Abstract
This study demonstrates an improvement in the photodetection response of a Cupric Oxide (CuO) thin film through the annealing process. The CuO thin film was deposited on silicon substrate using DC magnetron sputtering system. Annealing of the as-deposited film was carried out in a muffle furnace at 400 and 500 °C for two hours. X-ray diffraction patterns revealed the formation of a single phase CuO film whose crystallinity was improved with increase of the annealing temperature. The field emission scanning electron microscopy indicated a compact and fine granular structure of the as-deposited film whereas the segregation and agglomeration of grains was observed after the film’s annealing. The photodetection performance of CuO film with Al contacts was investigated under the exposure of visible light. The current–voltage graphs of as-deposited and annealed films displayed Schottky contact between the metal and semiconductor, owing to a lower work function of Al than that of the CuO. The photo-to-dark current ratio of the device was significantly enhanced after the film’s annealing. The increase in photocurrent became more pronounced upon increasing the light intensity from 58 to 511 µW/cm2. The maximum current gain and sensitivity values were found to be 66 and 6500% respectively at 10 V bias for the film annealed at 500 °C. The rise and fall time of the Al/CuO/Al photodetector was decreased after the film’s annealing.
Similar content being viewed by others
Availability of data and materials
All data is included inside the manuscript.
References
Abbas, S., Kumar, M., Kim, J.: All metal oxide-based transparent and flexible photodetector. Mater. Sci. Semicond. Processing. 88, 86–92 (2018)
Abd-Alghafour, N.M., Ahmed, N.M., Hassan, Z.: Fabrication and characterization of V2O5 nanorods based metal–semiconductor–metal photodetector. Sensors and Acutuators a: Physical 250, 250–257 (2016)
Afzal, N., Devarajan, M.: Fabrication and characterization of In0.83Al0.17N based MSM visible photodiode. Eur. Phys. J. Appl. Phys. 76, 10101 (2016)
Ahmad, H., Afzal, N., Rafique, M., Ahmed, A.A., Ahmad, R., Khaliq, Z.: Post-deposition annealed MoO3 film based high performance MSM UV photodetector fabricated on Si (100). Ceram. Int. 46, 20477–20487 (2020)
Akgul, F.A., Akgul, G., Yildirim, N., Unalan, H.E., Turan, R.: Influence of thermal annealing on microstructural, morphological, optical properties and surface electronic structure of copper oxide thin films. Mater. Phys. Chem. 147, 987–995 (2014)
Al- Kuhaili, M.F.: Characterization of copper oxide thin films deposited by the thermal evaporation of cuprous oxide (Cu2O). Vacuum 82, 623–629 (2008)
Al-Ghamdi, A.A., Khedr, M.H., Ansari, M.S., Hassan, P.M.Z., Abdel-Wahab, MSh., Farghali, A.A.: RF sputtered CuO thin films: Structural, optical and photo-catalytic behavior. Physica E Low Dimens. Syst. Nanostruct. 81, 83–90 (2016)
Bai, Z., Zhang, Y.: Self-powered UV–visible photodetectors based on ZnO/Cu2O Nanowire/electrolyte heterojunctions. J. Alloys Compd. 675, 325–330 (2016)
Bayansal, F., Taskopru, T., Sahin, B., Centinkara, H.A.: Effect of cobalt doping on nanostructured CuO thin films. Metal. Mater. Trans. A 45, 3670–3674 (2014)
Chen, R.S., Wang, W.C., Chan, C.H., Hsu, H.P., Tian, L.C., Chen, Y.J.: Photoconductivities in nanocrystalline layered V2O5 nanowires grown by physical vapor deposition. Nanoscale Res. Lett. 8, 443 (2013)
Chu, Y.L., Young, S.J., Ji, L.W., Tang, I.T., Te-Chu, T.: Fabrication of ultraviolet photodetectors based on Fe-doped ZnO nanorod structures. Sensors 20, 3861 (2020)
Dushaq, G., Nayfeh, A., Rasras, M.: Complementary metal oxide semiconductor (CMOS) compatible gallium arsenide metal-semiconductor-metal photodetectors (GaAs MSMPDs) on silicon using ultra-thin germanium buffer layer for visible photonic applications. J. Appl. Phys. 126, 193106 (2019)
Esteves, B., Pimenta, S., Vieira, E.M.F., Freitas, J.R., Rodrigues, J.A., Correia, J.H.: SnOx and a-Si thin-films based photodiode in a flexible substrate for visible spectral region. Mater. Lett. 286, 129251 (2021)
Farhad, F.U., Cherns, D., Smith, J.A., Fox, N.A., Fermín, D.J.: Pulsed laser deposition of single phase n- and p-type Cu2O thin films with low resistivity. Mater. Des. 193, 108848 (2020)
Farrukh, S., Afzal, N., Ahmed, A.A., Rafique, M., Raza, M.A.: Fabrication and characterization of MSM photodetector based on DC sputtered CuO film Accepted. J. Opt. optoelectron. Adv. Mater. (2021)
Figueiredo, V., Elangovan, E., Goncalves, G., Barquinha, P., Pereira, L., Franco, N., Alves, E., Martins, R., Fortunato, E.: Effect of post-annealing on the properties of copper oxide thin films obtained from the oxidation of evaporated metallic copper. Appl. Surf. Sci. 254, 3949–3954 (2008)
Ghicov, A., Tsuchyia, H., Macak, J.M.: Annealing effects on the photoresponse of TiO2 nanotubes. Phys. Stat. Sol. 203, 28–30 (2006)
Gulen, Y., Bayansal, F., Sahin, B., Centinkara, H.A., Guder, H.S.: Fabrication and characterization of Mn-doped CuO thin films by the SILAR method. Ceram. Int. 39, 6475–6480 (2013)
Gunassekran, S., Thangaraju, D., Marnadu, R., Chandrasekaran, J., Alshahrani, S.M., Durairajan, A., Graca, M.P.F., Elango, M.: Fabrication of high-performance SiO2@ p-CuO/n-Si core-shell structure based photosensitive diode for photodetection application. Surf. Interfaces. 20, 100622 (2020)
Hajimazdarani, M., Ghasali, E., Naderi, N., Orooji, Y.: Enhanced optical properties and photodetection behavior of ZnS thin film deposited by electron beam evaporation upon doping with europium oxide. Ceram. Int. 46, 28382–28389 (2020)
Hendi, A.A., Rashad, M.: Photo-induced changes in nano-copper oxide for optoelectronic applications. Physica B Condens Matter. 538, 185–190 (2018)
Hojabri, A., Hajakbari, F., Soltanpoor, N., Hedayati, M.S.: Annealing temperature effect on the properties of untreated and treated copper films with oxygen plasma. J. Theor. Appl. Phys. 8, 132 (2014)
Hojbari, A., Hajakbari, F., Meibodi, A.E.: Structural and optical properties of nanocrystalline α-MoO3 thin films prepared at different annealing temepratures. J. Theor. Appl. Phys. 9, 67–73 (2015)
Husham, M., Hassan, Z., Abass Selman, M.: Synthesis and characterization of nanocrystalline CdS thin films for highly photosensitive self-powered photodetector. Eur. Phys. J. Appl. Phys. 74, 10101 (2016)
Imran, M., Ahmad, R., Afzal, N., Rafique, M.: Copper ion implantation effects in ZnO film deposited on flexible polymer by DC magnetron sputtering. Vacuum 165, 72–80 (2019)
Johan, M.R., Suan, M.S.M., Hawari, N.L., Ching, H.A.: Annealing effects on the properties of copper oxide thin films prepared by chemical deposition. Int. J. Electrochem. Sci. 6, 6094–6104 (2011)
Lin, Q., Armin, A., Lyons, D.M., Burn, P.L.: Low noise, IR-Blind organohalide perovskite photodiodes for visible light detection and imaging. Adv. Mater. 27, 2060–2064 (2015)
Malek, M.K., Mamat, M.H., Musa, M.A.: Thermal annealing-induced formation of ZnO nanoparticles: Minimum strain and stress ameliorate preferred c-axis orientation and crystal-growth properties. J. Alloys Compd. 610, 575–588 (2014)
Moumen, A., Hartiti, B., Comini, E., Khalidi, Z.E., Arachchige, H.M.M., Fadili, S., Thevenin, P.: Preparation and characterization of nanostructured CuO thin films using spray pyrolysis technique. Superlattices Microstruct. 127, 2–10 (2019)
Muthe, K.P., Vyas, J.C., Narang, S.N., Aswal, D.K., Gupta, S.K., Bhattachraya, D., Pinto, R., Kothiyal, G.P., Sabharwal, S.C.: A study of the CuO phase formation during thin film deposition by molecular beam epitaxy. Thin Solid Films 324, 37–43 (1998)
Oku, T., Motoyoshi, R., Fujjimoto, K., Akiyama, T., Jeyadevan, B., Cuya, J.: Structures and photovoltaic properties of copper oxides/fullerene solar cells. J. Phys. Chem. Solids 72, 1206–1211 (2011)
Patel, M., Kim, H.S., Kim, J.: All transparent metal oxide ultraviolet photodetector. Adv. Electron. Mater. 1, 1500232 (2015)
Raghavendra, P.V., Bhat, J.S., Deshpande, N.G.: Visible light sensitive cupric oxide metal-semiconductor-metal photodetectors. Superlattices Microstruct. 113, 754–760 (2018)
Raship, N.A., Sahdan, M.Z., Adriyanto, F., Nurfazliana, M.F., Bakri, A.S.: Effect of annealing temperature on the properties of copper oxide films prepared by dip coating technique. AIP Conf. Proc. 1788, 030121 (2017)
Rehman, S., Mumtaz, A., Hasanain, S.K.: Size effects on the magnetic and optical properties of CuO nanoparticles. J Nanopart Res. 13, 2497–2507 (2011)
Shariffudin, S.S.: Preparation and characterization of nanostructured CuO thin films using sol-gel dip coating. Mater. Sci. Eng. 99, 012007 (2015)
Song, H.J., Seo, H.M., Choi, K.W., Jo, M.S., Yoo, J.Y., Yoon, J.B.: High-performance copper oxide visible-light photodetector via grain-structure model. Sci. Rep. 9, 7334 (2019)
Sullivan, I., Zoellner, B., Maggard, P.: Copper (I)-based p-type oxides for photoelectrochemical and photovoltaic solar energy conversion. Chem. Mater. 28, 5999–6016 (2016)
Tian, W., Lu, H., Li, L.: Nanoscale ultraviolet photodetectors based on one dimensional metal oxide nanostructures. Nano Res. 8, 382–405 (2015)
Tsai, D.S., Lu, K.K., Lien, D.H., Tsai, M.L., Kang, C.F., Lin, C.A., Li, L.J., He, J.R.: Few-layer MoS2 with high broadband photogain and fast optical switching for use in harsh environments. ACS Nano 7, 3905–3911 (2013)
Valtierra, J.M., Ortiz, J.R., Arroyo-Rojas, V.M., Ruiz, F.: Cyclohexane oxidation over Cu2O–CuO and CuO thin films deposited by CVD process on fiberglass. Appl. Catal. a: Gen. 238, 1–9 (2003)
Xie, C., Mak, C., Tao, X., Yan, F.: Photodetectors based on two-dimensional layered materials beyond graphene. Adv. Funct. Mater. 27, 1603886 (2017)
Younas, R., Afzal, N., Rafique, M., Imran, M., Saleem, M., Ahmad, R.: Nickel ion implantation effects on DC magnetron sputtered ZnO film prepared on Si (100). Cerm. Int. 45, 15547–15555 (2019)
Yusoff, M.Z.M., Hassan, Z., Hassan, A., Abdullah, M.J., Rusop, M., Pakhuruddin, M.Z.: AlxGa1−xN/GaN/AlN heterostructures grown on Si(1 1 1) substrates by MBE for MSM UV photodetector applications. Mater. Sci. Semicond. Proc. 34, 214–223 (2015)
Zhai, T., Fang, X., Liao, M., Xu, X., Zeng, H., Yoshio, B., Golberg, D.: A comprehensive review of one-dimensional metal-oxide nanostructure photodetectors. Sensors 9, 6504–6529 (2009)
Zhang, Q., Zhang, K., Xu, D., Yang, G., Huang, H., Nie, F., Liu, C., Yang, S.: CuO nanostructures: Synthesis, characterization, growth mechanisms, fundamental properties, and applications. Prog. Mater. Sci. 60, 208–337 (2014)
Zhou, C., Ai, Q., Chen, X., Gao, X., Liu, K., Shen, D.: Ultraviolet photodetectors based on wide bandgap oxide semiconductor films. Chin. Phys. B 28, 048503 (2019)
Zhu, H., Shan, C.X., Wang, L.K.: Metal−oxide−semiconductor-structured MgZnO ultraviolet photodetector with high internal gain. J. Phys. Chem. C 114, 7169–7172 (2010)
Acknowledgements
The authros acknowledge Dr. M. Javed Iqbal from Centre of excellence in solid state physics for the help in doing photodetection characterizations.
Funding
N/A.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
There is no conflict of interst/competing interst for this work.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Tariq, M., Afzal, N. & Rafique, M. Enhanced photodetection performance of sputtered cupric oxide thin film through annealing process. Opt Quant Electron 53, 685 (2021). https://doi.org/10.1007/s11082-021-03342-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11082-021-03342-8