Abstract
Physical aging behavior of glassy, amorphous poly(ether imide) (PEI) at a high aging temperature range (15 ∼ 25 °C below the polymer Tg of 215 °C) was investigated. A quantitative modeling approach was utilized to describe the aging process of PEI. The experimental data of enthalpy of relaxation for constructing the models were obtained using differential scanning calorimetry (DSC). At relatively low aging temperatures, the enthalpy of relaxation simply increases linearly with the logarithm of time. At high temperatures another parameter accounting for distribution is needed for better description. Furthermore, the sub-Tg molecular chain relaxation of aged PEI was characterized using dynamic mechanical analysis (DMA). Physical aging significantly suppressed the β chain relaxation but not the γ-relaxation, suggesting that the chain segmental motion for the β-relaxation is the one responsible for chain conformation changes reaching an equilibrium glassy state.
Similar content being viewed by others
References
L. C. E. Struik, Physical aging of amorphous polymers and other materials, Elsevier Sciences, New York, 1978.
D. J. Kemmish and J. N. Hay, Polymer, 26, 905 (1985).
A. A. Ogale and R. L. McCullough, Comp. Sci. Tech., 30, 1377 (1987).
K. Itoyama, Polymer, 35, 2117 (1994).
D. J. Plazek, J. Polym. Sci., Polym. Phys., 28, 431 (1990).
J. M. Hutchinson, D. McCarthy, S. Montserrat and P. Cortes, J. Polym. Sci., Polym. Phys. Ed., 34, 229 (1996).
H. W. Starkweather, Jr. and P. Avakian, Macromolecules, 22, 4060 (1989).
H. H.-D. Lee and F. J. McGarry, Polymer, 34, 4267 (1993).
L. Davids and S. Etienne, Macromolecules, 25, 4302 (1992).
A. Jonas and R. Legras, Macromolecules, 26, 813 (1993).
G. P. Johari, J. Chem. Phys., 77, 4619 (1982).
I. Echeverria, P.-C. Su, S. L. Simon and D. J. Plazek, J. Polym. Sci., Polym. Phys. Ed., 33, 2457 (1995).
A. B. Brennan and F. Feller III, J. Rheo., 39, 453 (1995).
E. M. Woo and S. M. Kuo, Polym. Eng. Sci., 37, 173 (1997).
A. J. Kovacs and J. M. Hutchinson, J. Polym. Sci., Polym. Phys. Ed., 17, 2031 (1979).
S. E. B. Petrie and A. S. Marshall, J. Appl. Phys., 46, 4223 (1975).
H. J. Otto, Colloid Polym. Sci., 257, 486 (1979).
S. Montserrat, J. Polym. Sci., Polym. Phys. Ed., 32, 509 (1994).
G. Williams and D. C. Watts, Trans. Faraday Soc., 66, 80 (1970).
J. M. G. Cowie and R. Ferguson, Macromolecules, 22, 2307 (1989).
J. Mijovic, T. Ho and T. K. Kwei, Polym. Eng. Sci., 29, 1604 (1989).
A. Agrawal, J. Polym. Sci., Polym. Phys. Ed., 27, 1449 (1989).
G. ten Brinke and R. Grooten, Colloid Polym. Sci., 267, 992 (1989).
J. M. G. Cowie and R. Ferguson, Macromolecules, 22, 2313 (1989).
I. M. Hodge and J. M. O’Reilly, Polymer, 33, 4883 (1992).
M. Pegoraro and L. D. Landro, Plastic Rubber Comp. Proc. Appl., 17, 269 (1992).
H. Tamada, S. Okita and K. Kobayashi, Polym. J., 25, 339 (1993).
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Kuo, S.M., Woo, E.M. Sub-Tg molecular relaxation and enthalpy relaxation behavior in amorphous glassy poly(ether imide). J Polym Res 4, 213–219 (1997). https://doi.org/10.1007/s10965-006-0027-x
Issue Date:
DOI: https://doi.org/10.1007/s10965-006-0027-x