Abstract
In this study, TiO2 nanoparticles (average particle size 16 nm) were successfully produced in molten salt phase and were showed to significantly enhance the specific heat capacity of a binary eutectic mixture of sodium and potassium nitrate (60/40) by 5.4 % at 390 °C and 7.5 % at 445 °C for 3.0 wt% of precursors used. The objective of this research was to develop a cost-effective alternate method of production which is potentially scalable, as current techniques utilized are not economically viable for large quantities. Enhancing the specific heat capacity of molten salt would promote more competitive pricing for electricity production by concentrating solar power plant. Here, a simple precursor (TiOSO4) was added to a binary eutectic mixture of potassium and sodium nitrate, heated to 450 °C, and cooled to witness the production of nanoparticles.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Concentrated Solar Power (CSP) technology operates through the collection and concentration of solar radiation utilizing the long-wave region of its spectrum as a source of energy (Gil et al. 2010; Medrano et al. 2010). The latter is stored and transported by the heat-transfer fluid (HTF) to the heat exchanger to produced steam and power turbine generating electricity in the process (Fig. 1). Currently, synthetic oils are commonly used in the primary loop system, but their low thermal stability since they decompose at operating temperatures exceeding 400 °C as well as toxicity, high purchasing cost, and high vapour pressure is pushing industrials and academics toward alternative materials to solve these challenges (Cavallaro 2010). Molten salt (Solar Salt) is currently seen as a viable option due to its low toxicity, cost and vapour pressure, as well as good thermal stability, since they decompose at operating temperatures exceeding 600 °C. However, their high freezing point and low thermo-physical properties are a disadvantage of using this material which might be offset by higher thermodynamic efficiency attained when running a CSP plant at 560 °C rather than 395 °C.
Schematic diagram of CSP plant—currently most plant utilizing molten salt run at a maximum of ≈560 °C with a minimum of 290 °C, whilst synthetic oil, such as VP1 Therminol, has a temperature range of 13–395 °C. Energy storage either direct or indirect is a viable option for this technology and is implemented in many CSP plants (Price et al. 2002; Medrano et al. 2010)
Current research is looking at enhancing the specific heat capacity through the addition of nanoparticles within the molten salt mixtures. The presence of nanoparticles into liquid (nanofluids) has been extensively studied and stems from the work of Choi and Eastman (1995), whereby anomalous enhancement of thermal conductivity was reported when nanoparticles (Al2O3, Au, Ag, Cu, TiO2, CuO, Carbon Nanotube, ZnO, Graphite, Graphene, SiC, etc.) (1–100 nm) were suspended into various liquid phase (Pumped oil, ethylene glycol, water, toluene, etc.) (Lee et al. 1999; Wang et al. 1999; Xuan and Li 2000; Eastman et al. 2001; Tsai et al. 2004; Yang et al. 2005; Kang et al. 2006; He et al. 2007; Zhang et al. 2007; Yu et al. 2009; Moosavi et al. 2010; Paul et al. 2010; Lee et al. 2011; Sharma et al. 2011; Yu et al. 2011). With thousands of papers studying these anomalous enhancements, the various factors (size of particle, shape, surface properties, concentration, and interaction with base fluid) encompassing this rise has made it difficult to model accurately (Xuan and Li 2000; Das et al. 2003, 2006; Lee et al. 2006; Prasher et al. 2006; Ding et al. 2007; Trisaksri and Wongwises 2007; Yang and Liu 2010; Yu and Xie 2012). This said, recent theory and understanding point to the effective medium theory by Maxwell as a good model for prediction of thermal conductivity (Keblinski et al. 2008; Buongiorno and Venerus 2009).
Whilst thermal conductivity of nanofluids has been extensively studied at low temperature for non-ionic fluids, very little has been published on high-temperature ionic fluid in comparison. Much like, non-ionic fluid, the preparation and suspension of nanoparticles into molten salt is going to be affected by the methodology employed in its making.
The most utilized technique in the production of molten salt nanofluids is the dispersion/dissolution in water coupled with sonication and drying which stems from the works of Shin (2011) and Jung (2012) thesis dissertations and also led to a patent application on a technique of production of in situ nanoparticles and nanofins (Shin and Banerjee 2010; Shin 2011; Shin and Banerjee 2011a, b; Jo et al. 2012; Jung 2012; Chieruzzi et al. 2013; Dudda and Shin 2013; Khodadadi et al. 2013; Lu and Huang 2013; Tiznobaik and Shin 2013a, b; Andreu-Cabedo et al. 2014; Banerjee and Jo 2014; Jo and Banerjee 2014; Chieruzzi et al. 2015; Tao et al. 2015) (Fig. 2a). Whilst this technique scatters the nanoparticles and potentially destroy aggregates that have formed, the evaporation of water might still promote their formation, as the volume gets reduced and the concentration of nanoparticle rises which is what is been observed by Shin and Banerjee (2013) in Fig. 1 where a fine and coarse structure is clearly visible in the petri-dish (Shin and Banerjee 2013). These changes in the spatial arrangement of the nanoparticles led to variation in specific heat capacity, whereby coarse structure (aggregated nanoparticles) showed no enhancement, whilst fine/dispersed nanoparticles displayed increases of 118–124 % compared to the base salt (Shin and Banerjee 2013). The theory behind these enhancements are due to the production of compressed layer (semi-solid layer of ions) around the formed nanostructure which are described by Shin and Tiznobaik (2014) as fractals (Shin and Tiznobaik 2014; Jo and Banerjee 2015). It has also been hypothesised that the surface phonon which are usually negligible might, due the large surface area-to-volume ratio, play a vital role in this increase in specific heat capacity.
Various methodologies that can be employed in the making of molten salt nanofluids. Whilst liquid dispersion (a) is the most used technique (Shin and Banerjee 2010, 2011a, b; Jo et al. 2012; Chieruzzi et al. 2013; Dudda and Shin 2013; Lu and Huang 2013; Tiznobaik and Shin 2013a, b; Andreu-Cabedo et al. 2014; Jo and Banerjee 2014; Chieruzzi et al. 2015; Tao et al. 2015), mechanical dispersion (b) can also be used (Lasfargues et al. 2015) as well as In Situ production (c) which has not been implemented in any research and will be looked at in this paper
Mechanical dispersion (Fig. 2b) is an alternate approach and could potentially be leveraged for scale-up synthesis. However, more research needs to be implemented on its effect and how to control the homogeneity of the mix. The size and type of bearing used, as well as the amount of time the mixture is homogenised and its speed is going to impact the uniformity of the mix in different ways. In this paper, we explore the in situ synthesis of titanium oxide nanoparticles in the molten salt phase [60 wt% Sodium nitrate (NaNO3) and 40 wt% Potassium Nitrate (KNO3) eutectic mix] using a precursor (Fig. 2c), such as titanium (IV) oxysulphate (TiOSO4), and how this might affect the specific heat capacity (Cp) of the mixture. The precursor was chosen because of TiO2 many applications throughout different industries (Dye in paint, paper, plastics, medicine, food; Sunscreen blocker; Photo-catalyst; Batteries) (Zhu et al. 2012).
Methodology
Sample production
Anhydrous NaNO3 (FISHER, UK) (>99 % Pure) and KNO3 (SIGMA-ALDRICH, UK) (>99 % Pure) as well as TiOSO4 (SIGMA-ALDRICH, UK) were purchased for these tests. The salt and precursors were mixed using a pestle and mortar with the following ratio (Table 1).
After grinding the mixture for 10–15 min manually, the latter was transferred to an aluminium crucible and inserted in a furnace (Carbolite, 1100, OAF 11/2, UK). The thermal program used for the sample production was a ramp up from room temperature to 450 °C at 10 °C/min with an isothermal of 30 min at 450 °C. Once finished, the crucible was removed and left to cool on a stainless steel sheet of metal (Fig. 3). This promoted a rapid temperature drop and crystallisation of the salt.
Once cooled the samples were analysed using scanning electron microscope (SEM) coupled with energy dispersive X-ray (EDX) for elemental analysis as well as backscattered electron (BSE) and transmission electron microscopy (TEM). Finally, utilizing thermo-gravimetric analyser combined with differential scanning calorimeter (DSC) sensor as well as a stand-alone DSC, the production of nanoparticles was analysed and the specific heat capacity (Cp) was measured.
SEM, BSE, and EDX
Morphological and elemental analysis of the samples was carried out using a field emission SEM (Hitachi SU8230, Berkshire, UK). Samples were mounted on 12 mm aluminium SEM stub and coated with a 3 nm mixture of platinum/palladium using an 80/20 ratio, via a high-resolution sputter coater.
TEM
Further analysis of the nanoparticles themselves was carried out using transmission electron microscopy (FEI TECNAI F20, Cambridge, UK). The samples were produced by dissolving the salt containing the produced nanoparticles into deionised water and sonicating the mixture for a couple of hours. Then, it was centrifuged, the supernatant was drained, and more deionised water was added with a further round of sonication to re-suspend the nanoparticles. This was repeated a number of times to remove the nitrate salt. Finally, using a 10 µl Gilson pipette, a small sample was withdrawn, applied onto a 3 mm copper grid and left to dry at room temperature before analysis.
DSC
The specific heat capacity was measured using a heat-flux DSC with automated sampler (Mettler Toledo, DSC-1 700, Leicester, UK). The samples used were first grinded in a pestle and mortar and inserted inside 30 µl platinum crucibles (Mettler Toledo, UK) with amounts varying between 30,000 and 35,000 mg. The samples were repeatedly melted and frozen several times (Table 2) before testing the Cp values. The thermal cycle employed was an isothermal of 5 min at 250 °C followed by a rapid ramp up to 450 °C at a rate of 40 °C/min with a final isothermal of 5 min at 450 °C. A sapphire standard (24.055 mg) was used as a standard to calculate the Cp.
As always the specific heat capacity of sapphire was checked to ensure the validity of this methodology. With results within ±0.55 % of the reference sapphire value, the process was considered precise and accurate enough to carry on the tests (Fig. 4).
Comparison between experimental and reference values of sapphire for specific heat capacity (Tiznobaik and Shin 2013b)
TGA/DSC
The production of nanoparticles in molten salt phase was followed using a TGA/DSC (Mettler Toledo, TGA/DSC, LF-1100, Leicester, UK). The sample was a combination of sodium and potassium nitrate (60/40) mixture with titanium oxysulphate. To obtain large enough peaks to analyse and as the aim of this test was just to observe how the decomposition reaction took place, ≈27.000 mg of salt (60 wt% NaNO3+ 40 wt% KNO3) was mixed with ≈3.000 mg of TiOSO4 and inserted inside a platinum crucible (40 µl). The thermal sample employed was an isothermal of 30 min at 50 °C followed by a ramp up to 450 °C at 10 °C/min with another isothermal at 450 °C for 30 min.
Results and discussion
The SEM analysis of the lowest concentration of TiOSO4 precursors (1.0 wt%) displayed what seemed to be aggregated nanoparticles (Fig. 5a). This is partially corroborated by backscattered electron analysis which clearly highlight a density change between the molten salt which appear dark grey and the nanoparticles which have a lighter colour (Fig. 5b). Furthermore, the BSE picture clearly showed that the adsorption of nanoparticles onto the molten salt surface (Fig. 5b: Top right) (Lu and Huang 2013; Chieruzzi et al. 2015) and a magnification of 100,000 times (Fig. 5c) seem to show that the nanoparticle in question are relatively homogenous in term of size. The elemental mapping utilizing the EDX (Fig. 6) revealed the presence of titanium and oxygen which looked to be superimposed implying the production of TiO2. This would make sense as the thermal decomposition of this precursor is as follow:
In this molten state, the ions would not take part in the reaction and the completion of the reaction could be partly indicated by the presence or absence of sulphur which was definitely not picked up by the EDX as a major component of this sample. Another interesting revelation provided by the EDX analysis was the packing of sodium and potassium atoms in relation to titanium. From Fig. 6, it can be seen that the potassium atoms are able to come into closer contact to the titanium than sodium. This could probably be explained by the fact that the larger ions are a better fit requiring less packing energy, thereby reducing entropy (better adhesion properties between the two materials). The EDX also showed that the potassium atoms are segregated from the sodium with very faint overlapping seen when close to the nanoparticle’s surface. This has been demonstrated by Jo and Banerjee (2014), in their molecular dynamic model which describe these chemical potential cause by enhanced adhesion properties between potassium and graphite in the compressed layers as an element which might be part of the increased storage mechanism seen in molten salt nanofluids (Jo and Banerjee 2014).
Analysis of the TEM images showed that the nanoparticles produced were homogenous in nature with an average diameter estimated at 16.35 nm ± 2.80 (Fig. 7a). The TEM diffraction pattern confirmed that anatase was produced (Fig. 7b). The lattice distance came to an average of 0.357 nm (Fig. 7b) which is in good agreement with the previous studies for the (101) plane of the anatase phase (Xie et al. 2009; Dai et al. 2010). The production of nanoparticles in molten salt state is definitely achievable, although it leads to the production of aggregates which would have to be broken down through the use of sonication at high temperature. Furthermore, the time, amount of precursors, maximum temperature, and production method used in the nucleation process are likely to affect the size of the nanoparticles.
From the TGA-DSC analysis (Fig. 8), it can be seen that the first melting cycle leads to the production of three endothermic peaks with an onset of 107.22, 221.94, and 333.16 °C, whilst the second melting cycle of the same sample only yield two at temperature of 109.68 and 216.03 °C. The first endothermic peak is likely to be water content/moisture, and both curves display this peak combined with mass loss. The second endothermic peak will be that of the salt melting which given the temperature at which it occurs correspond to a eutectic binary mixture of sodium and potassium nitrate (60/40). The third endothermic peak is only present in the first melting cycle and absent in the second. It is probably caused by the production of titanium sulphate (Ti(SO4)2) which has a boiling point of 330 °C. It is also important to notice that the sharpest drop in sample weight occurs right after the melting of the salt which would set off the decomposition reaction leading to the production of nanoparticles (Fig. 8—from 220 °C).
The production of TiO2 within molten salt phase seemed to provide on average an enhancement which was dependent on the amount of precursor utilize in the synthesise process, although the latter cannot be deemed reliable for 1.0 and 2.0 wt% of TiOSO4 due to the overlapping error bars. Still a trend is seen. At a concentration of 3.0 wt% of TiOSO4, a significant increase is obtained above 390 °C with a 5.4 % increase compared to base salt, rising to 7.5 % at 445 °C (Fig. 9). Providing a way to disperse the aggregate produced during the formation of TiO2 might enhance the specific heat capacity through the production of a more homogenous mix.
Clearly, the production in situ of nanoparticles does alter the storage capacity of molten salt which still raise the questions as to the exact mechanisms allowing these anomalous enhancements to occur as nanoparticles themselves have lower specific heat capacity compared to that of the salt used. Various hypotheses are mentioned in the literatures:
-
Nano-layers—Occurring at the interface of the liquid salt and the solid nanoparticles, the molten salt ions would be constrained into a semi-solid phase causing the production of layers with increase degree of freedoms away from the interface. The partial incorporation of the enthalpy of fusion in this semi-solid structure could partly provide an explanation for the rise in Cp (Jo and Banerjee 2014). This was observed by Oh et al. (2005) research team with the layering of aluminium atoms at the interface of sapphire (Oh et al. 2005). We hypothesise that these adsorbed layers of fluid or solvent molecules with nano-scale thickness would be strongly affected by the shape of the nanoparticles.
-
Interfacial Thermal or Kapitza Resistance—Storage at the interface of the solid and liquid due to the differences in electronic and vibrational properties of the different materials. This could be enhanced by the large surface area-to-volume ratio of nanoparticles (Shin and Banerjee 2011a, b).
-
Higher Cp of nanoparticles compared to their bulk counterpart. Reported by Tan et al. (2009), the increased exposure of surface atoms is showed to increase the Cp value measured in various tested nanoparticles (Tan et al. 2009). This mode is unlikely to play a major role in enhancement but might contribute to it.
Another hypothesis could also be:
-
Entrapment of molten salt in nanoparticle agglomerates could also promote the enhancement of Cp through the semi-solid arrangement of ions (Shin and Banerjee 2011a, b; Jo and Banerjee 2015). However, as seen in the EDX map, the wetting behaviour is crucial to the interaction between the nanoparticles and the molten salt.
Whilst each of these modes might play a certain extent in the enhancement of Cp, adsorbed layer of nano-scale thickness and entrapment of molten salt in agglomerate are likely to be the major component of this rise. What is clear is that the development of in situ production and dispersion of nanoparticles in molten salt phase would pave the way toward a cost-effective alternative toward the enhancement of specific heat capacity were it successful. However, the problem of agglomeration of nanoparticle is still a variable that need to be looked into for future research. Furthermore, this method could also be used in the production of nanoparticles, although separating the nanoparticle from the salt would be challenging.
Conclusions
In this study, the production of TiO2 nanoparticles was successfully achieved in a molten salt phase through the use of inexpensive precursors (TiOSO4). The produced nanoparticles were relatively homogenous in size (16.35 nm), although highly agglomerated. EDX mapping revealed that potassium ions could pack more tightly to the titanium oxide nanoparticle than sodium. DSC analysis showed that the increase in precursors was only significant when using 3.0 wt% of TiOSO4 precursors and at temperature of 390 °C and above.
Future work would concentrate on defining how the ratio of precursor used would affect the nanoparticle size as well as the time and temperature utilized to produce them. Furthermore, defining ways to destroy the formed aggregate might also prove useful in enhancing the Cp value. This is likely to affect the thermo-physical properties of the salt and a more detailed characterisation of these changes would need to be carried out.
References
Andreu-Cabedo P, Mondragon R et al (2014) Increment of specific heat capacity of solar salt with SiO2 nanoparticles. Nanoscale Res Lett 9(1):582
Banerjee D, Jo B et al (2014) Systems and methods for in-situ formation of nanoparticles and nanofins. T.-U. the texas A&M university system [US/US]; 3369 Tamu College Station
Buongiorno J, Venerus DC (2009) A benchmark study on the thermal conductivity of nanofluids. J Appl Phys 106(9):094312
Cavallaro F (2010) Fuzzy TOPSIS approach for assessing thermal-energy storage in concentrated solar power (CSP) systems. Appl Energy 87(2):496–503
Chieruzzi M, Cerritelli G et al (2013) Effect of nanoparticles on heat capacity of nanofluids based on molten salts as PCM for thermal energy storage. Nanoscale Res Lett 8:448
Chieruzzi M, Miliozzi A et al (2015) A new phase change material based on potassium nitrate with silica and alumina nanoparticles for thermal energy storage. Nanoscale Res Lett 10(1):984
Choi SUS, Eastman JA (1995) Enhancing thermal conductivity of fluids with nano-particles. International Mechanical Engineering Congress & Exposition, San Francisco
Dai SX, Wu YQ et al (2010) Preparation of highly crystalline TiO2 nanostructures by acid-assisted hydrothermal treatment of hexagonal-structured nanocrystalline titania/cetyltrimethyammonium bromide nanoskeleton. Nanoscale Res Lett 5(11):1829–1835
Das SK, Putra N et al (2003) Temperature dependence of thermal conductivity enhancement for nanofluids. J Heat Transf Trans Asme 125(4):567–574
Das SK, Choi SUS et al (2006) Heat transfer in nanofluids—a review. Heat Transf Eng 27(10):3–19
Ding YL, Chen HS et al (2007) Heat transfer intensification using nanofluids. Kona Powder Part 25:23–38
Dudda B, Shin D (2013) Effect of nanoparticle dispersion on specific heat capacity of a binary nitrate salt eutectic for concentrated solar power applications. Int J Therm Sci 69:37–42
Eastman JA, Choi SUS et al (2001) Anomalously increased effective thermal conductivities of ethylene glycol-based nanofluids containing copper nanoparticles. Appl Phys Lett 78(6):718–720
Gil A, Medrano M et al (2010) State of the art on high temperature thermal energy storage for power generation. Part 1-concepts, materials and modellization. Renew Sustain Energy Rev 14(1):31–55
He YR, Jin Y et al (2007) Heat transfer and flow behaviour of aqueous suspensions of TiO2 nanoparticles (nanofluids) flowing upward through a vertical pipe. Int J Heat Mass Transf 50(11–12):2272–2281
Jo B, Banerjee D (2014) Enhanced specific heat capacity of molten salt-based nanomaterials: effects of nanoparticle dispersion and solvent material. Acta Mater 75:80–91
Jo B, Banerjee D (2015) Enhanced specific heat capacity of molten salt-based carbon nanotubes nanomaterials. J Heat Transf 137(9):091013
Jo B, Jung S et al (2012) Anomalous rheological behavior of complex fluids (nanofluids). American Social Mechanical Engineers, New York
Johnsson M, Pettersson P et al (1997) Thermal decomposition of fibrous TiOSO4·2H2O to TiO2. Thermochim Acta 298(1–2):47–54
Jung S (2012) Numerical and experimental investigation of inorganic nanomaterials for thermal energy storage (TES) and concentrated solar power (CSP) applications. Doctor of Philosophy PhD—Thesis, Texas A&M, USA
Kang HU, Kim SH et al (2006) Estimation of thermal conductivity of nanofluid using experimental effective particle volume. Exp Heat Transf 19(3):181–191
Keblinski P, Prasher R et al (2008) Thermal conductance of nanofluids: is the controversy over? J Nanopart Res 10(7):1089–1097
Khodadadi JM, Fan L et al (2013) Thermal conductivity enhancement of nanostructure-based colloidal suspensions utilized as phase change materials for thermal energy storage: a review. Renew Sustain Energy Rev 24:418–444
Lasfargues M, Geng Q et al (2015) Mechanical dispersion of nanoparticles and its effect on the specific heat capacity of impure binary nitrate salt mixtures. Nanomaterials 5(3):1136
Lee S, Choi SUS et al (1999) Measuring thermal conductivity of fluids containing oxide nanoparticles. J Heat Transf Trans Asme 121(2):280–289
Lee D, Kim JW et al (2006) A new parameter to control heat transport in nanofluids: surface charge state of the particle in suspension. J Phys Chem B 110(9):4323–4328
Lee SW, Park SD et al (2011) Investigation of viscosity and thermal conductivity of SiC nanofluids for heat transfer applications. Int J Heat Mass Transf 54(1–3):433–438
Lu MC, Huang CH (2013) Specific heat capacity of molten salt-based alumina nanofluid. Nanoscale Res Lett 8:2927
Medrano M, Gil A et al (2010) State of the art on high-temperature thermal energy storage for power generation. Part 2-case studies. Renew Sustain Energy Rev 14(1):56–72
Moosavi M, Goharshadi EK et al (2010) Fabrication, characterization, and measurement of some physicochemical properties of ZnO nanofluids. Int J Heat Fluid Flow 31(4):599–605
Oh SH, Kauffmann Y et al (2005) Ordered liquid aluminum at the interface with sapphire. Science 310(5748):661–663
Paul G, Pal T et al (2010) Thermo-physical property measurement of nano-gold dispersed water based nanofluids prepared by chemical precipitation technique. J Colloid Interface Sci 349(1):434–437
Prasher R, Phelan PE et al (2006) Effect of aggregation kinetics on the thermal conductivity of nanoscale colloidal solutions (nanofluid). Nano Lett 6(7):1529–1534
Price H, Lupfert E et al (2002) Advances in parabolic trough solar power technology. J Solar Energy Eng Trans Asme 124(2):109–125
Sharma P, Baek IH et al (2011) Enhancement of thermal conductivity of ethylene glycol based silver nanofluids. Powder Technol 208(1):7–19
Shin D (2011) Molten salt nanomaterials for thermal energy storage and concentrated solar power applications. Doctor of philosophy thesis—PhD, Texas A&M, USA
Shin D, Banerjee D (2010) Effects of silica nanoparticles on enhancing the specific heat capacity of carbonate salt eutectic (work in progress). Int J Struct Changes Solids 2(2):25–31
Shin D, Banerjee D (2011a) Enhancement of specific heat capacity of high-temperature silica-nanofluids synthesized in alkali chloride salt eutectics for solar thermal-energy storage applications. Int J Heat Mass Transf 54(5–6):1064–1070
Shin DH, Banerjee D (2011) Enhanced specific heat of silica nanofluid. J Heat Transf 133:024501
Shin D, Banerjee D (2013) Enhanced specific heat capacity of nanomaterials synthesized by dispersing silica nanoparticles in eutectic mixtures. J Heat Transf 135(3):032801
Shin D, Tiznobaik H (2014) Specific heat mechanism of molten salt nanofluids. Appl Phys Lett 104(12):121914
Tan ZC, Wang L et al (2009) Study of heat capacity enhancement in some nanostructured materials. Pure Appl Chem 81(10):1871–1880
Tao YB, Lin CH et al (2015) Preparation and thermal properties characterization of carbonate salt/carbon nanomaterial composite phase change material. Energy Convers Manag 97:103–110
Tiznobaik H, Shin D (2013a) Enhanced specific heat capacity of high-temperature molten salt-based nanofluids. Int J Heat Mass Transf 57(2):542–548
Tiznobaik H, Shin D (2013b) Experimental validation of enhanced heat capacity of ionic liquid-based nanomaterial. Appl Phys Lett 102(17):173906
Trisaksri V, Wongwises S (2007) Critical review of heat transfer characteristics of nanofluids. Renew Sustain Energy Rev 11(3):512–523
Tsai CY, Chien HT et al (2004) Effect of structural character of gold nanoparticles in nanofluid on heat pipe thermal performance. Mater Lett 58(9):1461–1465
Wang XW, Xu XF et al (1999) Thermal conductivity of nanoparticle-fluid mixture. J Thermophys Heat Transf 13(4):474–480
Xie Y, Heo S et al (2009) Synthesis and photocatalytic activity of anatase TiO2 nanoparticles-coated carbon nanotubes. Nanoscale Res Lett 5(3):603–607
Xuan YM, Li Q (2000) Heat transfer enhancement of nanofluids. Int J Heat Fluid Flow 21(1):58–64
Yang X, Liu Z-H (2010) A kind of nanofluid consisting of surface-functionalized nanoparticles. Nanoscale Res Lett 5(8):1324–1328
Yang Y, Zhang ZG et al (2005) Heat transfer properties of nanoparticle-in-fluid dispersions (nanofluids) in laminar flow. Int J Heat Mass Transf 48(6):1107–1116
Yu W, Xie H (2012) A review on nanofluids: preparation, stability mechanisms, and applications. J Nanomater 2012:435873
Yu W, Xie H et al (2009) Investigation of thermal conductivity and viscosity of ethylene glycol based ZnO nanofluid. Thermochim Acta 491(1–2):92–96
Yu W, Xie HQ et al (2011) Significant thermal conductivity enhancement for nanofluids containing graphene nanosheets. Phys Lett A 375(10):1323–1328
Zhang X, Gu H et al (2007) Effective thermal conductivity and thermal diffusivity of nanofluids containing spherical and cylindrical nanoparticles. Exp Thermal Fluid Sci 31(6):593–599
Zhu P, Wu Y et al (2012) TiO2 nanoparticles synthesized by the molten salt method as a dual functional material for dye-sensitized solar cells. Rsc Adv 2(12):5123–5126
Acknowledgments
Financial support was provided by EPSRC EP/L014211/1 (Next generation grid scale thermal energy storage technologies) and EPSRC EP/K002252/1.
Author contributions
Mathieu Lasfargues wrote the manuscript and carried out all the experiments. Mathieu Lasfargues, Yulong Ding, and Andrew Bell revised the manuscript.
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflicts of interest
The authors declare no conflict of interest.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Lasfargues, M., Bell, A. & Ding, Y. In situ production of titanium dioxide nanoparticles in molten salt phase for thermal energy storage and heat-transfer fluid applications. J Nanopart Res 18, 150 (2016). https://doi.org/10.1007/s11051-016-3460-8