:798–803
Glasson DR (1958) Reactivity of lime and related oxides. I. Production of calcium oxide. J Appl Chem 8:793–797
Gratier J-P, Frery E, Deschamps P, Røyne A, Renard F, Dysthe D, Ellouz-Zimmerman N, Hamelin B (2012) How travertine veins grow from top to bottom and lift the rocks above them: the effect of crystallization force. Geology 40:1015–1018
Harada T, Idemitsu T, Watanabe A, Takayama S (1989) The design method for the demolition of concrete with expansive demolition agents. In: Shah SP, Swartz SE (eds) Fracture of concrete and rock: SEM-RILEM international conference June 17–19, 1987, Houston, Texas, USA. Springer, New York, pp 47–57. doi:10.1007/978-1-4612-3578-1_5
Henry KS (2000) A review of the thermodynamics of frost heave. ERDC/CRREL-TR-00-16. Cold Regions Research and Engineering Laboratory, US Army Corps of Engineers, Washington DC
Hepple RP, Benson SM (2005) Geologic storage of carbon dioxide as a climate change mitigation strategy: performance requirements and the implications of surface seepage. Environ Geol 47:576–585. doi:10.1007/s00254-004-1181-2
Hofstee C, Seeberger F, Orlic B, Mulders F, Van Bergen F, Bisschop R (2008) The feasibility of effective and safe carbon dioxide storage in the De Lier gas field. First Break 26:53–57
Hou MZ, Bauer S, Kolditz O, Xie H, Li X, Yang C, Yuan Y (2013) Use of the geological subsurface for production, storage and conversion of clean energy. In: ISRM SINOROCK 2013, 18–20 June, Shanghai, China. International Society for Rock Mechanics
Huerta NJ, Hesse MA, Bryant SL, Strazisar BR, Lopano C (2016) Reactive transport of CO2-saturated water in a cement fracture: application to wellbore leakage during geologic CO2 storage. Int J Greenh Gas Control 44:276–289. doi:10.1016/j.ijggc.2015.02.006
Idiart AE, López CM, Carol I (2011) Chemo-mechanical analysis of concrete cracking and degradation due to external sulfate attack: a meso-scale model. Cem Concr Compos 33:411–423. doi:10.1016/j.cemconcomp.2010.12.001
Ingraffea AR, Wells MT, Santoro RL, Shonkoff SBC (2014) Assessment and risk analysis of casing and cement impairment in oil and gas wells in Pennsylvania, 2000–2012. Proc Natl Acad Sci 111:10955–10960. doi:10.1073/pnas.1323422111
ISO 11960 (2004) Petroleum and natural gas industries—steel pipes for use as casing or tubing for wells. Int. Organ. Stand. Geneva
Israelachvili JN (2011) Intermolecular and surface forces: revised third edition. Academic Press, New York
Jackson RE, Dusseault MB (2014) Gas release mechanisms from energy wellbores. ARMA 14-7753
Jaeger J, Cook NG, Zimmerman RW (2007) Fundamentals of rock mechanics, 4th edn. Wiley, New York
Jamtveit B, Malthe-Sørenssen A, Kostenko O (2008) Reaction enhanced permeability during retrogressive metamorphism. Earth Planet Sci Lett 267:620–627. doi:10.1016/j.epsl.2007.12.016
Jamtveit B, Putnis CV, Malthe-Sørenssen A (2008) Reaction induced fracturing during replacement processes. Contrib Mineral Petrol 157:127–133. doi:10.1007/s00410-008-0324-y
Jordan MM, Kemp S, Sorhaug E, Sjursaether K, Freer B (2003) Effective management of scaling from and within carbonate oil reservoirs, North Sea Basin. Chem Eng Res Des 81:359–372. doi:10.1205/02638760360596919
Kaiser MJ (2015) Decommissioning forecast in the deepwater Gulf of Mexico, 2013–2033. Mar Struct 41:96–126. doi:10.1016/j.marstruc.2014.12.006
Kalil IA, McSpadden AR (2012) Casing burst stresses in particulate-filled annuli: where is the cement? SPE Drill Complet 27:473–485
Kamb WB (1959) Theory of preferred crystal orientation developed by crystallization under stress. J Geol 67(2):153–170
Kamb WB (1961) The thermodynamic theory of nonhydrostatically stressed solids. J Geophys Res 66:259–271
Kelemen PB, Hirth G (2012) Reaction-driven cracking during retrograde metamorphism: olivine hydration and carbonation. Earth Planet Sci Lett 345:81–89
Kelemen PB, Matter J, Streit EE, Rudge JF, Curry WB, Blusztajn J (2011) Rates and mechanisms of mineral carbonation in peridotite: natural processes and recipes for enhanced, in situ CO2 capture and storage. Annu Rev Earth Planet Sci 39:545–576. doi:10.1146/annurev-earth-092010-152509
Kennedy LA, White JC (2001) Low-temperature recrystallization in calcite: mechanisms and consequences. Geology 29:1027–1030
Keulen NT, Den Brok SWJ, Spiers CJ (2001) Force of crystallisation of gypsum during hydration of synthetic anhydrite rock. In: 13th DRT conference: deformation mechanisms, rheology, and tectonics
Khaimov-Mal’kov VYa, (1959) Experimental measurement of crystallization pressure. In: Shubnikov AV, Sheftal' NN (eds) Growth of crystals, vol 2. Springer, US, pp 14–19
Khaimov-Mal’kov VY (1959) The thermodynamics of crystallization pressure. In: Shubnikov AV, Sheftal' NN (eds) Growth of crystals, vol 2. Springer, US, pp 3–13
Kudłacz K, Rodriguez-Navarro C (2014) The mechanism of vapor phase hydration of calcium oxide: implications for CO2 capture. Environ Sci Technol 48:12411–12418. doi:10.1021/es5034662
Kupresan D, Heathman J, Radonjic M (2013) Application of a new physical model of expandable casing technology in mitigation of wellbore leaks. J Can Energy Technol Innov 1(5):1–4
Kupresan D, Heathman J, Radonjic M (2014) Experimental assessment of casing expansion as a solution to microannular gas migration. In: IADC/SPE drilling conference and exhibition, 4–6 March, Fort Worth, Texas, USA. Society of Petroleum Engineers. doi:10.2118/168056-MS
Ladva HKJ, Craster B, Jones TGJ, Goldsmith G, Scott D (2005) The cement-to-formation interface in zonal isolation. SPE Drill Complet. doi:10.2118/88016-PA
Lecampion B, Bunger A, Kear J, Quesada D (2013) Interface debonding driven by fluid injection in a cased and cemented wellbore: modeling and experiments. Int J Greenh Gas Control 18:208–223. doi:10.1016/j.ijggc.2013.07.012
Lehner FK (1990) Thermodynamics of rock deformation by pressure solution. In: Barber DJ, Meredith PG (eds) Deformation processes in minerals, ceramics and rocks. Springer, pp 296–333
Lehner FK (1995) A model for intergranular pressure solution in open systems. Tectonophysics 245:153–170
Lewis K, Zyvoloski GA, Kelkar S, Carey JW (2012) Coupled stress and flow along interfaces in the wellbore environment in relation to CO2 sequestration. In: 46th US rock mechanics/geomechanics symposium. American Rock Mechanics Association
Liversidge D, Taoutaou S, Agarwal S (2006) Permanent plug and abandonment solution for the North Sea. In: SPE Asia Pacific oil and gas conference and exhibition, 11–13 September, Adelaide, Australia. Society of Petroleum Engineers. doi:10.2118/100771-MS
Lothenbach B, Matschei T, Möschner G, Glasser FP (2008) Thermodynamic modelling of the effect of temperature on the hydration and porosity of Portland cement. Cem Concr Res 38:1–18
Mainguy M, Longuemare P, Audibert A, Lécolier E (2007) Analyzing the risk of well plug failure after abandonment. Oil Gas Sci Technol Rev 62:311–324. doi:10.2516/ogst
Marbun B (2006) Kinetik der Hydratation von CaO und MgO. Technischen Universität Clausthal, Clausthal-Zellerfeld
Matschei T, Lothenbach B, Glasser FP (2007) Thermodynamic properties of Portland cement hydrates in the system CaO–Al2O3–SiO2–CaSO4–CaCO3–H2O. Cem Concr Res 37:1379–1410
McLellan AG (1968) The chemical potential in thermodynamic systems under non-hydrostatic stresses. In: Proceedings of the Royal Society of London A: mathematical, physical and engineering sciences. The Royal Society, pp 1–13
Means WD, Li T (2001) A laboratory simulation of fibrous veins: some first observations. J Struct Geol 23:857–863
Meng Q, Xie Z, Feng L (2003) An introduction to the expandible casing technology. Drill Prod Technol 4:23
Merino E, Dewers T (1998) Implications of replacement for reaction–transport modeling. J Hydrol 209:137–146. doi:10.1016/S0022-1694(98)00150-4
Montgomery CT (2006) Implications of cementing for well production and performance. In: Nelson EB, Guillot D (eds) Well cementing. Schlumberger, Sugar Land, p 773
Nelson EB, Guillot D (eds) (2006) Well cementing, 2nd edn. Schlumberger, Sugar Land
Noiriel C, Renard F, Doan M-L, Gratier J-P (2010) Intense fracturing and fracture sealing induced by mineral growth in porous rocks. Chem Geol 269:197–209
Orlic B (2009) Some geomechanical aspects of geological CO2 sequestration. KSCE J Civ Eng 13:225–232. doi:10.1007/s12205-009-0225-2
Ostapenko GT (1976) Excess pressure on the solid phases generated by hydration (according to experimental data on the hydration of periclase). Traslated Geokhimikiya 6:824–844
Paterson MS (1973) Nonhydrostatic thermodynamics and its geologic applications. Rev Geophys 11:355–389
Paterson MS (1995) A theory for granular flow accommodated by material transfer via an intergranular fluid. Tectonophysics 245:135–151
Plumper O, Royne A, Magraso A, Jamtveit B (2012) The interface-scale mechanism of reaction-induced fracturing during serpentinization. Geology 40:1103–1106. doi:10.1130/G33390.1
Pluymakers AMH, Peach CJ, Spiers CJ (2014) Diagenetic compaction experiments on simulated anhydrite fault gouge under static conditions. J Geophys Res Solid Earth 119:4123–4148
Procesi M, Cantucci B, Buttinelli M, Armezzani G, Quattrocchi F, Boschi E (2013) Strategic use of the underground in an energy mix plan: synergies among CO2, CH4 geological storage and geothermal energy. Latium Region case study (Central Italy). Appl Energy 110:104–131. doi:10.1016/j.apenergy.2013.03.071
Putnis A, Janssen A, Jamtveit B, Putnis CV (2009) Reaction-induced fracturing during replacement reactions. Geochim Cosmochim Acta Suppl 73:1061
Ramachandran VS, Sereda PJ, Feldman RF (1964) Mechanism of hydration of calcium oxide. Nature 201:288–289
Ravi K, Bosma M, Gastebled O (2002) Safe and economic gas wells through cement design for life of the well. SPE 75700
Røyne A, Dysthe DK (2012) Rim formation on crystal faces growing in confinement. J Cryst Growth 346:89–100. doi:10.1016/j.jcrysgro.2012.03.019
Rudge JF, Kelemen PB, Spiegelman M (2010) A simple model of reaction-induced cracking applied to serpentinization and carbonation of peridotite. Earth Planet Sci Lett 291:215–227. doi:10.1016/j.epsl.2010.01.016
Scherer GW (1999) Crystallization in pores. Cem Concr Res 29:1347–1358. doi:10.1016/S0008-8846(99)00002-2
Scherer GW (2004) Stress from crystallization of salt. Cem Concr Res 34:1613–1624. doi:10.1016/j.cemconres.2003.12.034
Schutjens PMTM (1991) Experimental compaction of quartz sand at low effective stress and temperature conditions. J Geol Soc Lond 148:527–539
Shahidzadeh-Bonn N, Rafaï S, Bonn D, Wegdam G (2008) Salt crystallization during evaporation: impact of interfacial properties. Langmuir 24:8599–8605. doi:10.1021/la8005629
Smith I, Olstad E, Segura R (2011) Heightened regulations create demand for well abandonment services. Offshore 71(10):70–73
Steiger M (2005) Crystal growth in porous materials—I: the crystallization pressure of large crystals. J Cryst Growth 282:455–469. doi:10.1016/j.jcrysgro.2005.05.007
Steiger M (2005) Crystal growth in porous materials—II: influence of crystal size on the crystallization pressure. J Cryst Growth 282:470–481. doi:10.1016/j.jcrysgro.2005.05.008
Sun P, Grace JR, Lim CJ, Anthony EJ (2007) The effect of CaO sintering on cyclic CO2 capture in energy systems. AIChE J 53:2432–2442
Sun Z, Chi H, Fan L-S (2012) Physical and chemical mechanism for increased surface area and pore volume of CaO in water hydration. Ind Eng Chem Res 51:10793–10799
Taber S (1916) The growth of crystals under external pressure. Am J Sci 246:532–556
Taber S (1930) The mechanics of frost heaving. J Geol 38(4):303–317
Taylor HF, Famy C, Scrivener K (2001) Delayed ettringite formation. Cem Concr Res 31:683–693. doi:10.1016/S0008-8846(01)00466-5
Taylor HFW (1992) Cement chemistry. Academic Press, London
Tsui N, Flatt RJ, Scherer GW (2003) Crystallization damage by sodium sulfate. J Cult Herit 4:109–115. doi:10.1016/S1296-2074(03)00022-0
van Noort R, Spiers C, Kandianis M, Drury MR, Ten Grotenhuis SM (2010) Coupled geomechanical-geochemical aspects of CO2-sequestration in peridotites. In: AGU fall meeting abstracts, p 7
van Noort R, Spiers CJ, Peach CJ (2007) Effects of orientation on the diffusive properties of fluid-filled grain boundaries during pressure solution. Phys Chem Miner 34:95–112
van Noort R, Spiers CJ, Pennock GM (2008) Compaction of granular quartz under hydrothermal conditions: controlling mechanisms and grain boundary processes. J Geophys Res Solid Earth 113(B12206):1–23
van Noort R, Visser HJM, Spiers CJ (2008) Influence of grain boundary structure on dissolution controlled pressure solution and retarding effects of grain boundary healing. J Geophys Res Solid Earth 113(B03201):1–15
Visser HJM, Spiers CJ, Hangx SJT (2012) Effects of interfacial energy on compaction creep by intergranular pressure solution: theory versus experiments on a rock analog (NaNO3). J Geophys Res. Solid Earth 117(B11211):1–15
Voorhees HR, Sliepcevich CM, Freeman JW (1956) Thick-walled pressure vessels. Ind Eng Chem 48:872–881. doi:10.1021/ie50557a026
Warne P (2004) Decommissioning—North Sea. OGEL 2. http://www.ogel.org/article.asp?key=1254. Accessed 21 Mar 2017
Weyl PK (1959) Pressure solution and the force of crystallization: a phenomenological theory. J Geophys Res 64:2001–2025
Whittaker S, Rostron B, Hawkes C, Gardner C, White D, Johnson J, Chalaturnyk R, Seeburger D (2011) A decade of CO2 injection into depleting oil fields: monitoring and research activities of the IEA GHG Weyburn-Midale CO2 Monitoring and Storage Project. Energy Procedia 4:6069–6076. doi:10.1016/j.egypro.2011.02.612
Wolter A, Luger S, Schaefer G (2004) Zur Kinetik der Hydratation von Branntkalk. ZKG Int 57:60–68
Wolterbeek TKT, Hangx SJT, Spiers CJ (2016) Effect of CO2-induced reactions on the mechanical behaviour of fractured wellbore cement. Geomech Energy Environ 7:26–46. doi:10.1016/j.gete.2016.02.002
Wolterbeek TKT, Peach CJ, Raoof A, Spiers CJ (2016) Reactive transport of CO2-rich fluids in simulated wellbore interfaces: flow-through experiments on the 1–6 m length scale. Int J Greenh Gas Control 54:96–116. doi:10.1016/j.ijggc.2016.08.034
Yasuhara H, Elsworth D, Polak A (2003) A mechanistic model for compaction of granular aggregates moderated by pressure solution. J Geophys Res Solid Earth 108(B11):1–13
Zhang M, Bachu S (2011) Review of integrity of existing wells in relation to CO2 geological storage: What do we know? Int J Greenh Gas Control 5:826–840. doi:10.1016/j.ijggc.2010.11.006
Acknowledgements
Data used in this paper were acquired in experiments performed at the High Pressure and Temperature Laboratory, Utrecht University, the Netherlands. Data can be made available by the authors upon request. We thank Eimert de Graaff, Gert Kastelein, Peter van Krieken and Thony van der Gon Netscher for valuable technical support provided in the laboratory and Bart Verberne for help with using the Scanning Electron Microscope. The manuscript benefitted from the detailed feedback of two anonymous reviewers, for which we are thankful. This research was conducted within the context of CATO-2 (www.co2-cato.org), the Dutch national research program on Carbon Capture and Storage (CCS). The program is financially supported by the Dutch government (Ministry of Economic Affairs) and the CATO-2 consortium parties.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Wolterbeek, T.K.T., van Noort, R. & Spiers, C.J. Reaction-driven casing expansion: potential for wellbore leakage mitigation. Acta Geotech. 13, 341–366 (2018). https://doi.org/10.1007/s11440-017-0533-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11440-017-0533-5