Stress-induced and thermal-induced martensitic transformations (MTs) in compression were investigated in [001]-oriented Ti–50.6 at.% Ni single crystals aged at 573 K for 1.5 h, containing Ti3Ni4 particles. No staging associated with stress-induced B2-R MT is detected. The change in the sequence of stress-induced MT from R–B19' to B2–B19' is accompanied by a change in the slope of the stress-temperature dependence from 3 MPa/K in the first stage to 7.5 MPa/K in the second stage. During stress-induced R–B19' MT, thermal and stress hysteresis significantly decrease with an increase in the applied stress and test temperature. At the stressinduced B2–B19' MT, hysteresis is independent of the stress and temperature.
Similar content being viewed by others
References
P. Wollants, J. R. Roos, and L. Delaey, Prog. Mater. Sci., 37, 227−288 (1993).
Y. I. Chumlyakov, I. V. Kireeva, E. Y. Panchenko, et al., in: High-Strength Single Crystals, in: Shape Memory Alloys: Properties, Technologies, Opportunities, N. Resnina and V. Rubanik, eds., Trans Tech Publications Ltd, Switzerland (2015), pp. 108–174.
I. Kaya, H. E. Karaca, M. Souri, et al., Mater. Sci. Eng., 686, 73–81 (2017).
S. Miyazaki and K. Otsuka, Metall. Trans. A, 17, 53−63 (1986).
J. I. Kim and S. Miyazaki, Acta Mater., 53, 4545–4554 (2005).
R. F. Hamilton, H. Sehitoglu, Y. Chumlyakov, and H. J. Maier, Acta Mater., 52 3383–3402 (2004).
S. Miyazaki and C. M. Wayman, Acta Metall., 36, 181−192 (1998).
S. Miyazaki, S. Kimura, and K. Otsuka, Philos. Mag. A, 57, 467−478 (1988).
J. I. Kim, Y. Liu, and S. Miyazaki, Acta Mater., 52, 487–499 (2004).
A. L. Roytburd and Ju. Slusker, Scripta Metall. Mater., 32, 761–766 (1995).
P. Sittner, M. Landa, P. Lukas, and V. Novak, Mech. Mater., 38, 475–492 (2006).
I. V. Kireeva, C. Picornell, J. Pons, et al., Acta Mater., 68, 127–139 (2014).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Izvestiya Vysshikh Uchebnykh Zavedenii, Fizika, No. 12, pp. 78–82, December, 2018.
Rights and permissions
About this article
Cite this article
Timofeeva, Е.Е., Panchenko, E.Y., Surikov, N.Y. et al. Special Features of Thermal and Stress Hysteresis of B2–R–B19' Martensitic Transformations in Aged [001]-Oriented Ti–50.6 at.% Ni Single Crystals. Russ Phys J 61, 2231–2235 (2019). https://doi.org/10.1007/s11182-019-01660-9
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11182-019-01660-9