Abstract
The Pr3+-doped Sr2Al2SiO7 phosphors with red emission were synthesized by conventional solid-state reaction in air for the first time. The photoluminescence properties of the phosphors and structural phase were investigated. The red emission of the phosphors was observed under the range of 420–500 nm excitation, which covered the emission spectra of blue LED. The optimal emission intensity was obtained when Pr-doping content was 0.008 mol and the chromaticity coordinates of these phosphors could be slightly tuned by changing the Pr3+ concentration. Furthermore, the investigation of temperature dependence of luminescence and the water immersion experiment indicated that the Pr-doped Sr2Al2SiO7 phosphors were highly thermally stable and waterproof.
Similar content being viewed by others
References
Feldmann C, Justel T, Ronda CR, Schmidt PJ (2003) Adv Funct Mater 12:511
Sheu JK, Chang SJ, Kuo CH, Su YK, Wu LW, Lin YC et al (2003) IEEE Photonic Technol Lett 15:18
Ye S, Xiao F, Pan YX, Ma YY, Zhang QY et al (2010) Mater Sci Eng R 71:1
Höppe HA (2009) Angew Chem Int Ed 48:3572
Kuo T, Huang C, Chen T (2010) Opt Express 18:102
Qian FJ, Fu RL, Agathopoulos S, Gu XG, Song XF (2012) J Lumin 132:71
Wang XM, Wang CH, Kuang XJ, Zou RQ, Wang YX, Jing XP (2012) Inorg Chem 51:3540
Diallo PT, Boutinaud P, Mahiou R, Cousseins JC (1997) Phys Stat Sol A 160:255
Gaft M, Reisfeld R, Panczer G (2005) Luminescence spectroscopy of mineral’s and materials, vol 18. Springer, Heidelberg, p 133
Chawla S, Kumar N, Chander H (2009) J Lumin 12:114
Yang XY, Liu J, Yang H, Yu XB, Guo YZ, Zhou YQ et al (2009) J Mater Chem 19:3771
Sun HQ, Peng DF, Wang XS, Tang MM, Zhang QW (2011) J Appl Phys 110:016102
Sun HQ, Peng DF, Wang XS, Tang MM, Zhang QW et al (2012) J Appl Phys 111:046102
Peng DF, Sun HQ, Wang XS, Zhang JC, Tang MM et al (2012) J Alloy Compd 511:159
Peng DF, Sun HQ, Wang XS, Zhang JC, Tang MM et al (2011) Mater Sci Eng B 176(18):1513
Jiao HY, Wang YH (2010) Appl Phys B 98:423
Ding YL, Zhang YX, Wang ZY, Li W, Mao DL, Han HB et al (2009) J Lumin 129:294
Shanon RD (1976) Acta Crystallogr A32:751
Song ZG, Xu YY, Li C, Li YJ, Zhao ZY, Yang ZW et al (2013) Ceram Int 39:2821
Xie RJ, Mitomo M, Uheda K, Xu FF, Akumine Y (2002) J Am Ceram Soc 85:1229
Xia Z, Arcangeli A, Faoro R, Tonelli M (2011) Optoelectron Adv Mater 5:336
Huang X, Han S, Huang W, Liu X (2013) Chem Soc Rev 42:173
Pandey A, Rai VK (2013) Dalton Trans. doi:10.1039/c3dt50592h
Ji PT, Chen XY, Wu YQ (2011) Appl Surf Sci 258:1888
Chen L, Lin CC, Yeh CW, Liu RS (2012) Materials 3(3):2172
Chung JH, Ryu JH (2012) Ceram Int 38:4601
Ryu JH, Park YG, Won HS, Kim SH, Suziki H, Yoon C (2008) J Ceram Soc Jpn 116:389
Qin CX, Huang YL, Shi L, Chen JQ, Qiao XB, Seo HJ (2009) J Phys D Appl Phys 42:185105
Xie RJ, Hirosaki N, Mitomo M (2006) Appl Phys Lett 89:241103
Liu TC, Cheng BM, Hu SF, Liu RS (2011) Chem Mater 23:3698
Jung YW, Lee B, Singh SP, Sohn KS (2010) Opt Express 18:17805
Lin CC, Liu R-S (2011) J Phys Chem Lett 2:1268
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zou, H., Peng, D., Chu, Z. et al. A highly thermal stable and waterproof red phosphor: Pr3+-doped Sr2Al2SiO7 . J Mater Sci 48, 7981–7985 (2013). https://doi.org/10.1007/s10853-013-7609-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-013-7609-x