Abstract
In present paper the equilibrium of cobalt extraction with 1-(2-pyridyl)tridecan-1-one oxime from the chloride/sulphate solutions was studied. The presented results indicated that extraction depends on a number of process variables, including the pH, metal and Cl− concentration in the aqueous feed, and concentration of the oxime in the organic phase. The created cobalt-complexes with the 2-pyridine ketoxime were stable and only concentrated HCl was found to be a suitable stripping agent for coordinated metal. The separation of Co(II) from Zn(II), Ni(II) and Cu(II) was also studied, but the selective recovery of the metals was possible using the multi-stage stripping process.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Cobalt is a strategic and critical metal, which is used in many branches of industry e.g. as a component in superalloys, as a binder for tungsten carbide cutting tools, as pigments in glass, ceramics and paints, as catalysts in the petroleum industry and as an additive to Ni-metal hydride battery [1]. Those unique properties insure that the demand for cobalt will grow, therefore, its efficient recovery from poor primary sources is the most important goal to achieve.
Chloride leaching process using HCl is one of the most effective recovery route of cobalt from ore, concentrates and other primary sources, but, an optimisation of cobalt recovery, which related with a process selectivity and its less environmental influences led to develop the less aggressive leaching systems based on chloride salts or chloride/sulphate mixture [2–4]. Hybrid hydrochloric–sulphuric acidic leaching of a laterite ore has been proposed by Intec Limited and in this concept H2SO4 was used to regenerate HCl—a main leaching agent. Unfortunately, this process was not as effective as the chloride-circuits, but the observed effects led to continue of the studies [4]. A different hybrid process operates in a mixed chloride–sulphate magnesium brine system has been proposed by Anglo Research Nickel process (ARNi process) [5, 6]. In this concept decoupling reagents’ regeneration is promoted by utilising lowered solubility of magnesium sulphate in magnesium chloride solution and as a consequence, the resulting hydrochloric acid acts as the main circulating leach agent. Cominco Engineering Services Limited has also proposed chloride–sulphate leaching process, but the recovery of metals such as nickel, copper and cobalt from ore has been investigated using an acidic solution containing halide and sulphate ions in the presence of oxygen [7].
The pregnant solutions obtained in the chloride–sulphate leaching processes should be treated to selective separation of all dissolved payable metals in further stages. Solvent extraction is a process in which valuable metals are separated from worthless or other valuable metals, however, in case of cobalt extraction a lot of researchers have focused on an extraction and separation of cobalt from other metals from sulphate, ammonia or chloride solutions. In case of the mixed sulphate/chloride solutions, only NaPC-88A was studied as a potential selective extractant of cobalt(II) and nickel(II), but the selectivity of the process depended on the pH and the extractant’s concentration [8].
Over the last few years the extraction of metals ions from different aqueous solutions by hydrophobic 2-, 3- and 4-pyridylketoximes has been widely investigated. Especially, oxime of 1-(2-pyridyl)tridecan-1-one has shown good extraction abilities towards all studied metals copper(II), zinc(II), cadmium(II) and iron(III) ions from chloride and chloride/ammonia solutions [9–15], as well as copper(II) and nickel(II) ions from solutions containing both chloride and sulphate salts [16, 17]. Recent studies have also indicated the possibility to apply the oxime of 1-(2-pyridyl)tridecan-1-one for a separation of cobalt from nickel sulphate solution [18], but so far, the most efficient extraction of cobalt(II) ions using this oxime has been achieved only from the chloride/nitrate solution [19]. It has been assumed that the addition of chloride ions to cobalt sulphate solution should improve the extraction efficiency by oxime of 1-(2-pyridyl)tridecan-1-one, and also change the complexation mechanism. Therefore, in the present work, an extraction of cobalt(II) ions from the aqueous feed solutions containing both chloride and sulphate ions by oxime of 1-(2-pyridyl)tridecan-1-one was selected for a detailed analysis.
Experimental
Reagents
All reagents used in this study were of a reagent grade. Toluene (≥99.5 %, POCH, Poland) and decan-1-ol (≥98 %, Merck, Germany) were used as components of the organic phase. Sodium chloride (p.a., Chempur, Poland), hydrochloric acid (37 %) (p.a., POCH, Poland), sulphuric acid (p.a., POCH, Poland), cobalt(II) sulphate (heptahydrate) (p.a., Sigma-Aldrich, Germany) were used to compose the aqueous phase.
The oxime of 1-(2-pyridyl)tridecan-1-one (Fig. 1) was synthesised according procedure described in previous paper [9]: 1H NMR (400 MHz; CDCl3) δ (ppm): 9.53 (s, 1H, OH); 8.62 [m, 1H, Hpy(6)]; 7.83 [dd, 1H, Hpy(3), J = 11 and 7.8 Hz]; 7.69 [td, 1H, Hpy(4), J = 7.6 and 1.6 Hz]; 7.29 [ddd, 1H, Hpy(5), J = 1.1, 4.8 and 7.4 Hz]; 2.99 (t, 2H, CH2); 1.58 (q, 2H, CH2); 1.27–1.29 (m, 18H, CH2); 0.90 (t, 3H, CH3); 13C NMR (100 MHz; CDCl3) δ (ppm): 160.7; 154.0; 149.0; 136.3; 123.5; 120.9; 32.8; 31.9; 29.9; 29.7; 29.6; 29.4; 29.3; 29.1; 26.2; 25.6; 22.7; 14.1; LC-ESI/MS m/z (%): 291.2 (100) (MH)+; 274.0 (6.9); 256.2 (2.8); 235.4 (2.2); 179.0 (7.3); 161.2 (9.7); 151 (5.3); 133 (4.9); 79.2 (3.47); 52.2 (6.9).
Extraction procedure
Basic extraction and stripping studies were carried out in a test tube using organic to aqueous phases volume ratio (O: A) equal to 1. Both phases were shaken at room temperature (21–23 °C) using an orbital shaker Bio-mix BWR 04 and then separated in a separating funnel. Each experiment was carried out at least in duplicates, and the results agreed within 3–4 %. Aqueous feed solutions were prepared by dissolving the appropriate amounts of CoSO4 (heptahydrate, Sigma-Aldrich, Germany), Na2SO4 (POCH, Poland) and NaCl (POCH, Poland) in ultrapure water. The pH of aqueous solutions was adjusted to a desired value by adding 2 % H2SO4 (POCH, Poland) solution using combined glass pH electrode DG111-SC (T50 Titrator, Mettler Toledo). Toluene (Sigma-Aldrich, Germany) with 10 % (v/v) addition of decan-1-ol (Sigma-Aldrich, Germany) was used as an organic diluents [toluene with 10 % (v/v) decan-1-ol were chose because, they were not creating emulsion. This opportunity was used to faster separation two phases]. All reagents used in this study were of reagent purity grade.
Calculation
The metal content in the organic phase was determined by a mass balance between the concentration of the metal in the aqueous phase before and after the extraction. Distribution coefficient D was calculated from the following equation:
where [Co]aq and [Co]org are the cobalt(II) ions concentration after the extraction in the aqueous and organic phases. The estimation of cobalt complexes composition in an organic phase, equilibrium constants of the extraction, as well as a speciation analysis of cobalt(II) in an aqueous chloride/sulphate solution required a calculation of ions activity \( a_{i} \).
where c i and γ i are the concentration and activity coefficient of the positive or negative ionic species, respectively.
The activity coefficients of each ion in the aqueous phase were calculated using the Bromley equation [20], which can be adopted to concentrated solutions (up to I = 6 mol/dm3):
where, for specific cation c and anion a, the term F i becomes:
where z c and z a represent cation and anion charge number, respectively. B ca represents the Bromley constant.
Result and discussions
Effect of shaking time
The effect of shaking time on the extraction of 0.01 mol/dm3 Co(II) from aqueous sulphate/chloride solution (0.5 mol/dm3 \( {\text{SO}}_{4}^{2-}\) and 1 mol/dm3 Cl−) using 0.1 mol/dm3 1-(2-pyridyl)tridecan-1-one oxime dissolved in toluene with 10 % (v/v) addition of decan-1-ol was investigated over the range 5–60 min. The results have clearly indicated that equilibration was reached after 10 min, but the 15 min shaking was selected to further studies.
Effect of pH
The effect of pH on the extraction of 0.01 mol/dm3 of Co(II) ions from chloride/sulphate aqueous solutions (0.5 mol/dm3 \( {\text{SO}}_{4}^{2-}\) and 1 mol/dm3 Cl−) using 0.1 mol/dm3 1-(2-pyridyl)tridecan-1-one oxime dissolved in toluene with 10 % (v/v) addition of decan-1-ol was studied over the pH range 0.25–5.5. Presented results have shown a linear dependence of the cobalt extraction and the pH of the aqueous feed (Fig. 2). This dependence is very clear in the range of pH 1–3, wherein the extraction increases linear from 71 to 91 %. Further increase of the pH does not affect the extraction and the efficiency is approximately 91–92 %. Very good extraction results are also observed at strong acidic range of the pH (below 1), but unfortunately during the metal extraction an emulsion is observed.
Effect of chloride ions concentration
The effect of chloride ions concentration was estimated for the aqueous solutions containing a variable chloride ions’ concentration (from 0 to 4 mol/dm3) and at a constant sulphate ions concentration (0.5 mol/dm3). The pH of the aqueous feed solutions was equal to 3.5 and 5.0. The extraction results show that, regardless the aqueous phase’s pH, the influence of the chloride ions concentration on cobalt ions’ extraction is the most visible at the initial range of Cl− concentration (example at pH 3.5 the extraction increases from 50 % for 0 mol/dm3 Cl− to 89 % for 1 mol/dm3 Cl−) and above 1 mol/dm3 Cl− the extraction stabilises enabling the metal recovery on the level of 90–92 % (Fig. 3). This relationships can be attributed to dominating cobalt-chloride species coordination, however, a diagram distribution of all of cobalt(II) species dissolved in chloride/sulphate aqueous feed eliminates this theory (Fig. 4). It has been found that cobalt(II) sulphate dominates, depending on the composition of aqueous solution, but the increasing concentration of chloride ions decreases cobalt(II) sulphate fraction in favour of mainly Co2+.
Effect of extractant concentration
The effect of the oxime concentration on the extraction of 0.01 mol/dm3 Co(II) from aqueous sulphate/chloride solution (0.5 mol/dm3 \( {\text{SO}}_{4}^{2-}\) and 1 mol/dm3 Cl−; pH = 0.5, 3.5 and 5) was studied with the varying 1-(2-pyridyl)tridecan-1-one oxime concentrations (0.01–0.2 mol/dm3).
During the extraction using the organic solutions containing from 0.01 to 0.05 mol/dm3 of the oxime, it has been observed that the extraction of cobalt(II) ions linear increases from 9.3 to 69.2 at pH 3.5 or from 5.1 to 63.4 % at pH 5 (Fig. 5). Further increase of the oxime concentration to a level above 0.08 mol/dm3 results of a maximum recovery of metal, which mainly depends on the pH of the aqueous phase: 99–93 % extraction of cobalt(II) ions at pH of 0.5, 87.5–90.4 % extraction at pH of 3.5 and 87.7–90.5 % extraction at pH of 5.
Effect of temperature
The influence of temperature on extraction of cobalt(II) ions from solutions containing 0.5 mol/dm3 \( {\text{SO}}_{4}^{2-}\) and different concentration of chloride ions (0.01–4 mol/dm3 Cl−) with 1-(2-pyridyl)tridecan-1-one oxime dissolved in toluene with 10 % addition of decan-1-ol was studied in the temperature range of 294–319 K. The experimental results showed that the extraction percentages were closely related to the composition of the aqueous phase (Fig. 6). It was observed that in case of the solutions containing 0.5 mol/dm3 \( {\text{SO}}_{4}^{2-}\) and 0.5 mol/dm3 Cl− with increasing temperature the extraction initially increased from 69.6 (294 K) to 78.6 % (296 K) and then slightly decreased to value 76.3 % (319 K), but in case of the solution containing 0.5 mol/dm3 \( {\text{SO}}_{4}^{2-}\) and 3 mol/dm3 Cl− the increasing temperature increased the extraction from 81.3 (299 K) to 98.9 % (319 K). The enthalpy of the cobalt extraction were also calculated and the results obtained from the slopes of the Van’t Hoff plots [21] indicated the endothermic nature of the extraction process from the solution containing 0.5 mol/dm3 \( {\text{SO}}_{4}^{2-}\) and 1.5 or 3 mol/dm3 Cl− (∆H = 17.23 and 108.14 kJ/mol, respectively), whereas the cobalt(II) extraction from solution containing 0.5 mol/dm3 \( {\text{SO}}_{4}^{2-}\) and 0.1 mol/dm3 Cl− was exothermic process (∆H = −41.13 kJ/mol).
Effect of cobalt(II) ions concentration
The effect of cobalt(II) ions concentration on the extraction was studied over the range of Co2+ 0.01–0.15 mol/dm3 at constant concentration sulphate ions (0.5 mol/dm3) and constant concentration chloride ions (1 or 3 mol/dm3). The pH of the aqueous feed solutions was equal to 5. The toluene with 10 % (v/v) addition of decan-1-ol of 1-(2-pyridyl)tridecan-1-one oxime (0.1 mol/dm3) was used as the organic phase.
The obtained data presented in Fig. 7, have shown that in case of the aqueous solutions containing 1 mol/dm3 Cl−, the amount of extracted cobalt(II) ions increases from 0.0088 to 0.0380 mol/dm3 along with the increase of initial cobalt(II) ions concentration from 0.010 to 0.044 mol/dm3. The shaking of the organic phase with the aqueous solutions containing Co2+ above 0.05 mol/dm3 results in an achieving of a maximum loading capacity of 0.048–0.050 mol/dm3.
A different relation has been observed for the aqueous feed solutions containing besides sulphate and cobalt(II) ions, 3 mol/dm3 Cl− (Fig. 7). It has been observed that in all studied range of cobalt(II) ions concentration, the amount of the extracted metal ions increases linearly even for the solution containing more than 0.1 mol/dm3 Co2+. This effect may be attributed to the coordination of cobalt-chloride species, which have a tendency to aggregation especially at higher concentrations of chloride solutions [19]. The molecular aggregate formed an association complex. Finally, this effect enables to achieve a higher oxime capacity 0.078 mol/dm3 Co(II) [0.78 mol of Co(II) per mol of the oxime].
In this study the extraction isotherms have been obtained by contacting at O:A = 1 or 2 an aqueous solution containing 0.085 mol/dm3 Co(II), 0.5 mol/dm3 \( {\text{SO}}_{4}^{2-}\) and 1 or 3 mol/dm3 Cl− with 0.1 mol/dm3 toluene/dekan-1-ol solution of the 2-pyridineketoxime. The McCabe–Thiele diagrams presented in Figs. 8, 9 and 10 have shown that, regardless the chloride ions concentration and the phases ratio, the full cobalt(II) extraction can be achieved in two counter current stages. That predicted theoretical numbers of stages have also been confirmed by simulation tests and the assay results showed that from 1 M chloride solution cobalt(II) ions can be quantitatively extracted at the phases ratio of 1 in two counter current stages (94.8 % extraction) or in one stage at the phases ratio O:A = 2 (89 % extraction). In case of the 3 M aqueous solution, one stage counter current extraction process enables 76 % metal recovery, but in two-stages extraction cobalt(II) is transferred to the organic phase in 99.2 %.
Stripping process
Our recent studies have indicated that 1-(2-pyridyl)tridecan-1-one oxime forms stable complexes with cobalt(II) ions especially in the presence of chloride ions and an effective re-extraction is possible at reducing conditions [19]. This knowledge enables to assume a comparably high stability of the complexes created in the studied chloride/sulphate mixture, therefore a stripping test has been carried out using an aqueous solution of HCl (10, 20 and 30 %) at 30 °C, at phase ratios of 1 and with addition or without a metallic reductant in either an inert atmosphere or air. The stripping test at inert conditions was carried out using argon as inert gas and in the first step of the experiment a loaded organic phase was first purged with argon to displace dissolved air. Next, 0.5 mmol of metallic cobalt as powder was inserted to the organic solution. The freshly prepared organic phases then were contacted for over 10 min with HCl solution. The results of the stripping experiments using a loaded organic solution containing 3.48 g Co+2/dm3 have been presented in the Table 1. The 20 % HCl in the presence of cobalt powder in argon atmosphere has been found to be the most effective stripping agent, which after 5 min of shaking at 30 °C strips 98.6 % of Co(II).
Mechanism of the complexation
2-Pyridineketoxime such as 1-(2-pyridyl)tridecan-1-one oxime can extract metal ions from the aqueous solutions through solvating mechanism or by forming a stable chelate, however, so specific organic extractant in many cases cannot form a clear one-type complex e.g. copper(II) ions are coordinated simultaneously by deprotonated oxygen of hydroxyimine group and by interaction with pyridine nitrogen. Similar solvating-chelate complexes seem to appear in case of cobalt(II) ions extraction: a coordination as a solvate enables extraction over a wide range of pH, but the coordination as a chelate (e.g. Co–O– bond results in a hydrogen cation release) enables a stable complex formation.
Based on these assumptions, the reactions of cobalt(II) ions complexation by 1-(2-pyridyl)tridecan-1-one oxime can be described as follows:
with
where
In this equation β i,x is an overall stability constant of ith cobalt(II) chloro-complexes or overall stability constant of cobalt(II) sulphate-complex (\( \beta_{{{\text{SO}}_{4}^{2 - } }} \)) (Table 2).
Taking account of the cobalt(II) ions complexation in the aqueous phase, the distribution ratio can be rewritten as follow:
and
or
On the basis of the above considerations, the analysis of extracted complexes stoichiometry can be carried out using a graphical method, wherein the experimental values of the distribution coefficients of cobalt(II) ions are presented as a function of equilibrium pH and ligand’s concentration.
Figure 11 illustrates the logarithmic plot of the cobalt(II) distribution coefficient \( \left( {{ \log }D + { \log }\left( {1 + \beta_{{{\text{SO}}_{4}^{2 - } }} \left[ {{\text{SO}}_{4}^{2 - } } \right] + \mathop \sum \nolimits_{i = 1}^{4} \beta_{{i,{\text{Cl}}^{ - } }} \left[ {{\text{Cl}}^{ - } } \right]^{i} } \right)} \right) \) versus equilibrium pH. According the equation, the slope of the straight line given in the pH range between 1 and 3 should be close to 1 or its multiple, but it was found to be 0.52. That suggests that cobalt(II) ions coordination is a result of a binuclear complex formation stabilised by intramolecular hydrogen bond O–H–O [22, 23]. This theory could be confirmed by the logarithmic plot of the cobalt(II) distribution coefficient for the binuclear complex (\( D = \frac{{ [ {\text{Co]}}_{\text{org}} }}{{\left[ {\text{Co}} \right]_{\text{aq}}^{2} }} \)) versus equilibrium pH. The linear plot presented in Fig. 12 gives a slope equal to 0.985 (R 2 = 0.990) which is in agreement that cobalt(II) ion complexation, as the binuclear complex resulted in one proton release to the aqueous phase. The protonation of the unbound ligand seems to be less possible in the studied range of pH, especially if the equilibrium pH decreases with the increase of the cobalt ions concentration in the organic phase.
The graph \( \left( {{ \log }D + { \log }\left( {1 + \beta_{{{\text{SO}}_{4}^{2 - } }} \left[ {{\text{SO}}_{4}^{2 - } } \right] + \mathop \sum \nolimits_{i = 1}^{4} \beta_{{i,{\text{Cl}}^{ - } }} \left[ {{\text{Cl}}^{ - } } \right]^{i} } \right)} \right) \) as a function of log[oxime] shows that at pH of 3.5 and 5 the slopes are close to 2 (1.976 and 2.127, respectively) thus suggesting a relationship of two molecules of the oxime with one molecule of Co(II) (Fig. 13).
A different stoichiometry has been observed in a strong acidic solution (pH = 0.5). This confirmed the formation of a different complex than in weak acidic conditions: the slope is equal to 2.997 and it suggests that three molecule of the oxime per cobalt molecule are involved in the coordination.
The role of the chloride ions concentration seems to correlate with cobalt-chloride species coordination, but looking at a speciation diagram (Fig. 4) a salts-out effect should mainly be taken into account. However, if chloride ions participate in the metal complexation, especially as balancer of complexes with positive charges, the reaction of the extraction can be expressed as:
with
therefore, the distribution ratio can be rewritten as follow:
and
but at different ionic strength the chloride ions concentration should be replaced by chloride ions activity \( a_{{{\text{Cl}}^{ - } }} = \left[ {{\text{Cl}}^{ - } } \right]\gamma_{{{\text{Cl}}^{ - } }} \).
According to above assumption a plot of \( { \log }D + { \log }\left( {1 + \beta_{{{\text{SO}}_{4}^{2 - } }} \left[ {{\text{SO}}_{4}^{2 - } } \right] + \mathop \sum \nolimits_{i = 1}^{4} \beta_{{i,{\text{Cl}}^{ - } }} \left[ {{\text{Cl}}^{ - } } \right]^{i} } \right) \) versus \( \log a_{{{\text{Cl}}^{ - } }} \) constructed from experimental data obtained at constant initial pH and at constant cobalt and the oxime concentration should give a straight line with the slope indicating the number of chloride molecules participating in the cobalt complexation. The presented in Fig. 14 data give a slope equal to 0.9178 (R 2 = 0.9974) and this means that cobalt(II) is probably coordinated by one molecule of the chloride. Thus, on the basis of the conducted graphical analysis, cobalt(II) ions at pH above 3 are transported into organic phase as a CoL(HL)Cl complex.
Competitive extraction of Co(II) over Cu(II), Zn(II) and Ni(II)
The competitive extraction of Co(II) from solutions containing 0.5 mol/dm3 \( {\text{SO}}_{4}^{2-}\), 0.01 mol/dm3 Co(II), Cu(II), Zn(II) and Ni(II) ions and different concentration of chloride ions (0.1 or 3 mol/dm3 Cl−) was studied with 1-(2-pyridyl)tridecan-1-one oxime dissolved in toluene with 10 % addition of decan-1-ol. The obtained values of percent extraction has shown (Fig. 15a) that at low chloride ions concentrations (up to 0.1 mol/dm3) the studied oxime can be used for a selective extraction of Co(II) over Zn(II) and Ni(II) (extraction below 3 %), whereas the co-extracted Cu(II) can be selectively stripped with an aqueous solutions containing oxalate ions [16]. Unfortunately, the selectivity of the extraction process was reduced by increasing chloride ions concentration from 0.1 to 3 mol/dm3. As shown in Fig. 15b, at pH = 3.5 the percentage extraction of Zn(II) and Ni(II) increased from 2.6 to 45.1 %, whereas that of nickel(II) increased from 0.9 to 28.3 %, respectively. The co-extraction of the studied metals does not eliminate 1-(2-pyridyl)tridecan-1-one oxime as the extractant, but the selectivity of the stripping necessitates washing by water (Zn(II) re-extraction), next copper(II) should be stripped by mixing with 1 % solution of oxalic acid and 5 % Na2SO4, followed by nickel(II) stripping with 6–8 % HCl and remained in the organic phase Co(II) can be stripped with concentrated HCl in 90 %.
Conclusion
The extraction of cobalt(II) from the chloride/sulphate aqueous solutions with the oxime of 1-(2-pyridyl)tridecan-1-one was studied as a function of pH, temperature, metal and chloride ions’ concentration in the aqueous feed, and concentration of the oxime in the organic phase.
The study showed a linear dependence of the cobalt extraction and the pH of the aqueous feed especially in the range of pH 1–3 (the extraction increased linearly from 70.5 to 91 %). The efficient extraction was also observed at strong acidic range of the pH, but during the extraction an emulsion was observed. Moreover, the influence of the chloride ions concentration on cobalt ions extraction indicated that the most visible effect was observed at range of Cl− concentration 0–1 mol/dm3. Further increase of chloride ions concentration above 1 mol/dm3 Cl− caused the process stabilisation and the recovery level was not lower than 90–92 %, moreover, the calculated enthalpy indicated that the extraction of Co(II) from the solutions containing above 1 mol/dm3 Cl− was endothermic process.
The analysis of the cobalt concentration influence on the extraction also indicated the influence of chloride ions concentration on the loading capacity [0.5 and 0.78 mol of Co(II) per mol of the oxime at 1 and 3 mol/dm3 Cl−, respectively]. This effect may be attributed to the coordination of cobalt-chloride species which have a tendency to agglomeration especially at higher concentration of chloride solutions. Despite the high loading capacity, especially at the concentrated chloride solution, the McCabe–Thiele diagrams, confirmed by experimental data, show that regardless the chloride ions concentration and phases ratio, the full cobalt(II) extraction can be achieved in two counter current stages.
The stoichiometry studies of the complexes formed between cobalt(II) and oxime of 1-(2-pyridyl)trdecan-1-one indicated that cobalt(II) ions extraction underwent the hydrogen exchange reaction and chloride ions also participated in the complexes structure. Therefore, on the basis of the conducted graphical analysis, it was assumed that cobalt(II) ions at pH above 3 were transported into organic phase as a complex CoL(HL)Cl. The separation of Co(II) from Zn(II), Ni(II) and Cu(II) was also studied, but the selective recovery of the metals was possible using the multi-stage stripping process wherein the first stage was washing with water [Zn(II) re-extraction], next copper(II) was stripped by mixing with 1 % solution of oxalic acid and 5 % Na2SO4, the third stage was nickel(II) stripping with 6–8 % HCl and remained in the organic phase Co(II) was stripped with concentrated HCl in 90 %.
References
Moyes AJ (2005) The Intec nickel laterite process. Proceedings of the ALTA 2005. Nickel/Cobalt Conference 10. Perth, ALTA Metallurgical Services, Melbourne, Australia, May 16–18
Smyres GA, Kral RL, Lei KPV, Carnahan T G (1986) Calcium chloride–oxygen leaching and metals recovery from an arsenical copper–cobalt concentrate. Technical report for Bureau of Mines, US, 8999, 1986
Lalancette JM (2002) Method for recovering nickel and cobalt from laterite ores. European Patent WO0208477, January 31
Harris B, White C, Dry M, Evans P (2009) Treatment of nickel laterites by chloride and hybrid chloride sulphate processes. In: Budac JJ, Fraser R, Mihaylov I, Papangelakis VG, Robinson DJ (eds) Proceedings of hydrometallurgy of nickel and cobalt 48th CIM annual conference of metallurgists, Sudbury, Ontario, Canada, August 23–26. The Metallurgical Society of CIM, Montreal, p 523
Pelser M, Steyl J D T, Smit J (2009) Development of the Anglo Research Nickel (ARNi) process for the treatment of laterite ores. In: Budac JJ, Fraser R, Mihaylov I, Papangelakis VG, Robinson DJ (eds) Proceedings of hydrometallurgy of nickel and cobalt 48th CIM annual conference of metallurgists, Sudbury, Ontario, Canada, August 23–26. The Metallurgical Society of CIM, Montreal, p 409
Steyl JDT, Pelser M, Smit JT (2008) Atmospheric leach process for nickel laterite ores. In: Young CA, Corby PRT, Anderson G, Choi Y (eds) Hydrometallurgy 2008, proceedings of the sixth international symposium, SME, Phoenix, Arizona, August 17–21. The Society for Mining, Metallurgy & Exploration Inc. (SME), Englewood, Colorado, pp 541–550
Jones D, Moore R (2001) The application of the CESL nickel process to laterites. In: Proceedings of the ALTA 2001 Nickel/Cobalt-7, May 15–18, Perth, Australia, p 11
Parhi PK, Padhan E, Palai AK, Sarangi K, Nathsarma KC, Park KH (2011) Separation of Co(II) and Ni(II) from the mixed sulphate/chloride solution using NaPC-88A. Desalination 267(2–3):201–208
Klonowska-Wieszczycka K, Olszanowski A, Parus A, Zydorczak B (2009) Removal of copper(II) from chloride solutions using hydrophobic pyridyl ketone oximes. Solvent Extr Ion Exch 27(1):50–62
Wieszczycka K, Krupa M, Olszanowski A (2011) Solvent extraction of zinc(II) ions from aqueous chloride solutions by hydrophobic 3-pyridyl ketoximes. In: Valenzuela F, Moyer LBA (eds) Proceedings of the 19th international solvent extraction conference—ISEC 2011, 3–7 October, Santiago, Chile. Gecamin, Chile
Parus A, Wieszczycka K, Olszanowski A (2010) Solvent extraction of cadmium(II) from chloride solutions by pyridyl ketoximes. Hydrometallurgy 105:284–289
Parus A, Wieszczycka K, Olszanowski A (2011) Solvent extraction of iron(III) from chloride solutions in the presence of copper(II) and zinc(II) using hydrophobic pyridyl ketoximes. Sep Sci Technol 46(1):87–93
Parus A, Wieszczycka K, Olszanowski A (2012) Solvent extraction of zinc(II) ions from chloride solutions by hydrophobic alkyl–pyridyl ketoximes. Sep Sci Technol 48(2):319–327
Parus A, Jankowska A, Wieszczycka K (2015) Pyridylketoximes with branched alkyl chain as extractants of copper(II) ions from chloride solutions. Sep Sci Technol 50(2):214–222
Wieszczycka K, Kaczerwska M, Krupa M, Parus A, Olszanowski A (2012) Solvent extraction of copper(II) from ammonium chloride and hydrochloric acid solutions with hydrophobic pyridineketoximes. Sep Pur Technol 95:157–164
Wieszczycka K, Krupa M, Parus A, Olszanowski A (2012) Extraction of copper(II) with hydrophobic pyridyl ketoximes from chloride and sulphate solutions. Sep Sci Technol 47(9):1278–1284
Wieszczycka K, Krupa M, Wojciechowska A, Olszanowski A (2014) Recovery of nickel(II) ions from sulphate/chloride solutions using hydrophobic pyridylketoximes. Solvent Extr Ion Exch 32(3):267–280
Krupa M, Wieszczycka K, Wojciechowska A, Olszanowski A (2015) Selective removal of cobalt from nickel sulphate solutions using oxime of 1-(2-pyridyl)tridecan-1-one. Sep Sci Technol 50(5):654–660
Wieszczycka K, Wojciechowska A, Krupa M (2015) Equilibrium and mechanism of cobalt(II) extraction from chloride solution by hydrophobic 2-pyridineketoxime. Sep Pur Technol 142:129–136
Bromley LA (1973) Thermodynamic properties of strong electrolytes in aqueous solutions. AIChE J 19(2):313–320
Jia Q, Wang ZH, Li DQ, Niu CJ (2004) Adsorption of heavy rare earth(III) with extraction resin containing bis(2,4,4-trimethylpentyl) monothiophosphinic acid. J Alloys Compd 374:434–437
Kanderal OM, Kozłowski H, Dobosz A, Swiatek-Kozlowska J, Fritsky MF (2005) Effect of metal ionic radius and chelate ring alternation motif on stabilization of trivalent nickel and copper in binuclear complexes with double cis-oximato bridges. Dalton Trans 8:1428–1437
Moushi E, Constantinos GE, Perlepes SP, Papatriantafyllopoulou C (2007) Synthesis and structural characterization of a new tetranuclear nickel(II) sulfato complex containing the anionic form of di-2-pyridyl ketone oxime. Polyhedron 26(9–11):1830–1834
Bjerrum J, Halonin AS, Skibsted LH (1975) Studies on cobalt(II) halide complex formation. A spectrophotometric study of the chloro cobalt(II) complexes in strong aqueous chloride solutions. Acta Chem Scand 29:326–332
Sillen LG, Martel AE, Bjerrum J (1964) Stability constants of metal–ion complexes: section I. Inorganic ligands. Chemical Society, London, p 241
Acknowledgments
This work was supported by the Polish Ministry of Science and Higher Education statutory Grant No. 32/0500/2015 DS-PB.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Wieszczycka, K., Krupa, M., Wojciechowska, A. et al. Equilibrium studies of cobalt(II) extraction with 2-pyridineketoxime from mixed sulphate/chloride solution. J Radioanal Nucl Chem 307, 1155–1164 (2016). https://doi.org/10.1007/s10967-015-4246-7