Abstract
The purpose of the present study was to examine the oxidation of Mg–Al alloys in the atmosphere of oxygen at various temperatures. The basic examination methods used were differential scanning calorimetry (DSC) and thermogravimetry (TG). The results show that the oxide layer can either protect the material against progressive oxidation or it can cause complete disintegration of material. The nature of the oxide layer formed depends on the external conditions, i.e. on the atmosphere, temperature, and type of alloy. A model of the Mg–Al alloy oxidation was calculated from the TG curves.
Similar content being viewed by others
References
K. U. Kainer and F. Von Buch, in Magnesium-Alloys and Technologies. Institut für Werkstofforschung, ed. V. Kainer, Trans. F. Kaiser (Wiley-VCH Verlag GmbH & Co, Weinhein, 2003), p. 1.
L. Vehovar, in Korozija kovin in korozijsko preskušanje (Ljubljana, 1991), p. 1.
P. Kurze, in Magnesium-Alloys and Technologies, ed. V. Kainer, Trans. F. Kaiser (Wiley-VCH Verlag GmbH & Co, Weinheim, 2003), p. 218.
E. Ghali, W. Dietzel, and K. U. Kainer, Journal of Material Engineering and Performance 13, 7 (2004).
T. B. Massalski and H. Okamoto, in Binary Alloys Phase Diagrams, eds. P. R. Subramanian and L. Kaprzak, 2nd edn. (ASM, Metal Park, Ohio, 1990).
F. Czerwinski, Journal of the Minerals, Metals and Materials Society 56, 29 (2004).
C. Lea and J. Molinari, Journal of Material Science 19, 2336 (1984).
J. Medved and P. Mrvar, in High-temperature Oxidation of Mg Alloys, Vol. 3 (Livarski vestnik), p. 2006.
F. Czerwinski, Corrosion Science 46, 377 (2004).
F. Czerwinski, Acta Materialia 50, 2639 (2002).
J. Medved and P. Mrvar, Materials Science Forum 508, 603 (2006).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Medved, J., Mrvar, P. & Vončina, M. Oxidation Resistance of Cast Magnesium Alloys. Oxid Met 71, 257–270 (2009). https://doi.org/10.1007/s11085-009-9141-6
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11085-009-9141-6