Abstract
Photochemical modification of single-walled carbon nanotubes (SWCNTs) was carried out by covalent attachment of 2-propanol-2-yl radicals on the surface of SWCNTs, which were engendered by the photolysis of 1-[4-(2-Hydroxyethoxy)-phenyl]-2-hydroxy-2-methyl-1-propane-1-one (HPHMP) under ultraviolet (UV) light. Pristine single-walled carbon nanotubes (p-SWCNTs) were dispersed in acetone along with HPHMP photoinitiator. After that, the mixture was irradiated by UV light to generate the free radicals which were introduced onto the surface of SWCNTs. The modification of SWCNTs was supported by UV/visible spectroscopy, Fourier transform infrared spectroscopy (FT-IR), Raman spectroscopy, thermal gravimetric analysis–mass spectrometry (TGA–MS), and transmission electron microscopy (TEM). UV/visible results revealed the loss of van Hove singularities due to covalent modification. The modification was further verified by FT-IR showing the signals at 3421 and 1100 cm−1 due to stretching and bending of O–H group, respectively. Moreover, other peaks at 2927 and 2858 cm−1 indicated the asymmetric and symmetric stretching modes of aliphatic C–H bond, respectively. Raman spectra illustrated that the intensity ratio of the tangential mode to the disorder mode (I G/I D), for modified SWCNTs (F-SWCNTs), decreased nearly four times than p-SWCNTs. TGA–MS also evidenced the signal corresponding to m/z 59 at 400 °C indicating the presence of 2-propanol-2-yl groups. TEM and dispersibility data demonstrated that the sidewall modification detached the bundled structure, enhanced the dispersion in common organic solvents and retained the original size of SWCNTs without hefty modification, which could cut or damage the nanotubes.
Similar content being viewed by others
References
Iijima S (1991) Nature 354:56
Nishikawa M et al (2009) J Mater Sci 44(1):339. doi:10.1007/s10853-008-3127-7
Chen RJ, Zhang Y, Wang D (2001) J Am Chem Soc 123:3838
Barthos R, Méhn D, Demortier A (2005) Carbon 43:321
Wang Y, Iqbal Z, Mitra S (2005) Carbon 43(5):1015
Marcux PR, Schreiber J, Batail P (2002) Phys Chem Chem Phys 4:2278
Hu H, Zhao B, Hamon MA (2003) J Am Chem Soc 125:14893
Mickelson ET, Huffman CB, Rinzler AG (1998) Chem Phys Lett 296:188
Tasis D, Tagmatarchis N, Bianco A (2006) Chem Rev 106:1105
Liu M, Yang Y, Zhu T (2007) J Phys Chem 111(6C):2379
Nakamura T, Ishihara M (2004) Diam Relat Mater 13(11–12):1971
Nakamura T, Ohana T, Ishihara M (2008) Diam Relat Mater 17(4–5):559
Kovtyukhova NI, Mallouk TE, Pan L (2003) J Am Chem Soc 125:9761
Larsen RM (2009) J Mater Sci 44(3):799. doi:10.1007/s10853-008-3155-3
Najafi E, Kim J, Han S (2006) Colloids Surf 284(A):373
Umek P, Seo J, Hernadi K (2003) Chem Mater 15(25):4751
Wu W, Zhang S, Li Y (2003) Macromolecules 36(17):6286
Pavia D, Lampman G et al (2009) Introduction to spectroscopy. Cole Pub Co. Ltd, Florence
Liu M, Yang Y, Zhu T (2005) Carbon 43(7):1470
Ahmad MN, Xie JY, Ma YH, Yang WT (2010) New Carbon Mater 25(2):134
Peng H, Alemany L, Margrave J (2003) J Am Chem Soc 125(49):15174
Vacek K, Geimer J (1999) J Chem Soc Perk Trans 2(11):2469
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ahmad, M.N., Nadeem, M., Ma, Y. et al. Photochemical modification of single-walled carbon nanotubes using HPHMP photoinitiator for enhanced organic solvent dispersion. J Mater Sci 45, 5591–5597 (2010). https://doi.org/10.1007/s10853-010-4621-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-010-4621-2