Abstract
The vitrification treatment has been successfully exploited as a solution for the disposal of polluted dredging spoils from the industrial area close to the Venice Lagoon. The addition of 20% by wt. of glass cullet to the calcined sediments in the vitrification batch provides a suitable chemical composition for the production of an inert glass, despite the compositional variations of the sediments. The obtained waste glass, after being finely ground, has been employed (i) as a raw material for the manufacture of sintered glass-ceramics, by cold pressing and single-step sintering at about 940∘C, and (ii) as sintering additive (the maximum addition being 10% by wt.) for the manufacture of traditional red single firing ceramic tiles, with a maximum firing temperature of 1186∘C. Both applications have proved to be promising: in the first case, the sintered glass ceramic product exhibits notable mechanical properties (bending strength > 130 MPa, HV ≈ 6.5 GPa); in the second case, the addition of waste glass does not modify substantially the investigated physical and mechanical properties of the traditional product (water absorption, linear shrinkage, bending strength, planarity).
Similar content being viewed by others
References
P. COLOMBO, G. BRUSATIN, E. BERNARDO and G. SCARINCI, Curr. Opin. Solid State Mater. Sci. 7(3) (2003) 225.
R. GUTMAN, Glastech. Ber. Glass Sci. Technol. 69(9) (1996) 223.
E. J DE GUIRE and S. H. RISBUD, J. Mat. Sci. 19 (1984) 1760.
S. KLEMANTASKI, W. A. ARCHIBALD, S. SCHOLES, A. P. SIKORSKI and P. S. ROGERS, British Patent 986289 (1965).
A KARAMANOV, I. GUTZOW, I. CHOMAKOV, J. CHRISTOV and L. KOSTOV, Glastech. Ber. Glass Sci. Technol. 67(8) (1994) 227.
A. KARAMANOV, M. PELINO and I. GUTZOW, in Proc. XVIII Int. Cong. On Glass, S. Francisco (1998).
C. CANTALE, S. CASTELLI, A. DONATO, D. M. TRAVERSO, P. COLOMBO and G. SCARINCI, Rad. Waste Manag. Nucl. Fuel Cycle 16 (1991) 25.
G. SCARINCI, G. BRUSATIN, L. BARBIERI, A. CORRADI, I. LANCELLOTTI, P. COLOMBO, S. HREGLICH and R. DALL'IGNA, J. Eur. Ceram. Soc. 20 (2000) 2485.
A. G. BERNSTEIN, E. BONSEMBIANTE, G. BRUSATIN, G. CALZOLARI, P. COLOMBO, R. DALL'IGNA, S. HREGLICH and G. SCARINCI, Waste Management 22(8) (2002) 865.
G. BRUSATIN, A. G. BERNSTEIN, E. BONSEMBIANTE, G. CALZOLARI, P. COLOMBO, R. DALL'IGNA, S. HREGLICH and G. SCARINCI, in Proc. of the 6th World Congress on Integrated Resources Management, Geneva 12-15 Feb. 2002.
M. W. DAVIES, B. KERRISON, W. E. GROSS, M. J. ROBSON and D. F. WITCHALL, J. Iron Steel Inst. 208 (1973) 348.
P. D. SARKISOV, The Modern State of Technology and Application of Glass-Ceramics, in: Glass'89 Survey papers ot the XVth International Congress on Glass Leningrad (1989) p. 411.
L. BARBIERI, A. CORRADI and I. LANCELLOTTI, J. Europ. Ceram. Soc. 22(11) (2002) 1759.
A. KARAMANOV, G. TAGLIERI and M. PELINO, J. Am. Ceram. Soc. 82 (1999) 3012.
I. GUTZOW, R. PASCOVA, A. KARAMANOV and J. SCHMELZER J. Mater. Sci. 33 (1998) 5265.
R. MÜLLER, E. D. ZANOTTO and V. M. FOKIN, J. Non-Cryst. Sol. 274 (2000) 208.
K. HERITAGE, C. FRISY and H. HOLFENDER, Rev. Sci. Instru. 59 (1988) 973.
G. R. ANSTIS, P. CHANTIKUL, B. R. LAWN and D. B. MARSHALL, J. Amer. Ceram. Soc. 64 (1981) 533.
G. P. EMILIANI and F. CORBARA, Tecnologia Ceramica. Le Tipologie. Gruppo Editoriale Faenza editrice s.p.a. Vol III, pp. 679-718.
L. BARBIERI, I. LANCELLOTTI, T. MANFREDINI, I. QUERALT, J. MA. RINCÒN and M. ROMERO, Fuel 78 (1999) 271.
International Organisation for standardisation ISO13006.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Brusatin, G., Bernardo, E., Andreola, F. et al. Reutilization of waste inert glass from the disposal of polluted dredging spoils by the obtainment of ceramic products for tiles applications. J Mater Sci 40, 5259–5264 (2005). https://doi.org/10.1007/s10853-005-4421-2
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/s10853-005-4421-2