Abstract
Highly textured Ca3Co4O9 thermoelectrics were fabricated by a so-called multisheet cofiring (MSC) technique in combination with the commonly practiced spark plasma sintering (SPS) technique. X-ray diffraction analysis revealed that the MSC technique significantly enhances the degree of texture compared with the conventional SPS technique. This was confirmed by microstructure analysis performed on polished and chemically etched specimens. The power factor and the thermoelectric figure of merit for the specimen produced by the MSC technique were estimated to be ~5.2 × 10−4 W/mK2 and ~0.4, respectively, both of which are ~20% larger than those of the normally processed specimens. A comparative study of the thermoelectric properties, such as electrical resistivity and Seebeck coefficient, clearly demonstrated that texture mainly influences the electrical resistivity and consequently enhances the thermoelectric properties.
Similar content being viewed by others
References
Fujita K, Mochida T, Nakamura K (2001) Jpn J Appl Phys 40(7):4644
Koumoto K, Terasaki I, Funahashi R (2006) MRS Bull 31(3):206
Liu YH, Lin YH, Shi Z, Nan CW, Shen ZJ (2005) J Am Ceram Soc 88(5):1337
Sugiura K, Ohta H, Nomura K, Hirano M, Hosono H, Koumoto K (2006) Appl Phys Lett 89(3):032111
Shen JJ, Liu XX, Zhu TJ, Zhao XB (2009) J Mater Sci 44(7):1889. doi:10.1007/s10853-009-3279-0
Diez JC, Guilmeau E, Madre MA, Marinel S, Lemonnier S, Sotelo A (2009) Solid State Ionics 180(11–13):827
Son JY, Shin YH, Park CS (2008) J Appl Phys 104(3):033538
Guilmeau E, Itahara H, Tani T, Chateigner D, Grebille D (2005) J Appl Phys 97(6):064902
Zhou YQ, Matsubara I, Horii S, Takeuchi T, Funahashi R, Shikano M, Shimoyama J, Kishio K, Shin W, Izu N, Murayama N (2003) J Appl Phys 93(5):2653
Mikami M, Guilmeau E, Funahashi R, Chong KJ, Chateigner D (2005) J Mater Res 20(9):2491
Liu HQ, Wang FP, Liu F, Song Y, Jiang ZH (2006) J Mater Sci Mater Electron 17(7):525
Liu HQ, Zhao XB, Zhu TJ, Song Y, Wang FP (2009) Curr Appl Phys 9(2):409
Zhang YF, Zhang JX (2008) J Mater Process Technol 208(1–3):70
Wang DL, Chen LD, Wang Q, Li JG (2004) J Alloy Compd 376(1–2):58
Guilmeau E, Funahashi R, Mikami M, Chong K, Chateigner D (2004) Appl Phys Lett 85(9):1490
Prevel M, Lemonnier S, Klein Y, Hébert S, Chateigner D, Ouladdiaf B, Noudem JG (2005) J Appl Phys 98(9):093706
Masset AC, Michel C, Maignan A, Hervieu M, Toulemonde O, Studer F, Raveau B, Hejtmanek J (2000) Phys Rev B 62(1):166
Kanno T, Yotsuhashi S, Adachi H (2004) Appl Phys Lett 85(5):739
Shikano M, Funahashi R (2003) Appl Phys Lett 82(12):1851
Jo W, Kim DY, Hwang NM (2006) J Am Ceram Soc 89(8):2369
Moon JW, Nagahama D, Masuda Y, Seo WS, Koumoto K (2001) J Ceram Soc Jpn 109(8):647
Itahara H, Tani T (2004) R&D Rev Toyota CRDL 39(1):63
Jones JL, Iverson BJ, Bowman KJ (2007) J Am Ceram Soc 90(8):2297
Guilmeau E, Chateigner D, Noudem J, Funahashi R, Horii S, Ouladdiaf B (2005) J Appl Crystallogr 38:199
Lotgering FK (1959) J Inorg Nucl Chem 9(2):113
Acknowledgements
This work was supported by the Mid-career Researcher Program of NRF/MEST (2010-0000463) in association with the Converging Research Center Program through the Ministry of Education, Science and Technology (2009-0093723) and the Core Technology of Materials Research and Development Program of the Korea Ministry of Intelligence and Economy (K00060071-55512).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kwon, OJ., Jo, W., Ko, KE. et al. Thermoelectric properties and texture evaluation of Ca3Co4O9 prepared by a cost-effective multisheet cofiring technique. J Mater Sci 46, 2887–2894 (2011). https://doi.org/10.1007/s10853-010-5163-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-010-5163-3