Intralaboratory Repeatability of Residual Stress Determined by the Slitting Method

  • Published:
Experimental Mechanics Aims and scope Submit manuscript

Abstract

This paper presents repeated slitting method measurements of the residual stress versus depth profile through the thickness of identically prepared samples, which were made to assess repeatability of the method. Measurements were made in five 17.8 mm thick blocks cut from a single plate of 316L stainless steel which had been uniformly laser peened to induce a deep residual stress field. Typical slitting method techniques were employed with a single metallic foil strain gage on the back face of the coupon and incremental cutting by wire EDM. Measured residual stress profiles were analyzed to assess variability of residual stress as a function of depth from the surface. The average depth profile had a maximum magnitude of −668 MPa at the peened surface. The maximum variability also occurred at the surface and had a standard deviation of 15 MPa and an absolute maximum deviation of 26 MPa. Since measured residual stress exceeded yield strength of the untreated plate, microhardness versus depth profiling and elastic–plastic finite element analysis were combined to bound measurement error from inelastic deformation.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7

Similar content being viewed by others

References

  1. Rankin JE, Hill MR, Hackel LA (2003) The effects of process variations on residual stress in laser peened 7049 T73 aluminum alloy. Mater Sci Eng A 349(1–2):279–291.

    Google Scholar 

  2. Dewald AT, Rankin JE, Hill MR, Lee MJ, Chen H-L (2004) Assessment of tensile residual stress mititagion in alloy 22 welds due to laser peening. J Eng Mater Technol 126(4):465–473.

    Article  Google Scholar 

  3. Cheng W, Finnie I, Vardar O (1991) Measurement of residual stresses near the surface using the crack compliance method. J Eng Mater Technol 113(2):199–204.

    Google Scholar 

  4. Cheng W, Finnie I (1985) A method for measurement of axisymmetric axial residual stress in circumferentially welded thin walled cylinders. J Eng Mater Technol 107(3):181–185.

    Article  Google Scholar 

  5. Vaidyanathan S, Finnie I (1971) Determination of residual stress from stress intensity factor measurements. J Basic Eng 93:242–246.

    Google Scholar 

  6. Finnie I, Cheng W (1996) Residual stress measurement by the introduction of slots or cracks. Localized Damage IV Computer Aided Assessment and Control of Localized Damage—Proceedings of the International Conference 1996. Computational Mechanics Inc, Billerica, MA, USA., pp 37–51.

  7. Finnie I, Cheng W (2002) A summary of past contributions on residual stresses. Mater Sci Forum 404–407:509–514.

    Google Scholar 

  8. Prime M (1999) Residual stress measurement by successive extension of a slot: the crack compliance method. Appl Mech Rev 52(2):75–96.

    Google Scholar 

  9. Aydiner CC, Ustundag E, Prime MB, Peker A (2003) Modeling and measurement of residual stresses in a bulk metallic glass plate. J Non-Cryst Solids 316(1):82–95.

    Article  Google Scholar 

  10. Midha PS, Modlen GF (1976) Residual stress relief in cold-extruded rod. Met Technol 3(11):529–533.

    Google Scholar 

  11. Cook CS (1987) Straightening operations and residual stresses in tubing. 10th ASM Conference on Advances in the Production of Tubes, Bars, and Shapes, Orlando, FL, pp 61–68.

  12. Rankin JE, Hill MR (2003) Measurement of thickness-average residual stress near the edge of a thin laser peened strip. J Eng Mater Technol 125(3):283–293.

    Article  Google Scholar 

  13. Prime MB, Hill MR (2002) Residual stress, stress relief, and inhomogeneity in aluminum plate. Scripta Mater 46(1):77–82.

    Article  Google Scholar 

  14. Prime MB, Prantil VC, Rangaswamy P, Garcia FP (2000) Residual stress measurement and prediction in a hardened steel ring. Mater Sci Forum 347:223–228.

    Article  Google Scholar 

  15. Nowell D, Tochilin S, Hills DA (2000) Measurement of residual stresses in beams and plates using the crack compliance technique. J Strain Anal Eng Des 35(4):277–285.

    Article  Google Scholar 

  16. Hill MR, Lin WY (2002) Residual stress measurement in a ceramic–metallic graded material. J Eng Mater Technol 124(2):185–191.

    Article  Google Scholar 

  17. DeWald AT, Rankin JE, Hill MR, Schaffers KI (2004) An improved cutting plan for removing laser amplifier slabs from Yb:S-FAP single crystals using residual stress measurement and finite element modeling. J Cryst Growth 265(3–4):627–641.

    Article  Google Scholar 

  18. Dane CB, Hackel LA, Daly J, Harrisson J (1998) Laser peening of metals—enabling laser technology. High-Pressure Materials Research. Mater Res Soc Symp Proc 499:73–85.

    Google Scholar 

  19. Hammersley G (1999) Lasershot peening comes out of the lab. Mater World 7(5):281–282.

    Google Scholar 

  20. Hackel L (2003) Laser peening and laser peenforming: new tools for inducing surface stress. Light Met Age 61:30–31 (11–12 December).

    Google Scholar 

  21. Peyre P, Scherpereel X, Berthe L, Carboni C, Fabbro R, Beranger G, Lemaitre C (2000) Surface modifications induced in 316L steel by laser peening and shot-peening. Influence on pitting corrosion resistance. Mater Sci Eng A 280(2):294–302.

    Article  Google Scholar 

  22. Peyre P, Fabbro R, Merrien P, Lieurade HP (1996) Laser shock processing of aluminium alloys—application to high cycle fatigue behaviour. Mater Sci Eng A 210(1–2):102–113.

    Google Scholar 

  23. Dane CB, Zapata LE, Neuman WA, Norton MA, Hackel LA (1995) Design and operation of a 150 W near diffraction-limited laser amplifier with SBS wavefront correction. IEEE J Quantum Electron 31(1):148–163.

    Article  Google Scholar 

  24. Lee MJ, Hill MR (2005) Effect of strain gage length when determining residual stress by slitting. Accepted for publication in J. Eng. Mater. Technol., July 2006.

  25. Bevington PR, Robinson DK (1992) Data reduction and error analysis for the physical sciences, 2nd edn. McGraw-Hill, Inc, New York.

    Google Scholar 

  26. Taylor JR (1982) An introduction to error analysis: the study of uncertainties in physical measurements, 1st edn. University Science Books, Mill Valley, CA, pp 142–145.

    MATH  Google Scholar 

  27. Yakimets I, Richard C, Beranger G, Peyre P (2004) Laser peening processing effect on mechanical and tribological properties of rolling steel 100Cr6. Wear 256(3–4):311–320.

    Article  Google Scholar 

  28. Nobre JP, Dias AM, Kornmeier M (2004) An empirical methodology to estimate a local yield stress in work-hardened surface layers. Exp Mech 44(1):76–84.

    Google Scholar 

  29. Kirk MT, Wang Y-Y (1995) Wide range CTOD estimation formulae for SE(B) specimens. ASTM Special Technical Publication (no. 1256), Conshohocken, PA, USA, pp 126–141.

    Google Scholar 

  30. ABAQUS, version 6, Hibbitt, Karlsson, and Sorensen, Inc, Pawtucket, RI, 2003.

Download references

Author information

Authors and Affiliations

  1. Mechanical and Aeronautical Engineering, MAE Department, University of California, One Shields Avenue, Davis, CA, 95616, USA

    M. J. Lee & M. R. Hill (SEM member)

Authors
  1. M. J. Lee
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. M. R. Hill
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to M. R. Hill.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Lee, M.J., Hill, M.R. Intralaboratory Repeatability of Residual Stress Determined by the Slitting Method. Exp Mech 47, 745–752 (2007). https://doi.org/10.1007/s11340-007-9085-1

Download citation

  • Received:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11340-007-9085-1

Keywords

Search

Navigation