Microstructural Features of Low-Alloy Pipeline Steels that Determine Impact Strength of Welded Joint Heat-Affected Zone

  • Published:
Metallurgist Aims and scope

Microstructural mechanisms reducing the impact strength values of a coarse grained heat-affected zone are studied for two K60 microalloyed steels. Research is conducted on specimens subjected to simulation of a heat-affected zone. The microstructure and fracture surface are studied using scanning electron microscopy and backscattered electron diffraction. It is shown that titanium nitride inclusions have the greatest influence on impact strength of the heat-affected zone whose cleavage within large bainite packages may cause macro-brittle specimen fracture. The risk of such non-metallic inclusions depends on the their structural features. In particular, presence of aluminum oxide and calcium sulfide blocking contact of the ferritic matrix with nitride leads to an increase in cleavage stress and hinders macroscopic brittle fracture in the early stages of impact bending.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1.
Fig. 2.
Fig. 3.
Fig. 4.
Fig. 5.
Fig. 6.
Fig. 7.
Fig. 8.
Fig. 9.
Fig. 10.
Fig. 11.
Fig. 12.

Similar content being viewed by others

References

  1. I. Grivnyak, Steel Weldability [in Russian], Mashinostroenie, Moscow (1984).

    Google Scholar 

  2. N. E. Hannerz and B. M. Jonsson-Holmquist, “Influence of vanadium on the heat-affected-zone properties of mild steel,” Metal Science, 8, No. 1, 228–234 (1974).

  3. N. E. Hannerz, “Effect of Nb on HAZ ductility in constructional HT steels,” Welding Journal, 54, No. 5, 162 (1975).

  4. F. Fang, et al., “Microstructure and precipitation behavior in HAZ of V and Ti microalloyed steel,” J. of Iron and Steel Research Intern., 16, No. 3, 68–77 (2009).

    Article  CAS  Google Scholar 

  5. H. Ikawa, H. Oshige, and T. Tanoue, “Effect of martensite–austenite constituent on HAZ toughness of a high strength steel,” Transactions of the Japan Welding Society, 11, No. 2, 87–96 (1980).

  6. X. Li, et al., “Influence of prior austenite grain size on martensite–austenite constituent and toughness in the heat affected zone of 700 MPa high strength linepipe steel,” Materials Sci. and Eng.: A, 616, 141–147 (2014).

  7. A. Lambert, et al., “Microstructure of martensite–austenite constituents in heat affected zones of high strength low alloy steel welds in relation to toughness properties,” Science and Technology of Welding and Joining, 5, No. 3, 168–173 (2000).

  8. X. Li, et al., “Influence of martensite–austenite constituents formed at different intercritical temperatures on toughness,” Materials & Design, 67, 457–463 (2015).

    Article  CAS  Google Scholar 

  9. M. Mandal, et al., Mechanical Behaviour of Intercritically Reheated Coarse-Grained Heat Affected Zone in High Strength Line Pipe Steels, Int. Pipeline Conference. – American Society of Mechanical Eng. (2018).

  10. I. Kim, et al., “Effect of martensite–austenite constituent on low-temperature toughness in YS 500 MPa grade steel welds,” Metals, 8, No. 8, 638–649 (2018).

  11. L. Lan, et al., “Analysis of martensite–austenite constituent and its effect on toughness in submerged arc welded joint of low carbon bainitic steel,” J. of Mater. Sci., 47, No. 11, 4732–4742 (2012).

    Article  CAS  Google Scholar 

  12. K. Ohya, et al., “Microstructures relevant to brittle fracture initiation at the heat-affected zone of weldment of a low carbon steel,” Metallurgical and Materials Transactions A, 27, No. 9, 2574–2582 (1996).

  13. S. G. Lee, et al., “Effects of martensite–austenite constituent on crack initiation and propagation in inter-critical heat-affected zone of high-strength low-alloy (HSLA) steel,” Mater. Sci. and Eng.: A, 715, 332–339 (2018).

  14. Y. Li and T. N. Baker, “Effect of morphology of martensite–austenite phase on fracture of weld heat affected zone in vanadium and niobium microalloyed steels,” Mater. Sci. and Techn., 26, No. 9, 1029–1040 (2010).

    Article  CAS  Google Scholar 

  15. D. P. Fairchild, D. G. Howden, and W. A. T. Clark, “The mechanism of brittle fracture in a microalloyed steel: Part I. Inclusioninduced cleavage,” Metallurgical and Mater. Transactions A, 31, No. 3, 641–652 (2000).

    Article  Google Scholar 

  16. L. P. Zhang, C. L. Davis, and M. Strangwood, “Effect of TiN particles and microstructure on fracture toughness in simulated heataffected zones of a structural steel,” Metallurgical and Materials Transactions A, 30, No. 8, 2089–2096 (1999).

  17. W.W. Xu, et al., “Effect of welding heat input on simulated HAZ microstructure and toughness of a VN microalloyed steel,” J. of Iron and Steel Research, Int., 14, No. 5, 234–239 (2007).

  18. P. P. Stepanov, V. N. Zikeev, L. I. Éfron, I. I. Frantov, and Yu. D. Morozov, “Increase in steel weldability for thick-walled gas pipelines of considerable diameter by optimizing chemical composition,” Metallurg, No. 11, 62–67 (2010).

  19. S. Subramanian, L. Collins, Ch. Myao, I. Yan, and Ch. Shan, “Use of a DOE method in studying high-angle boundaries for combatting pipe steel brittle failure microalloyed with niobium,” in: Mater. Internat. Conf. “Production Testing and Practical Use of Large Diameter Pipes of Strength Categories X80-X90,” Moscow (2012), pp. 44–54.

  20. K. G. Vorkachev, P. P. Stepanov, L. I. Éfron, M. M. Kantor, A. V. Chastukhin, and S. V. Zharkov, “Effect of microstructure on the ductility of welded joints of high-strength low-alloy steels with simulation of a coarse-grained region of the heat-affected zone,” Metallurg, No. 9, 90–97 (2020).

  21. M. M. Kantor and V. A. Bozhenov, “Scatter of impact strength values for low-alloy steel in the critical cold brittleness range,” Materialoved., No. 11, 3–14 (2013).

  22. A. Martin-Meizoso, et al., “Modelling cleavage fracture of bainitic steels,” Acta Metallurgica et Materialia, 42, No. 6, 2057–2068 (1994).

  23. M. A. Tkachuk, et al., “Effect of alloying with molybdenum and chromium on the structure and properties of low-carbon pipe steel,” Metallurg, No. 10, 42–50 (2019).

    Google Scholar 

  24. H. Mohrbacher, “Metallurgical effects of niobium and molybdenum on heat-affected zone toughness in low-carbon steel,” Applied Sciences, 9, No. 9, 1847 (2019).

  25. E. Gudremon, Special Steels [in Russian], Vol. 2, Metallurgiya, Moscow (1966).

  26. H. Bhadeshia and L. E. Svensson, “Modelling the evolution of microstructure in steel weld metal,” Mathematical Modelling of Weld Phenomena, 1, 109–182 (1993).

    Google Scholar 

  27. V. Descotes, et al., “Modeling the titanium nitride (TiN) germination and growth during the solidification of a maraging steel,” in: Proceedings of the 2013 International Symp. on Liquid Metal Processing & Casting, Springer, Cham, (2013).

  28. B. Li, et al., “Study on precipitation and growth of TiN in GCr15 bearing steel during solidification,” Materials, 12, No. 9, 1463 (2019).

  29. M. Pudar, et al., “Computational analysis of precipitation during continuous casting of microalloyed steel,” Steel Research International, 81, No. 5, 372–380 (2010).

  30. C. Capurro and C. Cicutti, “Analysis of titanium nitrides precipitated during medium carbon steels solidification,” J. of Mater. Research and Technology, 7, No. 3, 342–349 (2018).

    Article  CAS  Google Scholar 

  31. J. Stock, et al., “Cooling rate effects on the as-cast titanium nitride precipitation size distribution in a low-carbon steel,” AIST Transaction, 11, No. 4, 180 (2014).

  32. J. Kunze, et al., “Precipitation of titanium nitride in low–alloyed steel during cooling and deformation,” Steel Research, 68, No. 10, 441–449 (1997).

Download references

Author information

Authors and Affiliations

  1. A. A. Baikov Institute of Metallurgy and Materials Science, Russian Academy of Sciences, Moscow, Russia

    V. V. Sudin, V. A. Bozhenov & M. M. Kantor

  2. AO Vyksa Metallurgical Plant, Vyksa, Russia

    P. P. Stepanov, L. E. Efron, S. V. Zharkov, A. V. Chastukhin & D. A. Ringinen

Authors
  1. V. V. Sudin
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. P. P. Stepanov
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. V. A. Bozhenov
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. M. M. Kantor
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. L. E. Efron
    View author publications

    You can also search for this author in PubMed Google Scholar

  6. S. V. Zharkov
    View author publications

    You can also search for this author in PubMed Google Scholar

  7. A. V. Chastukhin
    View author publications

    You can also search for this author in PubMed Google Scholar

  8. D. A. Ringinen
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to V. V. Sudin.

Additional information

Translated from Metallurg, Vol. 65, No. 5, pp. 24–35, May, 2021. Russian DOI: 10.52351/00260827_2021_05_24.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Sudin, V.V., Stepanov, P.P., Bozhenov, V.A. et al. Microstructural Features of Low-Alloy Pipeline Steels that Determine Impact Strength of Welded Joint Heat-Affected Zone. Metallurgist 65, 500–516 (2021). https://doi.org/10.1007/s11015-021-01184-z

Download citation

  • Received:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11015-021-01184-z

Keywords

Search

Navigation