Abstract
A stable Ni–Al4Ni3–Al2O3 superhydrophobic surface (SHS) was fabricated on aluminum (Al) substrate via etching, subsequent replacement deposition and then annealing. The water contact angle of the SHS could reach to 155°, and the water sliding angle was less than 2°. The morphology and chemical composition of the samples were characterized using scanning electron microscopy, X-ray diffraction pattern, energy-dispersive spectroscopy and X-ray photoelectron spectroscopy. Anti-corrosion behaviors of the samples were investigated via Tafel extrapolation and electrochemical impedance, and the SHS showed a better corrosion resistance than that of pure Al. In addition, when the water drops impinged on the SHS, the drops could fully bounce, exhibiting exquisite self-cleaning property. The catalytic property of the samples was evaluated by the reduction of 4-nitrophenol (4-NP) at room temperature, in which the SHS served as the hydrogen generator as well as a catalyst. The degradation rate of 4-NP at the existence of the superhydrophobic samples in NaOH aqueous solution was 97%. And the reaction rate constant of 4-NP at the existence of the superhydrophobic samples was 9.51 × 10−2 s−1, which was about twice as large as that at the existence of pure Al. This work offers an effective strategy to fabricate SHSs and expands industrial applications for Al and its alloys.
Similar content being viewed by others
References
Zheng S, Li C, Fu Q, Hu W, Xiang T, Wang Q, Du M, Liu X, Chen Z (2016) Development of stable superhydrophobic coatings on aluminum surface for corrosion-resistant, self-cleaning, and anti-icing applications. Mater Des 93:261–270
Wang E, Wang H, Hu Y, Liu Z, Zhu Y (2017) Corrosion-resistant engineering superhydrophobic and superoleophilic bulk materials with oil–water separation property. J Mater Sci 52(12):7130–7139. doi:10.1007/s10853-017-0948-2
Chen T, Yan W, Hongtao L, Zhu W, Guo K, Li J (2016) Facile preparation of superamphiphobic phosphate–Cu coating on iron substrate with mechanical stability, anti-frosting properties, and corrosion resistance. J Mater Sci 52(8):4675–4688. doi:10.1007/s10853-016-0710-1
Wenzel RN (1936) Resistance of solid surfaces to wetting by water. Ind Eng Chem 28:988–994
Cassie ABD, Baxter S (1944) Wettability of porous surfaces. Trans Faraday Soc 40:0546–0550
Cheng Y, Lu S, Xu W, Wen H, Wang J (2015) Fabrication of superhydrophobic Au–Zn alloy surface on a zinc substrate for roll-down, self-cleaning and anti-corrosion properties. J Mater Chem A 3(32):16774–16784
Wang D, Liu Y, Liu X, Zhou F, Liu W, Xue Q (2009) Towards a tunable and switchable water adhesion on a TiO(2) nanotube film with patterned wettability. Chem Commun 45:7018–7020
Wang P, Yao T, Sun B, Fan X, Dong S, Bai Y, Shi Y (2017) A cost-effective method for preparing mechanically stable anti-corrosive superhydrophobic coating based on electrochemically exfoliated graphene. Colloids Surf A 513:396–401
Guo P, Zhai S, Xiao Z, An Q (2015) One-step fabrication of highly stable, superhydrophobic composites from controllable and low-cost PMHS/TEOS sols for efficient oil cleanup. J Colloid Interface Sci 446:155–162
Zhao J, Leng B, Shao Z, de With G, Ming W (2013) Triple-scale structured superhydrophobic and highly oleophobic surfaces. RSC Adv 3(44):22332–22339
Wang Y, Liu X, Zhang H, Zhou Z (2015) Superhydrophobic surfaces created by a one-step solution-immersion process and their drag-reduction effect on water. RSC Adv 5(24):18909–18914
Abbas R, Khereby MA, Sadik WA, El Demerdash AGM (2014) Fabrication of durable and cost effective superhydrophobic cotton textiles via simple one step process. Cellulose 22(1):887–896
Khosravi M, Azizian S (2017) Preparation of superhydrophobic and superoleophilic nanostructured layer on steel mesh for oil-water separation. Sep Purif Technol 172:366–373
Ge B, Men X, Zhu X, Zhang Z (2015) A superhydrophobic monolithic material with tunable wettability for oil and water separation. J Mater Sci 50(6):2365–2369. doi:10.1007/s10853-014-8756-4
Zhang W, Zhai X, Xiang T, Zhou M, Zang D, Gao Z, Wang C (2016) Superhydrophobic melamine sponge with excellent surface selectivity and fire retardancy for oil absorption. J Mater Sci 52(1):73–85. doi:10.1007/s10853-016-0235-7
Alexander S, Eastoe J, Lord AM, Guittard F, Barron AR (2016) Branched hydrocarbon low surface energy materials for superhydrophobic nanoparticle derived surfaces. ACS Appl Mater Interfaces 8(1):660–666
Liu Y, Cao H, Chen S, Wang D (2015) Ag nanoparticle-loaded hierarchical superamphiphobic surface on an Al substrate with enhanced anticorrosion and antibacterial properties. J Phys Chem C 119(45):25449–25456
Gu CD, Lian JS, Jiang ZH, Jiang Q (2006) Enhanced tensile ductility in an electrodeposited nanocrystalline Ni. Scr Mater 54(4):579–584
Gu C, Lian J, He J, Jiang Z, Jiang Q (2006) High corrosion-resistance nanocrystalline Ni coating on AZ91D magnesium alloy. Surf Coat Technol 200(18–19):5413–5418
Gu C, Tu J (2011) One-step fabrication of nanostructured Ni film with lotus effect from deep eutectic solvent. Langmuir ACS J Surf Colloids 27(16):10132–10140
Cho H, Schaefer C, Toeroek B (2016) Hydrogenations and deuterium labeling with aluminum-based metal alloys under aqueous conditions. Curr Org Synth 13(2):255–277
Wang Q, Yu M, Chen G, Chen Q, Tian J (2016) Robust fabrication of fluorine-free superhydrophobic steel mesh for efficient oil/water separation. J Mater Sci 52(5):2549–2559. doi:10.1007/s10853-016-0548-6
He G, Lu S, Xu W, Szunerits S, Boukherroub R, Zhang H (2015) Controllable growth of durable superhydrophobic coatings on a copper substrate via electrodeposition. Phys Chem Chem Phys 17(16):10871–10880
Lin F, Li SH, Li YS, Li HJ, Zhang LJ, Zhai J, Song YL, Liu BQ, Jiang L, Zhu DB (2002) Super-hydrophobic surfaces: from natural to artificial. Adv Mater 14:1857–1860
De la Rosa E, Sepulveda-Guzman S, Reeja-Jayan B, Torres A, Salas P, Elizondo N, Yacaman MJ (2007) Controlling the growth and luminescence properties of well-faceted ZnO nanorods. J Phys Chem C 111(24):8489–8495
Suresh Kumar P, Sundaramurthy J, Mangalaraj D, Nataraj D, Rajarathnam D, Srinivasan MP (2011) Enhanced super-hydrophobic and switching behavior of ZnO nanostructured surfaces prepared by simple solution–immersion successive ionic layer adsorption and reaction process. J Colloid Interface Sci 363(1):51–58
Singh J, Yang J-K, Chang Y-Y (2016) Synthesis of nano zero-valent metals from the leaching liquor of automobile shredder residue: a mechanism and potential applications for phenol degradation in water. Process Saf Environ Prot 102:204–213
Guo Y, Liu X, Wang X, Iqbal A, Yang C, Liu W, Qin W (2015) Carbon dot/NiAl-layered double hydroxide hybrid material: facile synthesis, intrinsic peroxidase-like catalytic activity and its application. RSC Adv 5(116):95495–95503
Cai N, Liu Q, Tong X, Zhou G (2014) X-ray photoelectron spectroscopy study of the passivation of NiAl(100) by water vapor. Langmuir ACS J Surf Colloids 30(3):774–783
Liu F, Qiu L, Zhao L, Wang H, Kan Y, Song X (2006) Accurate measurements of the oxide thickness for ultra-thin SiO2 on Si by using XPS. Chemistry 69(5):393–398
Jiang L, Wang R, Yang B, Li TJ, Tryk DA, Fujishima A, Hashimoto K, Zhu DB (2000) Binary cooperative complementary nanoscale interfacial materials. Pure Appl Chem 72(1–2):73–81
Dong Z, Le X, Li X, Zhang W, Dong C, Ma J (2014) Silver nanoparticles immobilized on fibrous nano-silica as highly efficient and recyclable heterogeneous catalyst for reduction of 4-nitrophenol and 2-nitroaniline. Appl Catal B 158–159:129–135
Mustri B, Devendra A, Molly T, Gowhar AN, Mehraj US, Farid K (2016) Hierarchical synthesis of silver monoliths and their efficient catalytic activity for the reduction of 4-nitrophenol to 4-aminophenol. New J Chem 40:6787–6795
Quites FJ, Azevedo CKS, Alves EPP, Germino JC, Vinhas RCG, Landers R, Terezo AJ, Atvars TDZ (2016) Ag nanoparticles-based zinc hydroxide-layered hybrids as novel and efficient catalysts for reduction of 4-nitrophenol to 4-aminophenol. J Braz Chem Soc. doi:10.5935/0103-5053.20160152
Gupta VK, Atar N, Yola ML, Ustundag Z, Uzun L (2014) A novel magnetic Fe@Au core-shell nanoparticles anchored graphene oxide recyclable nanocatalyst for the reduction of nitrophenol compounds. Water Res 48:210–217
Dong Z, Le X, Dong C, Zhang W, Li X, Ma J (2015) Ni@Pd core–shell nanoparticles modified fibrous silica nanospheres as highly efficient and recoverable catalyst for reduction of 4-nitrophenol and hydrodechlorination of 4-chlorophenol. Appl Catal B 162:372–380
Hernandez-Gordillo A, Arroyo M, Zanella R, Rodriguez-Gonzalez V (2014) Photoconversion of 4-nitrophenol in the presence of hydrazine with AgNPs–TiO2 nanoparticles prepared by the sol–gel method. J Hazard Mater 268:84–91
Acknowledgements
The authors thank the National Natural Science Foundation of China (No. 21271027) for financial support.
Author information
Authors and Affiliations
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
About this article
Cite this article
Li, J., Lu, S., Xu, W. et al. Fabrication of stable Ni–Al4Ni3–Al2O3 superhydrophobic surface on aluminum substrate for self-cleaning, anti-corrosive and catalytic performance. J Mater Sci 53, 1097–1109 (2018). https://doi.org/10.1007/s10853-017-1569-5
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-017-1569-5