Abstract
Plasma-enhanced atomic layer deposition (PEALD) of tantalum nitride (TaN) thin films was investigated at a growth temperature of 230 °C using an alternating supply of tertiary-amylimido-tris(dimethylamido)tantalum (TAIMATA, Ta[NC(CH3)2C2H5][N(CH3)2]3) and hydrogen (H2) plasma. As the H2 plasma power increased from 75 to 175 W, the electrical resistivity of the films was improved from 1900 to 680 μΩ·cm, mainly due to the improved crystallinity. Moreover, the preferred orientation ratio between TaN (200) and TaN (111) planes also abruptly increased from 0.8 to 2.8 with increasing the H2 plasma power. This preferred orientation change of the films from (111) to (200) improves the adhesion properties between Cu and TaN, while the Cu diffusion barrier performance was not significantly affected.
Similar content being viewed by others
References
S. P. Murarka, R. J. Gutmann, Thin Solid Films 236, 257 (1993)
J. Torres, Appl. Surf. Sci. 91, 112 (1995)
Q. Xie, X. P. Qu, J. J. Tan, Y. L. Jiang, M. Zhou, T. Chen, G. P. Ru, Appl. Surf. Sci. 253, 1666 (2006)
S. H. Kwon, O. K. Kwon, J. S. Min, S. W. Kang, J. Electrochem. Soc. 153, G578 (2006)
F. Volpi, L. Cadix, G. Berthome, E. Blanquet, N. Jourdan, T. Torres, Microelectron. Eng. 85, 2068 (2008)
J. Y. Kim, K. W. Lee, H. O. Park, Y. D. Kim, H. Jeon, J. Korean. Phys. Soc. 45, 1069 (2004)
H. Kim, A. J. Kellock, S. M. Rossnagel, J. Appl. Phys. 92, 7080 (2002)
H. S. Chung, J. D. Kwon, S. W. Kang, J. Electrochem. Soc. 153, C751 (2006)
J. Li, H. S. Lu, Y. W. Wang, X. P. Qu, Microelectron. Eng. 88, 635 (2011)
Y. R. Shin, W. S. Kwack, Y. C. Park, J. H. Kim, S. Y. Shin, K. I. Moon, H. W. Lee, S. H. Kwon, Mater. Res. Bull. 47, 790 (2012)
L. Wang, Z. H. Cao, J. A. Syed, K. Hu, Q. W. She, X. K. Meng, Electrochem. Solid-State Lett. 15, H188 (2012)
X. P. Qu, J. J. Tan, M. Zhou, T. Chen, Q. Xie, G. P. Ru, B. Z. Li, Appl. Phys. Lett. 88, 151912 (2006)
J. W. Hong, K. I. Choi, Y. K. Lee, S. G. Park, S. W. Lee, J. M. Lee, S. B. Kang, G. H. Choi, S. T. Kim, U. I. Chung, J. T. Moon, Interconnect Technol. Conf. (2004). doi:10.1109/IITC.2004.1345665
K. H. Kim, S. J. Jeong, J. S. Yoon, Y. M. Kim, S. H. Kwon, ECS Trans. 25, 301 (2009)
T. Elangovan, S. Murugeshan, D. Mangalaraj, P. Kuppusami, S. Khan, C. Sudha, V. Ganesan, R. Divakar, E. Mohandas, J. Alloys Compd. 509, 6400 (2011)
G. Knuyt, C. Quaeyhaegens, J. D. Haen, L. M. Stals, Thin Solid Films 258, 159 (1995)
S. J. Jeong, Y. R. Shin, W. S. Kwack, H. W. Lee, Y. K. Jeong, D. I. Kim, H. C. Kim, S. H. Kwon, Surf. Coat. Technol. 205, 5009 (2011)
C. Wei, J. Y. Yen, Diam. Relat. Mater. 16, 1325 (2007)
M. H. Tsai, S. C. Sun, C. E. Tsai, S. H. Chuang, H. T. Chiu, J. Appl. Phys. 79, 6932 (1996)
Acknowledgments
This research was supported by the Global Frontier R&D Program (2013M3A6B1078874) on Center for Hybrid Interface Materials (HIM) funded by the Ministry of Science, ICT & Future Planning.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Lee, HJ., Park, JS. & Kwon, SH. Plasma-enhanced atomic layer deposition of tantalum nitride thin films using tertiary-amylimido-tris(dimethylamido)tantalum and hydrogen plasma. J Electroceram 36, 165–169 (2016). https://doi.org/10.1007/s10832-016-0015-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10832-016-0015-4