This article examines questions related to aspects of the production of castings of magnesium alloys in molds made by volumetric stamping without the use of the corresponding tooling. Information is presented on features of the gating-feeding systems used to obtain magnesium-alloy castings in molds made by volumetric stamping. Also examined are features of the effect of small additions of calcium on the susceptibility of alloys of type ML5 to oxidation during casting in stamped molds. It is shown that the use of calcium in magnesium alloys of the system Mg–Al–Zn is promising for preventing their excessive oxidation.
Similar content being viewed by others
References
I. J. Polmear, Light Metals: From Traditional Alloys to Nanocrystals, Elsevier Ltd., England (2005).
J. F. Nie, “Magnesium alloys,” Scr. Mat., 48, 981–984 (2003).
M. Aljarrah, M. Medraj, X. Wanga, et al., “Experimental investigation of the Mg–Al–Ca system,” J. Alloys and Compounds, 436,, 131–141 (2007).
A. Suzuki, N. D. Saddock, J. W. Jones, and T. M. Pollock, “Solidification paths and eutectic intermetallic phases in Mg–Al–Ca ternary alloys,” Acta Mater., 53, 2823–2834 (2005).
L. L. Rokhlin and N. I. Nikitina, “Effect of calcium on the properties of alloys of the system Mg–Al,” Metalloved. Term. Obrab. Met., No. 5, 14–17 (2003).
L. L. Rokhlin, T. V. Dobatkina, N. I. Nikitina, et al., “Study of phase equilibria and decomposition of a supersaturated solid solution in magnesium alloys alloyed with aluminum, calcium, and manganese,” Metally, No. 4, 86–91 (2008).
J. C. Oh, T. Ohkubo, T. Mukai, and K. Hono, “TEM and 3DAP characterization of an age-hardened Mg–Ca–Zn alloy,” Scr. Mat., 53, 675–679 (2005).
Author information
Authors and Affiliations
Corresponding author
Additional information
Translated from Metallurg, No. 5, pp. 67–70, May, 2010.
Rights and permissions
About this article
Cite this article
Belov, V.D., Koltygin, A.V., Belov, N.A. et al. Innovations in cast magnesium alloys. Metallurgist 54, 317–321 (2010). https://doi.org/10.1007/s11015-010-9313-2
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11015-010-9313-2