The phases obtained in copper aluminum bronze alloy (Cu – 10 wt.% Al – 2 wt.% Fe) cast into a permanent die were investigated. The parameters examined were the preheating temperatures of the die and the graphite coating thickness. The phases α and γ2 were detected as well as the metastable phases β′ and γ′. The intermetallics of the system Fe – Al were obtained in various stoichiometric compositions. The different cooling rates of the casting resulted in two mechanisms of transformation to α grains out of the unstable β phase, one being nucleation and growth producing needle-shaped α grains, the other exhibiting a massive transformation to spherical α grains. These two mechanisms determine the changes in the size of the α grains as a result of changes in the cooling rate in its various ranges.
Similar content being viewed by others
References
I. Cenoz and J. Fernandez, Rev. Met. Madrid, 43, 272 – 283 (2007).
V. Callcut, Metallurgy of Copper and Copper Alloys, Aluminium Bronze, Part 1, The Copper Page Innovations, The Copper Development Association Inc., USA (2002), pp. 3 – 6.
C. M. Friend, Scr. Metall., 23, 1.817 – 1.820 (1989).
W. S. Li, Z. P. Wang, Y. Lu, Y. H. Jin, L. H. Yuan, and F. Wang, Wear, 261, 155 – 163 (2006).
M. Kaplan and A. K. Yildiz, Mater. Lett., 57, 4.402 – 4.411 (2003).
A. Al-Hashem andW. Riad, Mater. Caracter., 48, 37 – 41 (2002).
M. Eddahbi and O. A. Ruano, Rev. Met. Madrid, 41, 251 – 257 (2005).
A. Monsalve and R. Morales, Rev. Met. Madrid, 40, 431 – 435 (2004).
E. Van Der Heide, E. D. Stam, H. Giraud, G. Lovato, N. Akdut, F. Clarysse, P. Caenen, and E. I. Heikillä, Wear, 261, 68 – 71 (2006).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 6, pp. 10 – 14, June, 2011.
Rights and permissions
About this article
Cite this article
Cenoz, I., Gutierrez, M. Phase transformations in Cu – Al alloy. Met Sci Heat Treat 53, 265–269 (2011). https://doi.org/10.1007/s11041-011-9380-4
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11041-011-9380-4