Abstract
The ternary composite (PPy/Ag/SFHM) was prepared by in situ polymerication of pyrrole with SFHM. The result composites were characterized by SEM, XRD, FTIR, VSM and TG, respectively. It shows that the conductivity, Ms and Hc of the ternary composite is 2.87 S/cm, 17.946 emu/g and 1.64 kOe and Ag/BFHM microspheres and PPy forms composites as shown in SEM images. PPy/Ag/SFHM (RL = −14.12 dB at 10.76 GHz) performs better electromagnetic absorption properties than PPy (RL = −4.58 dB at 9.94 GHz) and Ag/SFHM (RL = −10.25 dB at 10.36 GHz). Minimal reflection loss of the microwave absorption or matching condition occurs when the thickness of the absorbers approximates an odd number multiple of a quarter of the propagating wavelength. The matching frequency for minimum reflection loss decreases and the RL curves shift to the lower frequency with increasing thickness of the composite. The resulting composite can be utilized for reduction of radar signatures.
Similar content being viewed by others
References
W. Hu, H. Liu, H. Hao, Z. Yao, M. Cao, Z. Wang, Z. Song, J. Mater. Sci.: Mater. Electron. 25, 4730 (2014)
H. Qiu, J. Wang, S. Qi, Z. He, X. Fan, Y. Dong, J. Mater. Sci.: Mater. Electron. 26, 564 (2015)
P. Sharma, A. Verma, R.K. Sidhu, O.P. Pandey, J. Alloys Compd. 361, 257 (2003)
B. Kaur, M. Bhat, F. Licci, R. Kumar, S.D. Kulkarni, J. Magn. Magn. Mater. 305, 392 (2006)
H. Mocuta, L. Lechevallier, J.M.L. Breton, J.F. Wang, I.R. Harris, J. Alloys Compd. 364, 48 (2004)
Z. He, S. Qi, X. Zhong, O. Hua, J. Wang, J. Mater. Sci.: Mater. Electron. 25, 3455 (2014)
Z. Li, Y. Fu, Z. Wang, G. Rui, R. Huang, X. He, J. Phys. Chem. C 113, 2792 (2009)
C. Zhang, H. Zhang, B. Du, R. Hou, S. Guo, J. Colloid Interface Sci. 368, 97 (2012)
J. Yin, X. Qian, J. Yin, M. Shi, G. Zhou, Mater. Lett. 57, 3859 (2003)
Y. Yang, S. Qi, J. Wang, J. Alloys Compd. 520, 114 (2012)
T.H. Ting, R.P. Yu, Y.N. Jau, Mater. Chem. Phys. 126, 364 (2011)
W.L. Sang, S.Y. An, I.B. Shim, C.S. Kim, J. Magn. Magn. Mater. 290, 231 (2005)
C. Doroftei, E. Rezlescu, P.D. Popa, N. Cryst, Res. Technol. 41, 1112 (2006)
Y. Yang, S. Qi, Y. Qin, X. Zhang, J. Appl. Polym. Sci. 125, E383 (2012)
J. Jing, A. Lunhong, L. Liangchao, J. Phys. Chem. B 113, 1376 (2009)
Y. Xie, X. Hong, X. Wang, J. Zhao, Y. Gao, Y. Ling, Synth. Met. 162, 1643 (2012)
Z. He, S. Qi, X. Zhong, H. Ma, P. Wang, H. Qiu, J. Alloys Compd. 621, 194 (2015)
X. Liu, W. Zhong, S. Yang, Z. Yu, B. Gu, Y. Du, J. Magn. Magn. Mater. 238, 207 (2002)
J.F. Wang, C.B. Ponton, R. Grössinger, I.R. Harris, J. Alloys Compd. 369, 170 (2004)
A. Tadjarodi, H. Kerdari, M. Imani, J. Alloys Compd. 554, 284 (2013)
W. Jing, Z. Hong, B. Shuxin, C. Ke, Z. Changrui, J. Magn. Magn. Mater. 312, 310 (2007)
P. Liu, Y. Huang, X. Zhang, J. Alloys Compd. 596, 25 (2014)
X. Li, Advanced Ceramics (2008)
A.N. Yusoff, M.H. Abdullah, S.H. Ahmad, J. Appl. Phys. 92, 876 (2002)
H. Wu, L. Wang, H. Wu, Q. Lian, Appl. Phys. A 115, 1299 (2014)
S.M. Abbas, A.K. Dixit, R. Chatterjee, T.C. Goel, J. Magn. Magn. Mater. 309, 20 (2007)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Li, L., Li, M. & Qi, S. Preparation and microwave absorption properties of silver-coated Nd-deposed strontium ferrite hollow microspheres with polypyrrole composites. J Mater Sci: Mater Electron 28, 4288–4294 (2017). https://doi.org/10.1007/s10854-016-6052-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-016-6052-6