Abstract
The Mg3(PO4)2 ceramics were prepared by using the conventional solid-state reaction method. And the samples sintered at 1025 °C showed high relative density with 96.51 %. The crystal structure and dielectric properties of Mg3(PO4)2 ceramics were investigated. Optimized dielectric properties tested at 1 MHz were obtained in Mg3(PO4)2 ceramic sintered at 1025 °C for 2 h (εr ~ 5.9, tanδ ~ 0.0015 and τε ~ 40 ppm/°C). Meanwhile, Mg3(PO4)2 ceramic showed the chemical compatibility with Ag electrodes, which can be a promising candidate for multilayer components applications in high frequency.
Similar content being viewed by others
References
S.P. Wu, D.F. Chen, C. Jiang, Y.X. Mei, Q. Ma, Synthesis of monoclinic CaSnSiO5 ceramics and their microwave dielectric properties. Mater. Lett. 91, 239–241 (2013)
C. Su, L. Fang, Z. Wei, X. Kuang, H. Zhang, LiCa3ZnV3O12: a novel low-firing, high Q microwave dielectric ceramic. Ceram. Int. 40, 5015–5018 (2014)
H. Zhou, F. He, X. Chen, J. Chen, L. Fang, W. Wang, Y. Miao, A novel thermally stable low-firing LiMg4V3O12 ceramic: sintering characteristic, crystal structure and microwave dielectric properties. Ceram. Int. 40, 6335–6338 (2014)
H. Xie, C. Chen, R. Tian, H. Xi, A novel microwave dielectric ceramic of BaMgP2O7 with low ε r. Mater. Lett. 162, 91–93 (2016)
R. Umemura, H. Ogawa, H. Ohsato, A. Kan, A. Yokoi, Microwave dielectric properties of low-temperature sintered Mg3(VO4)2 ceramic. J. Eur. Ceram. Soc. 25, 2865–2870 (2005)
X.W. Jiang, C.C. Li, C.X. Su, Z.H. Wei, L. Fang, Low temperature firing and microwave dielectric properties of BaCaV2O7 ceramics. Ceram. Int. 41, 5172–5176 (2015)
L. Fang, F. Xiang, C. Su, H. Zhang, A novel low firing microwave dielectric ceramic NaCa2Mg2V3O12. Ceram. Int. 39, 9779–9783 (2013)
R.R. Tummala, Ceramic and glass-ceramic packaging in the 1990s. J. Am. Ceram. Soc. 74, 895–908 (1991)
D. Thomas, M.T. Sebastian, Temperature-compensated LiMgPO4: a new glass-free low-temperature co-fired ceramic. J. Am. Ceram. Soc. 93, 3828–3831 (2010)
J. Bian, D. Kim, K. Hong, Microwave dielectric properties of (Ca1−xZnx)2P2O7. Mater. Lett. 59, 257–260 (2005)
Y.Y. Ma, J.Q. Hu, E.H. Song, S. Ye, Q.Y. Zhang, Regulation of red to near-infrared emission in Mn2+ single doped magnesium zinc phosphate solid-solution phosphors by modification of the crystal field. J. Mater. Chem. C 3, 12443–12449 (2015)
A. Aaddane, M. Kacimi, M. Ziyad, Oxidative dehydrogenation of ethane and propane over magnesium–cobalt phosphates CoxMg3−x(PO4)2. Catal. Lett. 73, 47–53 (2001)
R. Lal, N.M. Gokhale, R. Krishnan, P. Ramakrishnan, Effect of sintering parameters on the microstructure and properties of strontium modified PZT ceramics prepared using spray-dried powders. J. Mater. Sci. 24, 2911–2916 (1989)
R.D. SruNNoN, G.R. RossvraN, Dielectric constants of silicate garnets and the oxide additivity rule. Am. Mineral. 77, 94–100 (1992)
A.J. Moulson, J.M. Herbert, Electroceramics: Materials, Properties, Applications (Wiley, New York, 2003)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zhang, S., Li, L. & Lv, X. Synthesis and characterization of a novel Mg3(PO4)2 ceramic with low dielectric constant. J Mater Sci: Mater Electron 28, 1620–1623 (2017). https://doi.org/10.1007/s10854-016-5703-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-016-5703-y