Abstract
To prepare zinc sillenite nanopowders, bismuth nitrate and zinc nitrate were taken in 12:1 and 12.66:0.33 mol ratios. Zinc sillenite (Bi12.66Zn0.33O19.33) nanocrystalline powder was prepared by simple chemical solution decomposition method via heat treatment. Studies were focused on the formation of single crystalline phases and their linear optical properties. TG–DTA, XRD, DRS, IR, Raman, FE-SEM–EDS, and TEM techniques were used systematically to characterize the zinc sillenites. X-ray powder diffraction studies confirm that the heat treatment at 650 °C leads to cubic structure with zinc sillenites phase. Lattice parameter and the band gap of zinc sillenite were estimated as (a=) 10.21 Å and 2.75 eV respectively. We could observe the bismuth-oxygen sublattice vibrational modes alone in the Raman/IR vibrational spectra of zinc sillenite.
Graphical abstract
Similar content being viewed by others
References
A.V. Egorysheva, T.I. Milenov, P.M. Rafailov, C. Thomsen, R. Petrova, V.M. Skorikov, M.M. Gospodinov, Solid State Commun. 149, 1616 (2009)
S.C. Abrahams, P.B. Jamieson, J.L. Bernstein, J. Chem. Phys. 47, 4034 (1967)
I.V. Kityk, M.K. Zamorskii, J. Kasperczyk, Phys. B 226, 381 (1996)
H. Sekhar, P. Prem Kiran, D. Narayana Rao, Proc. SPIE 7712, 77122J (2010)
P. Prem Kiran, S. Venugopal Rao, M. Ferrari, B.M. Krishna, H. Sekhar, S. Alee, D. Narayana Rao, Nonlinear Opt. Quantum Opt. 40, 223 (2010)
J. Tang, J. Ye, Chem. Phys. Lett. 410, 104 (2005)
M. Valant, D. Suvorov, Chem. Mater. 14, 3471 (2002)
R.J. Betsch, W.B. White, Spectrochim. Acta 34, 505 (1978)
M.F. Carrasco, S.K. Mendiratta, L. Marques, Appl. Phys. A 80, 361 (2005)
H. Sekhar, D. Narayana Rao, J. Nanopart. Res. 14, 976 (2012)
H. Sekhar, D. Narayana Rao, J. Mater. Sci. 47, 1964 (2012)
H. Sekhar, D. Narayana Rao, J. Alloys Comp. 517, 103 (2012)
C. Zaldo, C. Coya, J.L.G. Fierro, K. Polgar, L. Kovks, Z. Szaller, J. Phys. Chem. Solids 57, 1667 (1996)
S. Venugopalan, A.K. Ramdas, Phys. Rev. B 5, 4065 (1972)
B. Mihailova, M. Gospodinov, L. Konstantinov, J. Phys. Chem. Solids 60, 1821 (1999)
V.I. Burkov, V.S. Gorelik, A.V. Egorysheva, Yu.F. Kargian, J. Russ. Laser Res. 22, 243 (2001)
Acknowledgments
HS acknowledges the sustaining financial support from UGC-BSR-SRF fellowship-SOP, University of Hyderabad. DNR acknowledges DST-ITPAR program for the financial support.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Sekhar, H., Narayana Rao, D. Preparation, structural and linear optical properties of zinc sillenite (Bi12.66Zn0.33O19.33) nanocrystals. J Mater Sci: Mater Electron 24, 1569–1574 (2013). https://doi.org/10.1007/s10854-012-0977-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-012-0977-1