Effect of Varying Test Parameters on Elastic–plastic Properties Extracted by Nanoindentation Tests

  • Published:
Experimental Mechanics Aims and scope Submit manuscript

Abstract

A systematic experiment was performed in an effort to investigate how the levels of certain test parameters affect the values of elastic modulus, hardness, yield stress, and strain hardening constant obtained using nanoindentation test. Maximum applied load, loading (unloading) rate, and hold time at maximum load were varied at three levels. The effects of these testing parameters were investigated through a three-level, full factorial design of experiment. The experiments were conducted on ultrafine Al-Mg specimens that were mechanically extruded. Both longitudinal and transverse extrusion directions were examined to investigate effects of anisotropy on mechanical properties and evaluate the persistence of observed variations due to test parameters on different materials orientations. An indentation size effect (ISE) was observed demonstrating that maximum load—and thereby maximum indentation depth—can have a significant effect on values of hardness and elastic modulus. Hardness values decreased with higher loading rates, and higher rates of unloading resulted in higher values of elastic modulus (5–10 GPa increases). Strain-hardening exponent showed a decreasing trend with increasing loading rate while yield stress exhibited a consistent correlation to hardness across all studied parameters. The material exhibited very little creep during the hold period, and values of the calculated properties were not significantly altered by varying the length of the hold time. Anisotropy effect was observed, particularly in the values of yield strength. This is attributed to the preferred grain orientation due to extrusion.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11

Similar content being viewed by others

References

  1. Fischer-Cripps, Anthony C (2002) Nanoindentation. Springer-Verlag New York, Inc., New York

    Book  Google Scholar 

  2. Doerner MF, Nix WD (1986) A method for interpreting the data from depth-sensing instruments. J Mater Res 1:601–609

    Article  Google Scholar 

  3. Oliver WC, Pharr GM (1992) An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J Mater Res 7:1564–1583

    Article  Google Scholar 

  4. Dao M, Chollacoop N, Van Vliet KJ, Venkatesh TA, Suresh A (2001) Computational modeling of the forward and reverse problems in instrumented sharp indentation. Acta Mater 49:3899–3918

    Article  Google Scholar 

  5. Huang Y, Liu X, Zhou Y, Ma Z, Lu C (2011) Mathematical analysis on the uniqueness of reverse algorithm for measuring elastic–plastic properties by sharp indentation. J Mater Sci Technol 27:577–584

    Article  Google Scholar 

  6. Ogasawara N, Chiba N, Chen X (2006) Measuring the plastic properties of bulk materials by single indentation test. Scr Mater 54:65–70

    Article  Google Scholar 

  7. Das CR, Dhara S, Jeng Y, Tsai C, Hsu HC, Raj B, Bhaduri AK, Albert SK, Tyagi AK, Chen LC, Chen KH (2010) Direct observation of amophization in load rate dependent nanoindentation studies of crystalline Si. Appl Phys Lett 96:253113

    Article  Google Scholar 

  8. Wu Z, Baker TA, Ovaert TC, Niebur GL (2011) The effect of holding time on nanoindentation measurements of creep in bone. J Biomech 44:1066–1072

    Article  Google Scholar 

  9. Chudoba T, Richter F (2001) Investigation of creep behavior under load during indentation experiments and its influence on hardness and modulus results. Surf Coat Technol 148:191–198

    Article  Google Scholar 

  10. Goodall R, Clyne TW (2006) A critical appraisal of the extraction of creep parameters from nanoindentation data obtained at room temperature. Acta Mater 54:5489–5499

    Article  Google Scholar 

  11. Nohava J, Randall NX, Conté N (2009) Novel ultra nanoindentation method with extremely low thermal drift: principle and experimental results. J Mater Res 24:873–882

    Article  Google Scholar 

  12. Mayo MJ, Siegel RW, Narayanasamy A, Nix WD (1990) Mechanical properties of nanophase TiO2 as determined by nanoindentation. J Mater Res 5:1073–1082

    Article  Google Scholar 

  13. Burgess T, Laws KJ, Ferry M (2008) Effect of loading rate on the serrated flow of bulk metallic glass during nanoindentation. Acta Mater 56:4829–4835

    Article  Google Scholar 

  14. Amini A, He Y, Sun Q (2011) Loading rate dependency of maximum nanoindentation in nano-grained NiTi shape memory alloy. Mater Lett 65:464–466

    Article  Google Scholar 

  15. Nix WD, Gao H (1998) Indentation size effects in crystalline materials: a law for strain gradient plasticity. J Mech Phys Solids 46:411–425

    Article  MATH  Google Scholar 

  16. Mayo MJ, Nix WD (1988) A micro-indentation study of superplasticity in Pb, Sn, and Sn-38 wt% Pb. Acta Metall 36:2183–2192

    Article  Google Scholar 

  17. Maier V, Durst K, Mueller J, Backes B, Höppel HW, Göken M (2011) Nanoindentation strain-rate jump tests for determining the local strain-rate sensitivity in nanocrystalline Ni and ultrafine-grained Al. J Mater Res 26:1421–1430

    Article  Google Scholar 

  18. Harvey E, Ladani L, and Weaver M (2012) “Complete Mechanical Characterization of Nanocrystalline Al-Mg Alloy Using Nanoindentation,” Mech Mater 52:1–11. doi:10.1016/j.mechmat.2012.04.005

  19. Manika I, Maniks J (2006) Size effects in micro- and nanoscale indentation. Acta Mater 56:2049–2056

    Article  Google Scholar 

  20. Zong Z, Lou J, Adewoye OO, Elmustafa AA, Hammad F, Soboyejo WO (2006) Indentation size effects in the nano- and micro-hardness of FCC single crystal metals. Mater Sci Eng, A 434:178–187

    Article  Google Scholar 

  21. Elmustafa AA, Eastman JA, Rittner MN, Weertman JR, Stone DS (2000) Indentation size effect: large grained aluminum versus nanocrystalline aluminum-zirconium alloys. Scr Mater 43:951–955

    Article  Google Scholar 

  22. Durst K, Bakes B, Goken M (2005) Indentation size effect in metallic materials: correcting for the size of the plastic zone. Scr Mater 52:1093–1097

    Article  Google Scholar 

  23. Han L, Hu H, Northwood DO, and Li N (2008) “Microstructure and nanoscale mechanical behavior of Mg-Al and Mg-Al-Ca Alloys” Mater Sci Eng A 473: 16–27

    Google Scholar 

  24. Li J, Li F, Xue F, Cai J, and Chen B (2012) “Micromechanical behavior study of forged 7050 aluminum alloy by microindentation” Mater Des 37: 491–499

    Google Scholar 

  25. Xue F, Li F, Cai J, Yuan Z, Chen B, Liu T (2012) Characterization of the elasto-plastic properties of 0Cr12Mn5Ni4Mo3Al steel by microindentation. Sustain Mater Des Appl 36:81–87

    Google Scholar 

  26. Bolshakov A and Pharr G (1998) “Influences of pileup on the measurement of mechanical properties by load and depth sensing indentation techniques”, J Mater Res 13(4): 1049–1058

    Google Scholar 

  27. Giannakopoulos A and Suresh S (1999) “Determination Of elastoplastic properties by instrumented sharp indentation” Scr Mater 40(10): 1191–1198

    Google Scholar 

  28. Tabor D (1951) The hardness of metals. Oxford University Press Inc., New York

    Google Scholar 

  29. Ahn B, Mitra R, Lavernia EJ, Nutt SR (2010) Effect of grain size on strain rate sensitivity of cryomilled Al-Mg alloy. J Mater Sci 45:4790–4795

    Article  Google Scholar 

  30. Ahn B, Mitra R, Hodge AM, Lavernia EJ, Nutt SR (2008) Strain rate sensitivity studies of cryomilled Al alloy performed by nanoindentation. Mater Sci Forum 584–586:221–226

    Article  Google Scholar 

  31. Vlassak JJ, Nix WD (1993) “Indentation modulus of elastically anisotropic half spaces,” Phil Mag A 67:1045–1056

    Google Scholar 

  32. Vlassak JJ, Nix WD (1994) “Measuring the elastic properties of anisotropic materials by means of indentation experiments. J Mech Phys Solids 42:1223

    Article  Google Scholar 

  33. Han B, Lee Z, Witkin D, Nutt S, and Lavernia E (2005) “Deformation Behavior of Bimodal Nanostructured 5083 Al Alloys” Metall Mater Trans A 36: 957

    Google Scholar 

  34. Joshi S, Ramesh K, Han B and Lavernia E (2006) “Modeling the Constitutive Response of Bimodal Metals”, Metall Mater Trans A 37: 2397–2404

  35. Magee A, Ladani L, Topping T and Lavernia E (2012) “Effects of tensile test parameters on the mechanical properties of a bimodal Al–Mg alloy,” Acta Mater 60: 5838–5849

    Google Scholar 

  36. Fjeldly A, Roven HJ (1996) Observation and calculation of mechanical anisotropy and plastic flow of AlMgZn extrusion. Acta Mater 44(9):3497–3504

    Article  Google Scholar 

Download references

Acknowledgments

The authors would like to acknowledge the National Science Foundation for support of this research. This material is based upon work supported by the National Science Foundation under Grant No. 1053434. This work used resources in the Center for Materials for Information Technology which is supported by The University of Alabama.

Author information

Authors and Affiliations

  1. Department of Mechanical Engineering, University of Alabama, Tuscaloosa, AL, 35487, USA

    L. Ladani, E. Harvey & S. F. Choudhury

  2. Department of Mechanical and Aerospace Engineering, University of Florida, Gainesville, FL, 32611, USA

    C. R. Taylor

Authors
  1. L. Ladani
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. E. Harvey
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. S. F. Choudhury
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. C. R. Taylor
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to L. Ladani.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Ladani, L., Harvey, E., Choudhury, S.F. et al. Effect of Varying Test Parameters on Elastic–plastic Properties Extracted by Nanoindentation Tests. Exp Mech 53, 1299–1309 (2013). https://doi.org/10.1007/s11340-013-9732-7

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11340-013-9732-7

Keywords

Search

Navigation