Abstract
This paper reports an alternative approach to achieve orthorhombic HoMnO3 (HMO) structure by Ca doping at Holmium site. It is observed that pure HMO undergoes hexagonal (P6 3 cm) to orthorhombic (Pbnm) structural transformation when Ca is substituted at Ho site through high temperature sintering at 1,450 °C for 10 h. With the substitution of Ca in HMO (Ho1−xCaxMnO3, x = 0.05), hexagonal unit cell volume has been contracted significantly. However with further increase of Ca dopant concentration (x = 0.1, 0.2), unit cell volume for each composition are marginally enhanced. Spontaneous polarization (Ps), remanent polarization (Pr) values are observed to be enhanced up to the limiting doping value for x = 0.1. Further substitution of Ca in HMO (x > 0.2) reduces the Ps and Pr value marginally. Similarly dielectric constant (εr) and dielectric loss values are increased up to x = 0.1 and then decreased up to x = 0.2. These observations are expected to be linked with the structural and microstructural changes with the variation of x. At x = 0.1, larger grains are developed, with enhanced value of polarization and dielectric constant. In addition to above mentioned enhanced ferroelectric polarization and dielectric behaviour, we have observed peculiar magnetic property from M to H curve. In all Ho1−xCaxMnO3 (x = 0–0.2) samples, a switching behaviour in low field was observed in field dependence of magnetization at room temperature and the behaviour found to be enhanced with Ca concentration up to 0.1 and then decreases.
Similar content being viewed by others
References
H.W. Brinks, J. Rodrıguez-Carvajal, H. Fjellvag, A. Kjekshus, B.C. Hauback, Phys. Rev. B 63, 094411 (2001)
S. Lee, A. Pirogov, J.H. Han, J.G. Park, A. Hoshikawa, T. Kamiyama, Phys. Rev. B 71, 180413 (2005)
S.W. Cheong, M. Mostovoy, Nat. Mater. 6, 13 (2007)
T. Kimura, T. Goto, H. Shintani, K. Ishizaka, T. Arima, Y. Tokura, Nature 426, 55 (2003)
T. Lottermoser, T. Lonkai, U. Amann, D. Hohlwein, J. Ihringer, M. Fiebig, Nature 430, 541–544 (2004)
O.P. Vajk, M. Kenzelmann, J.W. Lynn, S.B. Kim, S.W. Cheong, Phys. Rev. Lett. 94, 087601 (2005)
P. Coeure, F. Guinet, J.C. Peuzin, G. Buisson, E.F. Bertaut, Int. Proc. Meeting on Ferroelectricity ed. by V. Dvorak, (Institute of Physics of the Czechoslovak Academy of Sciences, Prague, 1996), pp. 332–340
B.G. Ueland, J.W. Lynn, M. Laver, Y.J. Choi, S.W. Cheong, Phys. Rev. Lett. 104, 147204 (2010)
B. Lorenz, Y.Q. Wang, Y.Y. Sun, C.W. Chu, Phys. Rev. B 70, 212412 (2004)
Y. Wang, X. Lu, Y. Chen, F. Chi, S.H. Feng, X. Liu, J. Solid State Chem. 178, 1317 (2005)
J.A. Alonso, M.J. Martinez-Lope, M.T. Casais, M.T. Fernandez-Diaz, Inorg. Chem. 39, 917 (2000)
A. Waintal, J. Chenavas, C.R. Hebd, Seanc. Acad. Sci. 264B, 168 (1967)
A. Waintal, J. Chenavas, C.R. Hebd, Mater. Res. Bull. 2, 819 (1967)
C. Zener, Phys. Rev. 82, 403 (1951)
P.W. Anderson, H. Hasegawa, Phys. Rev. 100, 675 (1950)
P.G. De Gennes, Phys. Rev. 118, 141 (1960)
W. Hong Tao, Z. Tong, Bo Hong, Tao Qian, Xu Zhu-An, Chin. Phys. Lett. 28, 027501 (2011)
S. Karimi, I.M. Reaney, Y. Han, J. Pokorny, I. Sterianou, J. Material Sci. 44, 5102–5112 (2009)
J. Magesh, P. Murugave, R.V.K. Mangalam, K. Singh, Ch. Simon, W. Prellier, Appl. Phys. Lett. 101, 022902 (2012)
B.K. Roul, J. Supercond. 14(4), 529 (2001)
P.P. Rout, S.K. Pradhan, S.K. Das, B.K. Roul, Phys. B 407, 2072 (2012)
D. Guo, L. Zhang, M. Li, J. Liu, B. Yu, J. Am. Ceram. Soc. 91, 3280 (2004)
W. Li, K. Chen, Y.Y. Yao, J.S. Zhu, Y.N. Wang, Appl. Phys. Lett. 85, 4717 (2004)
R.K. Mishra, D.K. Pradhan, R.N.P. choudhary, A. Banerjee, J. Phy. Condens. Matter 20, 045218 (2008)
T. Kimura, T. Goto, H. Shintani, K. Ishizaka, T. Arima, Y. Tokura, Nature (London) 426, 55 (2003)
I.A. Sergienko, C. Sen, E. Dagotto, Phys. Rev. Lett. 97, 227204 (2006)
C.R. Serrao, J.R. Sahu, A. Ghosh, Bull. Mater. Sci. 33, 169 (2010)
Acknowledgments
Author Prajna Priyadarshinee Rout acknowledges Director, IMS for the research facilities received from Institute of Materials Science and CSIR for financial support.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Rout, P.P., Roul, B.K. Effect of Ca doping on enhancement of ferroelectricity and magnetism in HoMnO3 multiferroic system. J Mater Sci: Mater Electron 24, 2493–2499 (2013). https://doi.org/10.1007/s10854-013-1123-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-013-1123-4