Abstract
V0.13Mo0.87O2.935 powder was obtained by reducing acidified vanadate and molybdate solution at 60 °C by passing hydrogen sulfide gas through the solution. The obtained multicomponent mixed oxide was used as an anode material for the first time in the literature and tested in the solid oxide fuel cell for the temperatures of 700, 750, and 800 °C and the values of 0.38 ± 0.06 A/cm2 and 0.18 ± 0.03 W were respectively obtained as current density and power at 800 °C in the cell.
Similar content being viewed by others
References
A.H. Adams, F. Haaß, T. Buhrmester, J. Kunert, J. Ott, H. Vogel, H. Fuess, J. Mol. Catal. A 216(1), 67–74 (2004)
O. Mougin, J.L. Dubois, F. Mathieu, A. Rousset, J. Solid State Chem. 152(2), 353–360 (2000)
A. Chandra, A.J. Roberts, R.C.T. Slade, Solid State Commun. 147(3–4), 83–87 (2008)
M.M. Lin, Appl. Catal. A 250(2), 287–303 (2003)
T.P. Feist, P.K. Davies, Chem. Mater. 3, 1011–1012 (1991)
M. Schur, B. Berns, A. Dassenoy, I. Kassatkine, J. Urban, H. Wilmes, O. Hinrichsen, M. Muhler, R. Schlögl, Angew. Chem. Int. Ed. 42, 3815 (2003)
L. Espinal, K.A. Malinger, A.E. Espinal, A.M. Gaffney, S.L. Suib, Adv. Funct. Mater. 17(14), 2572–2579 (2007)
V. Lochař, H. Drobná, Appl. Catal. A 269(1–2), 27–31 (2004)
Y.H. Taufiq-Yap, K.C. Waug, Chem. Eng. Sci. 56, 5787–5792 (2001)
J. Tichỳ, Appl. Catal. A 157, 363–385 (1997)
C. Imawan, H. Steffes, F. Solzbacher, E. Obermeier, Sens. Actuators 77, 346–351 (2001)
X.K. Hu, D.K. Ma, J.B. Liang, Q. Xie, Y.C. Zhu, Y.T. Qian, J. Phys. Chem. C 111, 5882–5885 (2007)
Y.T. Hu, P.K. Davies, J. Solid State Chem. 105, 489–503 (1993)
L. Dupont, D. Larcher, M. Touboul, J. Solid State Chem. 143, 41–51 (1999)
M.M. Lin, Appl. Catal. A 250, 287–303 (2003)
H. Watanabe, Y. Koyasu, Appl. Catal. A 194–195, 479–485 (2000)
Acknowledgments
The author would like to thank the researchers at HYTEM laboratory of Mechanical Engineering Department at Niğde University for their assistance and scientific contribution. This work is financially supported by Scientific Research Foundation of Yıldız Technical University.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Beyribey, B. A new way of synthesis of V0.13Mo0.87O2.935 and an investigation on its structural, thermal, and anodic properties. Res Chem Intermed 39, 1183–1189 (2013). https://doi.org/10.1007/s11164-012-0676-9
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11164-012-0676-9