The effect of La2O3 addition on the microstructure of partially remelted Mg-9Al-1Zn (AZ91D) alloy was studied. The results indicate that small amounts of La2O3 additions to AZ91D alloy refined the partially remelted microstructure and caused the formation of new phase- LaAl4 in the microstructure. Moreover, the grain size of the partially remelted alloys is decreased with the increasing of La2O3 addition. In as-cast microstructure the LaAl4 phases have two morphologies: needle-like and particle-shape. The presence of more LaAl4 phases, especially, the particle-shape LaAl4 which dispersedly distributed within the grains can induce more dislocations, which can result in the occurring of a large amount of recrystallizations. Moreover, these LaAl4 phases can also restrain the growth and combination of the recrystallizations and partially remelted initial grains during the subsequent heat-treatment.
Similar content being viewed by others
References
M. C. FLEMINGS, Metall. Trans. A 22 (1991) 957.
J. L. WANG, Y. H. SU and C.-Y.A. TSAO, Scripta Mater. 37 (1997) 2003.
C. P. CHEN, C.-Y. A. TSAO, Mater. Sci. Eng. A 337 (2002) 73.
F. CZERWINSKI, A. ZIELINSKA-LIPIEC, Acta Mater. 51 (2003) 3319.
F. CZERWINSKI, ibid. 50 (2002) 3265.
IDEM. Scripta Mater. 48 (2003) 327.
C. P. CHEN and C.-Y. A. TSAO, Acta Mater. 45 (1997) 1955.
E. TZIMAS and A. ZAVALIANGOS, Mater. Sci. Eng. A 289 (2000) 228.
J. I. LEE, G. H. KIM and H. T. LEE, Mater. Sci. Technol. 14 (1998) 770.
W. MAO, A. ZHAO, C. CUI, et al., Acta Metall. Sin. 35 (1999) 971.
T. J. CHEN, Y. MA, Y. HAO, , et al. Trans Nonferrous Met. Soc. China 11 (2001) 98.
E. TZIMAS and A. ZAVALIANGOS, Mater. Sci. Eng. A 289 (2000) 217.
K. P. YOUNG, C. P. KYONKA and J. A. COURTOIS, U. S. PATENT 4,415,374,1983.
Q. D. WANG, Y. Z. LU, X. Q. ZENG, W. J. DING and Y. P. ZHU, Mater. Sci. Eng. A 227 (1999) 109.
H. Y. WANG, Q. C. JIANG, X. L. LI, J. G. WANG, Q. F. GUAN and H. Q. LIANG, Mater. Res. Bull. 38 (2003) 1387.
Z. P. LOU, D. Y. SONG and S. Q. ZHANG, J. Alloys Comp. 230 (1995) 109.
G. PETTERSEN, H. WESTENGEN, R. HøIER and O. LOHNE, Mater. Sci. Eng. A 207 (1996) 115.
Y. Z. Lü, Q. D. WANG, X. Q. ZENG, W. J. DING, C. Q. ZHAI and Y. P. ZHU, Mater. Sci. Eng. A 278 (2000) 66.
W. W. DO, Y. S. SUN, X. G. MIN, F. XUE, M. ZHU and D. G. WU, ibid. A 356 (2003) 1.
L. Y. WEI and G. L. DUNLOP, J. Alloys Comp. 232 (1996) 264.
L. Y. WEI, G. L. DUNLOP and H. WESTENGEN, Mater. Sci. Technol. 12 (1996) 741.
T. W. HONG, S. K. KIM, H. S. HA, M. G. KIM, D. B. LEE and Y. J. KIM, ibid. 16 (2000) 887.
J. G. WANG, P. LU, H. Y. WANG and Q. C. JIANG, Mater. Lett. 58 (2004) 3852.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lu, P., Wang, J.G., Liu, J.F. et al. Effect of La2O3 addition on the microstructure of partially remelted Mg-9Al-1Zn alloy. J Mater Sci 40, 6429–6432 (2005). https://doi.org/10.1007/s10853-005-1628-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-005-1628-1