Electron microscopy and thermomechanical analysis are used to study how introducing nanodispersed ZrO2 powder stabilized with Y2O3 into a zircon-based composite affects the production and properties of the composite. It was established that the introduction of more than 1 mass %of nanodispersed ZrO2 slows the consolidation of the zircon matrix during sintering. Sintering a zircon-based composite with 15 mass % ZrO2 by the regime that was developed in the study makes it possible to reduce the porosity of the material and significantly increase its ultimate compressive strength. It was also determined that nanodispersed particles of ZrO2 react with SiO2 formed during thermal dissociation of the zircon to form zircon of nonstoichiometric composition.
Similar content being viewed by others
References
V. L. Balkevich, Ceramics Engineering [in Russian], Izd-vo Lit. Stroit., Moscow (1968).
A. Kaiser, M. Lobert, and R. Telle, “Thermal stability of zircon (ZrSiO4),” J. Eur. Ceram. Soc., 28, No. 11, 2199 – 2211 (2008).
V. N. Antsiferov, V. B. Kul’met’eva, S. E. Porozova, et al., “Features of the thermal dissociation of zircon concentrates from different deposits,” Ogneupory i Tekh. Keram., No. 11 / 12, 56 – 59 (2008).
M. M. Sychev, Inorganic Adhesives [in Russian], 2nd edition, revised and expanded, Khimiya, Leningrad (1986).
V. B. Ku’met’eva, S. E. Porozova, E. S. Gnedina, et al., “Producing a composite material based on zircon concentrate and nanocrystalline zirconium dioxide,” Novye Ogneupory, No. 10, 33 – 37 (2009).
Author information
Authors and Affiliations
Additional information
Translated from Novye Ogneupory, No. 4, pp. 35 – 38, April 2011.
Rights and permissions
About this article
Cite this article
Antsiferov, V.N., Kul’met’eva, V.B., Porozova, S.E. et al. Effect of nanodispersed zirconium dioxide on the consolidation and properties of a zircon-based ceramic. Refract Ind Ceram 52, 151–154 (2011). https://doi.org/10.1007/s11148-011-9385-y
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11148-011-9385-y