Changes in curing behaviour of aminoresins during storage

Summary

The curing behaviour of commercial UF and MUF resins, stored at room temperature nearly up to gelation, is studied by simultaneous TG-DTA technique and structural changes of resins are also followed during aging. On the basis of ¹³C NMR spectra, the main chemical reaction during UF resin storage is the formation of methylenes and dimethylene ethers linked to secondary amino groups. Aging of resins results in a decrease of cure rate which is related to lower concentration of active functional groups and decrease in molecular mobility. On DTA curve, the resin with higher content of methylol groups reveals the curing exotherm earlier. With decreasing methylol content during storage, the peak maximum of exotherm is shifted to higher temperature value. Advanced polycondensation and sedimentation processes during storage produce partly locked in macromolecule structure water, and the water evaporation endotherm on DTA curve shifts to considerably higher temperature. The aged MUF resins are chemically less changed than UF resins and the aging process mainly involves noncovalent network formation due to complex molecular structure.