Abstract
The dynamic mechanical analysis storage and loss modulus of a NIST SRM 8456 Ultra High Molecular Weight Polyethylene is determined in 3-point bending in an interlaboratory test. Mean values of (1.18 ± 0.17) GPa for storage modulus and (62.0 ± 9.0) MPa for loss modulus were determined at 21 °C. In addition, the temperature (molecular) spectrum for the material is observed between −100 and +100 °C. These results permit the use of this material for calibration, conformance, and performance demonstration for dynamic mechanical analyzers.
Similar content being viewed by others
References
B31.5a. Refrigeration piping. New York NY: American Society of Mechanical Engineers; 1992. p. 45.
Perry RH, Green DW, Maloney JO. Perry’s chemical engineers’ handbook. New York, NY: McGraw-Hill; 1984. p. 6–92.
D638-02. Test method for tensile properties of plastics. Annual book of ASTM standards, vol 08.01. West Conshohocken PA: ASTM International (ASTM).
E2254-08. Test method for storage modulus calibration of dynamic mechanical analyzers. Annual book of ASTM standards, vol 14.02. West Conshohocken PA: ASTM International (ASTM).
E2425-06. Test method for loss modulus conformance of dynamic mechanical analyzers. Annual book of ASTM standards, vol 14.02. West Conshohocken PA: ASTM International (ASTM).
E691-09. Practice for conducting an interlaboratory study to determine the precision of a test method. Annual book of ASTM standards, vol 14.02. West Conshohocken PA: ASTM International (ASTM).
E1970-06. Practice for statistical treatment of thermoanalytical data. Annual book of ASTM standards, vol 14.02. West Conshohocken PA: ASTM International (ASTM).
SRM8456. Report of investigation for reference material SRM 8456. Gaithersburg MD: National Institute of Standards and Technology; 2008.
E1142-07. Terminology relating to thermophysical properties. Annual book of ASTM standards, vol 14.02. West Conshohocken PA: ASTM International (ASTM).
Khanna YP, Turi EA, Taylor TJ, Vickroy VV, Abbot RF. Dynamic mechanical relaxations in polyethylene. Macromolecules. 1985;18(6):1302–9.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Blaine, R. Dynamic mechanical properties of an ultra high molecular weight polyethylene reference material SRM 8456. J Therm Anal Calorim 109, 1111–1115 (2012). https://doi.org/10.1007/s10973-012-2358-7
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10973-012-2358-7