Abstract
The effect of Sn on highpermeability grain-oriented silicon steel was studied by PHI-700 Auger electron spectroscopy (AES), JEM-2100 transmission electron microscopy (TEM) and electron back-scattered diffraction (EBSD) technology. The results show that (1) the magnetic properties could be significantly increased by adding Sn; (2) the primary grain size becomes smaller with the addition of 0.19 wt% Sn and the Goss orientation crystal nucleus become more numerous as well; (3) the grain boundary segregation of Sn is still obvious at 970 °C in hightemperature annealing process; and (4) the average size of precipitates becomes smaller with the addition of 0.19 wt% Sn; meanwhile the dispersion and the inhibitor are also promoted. These conclusions are in agreement with the experimental results.
Similar content being viewed by others
References
Zhongzhi, H., Yu, Z., Haiwen, L.: Electrical Steel. Metallurgical Industry, Beijing (2012)
Matsuo, M.: Texture control in the production of grain oriented silicon steels. ISIJ Int. 29, 809–27 (1989)
Dunn, C.G., Lionetti, F.: The effect of orientation difference on grain boundary energies. Trans. AIME 185, 125–32 (1949)
Dunn, C., Daniels, F., Bolton, M.: Relative energies of grain boundaries in silicon iron. Trans. Am. Inst. Min. Metall. Engrs. 188, 1245 (1950)
Walter, J., Dunn, C.: Tertiary recrystallization in silicon iron Trans. AIME 215, 465–71 (1959)
Walter, J.L., Dunn, C.G.: An effect of impurity atoms on the energy relationship of (100) and (110) surfaces in high purity silicon iron. Acta Metallurgica 8, 497–503 (1960)
Flowers, J.W.: Grain growth inhibition by spherical particles with a distribution of sizes. IEEE Trans. Magn. 15, 1601–3 (1979)
Hayakawa, Y., Szpunar, J.A., Palumbo, G., Lin, P.: The role of grain boundary character distribution in Goss texture development in electrical steels. J. Magn. Magn. Mater. 160, 143–4 (1996)
Feng-e, C., Ping, Y., Wei-min, M.: Selective abnormal growth behavior of Goss grains in a grain-oriented silicon steel. J. University Sci. Technol. Beijing 32, 1157–62 (2010)
Li, Z.-c., Yang, P., Cui, F.-e., Liu, Y.-z., Mao, W.-m.: Analysis on the secondary recrystallization in grain oriented silicon steel. J. Chin. Electron Microsc. Soc. 1, 010 (2010)
Liu, Z., Liu, Z., LiJun, H.: Effects of Sn and Sb on structure and magnetic properties of high induction oriented silicon steel
Seah, M., Hondros, E.: Grain boundary segregation. Proc. R. Soc. Lond. A Math. Phys. Sci. 335, 191–212 (1973)
Iwayama, K., Kuroki, K., Yoshitomi, Y., Homma, K., Wada, T.: Roles of tin and copper in the 0.23-mm-thick high permeability grain-oriented silicon steel. J. Appl. Phys. 55, 2136–8 (1984)
Zhao, Y., He, Z.,Weng, Y.,Wu, B.: Grain boundary segregation of trace Sn in high induction oriented silicon steel. Acta Metallurgica Sinica 8, 000 (1992)
Hou, C.-K.: Effect of hot band annealing temperature on the magnetic properties of low-carbon electrical steels. ISIJ Int. 36(5), 563–571 (1996)
Muraki, M., Obara, T., Satoh, M.: Control of recrystallization during high-temperature hot-rolling of grain-oriented silicon steel. J. Mater. Eng. Perform 4(4), 413–417 (1995)
Horky, P., Pacl, P.: Effective grain growth inhibition in silicon steel. J. Magn. Magn. Mater. 41, 14–16 (1984)
Hu, H.: Acta Metal. 8, 124–126 (1960)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Fan, Lf., Dong, Rf., Qiu, St. et al. Effect of Sn on HighPermeability Grain-Oriented Silicon Steel. J Supercond Nov Magn 27, 1959–1965 (2014). https://doi.org/10.1007/s10948-014-2595-z
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-014-2595-z