Abstract
CoPt nanoparticles with various Ag contents were synthesized by sol–gel technique. L10 CoPt alloy phase was formed after annealing at 700 °C. The coercivity (Hc) increased when the Ag content increased from 0 to 15 at.%. And Hc decreased when the Ag content was over 15 at.%. A certain amount of Ag could enhance the ordering degree of CoPt nanoparticles and improve the magnetic properties. When the Ag addition was more than 15 at.%, the deteriorated magnetic properties were ascribed to the decrease of ordering degree.
Similar content being viewed by others
References
Ersen O, Goyhenex C, Pierron-Bohnes V (2008) Phys Rev B 78:035429
Zhang YJ, Yang YT, Liu Y, Wang YX, Yang LL, Wei MB, Fan HG, Zhai HJ, Liu XY, Liu YQ, Yang NN, Wu YH, Yang JH (2011) J Phys D Appl Phys 44:295003
Wang Y, Yuan R, Chai YQ, Yuan YL, Bai LJ, Liao YH (2011) Biosens Bioelectron 30:61–66
Sun S, Murray CB, Weller D, Folks L, Moser A (2000) Science 287:1989
Qin LJ, Zhang YH, Huang SP, Tian HP, Wang P (2010) Phys Rev B 82:075413
Xiong LF, Manthiram A (2004) J Mater Chem 14:1454–1460
Mandal M, Das B, Mandal K (2009) J Colloid Interface Sci 335:40–43
Calvo F, Mottet C (2011) Phys Rev B 84:035409
Abes M, Rastei MV, Venuat J, Carvalho A, Boukari S, Beaurepaire E, Panissod P, Dinia A, Bucher JP, Pierron-Bohnes V (2009) J Appl Phys 105:113916
Liu XB, Altounian Z (2011) J Appl Phys 109:07B762
Liu Y, Yang YT, Zhang YJ, Wang YX, Zhang XL, Jiang YH, Wei MB, Liu YQ, Liu XY, Yang JH (2013) Mater Res Bull 48:721–724
Sehdev N, Medwal R, Annapoorni S (2011) J Appl Phys 110:033901
Yu M, Liu Y, Moser A, Weller D, Sellmeyer DJ (1999) Appl Phys Lett 75:3992
Ahmed E, Takahashi M, Iwasaki H, Ohshima KI (2009) J Alloys Compd 473:1–4
Hsu CW, Chen SK, Liao WM, Yuan FT, Chang WC, Tsai JL (2008) J Alloys Compd 449:52–55
Dvorak J, Idzerd YU, Ogale SB, Shinde S, Wu T, Venkatesan T, Godfrey R, Ramesh R (2005) J Appl Phys 97:10C102
Castaldi L, Giannakopoulos K, Travlos A, Niarchos D, Boukari S, Beaurepaire E (2005) J Magn Magn Mater 290–291:544
Tang RJ, Zhang WL, Li YR (2010) J Alloys Compd 496:380–384
Seto T, Koga K, Takano F, Akinaga H, Orii T, Hirasawa M, Murayama M (2007) J Phys: Conf Ser 59:255
Tomou A, Panagiotopoulos I, Gournis D, Kooi B (2007) J Appl Phys 102:023910
Wang H, Xue SX, Yang FJ, Wang HB, Cao X, Wang JA, Gao Y, Huang ZB, Yang CP, Cheung WY, Wong SP, Li Q, Li ZY (2006) Thin Solid Films 505:77–80
Maeda T, Kai T, Kikitsu A, Nagase T, Akiyama JI (2002) Appl Phys Lett 80:2147
Yamaguchi H, Kitakami O, Okamoto S, Shimada Y, Oikawa K, Fukamichi K (2001) Appl Phys Lett 79:2001
Wang YX, Zhang XL, Liu Y, Jiang YH, Zhang YJ, Wang JS, Liu YQ, Liu HL, Sun YF, Beach GSD, Yang JH (2012) J Phys D Appl Phys 45:485001
Sehdev N, Medwal R, Annapooni S (2012) J Alloys Compd 522:85–89
Caporaletti O, Graham GM (1980) J Magn Magn Mater 22:25–34
Kong H, Jang J (2006) Chem Commun 28:3010–3012
Acknowledgments
This work is supported by Program for New Century Excellent Talents in University (NCET-09-0156 and NCET-11-0981) and Program for the development of Science and Technology of Jilin province (201201083 and 20140519003JH), the Twentieth Five-Year Program for Science and Technology of Education Department of Jilin Province (20110156), and Program for the master students’ scientific and innovative research of Jilin Normal University (201109).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wang, Y., Zhang, X., Liu, Y. et al. Microstructure and magnetic properties of L10 CoPt nanoparticles by Ag addition. J Sol-Gel Sci Technol 70, 528–533 (2014). https://doi.org/10.1007/s10971-014-3318-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10971-014-3318-4