The microwave dielectric properties of (1−x)Mg(Zr0.05Ti0.95)O3-xSrTiO3 ceramics prepared by conventional solid processing were investigated. With increasing x, the dielectric constant and the quality factor decreased, and the temperature coefficient of resonant frequency was tuned from negative to positive value. The effect of sintering temperature on microwave properties was also studied. After sintering at 1,390 °C for 4 h, the ceramics exhibited a near zero temperature coefficient of resonant frequency about 2.1 ppm/°C, an optimum dielectric constant of 20.9 and a high quality factor of 203000 (6.8 GHz), at the level of x = 0.05.
Similar content being viewed by others
References
S.B. Desu, H.M. O’Bryan, J. Am. Ceram. Soc. 68, 546 (1985)
I.M. Reaney, I. Qazi, W.E. Lee, J. Appl. Phys. 88(11), 6708 (2000)
C.F. Tseng, J. Am. Ceram. Soc. 91(12), 4125 (2008)
P.L. Wise, I.M. Reaney, W.E. Lee, D.M. Iddes, D.S. Cannell, T.J. Price, J. Mater. Res. 17, 2033 (2002)
I.M. Reaney, D. Iddles, J. Am. Ceram. Soc. 89(7), 2063 (2006)
M.P. Seabra, A.N. Salak, V.M. Ferreira, J.L. Ribeiro, L.G. Vieira, J. Eur. Ceram. Soc. 24, 2995 (2004)
C.L. Huang, S.S. Liu, J. Alloys Compd. 47, 109 (2009)
C.F. Tseng, J. Alloys Compd. 494, 252 (2010)
C.F. Tseng, H.J. Tang, J. Alloys Compd. 491, 314 (2010)
H. Shin, H.K. Shin, H.S. Jung, S.Y. Cho, K.S. Hong, Mater. Res. Bull. 40, 2021 (2005)
H.X. Liu, H.T. Yu, Z.Q. Tian, Z.H. Meng, Z.H. Wu, S.X. Ouyang, J. Am. Ceram. Soc. 88, 453 (2005)
H.T. Yu, H.X. Liu, H. Hao, D.B. Luo, M.H. Cao, Mater. Lett. 62, 1353 (2008)
Acknowledgments
This work was supported by the Ph. D. fund (No. 09zx7104) of Southwest University of Science and Technology.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Yu, H., Cheng, J., Zhang, W. et al. Microwave dielectric properties of Mg(Zr0.05Ti0.95)O3-SrTiO3 ceramics. J Mater Sci: Mater Electron 23, 572–575 (2012). https://doi.org/10.1007/s10854-011-0442-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10854-011-0442-6