Abstract
This study was performed to determine whether some flexural properties of a denture base resin material could be improved through reinforcement with five types of aesthetic fibers at 3% concentration by weight and in 2, 4, and 6 mm length. Five specimens of similar dimensions were prepared for each of the test groups; base resin and the same resin with glass, rayon, polyester, nylon 6 and nylon 6,6 fibers in three different lengths. Flexural properties were evaluated by using a 3-point bending test. A visual examination was also made to determine mode of fracture of the specimens. The incorporation of different fibers in varying lengths had no significant effect on flexural strength of the resin. The specimens reinforced with nylon 6,6 fibers of 6 mm length showed the highest flexural strength. Young’s modulus and maximum load suggests that such reinforcement makes resin resistant to fracture.
Similar content being viewed by others
References
T. KANIE, K. FUJII, H. ARIKAWA and K. INOQUE, Dent. Mater. 16 (2000) 150
P. CHITCHUMNONG, S. C. BROOKS and G. D. STAFFORD, Dent. Mater. 5 (1989) 2
D. C. JAGGER, A. HARRISON and K. D. JANDT, J. Oral Rehabil. 26 (1999) 185
P. K. VALLITTU, J. Prosthodont. 5 (1996) 270
N. YUNUS, A. A. RASHID, L. L. AZMI and M. I. ABU-HASSAN, J. Oral Rehabil. 32 (2005) 65
S. H. FOO, T. J. LINDQUIST, S. A. AQUILINO, R. L. SCHNEIDER, D. L. WILLIAMSON and D. B. BOYER, J. Prosthodont. 10 (2001) 148
A. G. ANDREOPOULOS and G. C. PAPANICOLAOU, J. Mater. Sci. 22 (1987) 3417
M. BRADEN, K. W. M. DAVY, S. PARKER, N. H. LADIZESKY and I. M. WARD, Br. Dent. J. 164 (1988) 109
J. M. BERRONG, R. M. WEED and J. M. YOUNG, Int. J. Prosthodont. 3 (1990) 391
S. Y. CHEN, W. M. LIANG and P. S. YEN, J. Biomed. Mater. Res. (Appl. Biomater.) 58 (2001) 203
J. DE BOER, S. G. VERMILYEA and R. E. BRADY, J. Prosthet. Dent. 51 (1984) 119
D. L. GUTTERIDGE, Br. Dent. J. 164 (1988) 177
D. C. JAGGER, R. G. JAGGER, S. M. ALLEN and A. HARRISON, J. Oral Rehabil. 29 (1999) 263
D. C. JAGGER, A. HARRISON, R. G. JAGGER and P. MILWARD, J. Oral Rehabil. 30 (2003) 231
J. JOHN, S. A. GANGADHAR and I. SHAH, J. Prosthet. Dent. 86 (2001) 424
N. H. LADIZESKY, M. K. M. PANG, T. W. CHOW and I. M. WARD, Aust. Dent. J. 38 (1983) 28
C. K. SCHREIBER, Br. Dent. J. 130 (1971) 29
G. S. SOLNIT, J. Prosthet. Dent. 66 (1991) 310
H. D. STIPHO, J. Prosthet. Dent. 79 (1998) 580
B. TANER, A. DOĞAN, T. TINÇER and A. E. AKINAY, J. Oral Sci. 41 (1999) 15
P. K. VALLITTU, V. P. LASSILA and R. LAPPALAINEN, J. Prosthet. Dent. 71 (1994) 607
P. K. VALLITTU, J. Oral Rehabil. 24 (1997) 124
P. K. VALLITTU, J. Prosthodont. 5 (1996) 115
P. K. VALLITTU and K. NARVA, Int. J. Prosthodont. 10 (1997) 142
P. K. VALLITTU, J. Prosthet. Dent. 79 (1998) 125
P. K. VALLITTU, I. E. RUYTER and K. EKSTRAND, Int. J. Prosthodont. 11 (1998) 340
P. K. VALLITTU, J. Prosthet. Dent. 81 (1999) 318
N. YAZDANIE and M. MAHOOD, J. Prosthet. Dent. 54 (1985) 543
S. Y. CHEN and W. M. LIANG, Mid. Taiwan J. Med. 9 (2004) 203
N. G. KATSIKAS, R. HUGGETT, A. HARRISON and R. W. VOWLES, Dent. Mater. 10 (1994) 2
ASTM Standard D790M-92, in “Annual Book of ASTM Standards”, Part 08.01 (American Society for Testing and Materials, Philadelphia, 1992)
R. Van NOORT, in “Introduction to Dental Materials”, 2nd ed, (Mosby, Edinburgh, 2002) p. 44
R. J. FRIED, in “Polymer Science and Technology”, (Prentice Hall, 2003) p. 391
B. R. SEYMOUR and C. CARRAHER, in “Polymer Chemistry”, (Marcel Decker Inc., New York, 1996) p. 233
O. M. DOGAN, G. BOLAYIR, S. KESKIN, A. DOGAN, B. BEK and A. BOZTUG, Dent. Mater. J. 26 (2007) 232
Acknowledgments
Special thanks to Associate Professor Ali Fazıl Yenidünya, Cumhuriyet University, Faculty of Science and Arts, Department of Biology, for his invaluable contribution in preparing this manuscript for submission.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Doğan, O.M., Bolayır, G., Keskin, S. et al. The evaluation of some flexural properties of a denture base resin reinforced with various aesthetic fibers. J Mater Sci: Mater Med 19, 2343–2349 (2008). https://doi.org/10.1007/s10856-007-3343-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10856-007-3343-8