The structure has been examined of austenite-ferrite steel 03Kh14N10K5M2Yu2T after laser processing with melting by the use of transmission electron microscopy. The causes have been established for the anomalously high hardness of the surface layer.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Yu. V. Kal’ner, “Crystal structure and low-temperature decomposition of carbon-bearing martensite obtained by laser quenching,” Metalloved. Term. Obrab. Met., No. 4, 50–55 (1988).
M. L. Bernshtein, S. D. Prokoshkin, M. N. Kryakina, et al., “The structure of martensite after laser steel quenching,” Fiz. Met. Metalloved., 65(4), 790–795 (1988).
V. M. Schastlivtsev, T. I. Tabatchikova, I. L. Yakovleva, and A. L. Osintseva, “Hardening of martensite-ageing steels after laser treatment,” Fiz. Met. Metalloved., 105(1), 138–145 (1994).
S. V. Grachev, L. A. Mal’tseva, and T. V. Mal’tseva, “RF Patent No. 2116373, IPC C 22 C 38/52, A two-phase austenite-ferrite steel,” Submitted April 10, 1994, Published July 27, 1998, Byull. Izobr. Polezn. Modeli, No. 21, 6 (1998).
S. V. Grachev, L. A. Mal’tseva, and T. V. Mal’tseva, “Laser processing for surface hardening of austenite-ferrite steel,” Neft’ Gaz, No. 3, 77–81 (2005).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 6, pp. 33–37, June, 2009.
Rights and permissions
About this article
Cite this article
Nemirovskii, Y.R., Khadyev, M.S., Mal’tseva, L.A. et al. Structure of 03KH14N10K5M2YU2T steel after laser treatment. Met Sci Heat Treat 51, 297 (2009). https://doi.org/10.1007/s11041-009-9158-0
Published:
DOI: https://doi.org/10.1007/s11041-009-9158-0