Abstract
Massive, pure cementite layers were grown on ferrite substrates by nitrocarburising in a dedicated NH3/H2/CO/N2 containing gas atmosphere at temperatures in the range of 783–843 K. From the parabolic layer-growth constants, an “apparent” activation energy for cementite-layer growth of 109 ± 12 kJ/mol was obtained. This “apparent” activation energy can be subdivided into a positive contribution due to the activation energy for (tracer) diffusion of carbon in cementite and a negative contribution due to the temperature dependence of the difference of the carbon activity in cementite at the surface and at the interface cementite/ferrite.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Cementite, Fe3C, is, besides ferrite, the major constituent of plain carbon and mildly alloyed steels. Notwithstanding its great technological importance, little is known about the intrinsic properties of cementite. This dearth of fundamental knowledge on cementite is mainly due to the difficulty in preparing single-phase (single- or polycrystalline) cementite specimens. In the past, several works dealt with the production of bulk cementite specimens applying different methods [1–5]. Yet, only recently, it was reported for the first time that massive cementite layers can be grown on ferrite substrates by a dedicated gaseous nitrocarburising process [6]. The addition of ammonia to the carburising gas mixture was found to be decisive for the suppression of both the formation of graphitic soot and the disintegration of cementite once formed (metal dusting).
Gaseous nitrocarburising of iron or iron-based alloys is a thermochemical heat treatment usually performed at temperatures between 773 and 853 K below the ternary eutectoid temperature of the Fe–N–C solid solution [7]. By this process, which gathered great technical importance during the last decades [8, 9], nitrogen and carbon delivered by the gas phase are diffusionally incorporated into the surface-region of the iron-based workpiece [7].
This results in (i) the formation of a compound layer (several 10-μm thick) containing, depending on the treatment temperature (and pressure) and the composition of the gas atmosphere, different phases, typically γ′-Fe4N1−y and ε-Fe3(N,C)1+x [10], but sometimes, under certain circumstances, also cementite [6, 11], and (ii) the formation of a diffusion zone (several 100-μm thick), enriched with interstitial nitrogen (and carbon). Whereas the compound layer is responsible for a considerable enhancement of the corrosion and wear resistance, the diffusion zone enhances the fatigue endurance [12].
The present work focuses on an analysis of cementite-layer growth kinetics. Massive cementite layers were grown on ferrite substrates in the treatment-temperature range of 783–843 K, thus extending the preceding study [6] in which only experiments at T = 823 K were conducted. The experimental values for the (temperature dependence of the) parabolic growth constant were determined. These results were evaluated in terms of an “apparent” activation energy for cementite-layer growth and discussed with reference to previous work on the kinetics of cementite (layer) growth [4, 13–19]. The discrepancy between the results of the present work and the literature data are discussed in terms of thermodynamic consequences of the different gas atmospheres used.
Experimental
Pure iron foils (20 mm × 25 mm) were produced by cold rolling a ferrite cast rod (Alfa Aesar, 99.98 wt% Fe) on both sides to a thickness of 1 mm. The specimens to be nitrocarburised were cut from this cold-rolled plate, ground, polished (final stage 1 μm diamond suspension) and cleaned ultrasonically in ethanol. Prior to the nitrocarburising process, the specimens were recrystallised at 973 K for 2 h under a hydrogen flow of 200 ml/min, polished (final stage 1 μm diamond suspension) and cleaned ultrasonically in ethanol.
Gaseous nitrocarburising was carried out in a vertical quartz-tube furnace. To retain solid states produced at the nitrocarburising temperature, the quartz-tube furnace was equipped at its end with a water (flushed with N2) container for quenching the specimens to room temperature. The iron foils were suspended on a quartz fibre and positioned in the middle of the furnace where the process temperature prevailed, controlled within ±1 K. In order to quench the specimens to room temperature, the quartz fibre was destroyed by a mechanical device and the specimen dropped into the water container. The gas atmosphere was composed of 13 vol.% ammonia (99.999 vol.% purity) as a nitrogen-providing medium, 58 vol.% hydrogen (99.999 vol.% purity), 20 vol.% carbon monoxide (99.97 vol.% purity) as a carbon-providing medium and 9 vol.% nitrogen (99.999 vol.% purity) as inert gas; each gas flux was controlled by a mass-flow controller. In order to ensure that ammonia dissociation, which would change the composition of the gas atmosphere, can be neglected, an overall linear flow rate of 13.5 mm/s (calculated for the gas volume at room temperature) through the quartz retort (diameter 28 mm) was maintained.
Four sets of nitrocarburising experiments were performed at T = 783, 803, 823 and 843 K (the data for T = 823 K were already reported in a preceding study [6]) for different treatment times in the range of 5 min–48 h.
After gaseous nitrocarburising and quenching, the specimens were cut into two pieces, one used for optical microscopy and one used for X-ray diffraction (XRD).
In order to avoid mechanical damage at the surface of the specimen (parts) used for metallographic analysis and to ensure a sufficient sharpness at the specimen surface in the cross-sections, the specimens were covered with a protective nickel layer electrodeposited at 333 K using a Watts bath [10, 20]. Thereafter, the specimens were embedded (Polyfast, Buehler GmbH), ground, polished (final stage 1 μm diamond suspension) and etched using 1 vol.% Nital containing 0.1 vol.% HCl [21]. To improve the optical contrast between the massive cementite layer and the ferrite substrate, the cross-sectional specimens were additionally stained using either an alkaline potassium permanganate solution (1 g NaOH, 1 g KOH and 4 g KMnO4 per 100 ml distilled water) at 328 K [6, 22] of which the effect is similar to that of a Murakami solution [10, 22] or an alkaline sodium picrate solution (25 g NaOH and 2 g picric acid per 75 ml distilled water) at room temperature [22]. By these procedures, the massive cementite layer gets, due to its high carbon content, severely stained and can therefore easily be distinguished upon light optical microscopy from the ferrite substrate, which remains unstained. Light optical microscopy was performed using a Zeiss Axiophot microscope.
For the determination of the cementite-layer thickness, several micrographs were taken from each specimen. From these micrographs, the area of the massive cementite layer was measured and divided through its lateral length, yielding, after averaging the experimental values obtained from several micrographs, the cementite-layer thickness.
Phase identification was carried out by X-ray diffraction to verify the presence of a massive cementite layer on the ferrite substrate. A PANalytical X’Pert Multi-Purpose Diffractometer equipped with a graphite monochromator in the diffracted beam, utilising CoKα radiation and Bragg–Brentano geometry, was used. To achieve better crystallite statistics, the specimens were rotated during the measurements around their surface normal.
Results and evaluation
All experiments performed led to the formation of massive cementite layers on the ferrite substrates (cf. Fig. 1).
The squared value of the experimentally determined cementite-layer thickness (cf. Sect. Experimental) was plotted versus the treatment time at the various temperatures (cf. Fig. 2). Occurrence of parabolic layer growth from t = 0 onwards is given by a straight line through the origin of the plot of the squared layer thickness versus time (cf. Fig. 2). Such a simple parabolic layer growth was assumed for treatment times larger than 1 h. Evidently, as follows from the data in Fig. 2, for treatment times t < 1 h cementite-layer growth occurred faster than indicated by such a parabolic relation. This can be discussed as follows.
At the beginning of the cementite formation, an incompletely closed cementite layer can occur. Hence, carbon can diffuse through ferrite to the (also bottom tip of the) cementite grains growing from the surface (this diffusion through ferrite is much faster than diffusion through cementite), thus bypassing the cementite. Further, shortly after establishment of a closed cementite layer, short-circuit diffusion of carbon may occur through thin and defect-rich parts of the cementite layer, exhibiting a relatively high grain-boundary density. Both ‘bypass/short-circuit’ mechanisms for carbon lead to relatively fast cementite growth as compared to later stages (cf. [6]). The initial ‘bypass/short-circuit’ mechanism involves that the parabolic cementite-layer growth law pertaining to later stages of cementite-layer growth has to be modified by introducing a hypothetical initial cementite-layer thickness S 0 (>0) at t = 0. Hence, the time-dependence of the cementite-layer growth is given by
where S denotes the cementite-layer thickness, k the growth constant and t the treatment time.
Least-squares fitting of Eq. 1 to the experimental data at the four treatment temperatures for t > 1 h (cf. Fig. 2) yielded the results for the growth constant and the hypothetical initial cementite-layer thickness shown in Table 1.
An Arrhenius-type temperature dependence is adopted for the growth constant k
where k 0 denotes a pre-exponential factor, Q app an “apparent” activation energy of cementite-layer growth, R the gas constant and T the treatment temperature. Then, a plot of the logarithm of the growth constant versus the inverse treatment temperature should yield a straight line. Such linear dependence is observed indeed (cf. Fig. 3), validating the application of Eq. 2 (see also Sect. Interpretation of the “apparent” activation energy). The slope of the plot, \( m = - {{Q_{\text{app}} } \mathord{\left/ {\vphantom {{Q_{\text{app}} } R}} \right. \kern-\nulldelimiterspace} R}, \) yields an “apparent” activation energy equal to 109 ± 12 kJ/mol.
Discussion
Parabolic layer growth for interstitial compounds
In the literature, the growth kinetics of pure iron nitride layers [23–26] but also of cementite layers [4, 15, 16] was described by a parabolic growth law. A comparison of the rates of cementite-layer growth and γ′-Fe4N1−y-layer growth indicates that, at the same temperature, γ′-Fe4N1−y-layer growth proceeds faster than cementite-layer growth, which can be ascribed to nitrogen volume diffusion in γ′-Fe4N1−y being faster than carbon volume diffusion in cementite.
Parabolic layer growth according to Eq. 1 with S0 = 0 is expected in particular for close-to-stoichiometric interstitial compounds like γ′-Fe4N and cementite if the following general assumptions are valid [18, 27]: (a) local equilibrium at the interface gas atmosphere/specimen surface; (b) local equilibrium at the interface compound layer/ferrite substrate; (c) a completely closed, massive compound layer; i.e. nitrogen/carbon mass transport proceeds exclusively via nitrogen/carbon (volume) diffusion through the massive compound layer.
If these conditions hold, the parabolic growth constant is proportional to the product of (i) the (tracer)diffusion coefficient of nitrogen/carbonFootnote 1 in the compound layer, D*—diffusion of the metal component (iron) can generally be neglected [29]—and of (ii) a function f(Δa) (taken as time independent), which increases monotonously with the difference of the activity of nitrogen/carbon in the solid at the surface, \( a^{\text{surface}} , \) and the activity of nitrogen/carbon in the solid at the interface layer/substrate, \( a^{\text{interface}} \) Footnote 2:
with
According to the assumption of local equilibrium at the surface (see above), the activity a surface is determined by the composition of the gas atmosphere, and is controlled as described in Sect. Thermodynamics of gaseous nitrocarburising. According to the assumption of local equilibrium at the layer/substrate interface, the activity \( a^{\text{interface}} \) is compatible with the corresponding phase boundary in the ternary phase diagram Fe–N–C.
Thermodynamics of gaseous nitrocarburising
Upon exposing the ferrite substrates to the NH3/H2/CO/N2-containing gas atmosphere, N and C are introduced into the solid, where NH3 and CO act as the nitrogen and carbon-providing media.Footnote 3
Since thermal decomposition of NH3 as well as decomposition of (metastable) iron nitrides are slow,Footnote 4 transfer of nitrogen from the gas atmosphere into the specimen can be described by the following heterogeneous chemical equilibrium:
where [N] denotes nitrogen either dissolved in the ferrite substrate (solid solution) or in iron nitride. The chemical potential \( \mu_{\text{N}}^{\text{surface}} \) and the activity \( a_{\text{N}}^{\text{surface}} \) of nitrogen dissolved in the solid at the surface (assumed to be in equilibrium with the gas atmosphere) obey:
where \( \mu_{{{\text{N}}_{ 2} }}^{ 0} , \) \( \mu_{{{\text{NH}}_{ 3} }}^{ 0} \) and \( \mu_{{{\text{H}}_{ 2} }}^{ 0} \) are the chemical potentials of nitrogen, ammonia and hydrogen in the gaseous reference state (pressure p 0 = 1 atm) and \( r_{\text{N}} = \tfrac{{p_{{{\text{NH}}_{ 3} }} }}{{p_{{{\rm H}_{2} }}^{3/2} }} \) denotes the so-called nitriding potential, where \( p_{{{\text{NH}}_{ 3} }} \) and \( p_{{{\text{H}}_{ 2} }} \) are the partial pressures of ammonia and hydrogen in the gas atmosphere. Hence, according to Eq. 6, the nitriding potentialFootnote 5 of the gas atmosphere at the surface fixes the chemical potential and the activity of nitrogen in the solid at the surface [31]. It follows that the activity \( a_{\text{N}}^{\text{surface}} \) of nitrogen dissolved in the solid at the surface (assumed to be in equilibrium with the gas atmosphere) obeys:
Transfer of carbon from the gas atmosphere into the specimen is associated with the presence of CO in the gas atmosphere and can proceed via the, in principle potently carburising, heterogeneous Boudouard equilibrium:
and the so-called heterogeneous water-gas equilibrium
where [C] denotes carbon dissolved either in the ferrite substrate (solid solution) or in cementite. The hydrogen necessary for the chemical equilibrium given by Eq. 9 is delivered by the H2-containing gas atmosphere. The chemical potentials \( \mu_{\text{C, (8)}}^{\text{surface}} \) and \( \mu_{\text{C, (9)}}^{\text{surface}} \) and the activities \( a_{\text{C, (8)}}^{\text{surface}} \) and \( a_{\text{C, (9)}}^{\text{surface}} \) of carbon dissolved in the solid at the surface (assumed to be in equilibrium with the gas atmosphere according to either Eqs. 8 or 9 obey:
and
where \( \mu_{\text{C}}^{ 0} \) is the chemical potential of graphite in the reference state (pressure p 0 = 1 atm) and \( \mu_{\text{CO}}^{ 0} , \) \( \mu_{{{\text{CO}}_{ 2} }}^{ 0} , \) \( \mu_{{{\text{H}}_{ 2} }}^{ 0} \) and \( \mu_{{{\text{H}}_{ 2} {\text{O}}}}^{ 0} \) are the chemical potentials of carbon monoxide, carbon dioxide, hydrogen and water in the gaseous reference state (pressure p 0 = 1 atm) and \( r_{\text{C, (8)}} = \tfrac{{p_{\text{CO}}^{ 2} }}{{p_{{{\text{CO}}_{ 2} }} }} \) and \( r_{\text{C, (9)}} = \tfrac{{p_{\text{CO}}\,\cdot\,p_{{{\text{H}}_{ 2} }} }}{{p_{{{\text{H}}_{ 2} {\text{O}}}} }} \) denote the so-called carburising potentials according to the equilibria given by Eqs. 8 and 9, where \( p_{\text{CO}} , \) \( p_{{{\text{CO}}_{ 2} }} , \) \( p_{{{\text{H}}_{ 2} }} \) and \( p_{{{\text{H}}_{ 2} {\text{O}}}} \) are the partial pressures of carbon monoxide, carbon dioxide, hydrogen and water in the gas atmosphere. The carburising potential fixes, similar to the nitriding potential (see above), the chemical potential and the activity of carbon in the solid at the surface. It follows that the activity \( a_{\text{C,(i)}}^{\text{surface}} \) of carbon in the solid at the surface (assumed to be in equilibrium with the gas atmosphere) obeys for the equilibria given by Eqs. 8 and 9 (i = 8, 9):
and
For each of the equilibria given by Eqs. 8 and 9, a separate carbon activity in the solid at the surface can be calculated. The heterogeneous water–gas equilibrium (Eq. 9) is established much faster than the Boudouard equilibrium (Eq. 8) [32]. Therefore, the heterogeneous water–gas equilibrium (Eq. 9) is considered to control the carburising.
In general, in case of equilibrium with the nitrocarburising gas atmosphere, the carbon activity in the solid at the surface complies with the occurrence of simultaneous equilibrium for all possible reactions in the gas atmosphere. Thus, the equilibria given by Eqs. 14–16, have to be considered as well:
In the present experiments, neither CO2 (cf. Eq. 8) nor H2O (cf. Eq. 9) were initially present in the nitrocarburising gas atmosphere (\( p_{{{\text{CO}}_{ 2} }} = p_{{{\text{H}}_{ 2} {\text{O}}}} = 0 \)). Hence, the carbon activity according to either Eqs. 12 or 13 equals (hypothetically) infinity.
No soot formation occurred in the present experiments. Further, as discussed in Sect. Parabolic layer growth for interstitial compounds, local equilibrium (or at least a stationary state) at the interface gas atmosphere/specimen surface is a prerequisite for parabolic (cementite) layer growth as observed in this work. It is concluded that in the present experiments a finite carbon activity appears to rule in the solid at the surface. Such a finite, “effective” carbon activity can prevail if e.g. due to the chemical reaction according to Eq. 15, a certain amount of water is produced. The stationary presence of this amount of water induces a specific finite, “effective” carbon activity in the solid at the surface according to the heterogeneous water–gas equilibrium (cf. Eq. 13). The value of this “effective” carbon activity at the surface can be estimated using literature data (see what follows in Sect. Interpretation of the “apparent” activation energy).
It is also imaginable that the water determining the carbon activity according to Eq. 13 is the product of the carbon-delivering reaction given in Eq. 9. However, this reaction and thereby water formation can only take place at the specimen surface, where its rate is limited by the carbon uptake due to this Eq. 9, which decreases with increasing time. On the other hand, (i) Eq. 15 can, in principle, occur both at the specimen surface, catalysed by the specimen surface, and in the bulk of the gas atmosphere, and (ii) water formation according to Eq. 15 is time independent. A time-dependent water concentration at the specimen surface (as in case of water formation due to Eq. 9) involves a time-dependent “effective” carbon activity in the solid at the surface, which would lead to a deviation from parabolic growth kinetics, which is not observed (cf. Fig. 2). Thus, a major role of water formation according to Eq. 9 seems unlikely.
Interpretation of the “apparent” activation energy
Values reported for the activation energy of carbon volume diffusion in metal carbides range from about 125 kJ/mol up to 230 kJ/mol [29]; for cementite activation, energy values of 154 kJ/mol [18] and 163–185 kJ/mol [13, 14]Footnote 6 have been reported. These values differ considerably with the value of 109 ± 12 kJ/mol determined in the present work for the “apparent” activation energy. This difference arises because in the previous works, e.g. [13, 14], the carbon activities in the solid at the surface and at the interface with the substrate were known and accounted for in the determination of \( D_{\text{C}}^{ *} \) and its activation energy. In the present work, the value of the carbon activity in the solid at the surface is not known directly (cf. Sect. Thermodynamics of gaseous nitrocarburising), but can be derived indirectly.
The “apparent” activation energy value equal to 109 ± 12 kJ/mol was determined by Arrhenius-type analysis (see Fig. 3 in Sect. Results and evaluation). The slope of the straight line in the plot of the logarithm of the growth constant versus the inverse treatment temperature (cf. Fig. 3) depends on the temperature dependences of both \( D_{\text{C}}^{ *} \) (which is certainly of Arrhenius-type) and \( f\left( {\Updelta a_{\text{C}} } \right). \) \( f\left( {\Updelta a_{\text{C}} } \right) \) varies under the present experimental conditions strongly as a function of the treatment temperature due to the treatment temperature-dependent “effective” \( a_{\text{C}}^{\text{surface}} \)(recognising a practically temperature independent \( a_{\text{C}}^{\text{interface}} \); see below). As an Arrhenius-type temperature dependence has been observed for k (cf. Fig. 3), it is suggested that both \( D_{\text{C}}^{ *} \) and (also) f eff obey an Arrhenius-type temperature dependence. Thus, it follows from Eq. 3:
with \( f_{\text{eff}} = f\left( {\Updelta a_{\text{C}} } \right), \) and \( D_{{ 0 , {\text{C}}}}^{ *} \) and f 0,eff are pre-exponential factors for the (tracer) diffusion coefficient of carbon in cementite and f eff, respectively, and Q D the activation energy for the (tracer)diffusion of carbon in cementite and \( Q_{{f_{\text{eff}} }} \)the energy describing the temperature dependence of f eff. The “apparent” activation energy Q app for the cementite-layer growth is composed of the sum of the activation energy for the (tracer) diffusion of carbon in cementite, Q D, and the energy \( Q_{{f_{\text{eff}} }} \)describing the temperature dependence of f eff: \( Q_{\text{app}} = Q_{\text{D}} + Q_{{f_{\text{eff}} }} \). The discrepancy between the presently determined Q app = 109 ± 12 kJ/mol and Q D = 154 kJ/mol [18] and Q D = 163–185 kJ/mol [13, 14] implies that \( Q_{{f_{\text{eff}} }} \)must be negative.
Adopting a monotonous increase of f eff with \( \Updelta a_{\text{C}} \) (cf. Sect. Results and evaluation), a negative value for \( Q_{{f_{\text{eff}} }} \) implies that the carbon activity difference \( \Updelta a_{\text{C}} \) decreases with increasing temperature under the applied cementite-layer growth conditions. The temperature dependence of \( \Updelta a_{\text{C}} \) is governed by the temperature dependence of the “effective” carbon activity in the solid at the surface; the influence of the temperature dependence of the carbon activity at the interface cementite layer/ferrite substrate is marginal (\( a_{\text{C}}^{\text{interface}} \) is practically constantFootnote 7). Therefore, a decreasing carbon activity difference, \( \Updelta a_{\text{C}} \), with increasing temperature (see above), involves a decreasing “effective” carbon activity in the solid at the surface with increasing temperature.
As compared to the present work, the available experiments reported in the literature [13–15, 19] were performed at lower treatment temperatures.Footnote 8 Therefore, the present experimental data (growth constants for four different temperatures) can only be compared with these literature data (growth constants for various carbon activities in the solid at the surface) by extrapolation of the present experimental data to these lower temperatures. Therefore, in Fig. 4, the straight line obtained by least-squares fitting of Eq. 2 to the experimental data obtained in this work was extrapolated to lower temperatures (dashed line). In [13, 14] and [15, 19], carbon activities in the solid at the surface were adjusted at various values at 723 and 773 K, and the corresponding k (growth constant) values were determined. These k values, corresponding to specific carbon activities as indicated in the figure, lie below the extrapolated dashed line corresponding to the data of the current work (cf. Fig. 4). In order to determine the (“effective”) carbon activity in the solid at the surface for the presently applied gas atmosphere at 723 and 773 K, the literature data pertaining to 723 and 773 K have been (linearly; k vs. \( a_{\text{C}}^{\text{surface}} \)) extrapolated up to the dashed line derived from the present experiments. This approach led to relatively high “effective” carbon activities prevailing at the surface: a c = 65 (at 773 K) and a c = 260 (at 723 K). Hence, for the presently applied constant gas atmosphere, the “effective” carbon activity at the surface decreases with increasing treatment temperature. This result is compatible with the negative value obtained for \( Q_{{f_{\text{eff}} }} . \)
This specific temperature dependence of the “effective” carbon activity in the solid at the surface can be understood as follows. As discussed in Sect. Thermodynamics of gaseous nitrocarburising, the presently applied NH3/H2/CO/N2 containing gas atmosphere is not in thermodynamic equilibrium. Several homogeneous and heterogeneous chemical reactions (equilibria) can occur within the gas atmosphere at the surface of the solid (Eqs. 5, 8, 9, 14–16). In general, chemical equilibria are established faster at elevated temperatures. Hence, it may be expected that more H2O is formed (different stationary state) at higher temperatures according to Eq. 15. This leads to an “effective” carbon activity in the solid at the surface which is smaller at higher temperatures.
Conclusions
-
(i)
Massive, pure cementite layers can be grown on ferrite substrates in the range of 783–843 K and 5 min–48 h using a gas atmosphere containing 13 vol.% NH3, 58 vol.% H2, 20 vol.% CO and 9 vol.% N2. The addition of ammonia to the gas atmosphere is essential to avoid both soot formation and “metal dusting”.
-
(ii)
Cementite-layer growth in the range of 783–843 K obeys a parabolic growth law for t > 1 h. For t < 1 h, ‘bypass/short-circuit’ mechanisms occur leading to relatively fast cementite growth as compared to later stages (t > 1 h).
-
(iii)
The parabolic growth constant exhibits an Arrhenius-type temperature dependence. It is proportional to the product of the (tracer-)diffusion coefficient of carbon in the compound layer and the function \( f\left( {\Updelta a_{\text{C}} } \right) \) containing the temperature-dependent activity difference of carbon over the thickness of the compound layer. Both factors separately comply with a temperature dependence according to the Arrhenius formalism.
-
(iv)
An “apparent” activation energy, Q app, of 109 ± 12 kJ/mol was obtained for cementite-layer growth. This “apparent” activation energy Q app is composed of a positive contribution Q D due to the activation energy for (tracer) diffusion of carbon in cementite and a negative contribution \( Q_{{f_{\text{eff}} }} \) due to a decreasing “effective” carbon activity in the solid at the surface with increasing temperature. The formation of a stationary amount of water in the gas atmosphere may induce such a fixed, finite “effective” carbon activity in the solid at the surface.
Notes
It was shown that, due to cementite layer/ferrite substrate misfit-strain development, specific crystallographic directions of cementite, [uvw]C with w large, occur parallel to the surface normal of the specimen [28]. The diffusion data for carbon presented in this work pertain to these directions.
For details concerning the dependence of k on the activities a surface and \( a^{\text{interface}} \) with respect to the operating diffusion mechanism (see [18]).
At atmospheric pressure and at the applied treatment temperatures, N2 does not react with solid iron; it can be regarded as an inert gas.
This implies that the reaction \( {\text{NH}}_{ 3} \rightleftharpoons \tfrac{ 1}{ 2}{\text{N}}_{ 2} + \tfrac{ 3}{ 2}{\text{H}}_{ 2} \) is necessarily not in equilibrium in the gas phase, which is assured by a sufficiently large gas flux though the furnace (cf. Sect. Experimental and Ref. [26]), which is a prerequisite for significant N transfer to the iron.
In the present experiments, a nitriding potential of rN = 0.3 atm−1/2 was applied (cf. Sect. Experimental) which, in absence of CO, would lead to the formation of a γ′-Fe4N1−y compound layer [30].
It should be noted that this data was not determined on the basis of growth-rate dependence on temperature. The (tracer-)diffusion coefficient of carbon in cementite, \( D_{\text{C}}^{ *} , \) was determined for only a single temperature. The activation energy for carbon volume diffusion in cementite was then calculated adopting the Arrhenius equation for the diffusion coefficient of carbon in cementite, \( D_{\text{C}}^{ *} , \) employing two different values for the pre-exponential factor \( D_{{ 0 , {\text{C}}}}^{ *} \) for general, interstitial diffusion within metals from the literature.
The carbon activity in cementite at the interface cementite layer/ferrite substrate was calculated according to [33]. It was found that \( a_{\text{C}}^{\text{interface}} \)varies as a function of temperature from 2.88 (at 783 K) to 2.13 (at 843 K). Hence, \( a_{\text{C}}^{\text{interface}} \) can be considered as (nearly) constant.
The present authors also performed experiments at lower temperatures (773 and 723 K) applying the same gas atmosphere as for the other here-reported experiments. The analysis (XRD and optical microscopy) of the resulting compound layers revealed the presence of surface-adjacent Hägg carbide and graphite, additionally to cementite; thus the layers produced were not single-phase cementite.
References
Toyota Jidoshi KK, Toyota, Aichi, JP (Nonoyama H, Fukuizumi T, Morita A) Japanese Patent P58-122201, 5 July 1983
Mizubayashi H, Li SJ, Yumoto H, Shimotomai M (1999) Script Mater 40:773
Grabke HJ (2003) Mater Corr 54:736
Schneider A, Grabke HJ (2003) Mater Corr 54:793
Umemoto M, Todaka Y, Takahashi T, Li P, Tokumiya R, Tsuchiya K (2003) J Metastat Nanocryst Mater 15:607
Gressmann T, Nikolussi M, Leineweber A, Mittemeijer EJ (2006) Script Mat 55:723
Somers MAJ (2000) Heat Treat Met 27:92
Liedtke D, Baudis U, Boßlet J, Huchel U, Klümper-Westkamp H, Lerche W, Spieß H-J (2006) Wärmebehandlung von Eisenwerkstoffen—Nitrieren und Nitrocarburieren. Expert-Verlag, Renningen Malmsheim
Unterweiser PM, Gray AG (eds) (1977) Source book on nitriding. ASM, Metals Park, OH
Colijn PF, Mittemeijer EJ, Rozendaal HCF (1983) Z Metallkd 74:620
Somers MAJ, Mittemeijer EJ (1987) Surf Eng 3:123
Mittemeijer EJ (1983) J Heat Treat 3:114
Ozturk B, Fearing VL, Ruth JA, Simkovich G (1982) Metall Trans A 13A:1871
Ozturk B, Fearing VL, Ruth JA, Simkovich G (1984) Solid State Ionics 12:145
Schneider A, Inden G, Grabke HJ (2000) In: Rühle M, Gleiter H (eds) Interface controlled materials (Euromat 99). Weinheim, Wiley-VCH
Schneider A (2002) Corr Sci 44:2353
Arabczyk W, Konicki W, Narkiewicz U, Jasińska I, Kałucki K (2004) Appl Catal A 266:135
Hillert M, Höglund L, Ågren J (2005) J Appl Phys 98:053511
Schneider A, Inden G (2007) Comp Coupl Phase Diagr Thermochem 31:141
Chatterjee-Fischer R, Bodenhagen R, Eysell F-W, Hoffmann R, Liedtke D, Mallener H, Rembges W, Schreiner A, Welker G (1995) Wärmebehandlung von Eisenwerkstoffen. Expert-Verlag, Renningen-Malmsheim
Wells A (1985) J Mater Sci 20:2439. doi:https://doi.org/10.1007/BF00556072
Petzow G (1999) Metallographic etching. ASM International, Materials Park, OH
Schwerdtfeger K, Grieveson P, Turkdogan ET (1969) Trans TMS AIME 245:2461
Somers MAJ, Mittemeijer EJ (1995) Metall Mater Trans A 26A:57
Middendorf C, Mader W (2003) Z Metallkd 94:333
Mittemeijer EJ, Somers MAJ (1997) Surf Eng 13:483
Wagner C (1951) Atom movements. ASM, Cleveland, OH
Nikolussi M, Leineweber A, Mittemeijer EJ (2008) Acta Mat 56:5837
Wallace TC (1968) In: Hausner H, Bowman MG (eds) Fundamentals of refractory compounds. Plenum Press, New York
Lehrer E (1930) Z Elektrochem 36:383
Mittemeijer EJ, Slycke JT (1996) Surf Eng 12:152
Grabke HJ (1975) Arch Eisenhüttenw 46:75
Kunze J (1990) Nitrogen and carbon in iron and steel. Akademie-Verlag, Berlin
Open Access
This article is distributed under the terms of the Creative Commons Attribution Noncommercial License which permits any noncommercial use, distribution, and reproduction in any medium, provided the original author(s) and source are credited.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This is an open access article distributed under the terms of the Creative Commons Attribution Noncommercial License (https://creativecommons.org/licenses/by-nc/2.0), which permits any noncommercial use, distribution, and reproduction in any medium, provided the original author(s) and source are credited.
About this article
Cite this article
Nikolussi, M., Leineweber, A. & Mittemeijer, E.J. Growth of massive cementite layers; thermodynamic parameters and kinetics. J Mater Sci 44, 770–777 (2009). https://doi.org/10.1007/s10853-008-3160-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-008-3160-6