NiAl Oxidation Reaction Processes Studied In Situ Using MEMS-Based Closed-Cell Gas Reaction Transmission Electron Microscopy

  • Original Paper
  • Published:
Oxidation of Metals Aims and scope Submit manuscript

Abstract

The nanoscale oxidation mechanisms and kinetics of a model β-NiAl system were investigated using in situ closed-cell gas reaction scanning transmission electron microscopy (STEM). Here, we directly visualize the dynamic structural and chemical changes that occur during high-temperature oxidation at a high spatial resolution of 50.3Ni–49.7Al (at.%) nanoparticles under static air conditions at 730 Torr with heating up to 750 °C at 5 °C/s. A MEMS-based gas cell system, with microfabricated heater devices and a gas delivery system, was used to reveal site-specific oxidation initiation sites. Through time-resolved annular dark-field STEM imaging, we tracked the nanoscale oxidation kinetics of Al2O3. After oxidation at 750 °C, nucleation of voids at the Ni/Al2O3 interface was observed along a NiAl grain boundary, followed by the formation of faceted NiO crystals. Small faceted cubic crystals of NiO were formed at the initial stage of oxidation at high PO2 due to the outward self-diffusion of Ni2+ ions, followed by the formation of a mixture of metastable and stable α-Al2O3 at the oxide/metal interface that is attributed to a PO2 decrease with oxidation time, which agreed with thermodynamic modeling calculations. The results from these in situ oxidation experiments in the β-NiAl system are in agreement with the established oxidation mechanisms; however, with in situ closed-cell gas microscopy it is now feasible to investigate nanoscale oxidation mechanisms and kinetics in real time and at high spatial resolution and can be broadly applied to understand the basic high-temperature oxidation mechanisms for a wide range of alloy compositions.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8

Similar content being viewed by others

References

  1. G. Frommeyer and R. Rablbauer, Steel Research International 79, 2008 (507–513).

    Article  Google Scholar 

  2. P. A. Pint, Oxidation of Metals 49, 1998 (531–559).

    Article  Google Scholar 

  3. J. Doychak, J. L. Smialek and T. E. Mitchell, Metallurgical Transactions A 20, 1989 (499).

    Article  Google Scholar 

  4. M. W. Brumm and H. J. Grabke, Corrosion Science 33, 1992 (167–1690).

    Article  Google Scholar 

  5. B. A. Pint, T. M. Treska and L. W. Hobbs, Oxidation of Metals 47, 1997 (1–20).

    Article  Google Scholar 

  6. B. A. Pint, J. R. Martin and L. W. Hobbs, Oxidation of Metals 39, 1993 (167–195).

    Article  Google Scholar 

  7. E. Schumann, J. C. Yang, M. J. Graham and M. Rühle, Materials and Corrosion 46, 1995 (218–222).

    Article  Google Scholar 

  8. E. Schumann, J. C. Yang, M. J. Graham and M. Rühle, Materials and Corrosion 47, 1996 (631–632).

    Article  Google Scholar 

  9. C.-M. Wang, A. Genc, H. Cheng, L. Pullan, D. R. Baer and S. M. Bruemmer, Scientific Reports 4, 2014 (1–6).

    Google Scholar 

  10. C.-M. Wang, D. K. Schreiber, M. J. Olszta, D. R. Baer and S. M. Bruemmer, Applied Materials & Interfaces 7, 2015 (17272–17277).

    Article  Google Scholar 

  11. Q. Jeangros, T. W. Hansen, J. B. Wagner, R. E. Dunin-Borkowski, C. Hebert, J. Hessler-Wyser, et al., Acta materialia 67, 2014 (362–372).

    Article  Google Scholar 

  12. L. F. Allard, S. H. Overbury, W. C. Bigelow, M. B. Katz, D. P. Nackashi and J. Damiano, Microscopy and Microanalysis 18, 2012 (656–666).

    Article  Google Scholar 

  13. L. F. Allard, W. C. Bigelow, S. Zhang, X. Pan, Z. Wu, S. H. Overbury, et al., Microscopy and Microanalysis 20, 2014 (1572–1573).

    Article  Google Scholar 

  14. L. F. Allard, W. C. Bigelow, Z. Wu, S. H. Overbury, K. A. Unocic, M. Chi, et al., Microscopy and Microanalysis 21, 2015 (97–98).

    Article  Google Scholar 

  15. S. J. Pennycook, Ultramicroscopy 30, 1989 (59–69).

    Article  Google Scholar 

  16. G. C. Wood and B. Chattopadhyay, Corrosion Science 10, 1970 (471–480).

    Article  Google Scholar 

  17. J. Doychak and M. Rühle, Oxidation of Metals 31, 1989 (431–452).

    Article  Google Scholar 

  18. H. J. Grabke, Intermetallics 7, 1999 (1153–1158).

    Article  Google Scholar 

  19. M. W. Brumm, H. J. Grabke and B. Wagemann, Corrosion Science 36, 1994 (37–53).

    Article  Google Scholar 

  20. B. Pint, Oxidation of Metals. 48, 1997 (303–328).

    Article  Google Scholar 

  21. W. J. Quadakkers and M. J. Bennett, Materials Science and Technology 10, 1994 (126–131).

    Article  Google Scholar 

  22. B. Pint and K. L. More, Journal of Materials Science 44, 2009 (1676–1686).

    Article  Google Scholar 

Download references

Acknowledgements

This research was supported by the U.S. Department of Energy, Office of Coal and Power R&D, Office of Fossil Energy (KAU, DS, LFA). Additional support was provided by the Center for Nanophase Materials Sciences, which is a U.S. Department of Energy Office of Science Scientific User Facility (RRU). The authors wish to thank K.L. More and B.A. Pint for providing comments on the manuscript.

Author information

Authors and Affiliations

  1. Materials Science & Technology Division, Oak Ridge National Laboratory, 1 Bethel Valley Road, Oak Ridge, TN, 37831, USA

    Kinga A. Unocic, Dongwon Shin & Lawrence F. Allard

  2. Center For Nanophase Materials Sciences Division, 1 Bethel Valley Road, Oak Ridge, TN, 37831, USA

    Raymond R. Unocic

Authors
  1. Kinga A. Unocic
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Dongwon Shin
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Raymond R. Unocic
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Lawrence F. Allard
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Kinga A. Unocic.

Electronic supplementary material

Below is the link to the electronic supplementary material.

Supplementary material 1 (MP4 10935kb)

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Unocic, K.A., Shin, D., Unocic, R.R. et al. NiAl Oxidation Reaction Processes Studied In Situ Using MEMS-Based Closed-Cell Gas Reaction Transmission Electron Microscopy. Oxid Met 88, 495–508 (2017). https://doi.org/10.1007/s11085-016-9676-2

Download citation

  • Received:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11085-016-9676-2

Keywords

Search

Navigation