Abstract
A novel visible-light-sensitive ZnVFeO4 photocatalyst has been fabricated by the precipitation method at different pH values for the enhanced photocatalytic degradation of malachite green (MG) dye as a representative pollutant under visible light irradiation at neutral pH conditions. The structure and optical characteristics of the prepared photocatalysts were investigated by XRD, FTIR, N2 adsorption–desorption, TEM, diffuse reflectance spectroscopy (DRS), and photoluminescence (PL) analyses. In addition, the photocatalytic activity of ZnVFeO4 photocatalysts superior the efficiency to be more than that of the mono and bi-metal oxides of iron and iron zinc oxides, respectively. The best sample, ZnVFeO4 at pH 3, significantly enhances the degradation rate under visible light to be 12.7 × 10−3 min−1 and can retain a stable photodegradation efficiency of 90.1% after five cycles. The effect of the catalyst dose and the initial dye concentration on the photodegradation process were studied. This promising behavior under visible light may be attributed to the low bandgap and the decreased electron–hole recombination rate of the ZnVFeO4 heterostructures. The scavenger experiment confirmed that the hydroxyl radicals induced the MG photodegradation process effectively. Hence, the ZnVFeO4 is a reliable visible-light-responsive heterostructure photocatalyst with excellent potential for the photodegradation of organic pollutants in wastewater treatment.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Avoid common mistakes on your manuscript.
Introduction
In the light of the rapidly increasing population and industrial production, millions of pollutants are being discharged into water bodies causing water scarcity and pollution to become a prominent issue. This problem must be addressed due to the growing damage it poses to water supply security, human health, natural ecosystems, and hence the quality of life. As the water is the origin of life, facing the severe water pollution issue is of great importance and essential to assure clean water to fill the requisites of human life along with other living beings and commercial activities (Nas et al. 2019; Amdeha 2021; Amdeha et al. 2021; Wang and Tang 2021). Manufacturing residues frequently include organic and inorganic pollutants involving heavy metals, synthetic dyes, insecticides, pesticides, pharmaceuticals, etc. These pollutants, notably synthetic organic dyes, regarded as one of the principal pollutants emitted into the environment, must be adequately handled before disposal (Eghbali et al. 2019; Senthil et al. 2020). Dyes are frequently made up of chromophores and auxochromes and have complex molecular structures. The color of the dye is determined by the chromophores, which have an aromatic structure.
Moreover, auxochromes containing –NH3, –COOH, –HSO3, or –OH groups determine the color intensity and make the molecule water-soluble (Moussavi and Mahmoudi 2009). Synthetic dyes are provided with ecologically more extended durability due to their complex structure and consistent resilience vs. light, temperature, and chemical compounds (Hassani et al. 2020). These dyes in water boost oxygen demand, causing aquatic species to suffer a lot (Gupta et al. 2020). As a result, there is a pressing need to identify more practical, cost-effective, and ecologically friendly technologies for removing dyes before releasing them into water sources to avoid harming aquatic ecosystems (Hassani et al. 2020).
For the treatment of dye effluents, traditional biological, chemical, and physical approaches such as adsorption (Bafana et al. 2011) and chemical precipitation (De Gisi et al. 2016) have been recognized. These processes are affected by high expenses, sludge creation, or secondary pollutant creation, such as dye adsorption on activated carbon material (Bhushan et al. 2020), where the pollutant is just transferred from the liquid phase to the solid phase, producing secondary pollution. Therefore, the decomposition of the dyes into non-toxic products is urgently required and favored. In the degradation process, the aromatic carbon in the dyes decomposes into innocuous CO2, whereas N2 and S decompose into inorganic ions such as ammonium and sulfate.
To attain the degradation, photocatalytic degradation as one of the advanced oxidation processes (AOPs) is highly recommended and applied (Eghbali et al. 2019; El-Salamony et al. 2021; Deriase et al. 2021; Hassani et al. 2021). AOPs have attracted considerable research interest as effective and economic technologies owing to better oxidizing ability and less secondary pollution (Paździor et al. 2019) due to the highly reactive oxygen species (ROS), e.g., •OH, •O2−, and 1O2 produced in the system (Yu et al. 2019; Chen et al. 2022; Hang et al. 2022). When photoactive catalysts like ZnO and TiO2 are irradiated with solar/UV light, ROS are created from the oxidation or reduction of different species in the water. Photocatalysis occurs when photons excite photoactive materials. When exposed to sunlight or UV irradiation, photocatalysis generates holes (h+) in the valence band (VB) and electrons (e−) in the conduction band (CB). To excite (e−) from the VB to the CB, the photon’s energy must be higher than the photocatalyst’s bandgap (Bhushan et al. 2020). The reactive radicals that originate from the reaction between the (e−) and the oxygen (or the h+ and the oxygen) in water react with the organic contaminants in the water, resulting in the formation of non-toxic products such as CO2 and H2O (Sheydaei et al. 2019; Ghanbari et al. 2019).
Conventional materials, like ZnO, TiO2, ZrO2, CeO2, and SnO2 are only active in ultraviolet (UV) light, which accounts for just 4% of the solar spectrum, limiting their usage in simulated or direct solar-light dye degradation over a broad visible range (Banerjee et al. 2014; Nkosi et al. 2014; Ovodok et al. 2018; Natarajan et al. 2018; Yadav et al. 2019; Kannan et al. 2020; Aliabadi et al. 2020; Luque et al. 2021). The advantage of using iron-based photocatalysts is that they can absorb 39% or more of the solar-light composition in visible light and hence have effective degradation efficiencies (Hassani et al. 2018; Madihi-Bidgoli et al. 2021). Hetero-mixed interfaces with more than two metal oxides have shown to be the most successful method for producing visible light photoactive materials. There are various intrinsic structural enhancements at the interface junctions of mixed metal oxides, including greater efficiency in generating, separating, and transporting charge carriers for optimal redox utilization in photocatalytic processes. These photocatalytic processes may be significantly enhanced on the composite oxide surfaces by creating oxygen vacancy defects which can function as electron trapping sites while increasing the reactive substrates’ redox activity adsorption/desorption (Sharma et al. 2021, 2022). Numerous metal orthovanadate (AVO4) (A = metal oxide) depending on BiVO4 (Wang et al. 2019), GdVO4 (Monsef et al. 2020), CeVO4 (Shafiq et al. 2021), InVO4 (Shandilya et al. 2019), LaVO4 (Wetchakun et al. 2017), and PrVO4 (Sajid et al. 2021) semiconductor materials have been successfully fabricated, characterized, and analyzed for photocatalytic structure properties to illustrate the significant photocatalytic improvement in hetero-mixed metal oxides.
The main objective is to enhance the photocatalytic performance by minimizing the bandgap of the prepared photocatalysts to increase the absorption edge toward the visible region to make good use of the solar light as the visible light stands for ~ 43% of the total solar light. Also, as the recombination of the (e−) and (h+) inhibits the photodegradation process, thus, inhibiting this recombination is of great importance to enhance the degradation efficiency (El-Salamony et al. 2017). Taking these points as motivates, the objective of this article is the improvement and preparation of novel Fe-based photocatalysts for the photocatalytic degradation of the malachite green (MG) dye under visible light (i.e.) with low energy consumption in terms of the degradation efficiencies; and removal (%), rate of reaction (k), and half-life time (t). The photocatalytic degradation process will be under neutral pH conditions to prevent the corrosion that happens when a strongly acidic or alkaline environment is used. Fe-based photocatalysts were successfully synthesized by the precipitation method. The prepared photocatalysts were characterized by different methods for understanding their properties. The effect of the initial dye concentrations and the catalyst dose were studied for maximum removal of MG dye. Through a free radical scavenger experiment, the radical which is responsible for the process was clarified. The recycling experiments were used to study the catalyst stability.
Experimental
Materials
In this study, the following chemicals and materials were used. Ammonium hydroxide (NH4OH, 28%), ammonium vanadate (NH4VO3, 99%), ferric chloride anhydrous (FeCl3, 99.9%), zinc chloride anhydrous (ZnCl2, 99.9%), tert-butyl alcohol ((CH3)3COH, 98.5%), 1,4-benzoquinone (C6H4O2, 99%), and ammonium oxalate ((NH4)2C2O4, 99%) are provided from Sigma-Aldrich. The malachite green (MG) dye (C23H25N2Cl; MW = 364.92 g) is provided from Fluka. All chemicals used in this study were analytical grade and utilized without additional purification.
Synthesis of pure iron oxide
Pure iron oxide was generated using a simple co-precipitation method in which ammonia solution (NH4OH) was added dropwise to anhydrous ferric chloride solution (160 g in distilled H2O at 80 °C) while stirring continuously. At pH 9, the reaction mixture was heated for 4 h with rapid mechanical stirring. The created precipitate was allowed overnight at room temperature after complete precipitation, and the resulting solid was centrifuged. The precipitate was washed several times with distilled H2O to eliminate ammonium ions before drying at 100 °C. The powder was calcined at 500 °C for 4 h after being crushed in a ball mill (300 rpm for 5 h).
Synthesis of iron zinc oxide-mixed phases
A solution containing 10 g of anhydrous zinc chloride was dissolved in distilled water. Then, ammonia solution was added dropwise to a vigorously stirred solution containing 40 g of anhydrous ferric chloride in distilled H2O at 80 °C to create iron zinc oxide nanomaterial-mixed phase. The reaction mixture was heated for 4 h at pH 9 using a magnetic stirrer with continuous stirring. After complete precipitation, the produced material was centrifuged and washed multiple times with distilled water to eliminate ammonium ions before drying at 100 °C. The powder was calcined at 500 °C for 4 h after being crushed by a ball mill (300 rpm for 5 h).
Synthesis of iron vanadium oxide-zinc oxide-mixed phases
A solution containing 10 g of ammonium vanadate was dissolved in distilled water. The ammonia solution was added dropwise to a well-stirred solution containing 40 g of anhydrous ferric chloride in distilled water. Then, a solution containing 10 g of anhydrous zinc chloride was dissolved in distilled water at 80 °C. At varying pH values of 3, 9, and 12, the reaction liquid was heated using a magnetic stirrer with continuous stirring for 4 h. After complete precipitation, the precipitated material was centrifuged, then washed multiple times with distilled water to eliminate ammonium ions before drying at 100 °C. The powder was calcined at 500 °C for 4 h after being crushed by a ball mill (at 300 rpm for 5 h). The iron oxide, iron zinc oxide, and iron vanadium oxide-zinc oxide at different pH values are named FO, FZ, FVZ3, FVZ9, and FVZ12, respectively, in which 3, 9, and 12 refer to the used pH value.
Characterization of the prepared samples
Using a Quantachrome NOVA 3200 automated gas sorption system (USA) at − 196 °C, the surface area of the prepared samples was evaluated using nitrogen adsorption–desorption isotherms. Degassing at 120 °C and 10–5 mm Hg for 3 h was used to prepare the samples. Before and after the activation, the weight of the sample was calculated. The surface area was derived from the adsorption branch using the Brunauer–Emmett–Teller (BET) equation in the relative pressure P/Po range of 0.05–0.35. The Barrett-Joyner-Halenda (BJH) method was used to compute the pore size distribution based on the desorption branches of the nitrogen isotherms. Dynamic light scattering was used to determine particle size distribution (DLS). The Brownian motion of the particles is measured by DLS and related to particle size. A sonic probe was used to combine nanoparticles with solvent. Dynamic light scattering was carried out using Zeta Sized Nano Series, Nano ZS, Malvern Instruments, UK. A Pan Analytical Model X’ Pert Pro with CuK radiation (λ = 0.1542 nm), Ni-filter, and general area detector was used to capture X-ray diffraction. A 40-kV accelerating voltage and a 40-mA emission current were employed. The diffraction was recorded using a 0.02 Ǻ step size and a 0.605 2θ scan rate in the 2θ range of 10–80°. Nicolet Is-10 FT-IR spectrophotometer utilizing the KBr method was used to evaluate the prepared samples’ Fourier transform infrared spectroscopy (FTIR): Thermo Fisher Scientific. Because the weight of the sample and the weight of KBr were constantly kept constant, the KBr procedure was carried out in an approximate quantitative manner for all samples. On a JEOL JEM-1230 electron microscope with a 120-kV acceleration voltage, pictures of transmission electron microscopy (TEM) were captured. The samples were made by soaking a carbon-coated copper grid in methanol HPLC for 15 min and coating it with suspended sonicated materials. The UV–vis diffuse reflectance spectroscopy (DRS) study of the produced photocatalysts was performed using a JASCO (Japan) UV-spectrophotometer model V-570, with BaSO4 serving as a standard reflectance reference in the 200–800 nm spectral region. A spectrofluorometer was used to detect photoluminescence (PL) at room temperature (JASCO FP-6500, Japan).
Photodegradation of malachite green dye
The photodegradation of MG dye assessed the photocatalysts’ performance under both UV and visible light irradiation. The selected dose of the catalyst was dispersed in a known concentration of MG solution under stirring at neutral pH conditions. After adsorption for 1 h, to avoid the interference of the adsorption throughout the photocatalytic processes, a UV (8 W VILBER–LOURMAT; λ = 254 nm) or visible light (100 W–TUNGSTEN lamp; λ > 400 nm) was turned on for 3 h. Periodically, a sample was collected, centrifuged, and the leftover MG dye concentration was evaluated by a JENWAY–6505 UV–visible spectrophotometer at λmax = 615 nm after suitable dilution to determine the efficiency of the reactions via the following equations: Eq. 1, Eq. 2 and Eq. 3. Similar protocol was adopted for parameters study, e.g., light source, photocatalyst dose, dye concentration, pH, and H2O2 concentration. The reactive oxygen species (ROS) scavenge experiments investigated the degradation mechanism, in which tert-butyl alcohol (BuOH), 1,4-benzoquinone (BQ), and ammonium oxalate (AO) were employed as scavengers for hydroxyl (•OH), superoxide (•O2−), and photogenerated (h+), respectively (Amdeha and Mohamed 2021). The stability and reusability of the most efficient photocatalyst were evaluated according to the measurements of five consecutive recently prepared 25 ppm MG solutions. The runs were done for 3 h. During the 1st run, MG solution (25 ppm) was poured on the catalyst (1 g/L). After the experiment, under visible light for 3 h at 25 °C, the solution was poured from the vessel, and the residual catalyst was washed with distilled water and then dried. A similar volume of MG solution (25 ppm) was added to the residual catalyst in the second run. The following cycles till the fifth one were repetitive in the same method. The solution temperature during the experiments was kept at 25 ± 1 °C.
Degradation (%)
The pseudo-first-order kinetic model
The half-life time of the dye degradation
where D (%), the degradation efficiency; Co, the initial MG concentration; Ct, the MG concentration at time t; and t1/2, the half-life time of the dye degradation.
Results and discussion
Characterization of photocatalysts
The diffraction patterns of the prepared Fe-based photocatalysts, FO, FZ, and various ZnVFeO4 at different pH values, were determined by XRD analysis (Fig. 1). XRD patterns of both FO and FZ (Fig. 1(a)) exhibit the characteristic peaks of iron oxide at 23.9°, 32.9°, 35.4°, 40.7°, 49.3°, 53.9°, 57.4°, 62.3°, 63.8°, 69.4°, 71.8°, and 75.3° which correspond to the (0 1 2), (1 0 4), (1 1 0), (1 1 3), (0 2 4), (1 1 6), (0 1 8), (2 1 4), (3 0 0), (2 0 8), (1 0 1 0), and (2 2 0) crystallographic planes of Fe2O3 (Almeida et al. 2009; Hua and Gengsheng 2009). These twelve peaks are matched to the rhombohedral (hexagonal) structure of hematite (Card no. 04–011-9585). There are no observable peaks for the zinc sample in the XRD pattern due to the low amount of zinc compared to the iron precursor revealing that zinc is embedded into the Fe2O3 lattice (Lassoued 2021). For FVZ samples (Fig. 1(b)), the peaks for vanadate oxide V2O5 phase (2θ = 27.64°) and iron vanadium oxide FeVO4 phase (2θ = 24.11°) are weak and not well defined due to the dominance of the Fe2O3 peaks (Elfadly et al. 2013). Moreover, the strong intensity of the Fe2O3 peaks is relatively decreased. The main peaks at 32.9° and 35.4° exhibited shifting to high 2θ for FVZ samples (e.g., 33.1° and 35.6° for FVZ3) due to the introduction of vanadium into the structure indicating strong interactions of these metals. Additionally, the d-spacing between the atoms became less as the vanadium occupied the interstitial positions leading to changes in the lattice structure (Rahimpour et al. 2020). The Scherer equation, Eq. 4 (Cao et al. 2021), was used to estimate the mean particle size of the produced nanocatalysts (Table 1).
where D, the mean crystallite size; β, the lengthening of the diffraction line measured at half-maximum intensity; λ, the X-ray radiation’s wavelength; and θ, the Bragg angle.
Figure 2 shows the FTIR spectra of FO, FZ, and FVZ nanoparticles and quaternary nanocomposites. The V = O bond’s vibration mode is allocated to the resolved IR band at 953 cm−1, whereas the V–O-V bond’s bridging oxygen atoms are attributed to the absorbance peaks between 750 and 850 cm−1. The IR bands with significant peaks at 550–700 cm−1 are caused by the vibration modes of V–O-Fe and V–O-Fe coupled bridging stretching (Kesavan et al. 2021). The IR bands at 850–1050 cm−1are also responsible for the mode of vibration stretch of the short vanadyl (V–O) bonds. The IR band at 894 cm−1 is produced by V–O and V–O-V coupled stretching (Sajid et al. 2018; Saravanakumar et al. 2020). The IR bands show the number of modes of vibration peaks at 974–983 cm−1, which reduces with higher V2O5 loadings while producing new larger bands owing to Fe–O and Fe–O-Fe. For FZ, the band at 480 cm−1 is associated with Zn–O bonds, whereas for ZnVFeO4 nanocatalysts, the band at 470 cm−1 is related to ZnVFeO4 nanocatalysts. At different pH 3, 9, and 12, a band at 576 cm−1 corresponds to F–O stretching vibrations of synthesized FO and FZ nanoparticles and shifts to 550 cm−1 ZnVFeO4 nanocatalysts.
The N2 adsorption–desorption isotherms of FO, FZ, and FVZ photocatalyst composites are exhibited in Fig. 3. As can be seen, the samples have type IV adsorption–desorption isotherms with an H3 hysteresis loop, indicative of mesoporous structure based on the IUPAC classification (Malibo et al. 2020; Thaba et al. 2022). The BJH method is used to analyze the pore size distribution (PSD) of the samples in the inset of Fig. 3. The average pore size diameters (Dpore) and the pore volume (Vpore) capacity of the Fe-based catalysts vary in the range of 42–59 nm and 0.018–0.139 cm3/g, respectively (Table 1). The significant decrease in the surface areas (SBET) of Fe-based photocatalysts is due to the introduction of zinc and vanadium oxide in the pores and structure of the catalysts, as confirmed by XRD, resulting in blocking some parts of mesopores and spaces and hence decreasing the surface area (Jiang et al. 2017).
The nanostructure morphology and particle size of Fe2O3-, FVZ3-, FVZ9-, and FVZ12-based catalysts were investigated using the TEM (Fig. 4). TEM tests revealed that the sample Fe2O3 had the largest size and hydrodynamic diameter, which indicates how the particles behave in a fluid. The crystalline size increased with increasing pH, reaching 83.92 nm and 113.9 nm for FVZ9 and FVZ12, respectively, due to the incorporation of Zn and V in the structure, as confirmed by XRD. The Fe, V, and Zn components are evenly distributed in the ZnVFeO4 catalysts. (Fe = 66.95 wt %); (V = 5.17 wt %); and (Zn = 10.20 wt %) were the preliminary metal levels in the FVZ catalysts.
The DRS and PL spectra of the Fe-based photocatalysts were determined to study their optical characteristics. The DRS was done to assess the optical properties and the bandgap of the Fe-based photocatalysts. The results are shown in Fig. S1. All three tri-composites, FVZ, exhibit a strong absorption band in both UV and visible regions, implying that these photocatalysts can be excited by an extensive range of light (Hang et al. 2022), and have excellent performance toward visible light response, indicating the photocatalytic ability under visible light. The optical band gap was calculated via the following equations: Eq. 5, Eq. 6 (Yu et al. 2018; Gupta et al. 2020):
Eg, the bandgap energy(eV); h, Planck’s constant; ν, light frequency; hν, the photon energy (eV); A, a proportional constant; α, the absorption coefficient; R, reflectance.
The bandgap energies of FVZ3, FVZ9, and FVZ12 are 1.90, 1.91, and 1.96 eV calculated from the Tauc method (Fig. S1). The inclusion of metal energy levels may have reduced the energy gap of the electronic transition, resulting in a narrow bandgap for FVZ (Kang et al. 2015). Besides, the excellent visible-light absorption could enhance the photocatalytic performance of the FVZ3 sample as it has the smallest bandgap (Manchala et al. 2021).
The separation of the photoinduced (e−)–(h+) pairs is crucial from the photocatalytic point of view. The behavior of these photo-generated charge carriers can be revealed through the PL measurements. In general, a high recombination rate of photogenerated electrons and holes suggests a high fluorescence intensity in PL spectra, whereas a low recombination rate can improve photocatalytic performance (Liu et al. 2022). The PL spectra of the Fe-based nanocomposites (Fig. 5) exhibit a main peak at 499 nm, which is referred to the recombination of excited (e−) and (h+) in the conduction and valence bands, respectively. This peak is attributed to the visible light emission caused by defects such as oxygen vacancies or Zn interstitial (Thein et al. 2016). A significant intensity variation is due to the different samples’ compositions. A decrease in the intensity of the FVZ3 is owing to the weak fluorescence response as compared to the FO and FZ undoubtedly shows that the recombination of photogenerated (e−)–(h+) is minimized in the tri-composite (Liu et al. 2022). This indicates that the FVZ3 composite can display more significant photocatalytic activity to the dye degradation than the other photocatalysts. The narrow bandgap of FVZ3 at 1.90 eV may encourage lattice defects under UV–visible light irradiation, which can act as an exciton center that hinders the recombination to enhance its photoactivity (Li et al. 2011).
The photocatalytic activity of the visible-light-responsive Fe-based photocatalysts
The activity of the visible-light-sensitive Fe-based photocatalysts was evaluated using malachite green (MG), one of the industrial dyes’ effluents, as a target organic compound model under visible light irradiation. The performance of the Fe-based photocatalysts, i.e., FO, FZ, FVZ3, FVZ9, and FVZ12, was found unsatisfactory in the absence of light, i.e., adsorption, with only 3–4% of dye was removed after 60 min without light irradiation. Also, in the absence of the photocatalyst, i.e., direct photolysis, less than 3% of dye was photodegraded under UV and visible light irradiation. It can be concluded that the MG removal efficiency is relatively poor under photolysis and adsorption. Consequently, a high-performance photocatalyst and suitable light source are required conditions for effective MG degradation (Du et al. 2020). The results show that the process can reach a saturation adsorption state within 60 min prior to the light irradiation and has almost no effect on the photodegradation performance and the rate. Figure 6 shows the MG degradation (%) after 180 min for the catalysts under UV and visible light irradiation. From this figure, the FVZ3 sample provides the highest MG photodegradation efficiency of 98% under visible light, while the photocatalytic performance of the same sample offers only 86% under UV light. This is due to the low band-gap energy of the FVZ3 photocatalyst, as mentioned in the optical properties. Also, this behavior is coincident with the previous study (El-Salamony et al. 2017) in which, under UV light, the radical recombination exceeds the separation, while under visible light, the electron–hole generation is prevalent, and the recombination is poor. This behavior could prove the catalyst activity under visible light and subsequently under sunlight, in which no energy consumption is required, which is a good point from an economic and energy-saving point of view. Therefore, visible light is nominated for further experiments due to the outstanding photocatalytic degradation efficiency.
The photocatalytic degradation of pollutants by photocatalysts generally follows the pseudo-first-order-kinetic model (Chiang and Doong 2015). Table 2 presents the reaction rate constant k, the half-life time t1/2, and the degradation (%) acquired by Eq. 1, Eq. 2, and Eq. 3. From Table 2, the calculated k values were 3.8 × 10−3 min−1, 5.5 × 10−3 min−1, 12.7 × 10−3 min−1, 11 × 10−3 min−1, and 9.5 × 10−3 min−1, for FO, FZ, FVZ3, FVZ9, and FVZ12, respectively. Noteworthy, the FVZ3 reveals the highest rate constant, k of 12.7 × 10−3 min−1, approximately 3.3 times higher than the FO sample. This result shows that the MG photodegradation rate follows the order FVZ3 > FVZ9 > FVZ12 > FZ > FO. FO and FZ show medium photocatalytic activity for MG degradation under visible light, possibly due to the rapid recombination of the photogenerated carriers (Ahmad et al. 2019). While FVZ3 exhibits higher activity than other photocatalysts, this agrees well with the optical data derived from the PL spectra. It is also worth noting that the photocatalytic degradation of organic compounds is a surface-mediated reaction (Han et al. 2016), with dye adsorption onto photocatalyst surfaces being the first step. Cationic MG dye can simply be adsorbed onto the negatively charged catalysts and FVZ3 exhibits excellent photocatalytic performance and rate compared to the other prepared photocatalysts due to its relatively high pore volume.
Factors affecting the photocatalytic degradation of MG dye
To determine the best conditions for MG photodegradation, reasonable runs are conducted. The impact of FVZ3 dosage on the photodegradation of the MG dye is displayed in Fig. 7(a). As the dose increases from 0.25 to 1 g/L, the MG degradation enhanced from 83.4 up to 92.0% for the degradation of 100 ppm MG. As the quantity of FVZ3 composite photocatalyst increased, the photoactive sites also increased, leading to an increase in the degradation efficiency. The increased catalyst dose enables a larger surface area for catalyst interaction and a higher concentration of free radicals per mL of the MG solution, resulting in a higher dye removal percentage (Xu and Wang 2011; Bhushan et al. 2020). When the dose was increased to 1.25 g/L and 1.5 g/L, the degradation efficiency dropped to 91.5% and 90.6%, respectively. Excess catalyst in the solution can prevent visible light from reaching the reaction suspension, resulting in a loss of accessible radiation and, as a result, low photoactive sites (Li et al. 2019). As a result, the best dosage for MG photodegradation using FVZ3 was 1 g/L.
The photodegradation of different MG initial concentrations was studied under visible light irradiation for all Fe-based photocatalysts with 1 g/L as a catalyst dose (Fig. 7(b)). The efficiency of MG photodegradation reduces as the starting dye concentration rises from 25 to 100 ppm. From Fig. 7(b), after 180 min of visible light irradiation, a nearly complete photodegradation (~ 98%) of 25 ppm MG by 1 g/L of FVZ3 is seen. When the starting concentration is increased to 100 ppm, only 92% of the MG is photodegraded. The inhibitory impact of the adsorbed MG molecules on light penetration could explain the decrease in MG photodegradation at high starting concentrations. It is worth noting that MG is a green dye, and thus, increasing its concentration would cause it to absorb more light. As a result, increasing the initial MG concentration reduces photon penetration to the photocatalyst surface, lowering the MG photocatalytic degradation efficiency (Pitchaimuthu et al. 2014). Another possible explanation for the lower efficiency is the photocatalyst’s restricted number of active sites.
Reusability of the catalyst
The reusability of the FVZ3 photocatalyst is of supreme significance from a financial standpoint because of the cost related to the catalyst preparation. The reusability was investigated by successive reusability tests, in which the photodegradation efficiencies of the FVZ3 sample in five continuous cycles were tested. Figure 8(a) displays the reusability test of the 25 ppm MG with 1 g/L of catalyst dose under visible light irradiation. After the third cycle, FVZ3 still displays an excellent visible-light responsive activity with a high MG degradation of about 94.4%. The third cycle efficiency is decreased only by 3.6% from the first one, which may be caused by the accumulation of intermediates after the MG photocatalytic degradation (Nguyen and Doong 2016).
Furthermore, the structure of the used FVZ3 was characterized using XRD (Fig. 8(b)). Compared with the freshly prepared sample, the recovered catalyst shows no significant structural changes in the XRD of the FVZ3 composite, which indicates its superior stability. The multiple catalyst reusability makes it a good choice for photodegradation of the pollutants existing in the water.
Photocatalytic reaction mechanism (scavengers test)
Reactive species have a crucial role in the photodegradation process of the contaminants. Superoxide radical anions (•O2–), hydroxyl radicals (•OH), and photoinduced holes (h+) are among the reactive species. The decrease of the photodegradation activity reveals the vital role of the active radicals. The influence of the active species follows the order •OH > •O2– > h+ agreeing to the results in Fig. 9. The MG degradation % decreased from 94.3 to 90.3%, 89.2%, and 80.5% after adding AO, BQ, and BuOH scavengers, respectively. Agreeing to the obtained results, the introduction of t-butyl alcohol significantly could reduce the MG degradation efficiency, indicating that the ⋅OH radicals are the principal active species. Another contributed ROS is •O2– because the presence of BQ significantly reduces the MG degradation efficiency. In contrast, a slight decrease in the efficiency was detected in the presence of the AO, suggesting that h+ has a limited contribution to the MG photodegradation (Chen et al. 2022).
Based on the previous analysis, a probable mechanism for MG degradation was proposed, in which the ⋅OH may directly oxidize MG dye. The bandgap of the composite catalyst has been lowered, and the visible light response has been improved. As a result, more electrons will be excited from the valence band into the conduction band of FVZ3 and produce photo-generated electron–hole pairs during visible light irradiation.
In addition, the low recombination rate of photo-generated electron–hole pairs for FVZ3 enhances the photocatalytic degradation activity. The photo-generated (e−)–(h+) pairs split quickly and travel to the photocatalyst’s surface. The effectual separation of the photo-generated (e−)–(h+) pairs results in more electrons participating in the continuous degradation reaction (Eq. 7). The electrons react with O2 to produce •O2– and •OH (Eq. 8 and Eq. 9) (Chen et al. 2022); these radicals, in turn, degrade the MG molecule.
Comparison of FVZ3 photocatalyst efficiency with literature
The FVZ3 composite was compared with some previously reported photocatalysts regarding initial MG concentration, photocatalyst dose, irradiation source, time, and degradation (%). From Table 3, it can be concluded that the current study provides a more efficient photocatalyst that can degrade high MG concentrations up to 100 ppm with a reasonable dose of 1 g/L under visible light irradiation. From an economic and energy-saving point of view, these valued data suggest that FVZ3 would be a promising photocatalyst for the photocatalytic degradation of dyes.
Conclusion
In this study, a novel ZnVFeO4 has been successfully fabricated at different pH by precipitation method. The enhanced photocatalytic degradation of MG dye as a model pollutant at neutral pH conditions under visible light irradiation has been investigated. The XRD and FTIR analyses confirmed the presence of Fe, Zn, and V in the ZnVFeO4 samples with crystalline size in the range of 30–65 nm. The optical properties indicate that all the prepared Fe-based photocatalysts absorbed effectively in the UV–Vis region and have a low bandgap. The calculated bandgap from DRS was in the range of 1.9–1.96 eV for ZnVFeO4 at different pH values. Compared to the FO sample, the low bandgap and the decreased photoluminescence intensity at around 488 nm of the FVZ3 accelerated the rate and photodegradation efficiency of MG dye under visible light irradiation. The photodegradation rate of MG dye by the prepared photocatalysts follows the order FVZ3 (12.7 × 10−3 min−1) > FVZ9 (11 × 10−3 min−1) > FVZ12 (9.5 × 10−3 min−1) > FZ (5.5 × 10−3 min−1) > FO (3.8 × 10−3 min−1). The effect of the catalyst dosage and the initial dye concentration on the photocatalytic performance were elucidated. The optimum catalyst dose is 1 g/L to attain a high degradation efficiency with a low cost. Furthermore, cycling experiments for the fabricated photocatalyst demonstrated remarkable stability and recyclability of FVZ3 with high photocatalytic efficiency (> 90%) even after five cycles of use under visible light irradiation. The dye degradation probable mechanism was driven by studying the process efficiency under the existence of the scavengers, in which the contribution of the active species follows the order •OH > •O2– > h+, confirming the primary role of •OH and •O2–. According to these findings, these photocatalysts have the potential to be employed without changing the pH for the cost-effective treatment of dye-contaminated wastewater when exposed to visible light.
Data availability
All obtained data during this work are included in this manuscript.
References
Ahmad M, Chen S, Ye F et al (2019) Efficient photo-Fenton activity in mesoporous MIL-100(Fe) decorated with ZnO nanosphere for pollutants degradation. Appl Catal B Environ 245:428–438. https://doi.org/10.1016/j.apcatb.2018.12.057
Aliabadi BG, Gilani N, Pasikhani JV, Pirbazari AE (2020) Boosting the photoconversion efficiency of TiO2 nanotubes using UV radiation-assisted anodization as a prospective method: an efficient photocatalyst for eliminating resistant organic pollutants. Ceram Int 46:19942–19951. https://doi.org/10.1016/j.ceramint.2020.05.061
Almeida TP, Fay M, Zhu Y, Brown PD (2009) Process map for the hydrothermal synthesis of r-Fe2O3 nanorods. J Phys Chem C 113:18689–18698. https://doi.org/10.1021/jp907081j
Alsulami QA, Rajeh A, Mannaa MA et al (2021) Preparation of highly efficient sunlight driven photodegradation of some organic pollutants and H2 evolution over rGO/FeVO4 nanocomposites. Int J Hydrogen Energy 46:27349–27363. https://doi.org/10.1016/j.ijhydene.2021.05.211
Amdeha E (2021) Recovery of nanomaterials from agricultural and industrial wastes for water treatment applications. In: Makhlouf ASH, Ali GAM (eds) Waste Recycling Technologies for Nanomaterials Manufacturing. Springer, Cham, pp 385–417
Amdeha E, Mohamed RS (2021) A green synthesized recyclable ZnO/MIL-101(Fe) for Rhodamine B dye removal via adsorption and photo-degradation under UV and visible light irradiation. Environ Technol (united Kingdom) 42:842–859. https://doi.org/10.1080/09593330.2019.1647290
Amdeha E, Mohamed RS, Dhmees AS (2021) Sonochemical assisted preparation of ZnS–ZnO/MCM-41 based on blast furnace slag and electric arc furnace dust for Cr (VI) photoreduction. Ceram Int 47:23014–23027. https://doi.org/10.1016/j.ceramint.2021.05.015
Arsalani N, Bazazi S, Abuali M, Jodeyri S (2020) A new method for preparing ZnO/CNT nanocomposites with enhanced photocatalytic degradation of malachite green under visible light. J Photochem Photobiol A Chem 389.https://doi.org/10.1016/j.jphotochem.2019.112207
Bafana A, Devi SS, Chakrabarti T (2011) Azo dyes: past, present and the future. Environ Rev 19:350–370. https://doi.org/10.1139/a11-018
Banerjee S, Pillai SC, Falaras P et al (2014) New insights into the mechanism of visible light photocatalysis. J Phys Chem Lett 5:2543–2554. https://doi.org/10.1021/jz501030x
Bassi A, Hasan I, Qanungo K et al (2022) Visible light assisted mineralization of malachite green dye by green synthesized xanthan gum/agar@ZnO bionanocomposite. J Mol Struct 1256:132518. https://doi.org/10.1016/j.molstruc.2022.132518
Bhushan B, Jahan K, Verma V et al (2020) Photodegradation of methylene blue dye by powders of Ni–ZnO floweret consisting of petals of ZnO nanorod around Ni-rich core. Mater Chem Phys 253:123394. https://doi.org/10.1016/j.matchemphys.2020.123394
Cao A, Wang Z, Li H, Nørskov JK (2021) Relations between surface oxygen vacancies and activity of methanol formation from CO2 hydrogenation over In2O3 surfaces. ACS Catal 11:1780–1786. https://doi.org/10.1021/acscatal.0c05046
Chen X, Zhang M, Qin H et al (2022) Synergy effect between adsorption and heterogeneous photo-Fenton-like catalysis on LaFeO3/lignin-biochar composites for high efficiency degradation of ofloxacin under visible light. Sep Purif Technol 280:119751. https://doi.org/10.1016/j.seppur.2021.119751
Chiang LF, Doong RA (2015) Enhanced photocatalytic degradation of sulfamethoxazole by visible-light-sensitive TiO2 with low Cu addition. Sep Purif Technol 156:1003–1010. https://doi.org/10.1016/j.seppur.2015.10.011
De Gisi S, Lofrano G, Grassi M, Notarnicola M (2016) Characteristics and adsorption capacities of low-cost sorbents for wastewater treatment: a review. Sustain Mater Technol 9:10–40. https://doi.org/10.1016/j.susmat.2016.06.002
Deriase SF, El-Salamony RA, Amdeha E, Al-Sabagh AM (2021) Statistical optimization of photocatalytic degradation process of methylene blue dye by SnO–TiO2–AC composite using response surface methodology. Environ Prog Sustain Energy 40:e13639. https://doi.org/10.1002/ep.13639
Du Z, Li K, Zhou S et al (2020) Degradation of ofloxacin with heterogeneous photo-Fenton catalyzed by biogenic Fe-Mn oxides. Chem Eng J 380:122427. https://doi.org/10.1016/j.cej.2019.122427
Eghbali P, Hassani A, Sündü B, Metin Ö (2019) Strontium titanate nanocubes assembled on mesoporous graphitic carbon nitride (SrTiO3/mpg-C3N4): preparation, characterization and catalytic performance. J Mol Liq 290:111208. https://doi.org/10.1016/j.molliq.2019.111208
Elfadly AM, Badawi AM, Yehia FZ et al (2013) Selective nano alumina supported vanadium oxide catalysts for oxidative dehydrogenation of ethylbenzene to styrene using CO2 as soft oxidant. Egypt J Pet 22:373–380. https://doi.org/10.1016/j.ejpe.2013.10.007
El-Salamony RA, Amdeha E, Ghoneim SA et al (2017) Titania modified activated carbon prepared from sugarcane bagasse: adsorption and photocatalytic degradation of methylene blue under visible light irradiation. Environ Technol (united Kingdom) 38:3122–3136. https://doi.org/10.1080/21622515.2017.1290148
El-Salamony RA, Amdeha E, El Shafey AM, Al Sabagh AM (2021) Preparation and characterisation of Ce-doped SiO2 nano-materials as effective photo-catalyst under visible light. Int J Environ Anal Chem. https://doi.org/10.1080/03067319.2020.1865328
Ghanbari F, Ahmadi M, Gohari F (2019) Heterogeneous activation of peroxymonosulfate via nanocomposite CeO2-Fe3O4 for organic pollutants removal: the effect of UV and US irradiation and application for real wastewater. Sep Purif Technol 228:115732. https://doi.org/10.1016/j.seppur.2019.115732
Gupta NK, Ghaffari Y, Kim S et al (2020) Photocatalytic degradation of organic pollutants over MFe2O4 (M = Co, Ni, Cu, Zn) nanoparticles at neutral pH. Sci Rep 10:1–11. https://doi.org/10.1038/s41598-020-61930-2
Han C, Zhang N, Xu YJ (2016) Structural diversity of graphene materials and their multifarious roles in heterogeneous photocatalysis. Nano Today 11:351–372. https://doi.org/10.1016/j.nantod.2016.05.008
Hang J, Yi XH, Wang CC et al (2022) Heterogeneous photo-Fenton degradation toward sulfonamide matrix over magnetic Fe3S4 derived from MIL-100(Fe). J Hazard Mater 424:127415. https://doi.org/10.1016/j.jhazmat.2021.127415
Hassani A, Eghbali P, Ekicibil A, Metin Ö (2018) Monodisperse cobalt ferrite nanoparticles assembled on mesoporous graphitic carbon nitride (CoFe2O4/mpg-C3N4): a magnetically recoverable nanocomposite for the photocatalytic degradation of organic dyes. J Magn Magn Mater 456:400–412. https://doi.org/10.1016/j.jmmm.2018.02.067
Hassani A, Faraji M, Eghbali P (2020) Facile fabrication of mpg-C3N4/Ag/ZnO nanowires/Zn photocatalyst plates for photodegradation of dye pollutant. J Photochem Photobiol A Chem 400:112665. https://doi.org/10.1016/j.jphotochem.2020.112665
Hassani A, Krishnan S, Scaria J et al (2021) Z-scheme photocatalysts for visible-light-driven pollutants degradation: a review on recent advancements. Curr Opin Solid State Mater Sci 25:100941. https://doi.org/10.1016/j.cossms.2021.100941
Hua J, Gengsheng J (2009) Hydrothermal synthesis and characterization of monodisperse α-Fe2O3 nanoparticles. Mater Lett 63:2725–2727. https://doi.org/10.1016/j.matlet.2009.09.054
Huang S, Hu B, Zhao S et al (2022) Multiple catalytic sites of Fe-Nx and Fe-N-C single atoms embedded N-doped carbon heterostructures for high-efficiency removal of malachite green. Chem Eng J 430:132933. https://doi.org/10.1016/j.cej.2021.132933
Jiang Y, Liu P, Tian S et al (2017) Sustainable visible-light-driven Z-scheme porous Zn3(VO4)2/g-C3N4 heterostructure toward highly photoredox pollutant and mechanism insight. J Taiwan Inst Chem Eng 78:517–529. https://doi.org/10.1016/j.jtice.2017.06.032
Kang S, Fang Y, Huang Y et al (2015) Critical influence of g-C3N4 self-assembly coating on the photocatalytic activity and stability of Ag/AgCl microspheres under visible light. Appl Catal B Environ 168–169:472–482. https://doi.org/10.1016/j.apcatb.2015.01.002
Kannan K, Radhika D, Sadasivuni KK et al (2020) Nanostructured metal oxides and its hybrids for photocatalytic and biomedical applications. Adv Colloid Interface Sci 281:102178. https://doi.org/10.1016/j.cis.2020.102178
Karadeniz D, Kahya N, Erim FB (2022) Effective photocatalytic degradation of malachite green dye by Fe(III)-cross-linked alginate-carboxymethyl cellulose composites. J Photochem Photobiol A Chem 428:113867. https://doi.org/10.1016/j.jphotochem.2022.113867
Kesavan G, Pichumani M, Chen SM (2021) Influence of crystalline, structural, and electrochemical properties of iron vanadate nanostructures on flutamide detection. ACS Appl Nano Mater 4:5883–5894. https://doi.org/10.1021/acsanm.1c00802
Lassoued A (2021) Synthesis and characterization of Zn-doped α-Fe2O3 nanoparticles with enhanced photocatalytic activities. J Mol Struct 1239:130489. https://doi.org/10.1016/j.molstruc.2021.130489
Li X, Hou Y, Zhao Q, Chen G (2011) Synthesis and photoinduced charge-transfer properties of a ZnFe2O4-sensitized TiO2 nanotube array electrode. Langmuir 27:3113–3120. https://doi.org/10.1021/la2000975
Li L, Lai C, Huang F et al (2019) Degradation of naphthalene with magnetic bio-char activate hydrogen peroxide: synergism of bio-char and Fe–Mn binary oxides. Water Res 160:238–248. https://doi.org/10.1016/j.watres.2019.05.081
Liu Y, Wang X, Sun Q et al (2022) Enhanced visible light photo-Fenton-like degradation of tetracyclines by expanded perlite supported FeMo3Ox/g-C3N4 floating Z-scheme catalyst. J Hazard Mater 424:127387. https://doi.org/10.1016/j.jhazmat.2021.127387
Luque PA, Garrafa-Gálvez HE, Nava O et al (2021) Efficient sunlight and UV photocatalytic degradation of methyl orange, methylene blue and rhodamine B, using citrus×paradisi synthesized SnO2 semiconductor nanoparticles. Ceram Int 47:23861–23874. https://doi.org/10.1016/j.ceramint.2021.05.094
Madihi-Bidgoli S, Asadnezhad S, Yaghoot-Nezhad A, Hassani A (2021) Azurobine degradation using Fe2O3@multi-walled carbon nanotube activated peroxymonosulfate (PMS) under UVA-LED irradiation: performance, mechanism and environmental application. J Environ Chem Eng 9:106660. https://doi.org/10.1016/j.jece.2021.106660
Malibo PM, Makgwane PR, Baker PG (2020) Heterostructured redox-active V2O5/SnO2 oxide nanocatalyst for aqueous-phase oxidation of furfural to renewable maleic acid. ChemistrySelect 5:6255–6267. https://doi.org/10.1002/slct.201904852
Manchala S, Gandamalla A, Vempuluru NR et al (2021) High potential and robust ternary LaFeO3/CdS/carbon quantum dots nanocomposite for photocatalytic H2 evolution under sunlight illumination. J Colloid Interface Sci 583:255–266. https://doi.org/10.1016/j.jcis.2020.08.125
Mohanty L, Pattanayak DS, Dash SK (2021) An efficient ternary photocatalyst Ag/ZnO/g-C3N4 for degradation of RhB and MG under solar radiation. J Indian Chem Soc 98:100180. https://doi.org/10.1016/j.jics.2021.100180
Monsef R, Ghiyasiyan-Arani M, Amiri O, Salavati-Niasari M (2020) Sonochemical synthesis, characterization and application of PrVO4 nanostructures as an effective photocatalyst for discoloration of organic dye contaminants in wastewater. Ultrason Sonochem 61:104822. https://doi.org/10.1016/j.ultsonch.2019.104822
Moussavi G, Mahmoudi M (2009) Removal of azo and anthraquinone reactive dyes from industrial wastewaters using MgO nanoparticles. J Hazard Mater 168:806–812. https://doi.org/10.1016/j.jhazmat.2009.02.097
Nas MS, Calimli MH, Burhan H et al (2019) Synthesis, characterization, kinetics and adsorption properties of Pt-Co@GO nano-adsorbent for methylene blue removal in the aquatic mediums using ultrasonic process systems. J Mol Liq 296:112100. https://doi.org/10.1016/j.molliq.2019.112100
Natarajan TS, Thampi KR, Tayade RJ (2018) Visible light driven redox-mediator-free dual semiconductor photocatalytic systems for pollutant degradation and the ambiguity in applying Z-scheme concept. Appl Catal B Environ 227:296–311. https://doi.org/10.1016/j.apcatb.2018.01.015
Nguyen TB, Doong RA (2016) Fabrication of highly visible-light-responsive ZnFe2O4/TiO2 heterostructures for the enhanced photocatalytic degradation of organic dyes. RSC Adv 6:103428–103437. https://doi.org/10.1039/c6ra21002c
Nkosi SS, Kortidis I, Motaung DE et al (2014) An instant photo-excited electrons relaxation on the photo-degradation properties of TiO2-x films. J Photochem Photobiol A Chem 293:72–80. https://doi.org/10.1016/j.jphotochem.2014.07.012
Ovodok E, Maltanava H, Poznyak S et al (2018) Rhodamine-loaded TiO2 particles for detection of polymer coating UV degradation. Mater Today Proc 20:320–328. https://doi.org/10.1016/j.matpr.2019.10.069
Paździor K, Bilińska L, Ledakowicz S (2019) A review of the existing and emerging technologies in the combination of AOPs and biological processes in industrial textile wastewater treatment. Chem Eng J 376:120597. https://doi.org/10.1016/j.cej.2018.12.057
Pitchaimuthu S, Rajalakshmi S, Kannan N, Velusamy P (2014) Corrigendum to enhanced photocatalytic activity of titanium dioxide by β-cyclodextrin in decoloration of Acid Yellow 99 dye (https://doi.org/10.1080/19443994.2013.799049). Desalin Water Treat 52:. https://doi.org/10.1080/19443994.2013.813620
Rahimpour R, Chaibakhsh N, Zanjanchi MA, Moradi-Shoeili Z (2020) Fabrication of ZnO/FeVO4 heterojunction nanocomposite with high catalytic activity in photo-Fenton-like process. J Alloys Compd 817:152702. https://doi.org/10.1016/j.jallcom.2019.152702
Saad AM, Abukhadra MR, Abdel-Kader Ahmed S et al (2020) Photocatalytic degradation of malachite green dye using chitosan supported ZnO and Ce–ZnO nano-flowers under visible light. J Environ Manage 258:110043. https://doi.org/10.1016/j.jenvman.2019.110043
Sajid MM, Khan SB, Shad NA et al (2018) Visible light assisted photocatalytic degradation of crystal violet dye and electrochemical detection of ascorbic acid using a BiVO4/FeVO4 heterojunction composite. RSC Adv 8:23489–23498. https://doi.org/10.1039/c8ra03890b
Sajid MM, Zhai H, Shad NA et al (2021) Photocatalytic performance of ferric vanadate (FeVO4) nanoparticles synthesized by hydrothermal method. Mater Sci Semicond Process 129:105785. https://doi.org/10.1016/j.mssp.2021.105785
Saravanakumar B, Karthikeyan N, Periasamy PA et al (2020) Polyethylene glycol mediated synthesis of iron vanadate (FeVO4) nanoparticles with supercapacitive features. Mater Res Express 7:064010. https://doi.org/10.1088/2053-1591/ab997f
Sekar A, Yadav R (2021) Green fabrication of zinc oxide supported carbon dots for visible light-responsive photocatalytic decolourization of malachite green dye: optimization and kinetic studies. Optik (Stuttg) 242.https://doi.org/10.1016/j.ijleo.2021.167311
Senthil RA, Osman S, Pan J et al (2020) One-pot preparation of AgBr/α-Ag2WO4 composite with superior photocatalytic activity under visible-light irradiation. Colloids Surfaces A Physicochem Eng Asp 586:124079. https://doi.org/10.1016/j.colsurfa.2019.124079
Shafiq I, Hussain M, Rashid R et al (2021) Development of hierarchically porous LaVO4 for efficient visible-light-driven photocatalytic desulfurization of diesel. Chem Eng J 420:130529. https://doi.org/10.1016/j.cej.2021.130529
Shandilya P, Mittal D, Sudhaik A et al (2019) GdVO4 modified fluorine doped graphene nanosheets as dispersed photocatalyst for mitigation of phenolic compounds in aqueous environment and bacterial disinfection. Sep Purif Technol 210:804–816. https://doi.org/10.1016/j.seppur.2018.08.077
Sharma S, Mittal A, Singh Chauhan N et al (2021) Developments in visible-light active TiO2/SnX (X = S and Se) and their environmental photocatalytic applications – a mini-review. Inorg Chem Commun 133:108874. https://doi.org/10.1016/j.inoche.2021.108874
Sharma S, Kumar N, Makgwane PR et al (2022) TiO2/SnO2 nano-composite: new insights in synthetic, structural, optical and photocatalytic aspects. Inorganica Chim Acta 529:120640. https://doi.org/10.1016/j.ica.2021.120640
Sheydaei M, Karimi M, Vatanpour V (2019) Continuous flow photoelectrocatalysis/reverse osmosis hybrid reactor for degradation of a pesticide using nano N-TiO2/Ag/Ti electrode under visible light. J Photochem Photobiol A Chem 384:112068. https://doi.org/10.1016/j.jphotochem.2019.112068
Thaba KP, Mphahlele-Makgwane MM, Kyesmen PI et al (2022) Composition-dependent structure evolution of FeVO4 nano-oxide and its visible-light photocatalytic activity for degradation of methylene blue. Colloids Surfaces A Physicochem Eng Asp 633:127856. https://doi.org/10.1016/j.colsurfa.2021.127856
Thein MT, Pung SY, Aziz A, Itoh M (2016) Effect of Ni coupling on the photoluminescence property and photocatalytic activity of ZnO nanorods. J Taiwan Inst Chem Eng 61:156–165. https://doi.org/10.1016/j.jtice.2015.11.024
Wang J, Tang J (2021) Fe-based Fenton-like catalysts for water treatment: catalytic mechanisms and applications. J Mol Liq 332:115755. https://doi.org/10.1016/j.molliq.2021.115755
Wang M, Hu X, Zhan Z et al (2019) Facile fabrication of CeVO4 hierarchical hollow microspheres with enhanced photocatalytic activity. Mater Lett 253:259–262. https://doi.org/10.1016/j.matlet.2019.06.081
Wang S, Chen Z, Zhao Y et al (2021) High photocatalytic activity over starfish-like La-doped ZnO/SiO2 photocatalyst for malachite green degradation under visible light. J Rare Earths 39:772–780. https://doi.org/10.1016/j.jre.2020.04.009
Wetchakun N, Wanwaen P, Phanichphant S, Wetchakun K (2017) Influence of Cu doping on the visible-light-induced photocatalytic activity of InVO4. RSC Adv 7:13911–13918. https://doi.org/10.1039/c6ra27138c
Xu L, Wang J (2011) A heterogeneous Fenton-like system with nanoparticulate zero-valent iron for removal of 4-chloro-3-methyl phenol. J Hazard Mater 186:256–264. https://doi.org/10.1016/j.jhazmat.2010.10.116
Yadav S, Kumar N, Kumari V et al (2019) Photocatalytic degradation of Triclopyr, a persistent pesticide by ZnO/SnO2 nano-composities. Mater Today Proc 19:642–645. https://doi.org/10.1016/j.matpr.2019.07.746
Yu C, Yang P, Tie L et al (2018) One-pot fabrication of β-Bi2O3@Bi2S3 hierarchical hollow spheres with advanced sunlight photocatalytic RhB oxidation and Cr(VI) reduction activities. Appl Surf Sci 455:8–17. https://doi.org/10.1016/j.apsusc.2018.04.201
Yu Y, Huang F, He Y et al (2019) Heterogeneous fenton-like degradation of ofloxacin over sludge derived carbon as catalysts: mechanism and performance. Sci Total Environ 654:942–947. https://doi.org/10.1016/j.scitotenv.2018.11.156
Yulizar Y, Apriandanu DOB, Ashna RI (2020) La2CuO4-decorated ZnO nanoparticles with improved photocatalytic activity for malachite green degradation. Chem Phys Lett 755:137749. https://doi.org/10.1016/j.cplett.2020.137749
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Author information
Authors and Affiliations
Contributions
Eman M. Mostafa: conceptualization, methodology, validation, synthesis, characterization, data interpretation, writing—original draft, editing.
Enas Amdeha: conceptualization, methodology, investigation, characterization, photocatalytic application, data curation and interpretation, writing—original draft, editing and reviewing.
Corresponding author
Ethics declarations
Ethics approval
The manuscript is prepared in compliance with the Publishing Ethics Policy.
Consent to participate
Not applicable.
Consent for publication
Not applicable.
Competing interests
The authors declare no competing interests.
Additional information
Responsible Editor: Sami Rtimi
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mostafa, E.M., Amdeha, E. Enhanced photocatalytic degradation of malachite green dye by highly stable visible-light-responsive Fe-based tri-composite photocatalysts. Environ Sci Pollut Res 29, 69861–69874 (2022). https://doi.org/10.1007/s11356-022-20745-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11356-022-20745-6