Effect of fungal decay on the hygroscopic thickness swelling rate of lignocellulosic filler-polyolefin biocomposites

  • Published:
Mechanics of Composite Materials Aims and scope

The influence of fungal decay on the hygroscopic thickness swelling rate of lignocellulosic filler-polyolefin biocomposites has been investigated. Composites based on polypropylene (PP), bagasse fiber (BF), and a coupling agent (PP-g-MA) were made by melt compounding and injection molding. The weigt ratio of BF to PP was controlled at 60/40 for all blends. The amount of coupling agent was fixed at 2% for all formulations. The samples obtained were exposed to the action of brown-rot (Coniophora puteana) and white-rot (Trametes versicolor) fungi for 8, 12, and 16 weeks according to the Kolle–flask method. The thickness swelling of the samples was evaluated by immersing them in water at room temperature for several weeks. The morphology of the composites was characterized using the scanning electron microscopy (SEM). The results indicated that the fungal decay had an adverse affect on the dimensional stability of BF/PP composites due to an increase in the thickness swelling rate. The thickness swelling of white-rotted samples was higher than that of brown-rotted ones and control samples. Also, the thickness swelling of BF/PP composites increased with increasing time of fungal decay. In addition, after 16 weeks of exposure to white-rot fungi, the composites exhibited a higher parameter of swelling rate K SR than control samples. The K SR of the composites was influenced both by the type of rooting and the exposure time. Furthermore, the SEM micrographs showed that the extent of degradation increased with growing exposure time to fungi.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2

Similar content being viewed by others

References

  1. A. K Bledzki and J Gassan, “Composites reinforced with cellulose based fibers,” J. Polym. Sci., 24, 221-274 (1999).

    Google Scholar 

  2. R. M. Rowell, A. R. Sandi, D. F. Gatenholm, and R. E. Jacobson, “Utilization of natural fibers in plastic composites: Problem and opportunities in lignocellulosic composites,” J. Compos. Mater. 18, 23-51 (1997).

    Google Scholar 

  3. K. Oksman and M. Sain, Wood-Polymer Composites, Woodhead Publ. Ltd, Great Abington, Cambridge, UK, 2008.

    Book  Google Scholar 

  4. A. Nourbakhsh and M. Kouhpayehzadeh, “Mechanical properties and water absorption of fiber-reinforced polypropylene composites prepared by bagasse and beech fiber, J. Appl. Polym. Sci., 114, 653-657 (2009).

    Article  Google Scholar 

  5. B. Kord, “Effects of compatibilizer and nanolayered silicate on physical and mechanical properties of PP/bagasse composites,” Turk. Agric. For., 36, 510-517 (2012).

    Google Scholar 

  6. S. M. Zabihzadeh, “Flexural properties and orthotropic swelling behavior of baggase/thermoplastic composites,” Biores, 5, No. 2, 650-660 (2010).

    Google Scholar 

  7. C. Clemons, R. A. Young, and R. M. Rowell, “Moisture sorption properties of composite boards from etherified aspen fiber,” Wood Fiber Sci., 24, No. 3, 353-363 (1992).

    Google Scholar 

  8. P. A. Cooper, “Rate of swelling of vacuum impregnated wood,” Wood Fiber Sci., 28, No. 1, 28-38 (1996).

    Google Scholar 

  9. S. Q. Shi and D. J. Gardner, “Hygroscopic thickness swelling rate of compression molded wood fiberboard and wood fiber/polymer composites,” Composites: Pt A, 37, 1276-1285 (2006).

    Google Scholar 

  10. W. D. Ellis, “Moisture sorption and swelling of wood-polymer composites,” Wood Fiber Sci., 26, No. 3, 333-341 (1994).

    Google Scholar 

  11. S. Mishra, J. B. Naik, and Y. P. Patil, “Studies on swelling properties of wood polymer composites based on agrowaste and novolac,” J. Adv. Polym. Technol., 23, No. 1, 46-50 (2004).

    Google Scholar 

  12. R. E. Ibach, C. M. Clemons, and R. L. Schumann, Wood-plastic composites with reduced moisture: Effects of chemical modification on durability in the laboratory and field,” 9th Int. Conf. on Wood and Bio-fiber Plastic Composites, 2007, Madison, Wisconsin, USA

  13. E. Nadali, A. Karimi, M. Tajvidi, and R. Naghdi, “Natural durability of a bagasse fiber/polypropylene composite exposed to rainbow fungus (coriolus versicolor),” J. Reinf. Plas. Compos., 29, No, 7, 1028-1037 (2010).

    Article  Google Scholar 

  14. S. A. Varhey and P. E. Lakes, “Fungal resistance of wood fiber/thermoplastic composites, enhancing the durability of lumber and engineered wood product,” Orlando, Florida, USA (2002).

  15. A. Karimi, M. Tajvidi, and S. Pourabbasi, “Effect of compatibilizer on the natural durability of wood flour/high density polyethylene composites against the rainbow fungus (coriolus versicolor),” Polym. Compos., 28, 273-277 (2007).

    Article  Google Scholar 

  16. S. M. Zabihzadeh, S. K. Hosseini Hashemi, H. Mehregan Nikoo, and S. M. J. Sepidehdam, “Influence of fungal decay on physico-mechanical properties of a commercial extruded bagasse/PP composite,” J. Reinf. Plas. Compos., 29, No. 11, 1750-1756 (2010).

    Article  Google Scholar 

  17. K. Hosseini Hashemi, M. Modirzare, V. Safdari, and B. Kord, Decay resistance, hardness, water absorption, and thickness swelling of a bagasse fiber/plastic composite,” Biores 6, No. 3, 3289-3299 (2011).

    Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Assistent Professor, Department of Paper and Packaging Technology, Faculty of Chemistry and Petrochemical Engineering, Standard Research Institute (SRI), Karaj, P.O. Box: 31745-139, Iran

    B. Kord

  2. Department of Wood Science and Paper Technology, Karaj Branch, Islamic Azad University, Karaj, Iran

    S. Kh. Hosseinihashemi

Authors
  1. B. Kord
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. S. Kh. Hosseinihashemi
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to B. Kord.

Additional information

Russian translation published in Mekhanika Kompozitnykh Materialov, Vol. 49, No. 6, pp. 1029-1040 , November-December, 2013.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Kord, B., Hosseinihashemi, S.K. Effect of fungal decay on the hygroscopic thickness swelling rate of lignocellulosic filler-polyolefin biocomposites. Mech Compos Mater 49, 691–698 (2014). https://doi.org/10.1007/s11029-013-9386-7

Download citation

  • Received:

  • Revised:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11029-013-9386-7

Keywords

Search

Navigation